CN101422974B - 太阳能反光膜及其制备方法 - Google Patents

太阳能反光膜及其制备方法 Download PDF

Info

Publication number
CN101422974B
CN101422974B CN2008101841225A CN200810184122A CN101422974B CN 101422974 B CN101422974 B CN 101422974B CN 2008101841225 A CN2008101841225 A CN 2008101841225A CN 200810184122 A CN200810184122 A CN 200810184122A CN 101422974 B CN101422974 B CN 101422974B
Authority
CN
China
Prior art keywords
solar energy
base material
membrane
reflective film
aluminium film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008101841225A
Other languages
English (en)
Other versions
CN101422974A (zh
Inventor
徐显波
谢二庆
宋曦
宋杰
侯晨光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lanzhou University
Original Assignee
Lanzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lanzhou University filed Critical Lanzhou University
Priority to CN2008101841225A priority Critical patent/CN101422974B/zh
Publication of CN101422974A publication Critical patent/CN101422974A/zh
Application granted granted Critical
Publication of CN101422974B publication Critical patent/CN101422974B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明的目的是提供一种太阳能反光膜，其包括基材和铝膜，并在铝膜上均匀涂有1um～2um厚的氟碳涂料。其制备方法是先用固体胶将基材与铝膜粘合在一起，再采用静电喷涂技术将氟碳涂料喷涂于铝膜上，使铝膜表面形成一层均匀，致密，光滑的保护涂层，大大延长了铝膜的使用寿命；同时由于氟碳涂层化学稳定性好，能够抗光催化剂的氧化还原作用，附着力牢固，不致于短期粉化、脱落。据测试，本发明反光膜的使用寿命在10～12年；本发明的太阳能反光膜，反光率高。经测定，本发明太阳能反光膜的反光率高可达85％以上。

