CN101429663B - 一种铂钽铂三层复合网及其制备方法 - Google Patents
一种铂钽铂三层复合网及其制备方法 Download PDFInfo
- Publication number
- CN101429663B CN101429663B CN2008102324724A CN200810232472A CN101429663B CN 101429663 B CN101429663 B CN 101429663B CN 2008102324724 A CN2008102324724 A CN 2008102324724A CN 200810232472 A CN200810232472 A CN 200810232472A CN 101429663 B CN101429663 B CN 101429663B
- Authority
- CN
- China
- Prior art keywords
- platinum
- tantalum
- layer
- plate
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种铂钽铂三层复合网,由铂钽铂三层金属构成,基层为钽层,所述基层的上下两面复合层为铂层,所述钽层的厚度大于铂层的厚度,所述铂层厚度为3μm~3mm。本发明还提供了一种制备上述复合网的方法,该方法采用二次爆炸复合方法制备复合坯料,然后采用轧制、中间退火、轧制、冲网、裁剪等工序加工出铂钽铂三层复合网,复层金属和基层金属达到冶金结合。本发明通过冶金加工的方法加工出铂钽铂三层复合网,复层和基层都由致密金属构成,无孔隙、漏洞,结合更紧密,复层金属和基体金属元素间相互扩散,达到冶金结合,电化学性能接近纯铂,适应在腐蚀环境中长时间使用,使用寿命可按纯铂的使用量计算,是一种理想的阳极材料。
Description
技术领域
本发明涉及一种电化学阳极材料及其制备方法,特别是涉及一种铂钽铂三层复合网及其制备方法。
背景技术
铂是化学性质最稳定的金属,也是最佳的阳极材料,而钽是击穿电压最高的“阀性”金属,当在含水的环境中阳极极化时,钽的表面上会立即形成一种绝缘氧化膜,起到自我保护的作用。当钽上复铂时,暴露的部分会形成保护性氧化膜,而阳极电化学反应仅在铂上出现。由于铂的化学性质极为稳定,所以消耗量极低。在含氯化物,硫酸盐的腐蚀环境中用铂阳极进行外加电流的阴极保护,具有高效率、高可靠性、长寿命的特点,也是一种较为理想的腐蚀防护方法。国内外同类型产品大多采用电镀、表面沉积、涂覆等技术方法获得,容易出现镀层不均匀、多孔,镀层与基体材料间结合力弱等问题。
发明内容
本发明的目的是克服现有技术的不足,提供一种复合层和基层都由致密金属构成,无孔隙、漏洞,复合层和基层结合更紧密的铂钽铂三层复合网,该复合网的复合层金属和基层金属元素间相互扩散,达到冶金结合,电化学性能接近纯铂,适应在腐蚀环境中长时间使用。
为解决上述技术问题,本发明采用的技术方案是:一种铂钽铂三层复合网,其特征在于由铂钽铂三层金属构成,基层为钽层,所述基层的上下两面复合层为铂层,所述钽层的厚度大于铂层的厚度,所述铂层厚度为3μm~3mm。
本发明还提供了一种铂钽铂三层复合网的制备方法,其特征在于制备过程为:
(1)将两块复合层铂板均轧制成厚度相同的片材,将两块厚度相同的片材剪裁成长宽尺寸与基层钽板相同的两片片材;
(2)爆炸复合:采用平行端起爆的方法先将步骤(1)中的一片铂板与基层钽板复合为一次复合铂钽板,经表面打磨处理并平整后将另一片铂板与所述一次复合铂钽板二次复合成二次复合铂钽铂板;
(3)将步骤(2)中的二次复合铂钽铂板用轧机进行轧制、退火,每道次加工率为10%-20%,两次退火间加工率为60%;
(4)冲网:用冲网机将步骤(3)中轧制后的铂钽铂板冲网为复合网;
(5)剪裁:用滚剪机将所述复合网分剪成网带。
