CN101428990A - 一种新型透水砖 - Google Patents

一种新型透水砖 Download PDF

Info

Publication number
CN101428990A
CN101428990A CNA2008100720647A CN200810072064A CN101428990A CN 101428990 A CN101428990 A CN 101428990A CN A2008100720647 A CNA2008100720647 A CN A2008100720647A CN 200810072064 A CN200810072064 A CN 200810072064A CN 101428990 A CN101428990 A CN 101428990A
Authority
CN
China
Prior art keywords
ceramic tile
permeable brick
raw material
waste ceramic
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100720647A
Other languages
English (en)
Inventor
黄坚强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUJIAN SANJIAOZHOU CERAMIC AGGREGATE TECHNOLOGY Co Ltd
Original Assignee
FUJIAN SANJIAOZHOU CERAMIC AGGREGATE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUJIAN SANJIAOZHOU CERAMIC AGGREGATE TECHNOLOGY Co Ltd filed Critical FUJIAN SANJIAOZHOU CERAMIC AGGREGATE TECHNOLOGY Co Ltd
Priority to CNA2008100720647A priority Critical patent/CN101428990A/zh
Publication of CN101428990A publication Critical patent/CN101428990A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型透水砖，其以废瓷砖颗粒为主要原料，在此废瓷砖颗粒中添加粘结剂制备而成。本发明的透水砖以废瓷砖颗粒为主要原料，废瓷砖颗粒的强度堪比花岗岩，粒度较小的废瓷砖颗粒也具有很高的强度。用废瓷砖颗粒来制备透水砖，当选用粒度合适的废瓷砖颗粒为原料时，与现有的废混凝土颗粒相比，制备出来的透水砖既具有较高的透水性，又具有较高的强度。而且，废瓷砖颗粒断面较为光滑，进一步提高其透水性。

