CN101417830A - Filter material for micro electrolysis and preparation method thereof - Google Patents
Filter material for micro electrolysis and preparation method thereof Download PDFInfo
- Publication number
- CN101417830A CN101417830A CNA2008100424732A CN200810042473A CN101417830A CN 101417830 A CN101417830 A CN 101417830A CN A2008100424732 A CNA2008100424732 A CN A2008100424732A CN 200810042473 A CN200810042473 A CN 200810042473A CN 101417830 A CN101417830 A CN 101417830A
- Authority
- CN
- China
- Prior art keywords
- powder
- magnesium
- filter material
- water
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a filter material used by brine micro-electrolysis, which comprises the following components by weight percent: 20-40 percent of 50-500nm metal magnesium powder, 20-40 percent of 50-500nm tourmaline powder, 10-20 percent of magnesia powder, 1-10 percent of silicate, 1-15 percent of magnesium nitride powder, 1-20 percent of 50-100 meshes of alkali stone and 0.1-5 percent of 85000ppm unit of nano-silver efficient antibacterial powder. The invention further provides a filter core prepared by the filter material and a preparation method thereof, wherein the method comprises the following steps of: mixing the components, stirring, adding water, preparing into spheres and naturally solidifying into nanometer metal magnesium particles. The filter core has the advantages of lower cost, high service efficiency and zero environment pollution, which can be recovered to be used in fish pond aquaculture.
Description
Technical field
The present invention relates to water treatment field, specifically, the present invention relates to a kind of filter material for micro electrolysis and preparation method thereof.
Background technology
Make constant progress and the raising of living standard along with socioeconomic, people are also more and more higher to the safety of drinking water standard-required.The process for purifying water that generally adopts mainly contains following several at present.
Based on photochemical catalysis drink water purifying technology.After the tap water process chlorination germicidal treatment, cause the generation of carcinogenic in a large number organic chloride, make that the water quality of tap water and mouthfeel thereof are all very poor.Do not carry out organic purifying treatment in the domestic tap water.Photocatalysis technology can sterilization and is purified organic poison; Can under without the situation of chlorine, carry out the purification of sterilization and organic pollutant, improve the quality and the mouthfeel of tap water tap water; Also can utilize photocatalysis technology direct purification swimming pool and not need to add chemical agent.This kind technology can develop into the terminal light catalytic purifying assembly in family, hotel, or large-scale purification assembly, has vast market prospect.
The nano anti-biotic material water purification technology.Develop the antibiotic and sterilization material of water-insoluble nano inorganic, adopt the inorganic composite oxide technology of preparing, synthetic have antibiotic and nano inorganic material and inorganic porous membrane bactericidal property, has been applied to the sterilizing filter etc. that water purifies and is used for antibiotic electrical equipment and furniture, recirculated cooling water, snitaryware, anti-biological weapon at present.
In addition, the tap water that has occurred has the tubular water purification, and tap water strainer etc. carry out impurity screening, purification, sterilization, sterilization and even add the nutrition and health care composition tap water.A few days ago, the water tumbler product that has also occurred the pH value function of some water that change on the market.For example, Tourmaline active gut purge cup, the Tourmaline ore at the mineral magnetic field that utilization covers and the cup end, produce permanent-magnetic field, under the effect in the driving fit loop of vacuum, produce eddy current magnetoelectricity field gravitation, cooperate the horizontal conductive of wall of cup nanometer silver coating to promote mutually, come brine electrolysis and discharge a large amount of active elements, and then be weakly alkaline biological running water common tap water electrolysis.
But most of water purifier material is not enough to little electrolysis of water.
Brine electrolysis, in the water, positively charged ions such as the calcium of positively charged, potassium, MAGNESIUM METAL, sodium are pooled to negative electrode becomes the alkaline electrolysis reductive water that has (-) current potential to tap water after be about to purifying by having galvanic electrolytic separation equipment (according to the same sex principle that there is a natural attraction between the sexes of repelling each other); And have chlorine, haloform, phosphoric acid, sulfuric acid, the nitric acid of negative potential ... be pooled to anode Deng negatively charged ion and become the acidic oxidation water that has () current potential.