本发明与现有技术相比具有以下优点:本发明通过冶金加工的方法加工出铂钽铂三层复合网,复层和基层都由致密金属构成,无孔隙、漏洞,结合更紧密,复层金属和基体金属元素间相互扩散,达到冶金结合,电化学性能接近纯铂,适应在腐蚀环境中长时间使用,使用寿命可按纯铂的使用量计算,是一种理想的阳极材料。
下面通过附图和实施例,对本发明做进一步的详细描述。
附图说明
图1为本发明制备工艺过程中制备的一次复合板的结构示意图。
图2为采用本发明制备方法制成的二次复合板的结构示意图。
具体实施方式
实施例1
以成品网铂层厚度3μm为例,成品网尺寸要求铂层厚度3μm,钽层厚度0.2mm,网宽30mm。
如图1和图2所示,加工过程为:
(1)准备铂板1、2,将铂板1、2轧制成厚度为0.3mm片材,剪裁成0.3×150×200mm片材两片。
(2)钽板3,尺寸为20×150×200mm一块。
(3)爆炸复合,采用平行端起爆的方法先将一块铂板1与钽板3复合,经表面打磨处理并平整后将另一块铂板2与一次复合板4二次复合成二次复合板5。
(4)将二次复合板5用D550型轧机进行轧制,每道次加工率为10%-20%,两次退火间加工率60%,终轧厚度0.206mm。
(5)冲网:采用200MM型冲网机冲网,铂钽铂三层复合网网格尺寸1×2mm。
(6)剪裁:采用ZTG-360型滚剪机将铂钽铂三层复合网分剪成30mm宽网带。
实施例2
以成品网铂层厚度10μm为例,成品网尺寸要求铂层厚度10μm,钽层厚度0.3mm,网宽50mm。
如图1和图2所示,加工过程为:
(1)准备铂板1、2,将铂板1、2轧制成厚度为1.0mm片材,剪裁成0.3×150×200mm片材两片。
(2)钽板3,尺寸为30×200×400mm一块。
(3)爆炸复合,采用平行端起爆的方法先将一块铂板1与钽板3复合,经表面打磨处理并平整后将另一块铂板2与一次复合板4二次复合成二次复合板5。
(4)将二次复合板5用D550型轧机进行轧制,每道次加工率为10%-20%,两次退火间加工率60%,终轧厚度0.32mm。
(5)冲网:采用200MM型冲网机冲网,铂钽铂三层复合网网格尺寸2×3mm。
(6)剪裁:采用ZTG-360型滚剪机将铂钽铂三层复合网分剪成50mm宽网带。
实施例3
如图1和图2所示,以成品网铂层厚度0.1mm为例,成品网尺寸要求铂层厚度0.1mm,钽层厚度1mm,网宽50mm。
加工过程为:
(1)准备铂板1、2,将铂板1、2轧制成厚度为1.0mm片材,剪裁成1.0×200×400mm片材两片。
(2)钽板3,尺寸为10×200×400mm一块。
(3)爆炸复合,采用平行端起爆的方法先将一块铂板1与钽板3复合,经表面打磨处理并平整后将另一块铂板2与一次复合板4二次复合成二次复合板5。
(4)将二次复合板5用D550型轧机进行轧制,每道次加工率为10%-20%,两次退火间加工率60%,终轧厚度1.2mm。
(5)冲网:采用CJ125型冲网机冲网,铂钽铂三层复合网网格尺寸3×4mm。
(6)剪裁:采用ZTG-360型滚剪机将铂钽铂三层复合网分剪成50mm宽网带。
Claims (1)
1.一种铂钽铂三层复合网的制备方法,复合网由铂钽铂三层金属构成,基层为钽层,所述基层的上下两面复合层为铂层,所述钽层的厚度大于铂层的厚度,所述铂层厚度为3μm~3mm,其特征在于制备过程为:
(1)将两块复合层铂板均轧制成厚度相同的片材,将两块厚度相同的片材剪裁成长宽尺寸与基层钽板相同的两片片材;
(2)爆炸复合:采用平行端起爆的方法先将步骤(1)中的一片铂板与基层钽板复合为一次复合铂钽板,经表面打磨处理并平整后将另一片铂板与所述一次复合铂钽板二次复合成二次复合铂钽铂板;
(3)将步骤(2)中的二次复合铂钽铂板用轧机进行轧制、退火,每道次加工率为10%-20%,两次退火间加工率为60%;
(4)冲网:用冲网机将步骤(3)中轧制后的铂钽铂板冲网为复合网;
(5)剪裁:用滚剪机将所述复合网分剪成网带。