CN101418202B - 竹地板粘合剂及制备方法 - Google Patents

竹地板粘合剂及制备方法 Download PDF

Info

Publication number
CN101418202B
CN101418202B CN2008103056732A CN200810305673A CN101418202B CN 101418202 B CN101418202 B CN 101418202B CN 2008103056732 A CN2008103056732 A CN 2008103056732A CN 200810305673 A CN200810305673 A CN 200810305673A CN 101418202 B CN101418202 B CN 101418202B
Authority
CN
China
Prior art keywords
article
adhesive
portions
isocyanic ester
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008103056732A
Other languages
English (en)
Other versions
CN101418202A (zh
Inventor
张继强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Lvdian Fine Chemical Co., Ltd.
Original Assignee
HUZHOU LVDIAN FINE CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUZHOU LVDIAN FINE CHEMICAL CO Ltd filed Critical HUZHOU LVDIAN FINE CHEMICAL CO Ltd
Priority to CN2008103056732A priority Critical patent/CN101418202B/zh
Publication of CN101418202A publication Critical patent/CN101418202A/zh
Application granted granted Critical
Publication of CN101418202B publication Critical patent/CN101418202B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种竹地板粘合剂及其制备方法。本发明生产1000重量份粘合剂主剂是用以下原料：多元醇80～120份、乳化剂1～3份、异氰酸脂10～20份、丙烯酸乳液150～250份、防腐剂1～4份和足量的水，经加热搅拌多元醇和乳化剂，滴加异氰酸脂和丙烯酸乳液，再加入防腐剂，制备而成。本发明具有以下优点：产品易于生产，生产成本低，粘合剂的粘度和流动性适宜，手刷和机滚均很方便，产品活性期长，陈放时间长，使用方便，生产效率高，制作的竹地板可以100％达到欧洲E0标准和日本环保产品标准。

Description

竹地板粘合剂及制备方法
技术领域
本发明涉及一种地板生产用的粘合剂，特别是竹地板生产用的粘合剂。
背景技术
目前，市场上还没有用于竹地板生产的专用粘合剂。竹地板生产厂家为了生产甲醛含量不超标的竹地板，一般是采用进口的供木地板生产用的木材拼版胶作为竹地板粘合剂。这种拼版胶不但价格昂贵，而且由于不是针对竹地板生产研制的专用粘合剂，存在诸如粘合剂的粘度偏大，流动性差，手刷和机滚均有难度；活性期短，应用不方便；陈放时间短，影响生产效率等缺点。由于以上原因，所制竹地板的级别不高，达到欧洲E0标准和日本环保产品标准的合格率较低。
发明内容
本发明的目的在于，提供一种竹地板粘合剂及制备方法。本发明的竹地板粘合剂具有生产成本低、流动性好、活性期长和陈放时间长的特点。
本发明的技术方案。竹地板粘合剂，其特征在于：生产1000重量份粘合剂是加入以下重量配比的原料制成；
多元醇    80～120份  乳化剂       1～3份
异氰酸酯  10～20份   丙稀酸乳液   150～250份
防腐剂    1～4份
其余为水。
上述的竹地板粘合剂中，生产1000公斤重量份粘合剂较好的是加入以下重量配比的原料制成；
多元醇    90～110份  乳化剂      1～2份
异氰酸酯  13～18份   丙稀酸乳液  190～210份
防腐剂    1～3份
其余为水。
前述的竹地板粘合剂中，所述的多元醇最好是聚乙烯醇。
前述的竹地板粘合剂中，所述的异氰酸酯最好是芳香族异氰酸酯。
前述竹地板粘合剂的制备方法，其特征在于：按以下步骤制备；
A、将多元醇加入水浸泡，加热溶化后降至常温，加入乳化剂搅拌均匀，得A品；
B、向A品滴加异氰酸酯和丙稀酸乳液，搅拌均匀后得B品；
C、向B品加入防腐剂，拌匀后得成品。
上述的制备方法中，所述的步骤A中，加热温度不超过97摄氏度。
前述的制备方法中，所述的步骤B比较好的是，在搅拌状态下，向A品滴加异氰酸酯和丙稀酸乳液，搅拌均匀后得B品。
与现有技术相比，本发明采用合理的原料及配比，再加之适宜的制备方法，得到的竹地板粘合剂，具有非常好的技术效果。本发明具有以下优点：
1)产品易于生产、生产成本低，每吨不超过9500元。拼版胶价格每吨高达16000元，有的在2万多元。
2)产品是供竹地板生产用的专用粘合剂，粘合剂的粘度和流动性适宜，手刷和机滚均很方便。
3)产品活性期长、大于1.5小时，应用方便；陈放时间长、达到25分钟以上；可提高竹地板生产效率。拼版胶的活性期短、小于1小时，陈放时间短、小于15分钟，因此应用不方便，影响竹地板的生产效率。
4)利用本发明产品制作的竹地板的级别高，可以完全达到欧洲E0标准和日本环保产品标准，合格率可达100％。
5)产品无污染。
具体实施方式
下面结合实施例对本发明作进一步的详细说明，但并不作为对本发明做任何限制的依据。
实施例。以生产1000kg竹地板粘合剂的主剂为例，准备以下原料：多元醇95kg、乳化剂2kg、异氰酸酯16kg、丙稀酸乳液200kg和防腐剂2kg，其余为水；按以下步骤制备。
A、将多元醇加入水中加热至不超过97摄氏度搅拌溶化后，降至常温加乳化剂，搅拌均匀，使多元醇充分溶解，得A品；
B、在搅拌状态下，向A品滴加异氰酸酯和丙稀酸乳液，搅拌均匀后得B品；
C、向B品加入防腐剂，拌匀后得成品。
成品为主剂，使用时以异氰酸酯(最好是芳香族异氰酸酯)为固化剂，按主剂∶固化剂＝100∶14～15的比例混匀后使用。
本例中。多元醇比较好的是用聚乙烯醇；异氰酸酯最好是使用芳香族异氰酸酯，如烟台万华公司、拜尔公司、巴斯夫公司的产品；乳化剂可用市售的T×-10、OP-10乳化剂；丙稀酸乳液可用市售浓度为30％～60％的产品。防腐剂可用市售的卡松系列防腐剂。

Claims (4)

1.一种竹地板粘合剂，其特征在于：生产1000重量份粘合剂是加入以下重量配比的原料制成；
多元醇    90～110份  乳化剂      1～2份
异氰酸酯  13～18份   丙烯酸乳液  190～210份
防腐剂    1～3份
其余为水；
所述的多元醇是聚乙烯醇；所述的异氰酸酯是芳香族异氰酸酯。
2.根据权利要求1所述竹地板粘合剂的制备方法，其特征在于：按以下步骤制成；
A、将多元醇加入水浸泡，加热溶化后降至常温，加入乳化剂搅拌均匀，得A品；
B、向A品滴加异氰酸酯和丙烯 酸乳液，搅拌均匀后得B品；
C、向B品加入防腐剂，拌匀后得成品。
3.根据权利要求2所述的制备方法，其特征在于：所述的步骤A中，加热温度不超过97摄氏度。
4.根据权利要求2所述的制备方法，其特征在于：所述的步骤B是，在搅拌状态下，向A品滴加异氰酸酯和丙烯 酸乳液，搅拌均匀后得B品。 
CN2008103056732A 2008-11-21 2008-11-21 竹地板粘合剂及制备方法 Active CN101418202B (zh)