Though in general food and drinking-water, calcium, potassium, MAGNESIUM METAL are arranged also ... in mineral substance, but mostly the kind material is the complex morphological that stability is very strong, is difficult for being absorbed by the body; And its mineral substance acid group of the reductive water of brine electrolysis has been separated into ionic forms, and have reduction (-) current potential, be absorbed easily after entering human body, and can constantly look for acid toxin and the metabolite combination that has carbonium in vivo, excrete rapidly, therefore, the long-term drinking electrolytic reduction water, physique be can effectively improve, the antibody of human body and the vis medicatrix naturae of nature promoted.We emphasize that again and again electrolytic reduction water is not only clean water, and it can improve health physique, can have curative effect to each disease, mainly is its three big characteristics:
Be alkalescence: water when electrolysis, the calcium in the water, potassium, MAGNESIUM METAL, sodium ... after waiting positive ion to be drawn by negative electrode, hydroxide ion increases and alkalize, can in and acid poison in the body, change acidic constitution.
Micromolecular water: the molecular grouping of general water is about 13-16 molecular grouping, and water clusters is contracted to 5-6 molecular grouping after electrolysis, and mineral substance is ionized, solvency power, seepage force are strong, human body absorbs easily, and more effectively the old refuse in scavenger cell and the blood enhances metabolism.
Have reduction potential: have-the following surprising redox potential of 250mv, can eliminate free radical (active oxygen) rapidly, the neutralizing acid poison is thoroughly removed human body cause illness's factor.The effect gastroenteropathy of alkaline water: drink alkaline water can in and hydrochloric acid in gastric juice, long-term drinking can be improved maldigestion, hyperchlorhydria, symptom gouts such as diarrhea: the uric acid that each hundred milligrams of solubilized of alkaline water are 21.3 milligrams, be more than two times of general drinking-water, but the uric acid reducing value of often drinking water, diabetes, the obese person uses, only in the outward appearance luxury of equipment, aspects such as power consumption and automatic water outlet degree are at war with, not only bring a high price, also hindered the practical popularization of social enviroment protection of Water purifier, its result of use is unsatisfactory, and some electricity consumption produces ozone sterilization, with the water that produces electrolysis with electrode, not only waste energy, the water cost is also high, as a large amount of uses, also can cause to a certain degree destruction to environment, and more renew cartridge prices are rather stiff.
Summary of the invention
For overcoming described existing problem, the object of the present invention is to provide a kind of filter material for micro electrolysis and preparation method thereof, described filtering material cost is lower, and the service efficiency height is free from environmental pollution, and recovery can be made the fish pond aquaculture and use.The tap water of its production can meet or exceed the healthy water standard that national tap water Health Professions Council advocates.
For reaching described purpose, technical scheme of the present invention realizes like this:
A kind of filter material for micro electrolysis is characterized in that, comprises the MAGNESIUM METAL powder of following composition: 50-500nm: 20-40% by weight percentage; The tourmaline powder of 50-500nm: 20-40%; Magnesium oxide powder: 10-20%; Silicate: 1-10%; Magnesium nitride powder: 1～15%; 50-100 purpose alkali stone: 1～20%; Nano silver high-efficiency antibacterial powder: 0.1-5%.
Preferably, the MAGNESIUM METAL powder of 50-500nm: 25-35% in the described filtering material; The tourmaline powder of 50-500nm: 25-35%; Magnesium oxide powder: 15-10%; Silicate: 3-5%; Magnesium nitride powder: 5～10%; 50-100 purpose alkali stone: 5～10%; Nano silver high-efficiency antibacterial powder: 0.2-2%.
Preferably, described filtering material also comprises the KDF filtrate of 50～200nm: 5-10%.