Description

一种新型透水砖
技术领域
本发明涉及建筑材料领域，尤其涉及一种透水砖。
背景技术
硬化路面虽然整齐耐用，但其最大缺点就是不透水。路面不透水，使得降雨时雨水对地下水的补充完全被阻断，会使下降的地下水位难以回升；相反，雨水从路面流失或被阳光蒸发掉，使城市变为地表干燥的缺水地区，加重城市扬尘污染，还会因地表干燥而给城市绿化带来很大困难。下大雨时，雨水排泄不畅，将在城市的大街小巷形成水淹状况，或者使城市周边地区产生水灾。而且雨水在路面淤积，一方面会引起交通堵塞，加重机动车尾气排放的污染，另一方面，雨水横流时会溶入大量城市污染物，如汽车排放的重金属、轮胎的磨损物、生活垃圾、建筑工地上的粉尘和化学物、城市草地喷洒的农药等等，这些雨水经管道直接排放到当地河流中，会导致大规模象SARS这类莫名其妙的病毒的产生。大雨时在路面形成的水坑常常会存在好几天，滋生蚊蝇，极大地影响着城市卫生。
上世纪90年代以来，国际上流行用透水性能好的透水砖铺砌办法来覆盖城市的路面。例如在德国，人们正在将以前铺设的一些硬化路面改为透水性路面，以增强城市的生态效果。
现已有采用废混凝土作为主要原料的透水砖，其工艺过程为：废混凝土破碎→筛分→清洗→添加粘结剂→搅拌混合→静压成型→养护→成品，为了使透水砖外形美观、颜色鲜艳，达到美化环境的效果，将透水砖分为两层制备：面层和底层，面层还增加了颜料制成彩色的砖面。现有的这种透水砖，其采用废混凝土作为主要原料，为了使透水砖获得较好的透水性，所用的废混凝土颗粒的粒径不能太大，但若废混凝土颗粒的粒径较小，则制备出的透水砖强度不够，透水性与强度两者无法兼得。而且，废混凝土颗粒的断面较粗糙，即使是采用粒径较小的废混凝土颗粒所制备出来的透水砖，其透水性也不太好。
发明内容
本发明的目的是提供一种透水性好且强度高的新型透水砖。
本发明的技术方案是这样的：一种新型透水砖，以废瓷砖颗粒为主要原料，在此废瓷砖颗粒中添加粘结剂制备而成。
透水砖由面层和底层组成，其中，面层的原料包括：175-185重量份的白水泥、790-810重量份粒径为2-5mm的废瓷砖颗粒、18-22重量份的颜料和90-100重量份的水；底层的原料由1350-1380重量份的普通水泥、800-830重量份的砂、4600-4640重量份粒径为6-10mm的废瓷砖碎粒和400-420重量份的水组成。
上述面层的原料还包括8-10重量份的光亮剂。
采用上述方案后，本发明的透水砖以废瓷砖颗粒为主要原料，废瓷砖颗粒的强度堪比花岗岩，粒度较小的废瓷砖颗粒也具有很高的强度。用废瓷砖颗粒来制备透水砖，当选用粒度合适的废瓷砖颗粒为原料时，与现有的废混凝土颗粒相比，制备出来的透水砖既具有较高的透水性，又具有较高的强度。而且，废瓷砖颗粒断面较为光滑，进一步提高其透水性。
具体实施例
本发明的一种新型透水砖，由面层和底层一体浇注压制而成，以制一块300*300*50mm的透水砖为例。
实施例一：
面层的原料包括180克的白水泥、800克粒径为2-5mm的废瓷砖颗粒、19克的颜料、9克的光亮剂和90-100克的水；水在此范围内按经验加，以不出现漂浆，具有一定粘性为准。底层的原料由1360克的普通水泥(325R)、816克的砂、4620克粒径为6-10mm的废瓷砖碎粒和400-420克的水组成。水在此范围内按经验加，以不出现漂浆，具有一定粘性为准。
实施例二：
面层的原料包括175克的白水泥、810克粒径为2-5mm的废瓷砖颗粒、18克的颜料、10克的光亮剂和90-100克的水；水在此范围内按经验加，以不出现漂浆，具有一定粘性为准。底层的原料由1350克的普通水泥(325R)、830克的砂、4600克粒径为6-10mm的废瓷砖碎粒和400-420克的水组成。水在此范围内按经验加，以不出现漂浆，具有一定粘性为准。
实施例三：
面层的原料包括185克的白水泥、790克粒径为2-5mm的废瓷砖颗粒、22克的颜料、8克的光亮剂和90-100克的水；水在此范围内按经验加，以不出现漂浆，具有一定粘性为准。底层的原料由1380克的普通水泥(325R)、800克的砂、4640克粒径为6-10mm的废瓷砖碎粒和400-420克的水组成。水在此范围内按经验加，以不出现漂浆，具有一定粘性为准。
生产时，将面层的原料混合搅拌在一起，然后浇注成型；再将底层的原料混合搅拌在一起，然后浇注在成型的面层上，经过液压机静压成型，然后按常规方法进行脱模和养护即可。
本发明的透水砖以废瓷砖颗粒为主要原料，废瓷砖颗粒的强度堪比花岗岩，粒度较小的废瓷砖颗粒也具有很高的强度。用废瓷砖颗粒来制备透水砖，当选用粒度合适的废瓷砖颗粒为原料时，与现有的废混凝土颗粒相比，制备出来的透水砖既具有较高的透水性，又具有较高的强度。而且，废瓷砖颗粒断面较为光滑，进一步提高其透水性。

Claims (3)

1、一种新型透水砖，其特征在于：以废瓷砖颗粒为主要原料，在此废瓷砖颗粒中添加粘结剂制备而成。
2、根据权利要求1所述的一种新型透水砖，其特征在于：透水砖由面层和底层组成，其中，面层的原料包括：175-185重量份的白水泥、790-810重量份粒径为2-5mm的废瓷砖颗粒、18-22重量份的颜料和90-100重量份的水；底层的原料由1350-1380重量份的普通水泥、800-830重量份的砂、4600-4640重量份粒径为6-10mm的废瓷砖碎粒和400-420重量份的水组成。
3、根据权利要求2所述的一种新型透水砖，其特征在于：上述面层的原料还包括8-10重量份的光亮剂。
CNA2008100720647A 2008-10-31 2008-10-31 一种新型透水砖 Pending CN101428990A (zh)