Description

太阳能反光膜及其制备方法
技术领域
本发明属于太阳能应用技术领域，涉及一种用于收集太阳能的反光膜，本发明同时还涉及该反光膜的制备方法。
背景技术
目前，用来收集太阳能的反光膜有金属薄膜，如铝薄膜、锡薄膜等，直接的金属薄膜易破损，且有漏光现象，反光率低。也有是在某种基材的一面镀有金属薄膜，另一面贴有底衬面，这种反光膜其基材与底衬面结合较差，容易脱落；而且，在基材的一面上镀金属薄膜的反光膜，都是单面镀膜，同样存在着漏光现象，反光低的问题，特别是镀膜在使用中被划损后，划损部分没有反光性。
中国专利申请200810001420.6公开了一种反光膜，其选用4～5丝厚的PET高透明塑料薄膜做基材，用真空镀膜机在基材的双面真空镀铝，在基材的一个镀有铝膜的面上涂油性压敏胶，将底衬面粘贴上去；在基材的另一个镀有铝膜的面上用涂布机辊涂加有550固化剂的有机硅101玻璃树脂。该反光膜的表面涂层硬度到达4H以上，反光率可达85％，反光膜可使用三年以上。
氟碳涂料是以氟树脂为主要成膜物质的涂料，又称氟碳漆、氟涂料、有机氟涂料、氟树脂涂料等。氟碳涂料由于氟元素电负性大，碳氟键能强，因此它不但具有超强的耐候性、耐热性、耐低温性及耐化学品性。其中FEVE氟碳涂料可以在常温下固化，通过刷涂、辊涂、喷涂等普通涂装方法可以涂覆在各种基材表面，有着很大的应用领域。但是，其在太阳能利用方面的应用尚未报道。
发明内容
本发明的目的是提供一种太阳能反光膜。
本发明的另一目的是提供该太阳能反光膜的制备方法。
本发明的太阳能反光膜，包括基材和铝膜，在铝膜上均匀涂有1um～2um厚的氟碳涂层。
所述基材采用2mm～3mm厚的PVC塑料板。
所述铝膜的厚度为200～300um。
所述氟碳涂料为FEVE氟碳涂料。
本发明太阳能反光膜的制备方法，是先用固体胶将基材与铝膜粘合在一起，再采用静电喷涂技术将氟碳涂料喷涂于铝膜上，使铝膜表面生长一层1um～2um厚的氟碳涂料。
所述静电喷涂的工艺条件为：喷腔距工件的距离为350mm～400mm，电压为60kv～80kv，喷气压力是0.3～0.5Mpa。
本发明采用电子机械式升降机运载自动静电空气喷枪，实行氟碳涂料的自动喷涂。
本发明与现有技术相比具有以下优点：
1、本发明以PVC塑料板为基材，以铝膜为反射面，并在铝膜上喷涂有氟碳涂层，使铝膜表面形成一层均匀，致密，光滑的保护涂层，大大延长了铝膜的使用寿命；同时由于氟碳涂层化学稳定性好，能够抗光催化剂的氧化还原作用，附着力牢固，不致于短期粉化、脱落。据测试，本发明反光膜的使用寿命在10～12年。
2、本发明的太阳能反光膜，反光率高。由于氟碳涂层的光透射率高，故对铝膜的反光性能的影响极小。经测定，本发明太阳能反光膜的反光率高可达85％以上。
3、本发明采用静电喷涂技术，将氟碳涂料喷涂于铝膜上，由于静电吸附，使涂料吸附力特别强，可有效地防止涂料逃逸。
4、本发明采用用PVC塑料板作基材，质量轻，易成型，可根据需要制备成不同形状的反光膜。
附图说明
图1为本发明太阳能反光膜的结构图
1——PVC塑料板  2——胶层  3——铝膜  4——氟碳涂层
具体实施方式
一种太阳能反光膜，依次包括PVC塑料板基材、铝膜和FEVE氟碳涂层，其中PVC塑料板的厚度为2mm～3mm，铝膜的厚度为200～300um，PVC塑料板与铝膜采用固体胶牢牢地粘合在一起。氟碳涂层的厚度为1um～2um，其均匀喷涂在铝膜上。
本发明太阳能反光膜的制备方法，是先用固体胶将基材与铝膜粘合在一起，再采用静电喷涂技术将氟碳涂料喷涂于铝膜上，使铝膜表面生长一层1um～2um厚的氟碳涂料。
静电喷涂采用电子机械式升降机运载自动静电空气喷枪，实行氟碳涂料的自动喷涂。整个表面处理工艺包括表面清洁、喷漆、固化等过程，在铝膜表面形成一层均匀，致密，光滑的保护涂层。喷涂的工艺条件控制在：喷腔距工件的距离为350mm～400mm，电压为60kv～80kv，喷气压力是0.3～0.5Mpa。

Claims (6)

1.一种太阳能反光膜，包括基材和铝膜，其特征在于：采用静电喷涂技术在铝膜上均匀涂有1um～2um厚的氟碳涂层；所述静电喷涂的工艺条件为：喷腔距工件的距离为350mm～400mm，电压为60kv～80kv，喷气压力是0.3～0.5Mpa。
2.如权利要求1所述太阳能反光膜，其特征在于：所述基材为2mm～3mm厚的PVC塑料板。
3.如权利要求1所述太阳能反光膜，其特征在于：所述铝膜的厚度为200～300um。
4.如权利要求1所述的太阳能反光膜，其特征在于：所述氟碳涂层为FEVE氟碳涂层。
5.如权利要求1所述太阳能反光膜的制备方法，是先用固体胶将基材与铝膜粘合在一起，再采用静电喷涂技术将氟碳涂料喷涂于铝膜上，使铝膜表面生长一层1um～2um厚的氟碳涂层。
6.如权利要求5所述太阳能反光膜的制备方法，其特征在于：所述静电喷涂的工艺条件为：喷腔距工件的距离为350mm～400mm，电压为60kv～80kv，喷气压力是0.3～0.5Mpa。
CN2008101841225A 2008-12-08 2008-12-08 太阳能反光膜及其制备方法 Expired - Fee Related CN101422974B (zh)