Preferably, described MAGNESIUM METAL powder is selected 150-200nm for use; Described tourmaline powder is selected 150-200nm for use; Described magnesium oxide powder is selected 100～200nm for use, and described silicate is selected 100～300nm for use; Described magnesium nitride powder is selected 100～200nm for use; Described nano silver high-efficiency antibacterial powder is selected 85000ppm unit for use.
The chemical property of reactive metal magnesium:
1, with the reaction of non-metal simple-substance: 2Mg+O
2==2MgO 3Mg+N
2=Mg3N
2
2, with the reaction of water: Mg+2H
2O=Mg (OH) 2+H
2(heating)
3, with sour reaction: Mg+2HCl+MgCl
2+ H
2
4, with the reaction of oxide compound: 2Mg+CO
2=2MgO+C (lighting)
Under the activation of alkaline ore powder, MAGNESIUM METAL is a kind of organism normal activities and requisite element of metabolic process of participating in.MAGNESIUM METAL influences the multiple biological function of cell: influence the transhipment of potassium ion and calcium ion, the transmission of adjustment signal participates in the synthetic of energy metabolism, protein and nucleic acid; Can be by complexing negative charge group, especially the phosphate group in the Nucleotide is brought into play the 26S Proteasome Structure and Function of keeping material; The regulation and control of the activation of katalaze enzyme and inhibition and cell cycle, cell proliferation and differentiation; MAGNESIUM METAL also participates in keeping genomic stability, and takes place relevant with body oxidative stress and tumour.
Alkali stone is concentrated crystal soda (Na
2CO
3NaHCO
32H
2O).
Nano-silver antibacterial powder is the antibiotic powder of AGP-ZP003 inorganic nano-silver, is to be carrier with the zirconium phosphate, makes by ion-exchange techniques, and its characteristics are anti-microbial property excellence, high temperature resistant, nondiscoloration, and effect is lasting, broad-spectrum antimicrobial, safety non-toxic.Described nano silver high-efficiency antibacterial powder preferably uses 85000ppm unit
Tourmalinite is the special polarity xln of a kind of structure, contains more than 10 kind of trace elements favourable to human body such as MAGNESIUM METAL, aluminium, iron, boron.Self can forever discharge negative ion and far infrared rays, has special electromagnetic wave proof function.The high negative oxygen ion subset running water that produces through tourmalinite will assist human body to adjust in the body negative ion voluntarily to normal level, the pressure that helps to releive, promote the intelligence agility and will promote function of immune system.
Kai Defei (KDF) is highly purified copper/zinc alloy granules, it carries out water treatment work by little electrochemical oxidation-reduction reaction, when contacting with water, two kinds of metals in the alloy constitute countless little galvanic cell systems on submicroscopic yardstick, this material has powerful response capacity and the speed of response that is exceedingly fast in water, can remove in the water up to metal ion and compound such as dissolved lead, mercury, nickel, chromium in 99% chlorine and the water, to suppress bacterium, fungi, dirt, algae to grow effect distinguished, be used to pre-treatment, the main processing and sewage treatment equipment.KDF improves or replaces prior art, and the spoke degree has prolonged lifetime of system greatly, has reduced heavy metal, microorganism, dirt, has reduced total expenses, simplifies system maintenance.
The present invention also provides a kind of preparation method of described filter material for micro electrolysis, it is characterized in that, may further comprise the steps: with MAGNESIUM METAL powder, tourmaline powder, magnesium oxide powder, magnesium nitride powder, alkali stone flour body, silicate powder, after mixing, stir, efficient nano silver antimicrobial powder adds entry, make spherical particle, become nano metal magnesium grain through natural coagulation.Institute adds the water gross weight and accounts for filter core gross weight 1～3.5%.
Preferably, use roller forming machine rolling moulding to make spherical particle.
Preferably, described spherical particle diameter is the 3-30 millimeter.
Filtering material of the present invention has: the magnetizing function of negative potential water; The weakly alkaline function; Activation broad-spectrum antimicrobial function; Other purification functions.Tap water is carried out little electrolysis, obtain the active function at interface, the stabilization of chlorine, the passivation of iron, reducing, removal silicon-dioxide and the binding various effects such as (microorganism aggregates) of water.Simultaneously, micro-electrolytic water can dwindle the water molecules bundle.Water molecules (H
2O) be not Individual existence, its molecule can mutually combine, and forms molecular beam.The less water of molecular beam can be removed chlorine or impurity, and taste is good, and can improve the seepage force of health.In addition, cost of the present invention is lower, and the service efficiency height is free from environmental pollution, and recovery can be made the fish pond aquaculture and use.The tap water of its production can reach the healthy water standard that national tap water Health Professions Council advocates.
Embodiment
Below for a more detailed description with embodiment to the present invention.These embodiment only are the descriptions to best mode for carrying out the invention, scope of the present invention are not had any restriction.
Embodiment 1:
The MAGNESIUM METAL powder of 150-200nm: 20g; The tourmaline powder of 150-200nm: 20g; 200-250 magnesium oxide powders: 10g; The silicate of 150-200nm: 10g; The magnesium nitride powder of 150-200nm: 10g; 80-100 purpose alkali stone: 10g; Nano silver high-efficiency antibacterial powder 85000ppm unit: 1g.
To add entry after above composition mixing, the stirring, roller forming machine rolling moulding is made spherical, becomes nano metal magnesium grain through natural coagulation, and particle diameter is 3-10mm.
Embodiment 2:
The MAGNESIUM METAL powder of 200-250nm: 35g; The tourmaline powder of 250-300nm: 30g; 200-250nm magnesium oxide powder: 15g; The silicate of 200-250nm: 10g; The magnesium nitride powder of 200-250nm: 15g; 50-80 purpose alkali stone: 20g; Nano silver high-efficiency antibacterial powder 85000ppm unit: 0.5g.
To add entry after above composition mixing, the stirring, roller forming machine rolling moulding is made spherical, becomes nano metal magnesium grain through natural coagulation, and particle diameter is 7-16mm.
Embodiment 3:
The MAGNESIUM METAL powder of 250-400nm: 25g; The tourmaline powder of 250-400nm: 35g; The magnesium oxide powder of 200-250nm: 8g; 200-250nm silicate: 4g; The magnesium nitride powder of 200-250nm: 5g; 70-100 purpose alkali stone: 10g; Nano silver high-efficiency antibacterial powder 85000ppm unit: 1.5g.
To add entry after above composition mixing, the stirring, roller forming machine rolling moulding is made spherical, becomes nano metal magnesium grain through natural coagulation, and particle diameter is 10-30mm.
Embodiment 4:
The MAGNESIUM METAL powder of 250-400nm: 35g; The tourmaline powder of 250-400nm: 25g; 200-250 magnesium oxide powder: 12g; 1500-250 silicate: 5g; The magnesium nitride powder of 100-250nm: 8g; 50-100 purpose alkali stone: 6g; The nano silver high-efficiency antibacterial powder 85000ppm unit of 200-250nm: 1g.
To add entry after above composition mixing, the stirring, roller forming machine rolling moulding is made spherical, becomes nano metal magnesium grain through natural coagulation, and particle diameter is 10-30mm.
Embodiment 5:
The MAGNESIUM METAL powder of 150-200nm: 30g; The tourmaline powder of 150-200nm: 30g; The magnesium oxide powder of 150-200nm: 12g; The silicate of 150-200nm: 4g; The magnesium nitride powder of 150-200nm: 10g; 50-100 purpose alkali stone: 10g; 150-200nm nano silver high-efficiency antibacterial powder 85000ppm unit: 1g.
To add entry after above composition mixing, the stirring, roller forming machine rolling moulding is made spherical, becomes nano metal magnesium grain through natural coagulation, and particle diameter is 3-20mm.
Embodiment 6:
The MAGNESIUM METAL powder of 400-500nm: 25g; The tourmaline powder of 400-500nm: 25g; The magnesium oxide powder of 150-200nm: 10g; The silicate of 150-200nm: 10g; The magnesium nitride powder of 150-200nm: 10g; 50-100 purpose alkali stone: 10g; The nano silver high-efficiency antibacterial powder 85000ppm unit of 150-200nm: 1g; The KDF filtrate of 50～200nm: 5g.
To add entry after above composition mixing, the stirring, roller forming machine rolling moulding is made spherical, becomes nano metal magnesium grain through natural coagulation, and particle diameter is 10-30mm.
Filtering material of the present invention has: the magnetizing function of negative potential water; The weakly alkaline function; Other purification functions such as activation broad-spectrum antimicrobial function.Tap water is carried out little electrolysis, obtain the active function at interface, the stabilization of chlorine, the passivation of iron, reducing, removal silicon-dioxide and the binding various effects such as (microorganism aggregates) of water.Simultaneously, micro-electrolytic water can dwindle the water molecules bundle.Water molecules (H
2O) be not Individual existence, its molecule can mutually combine, and forms molecular beam.The less water of molecular beam can be removed chlorine or impurity, and taste is good, and can improve the seepage force of health.In addition, cost of the present invention is lower, and the service efficiency height is free from environmental pollution, and recovery can be made the fish pond aquaculture and use.The tap water of its production can reach the healthy water standard that national tap water Health Professions Council advocates.
Claims (7)
1, a kind of filter material for micro electrolysis is characterized in that, comprises the MAGNESIUM METAL powder of following composition: 50-500nm: 20-40% by weight percentage; The tourmaline powder of 50-500nm: 20-40%; Magnesium oxide powder: 10-20%; Silicate: 1-10%; Magnesium nitride powder: 1～15%; 50-100 purpose alkali stone: 1～20%; Nano silver high-efficiency antibacterial powder: 0.1-5%.
2, filter material for micro electrolysis as claimed in claim 1 is characterized in that, the MAGNESIUM METAL powder of 50-500nm: 25-35% in the described filtering material; The tourmaline powder of 50-500nm: 25-35%; Magnesium oxide powder: 15-10%; Silicate: 3-5%; Magnesium nitride powder: 5～10%; 50-100 purpose alkali stone: 5～10%; Nano silver high-efficiency antibacterial powder: 0.2-2%.
3, filter material for micro electrolysis as claimed in claim 1 is characterized in that, described MAGNESIUM METAL powder is selected 150-200nm for use; Described tourmaline powder is selected 150-200nm for use; Described magnesium oxide powder is selected 100～200nm for use, and described silicate is selected 100～300nm for use; Described magnesium nitride powder is selected 100～200nm for use; Described nano silver high-efficiency antibacterial powder is selected 85000ppm unit for use.
4, filter material for micro electrolysis as claimed in claim 1 or 2 is characterized in that, described filtering material also comprises the KDF filtrate of 50～200nm: 5-10%.
5, the preparation method of filter material for micro electrolysis according to claim 1, it is characterized in that, may further comprise the steps: with MAGNESIUM METAL powder, tourmaline powder, magnesium oxide powder, magnesium nitride powder, alkali stone flour body, silicate powder, after mixing, stir, efficient nano silver antimicrobial powder adds entry, make spherical particle, become the nano metal magnesium granules through natural coagulation, institute adds the water gross weight and accounts for filter core gross weight 1～3.5%.
6, as the preparation method of filter material for micro electrolysis as described in the claim 4, it is characterized in that, use roller forming machine rolling moulding to make spherical particle.
7, as the preparation method of filter material for micro electrolysis as described in the claim 4, it is characterized in that described spherical particle diameter is the 3-30 millimeter.