CN101407960A - Ramie / terylene double fabric for textile wall cloth and curtain cloth and preparing method thereof - Google Patents
Ramie / terylene double fabric for textile wall cloth and curtain cloth and preparing method thereof Download PDFInfo
- Publication number
- CN101407960A CN101407960A CNA2008100465840A CN200810046584A CN101407960A CN 101407960 A CN101407960 A CN 101407960A CN A2008100465840 A CNA2008100465840 A CN A2008100465840A CN 200810046584 A CN200810046584 A CN 200810046584A CN 101407960 A CN101407960 A CN 101407960A
- Authority
- CN
- China
- Prior art keywords
- ramie
- terylene
- thread
- fabric
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a ramee/terylene double woven fabric used for wall cloth and window blind fabrics, which comprises a surface layer and an inner layer, wherein, the surface layer is weaved by ramee yarns and the inner layer is weaved by terylene yarns, or the surface layer is weaved by terylene yarns and the inner layer is weaved by ramee yarns, and the surface layer and the inner layer are bond into a whole by binding joints which are not exposed on the right side and the reverse side of the fabric. The preparation method of the ramee/terylene double woven fabric adopts the ramee yarns and the terylene yarns as raw materials, and comprises a preparation procedure and a weaving procedure, and the fabric is prepared by adopting a shuttleless loom or loom with shuttles according to selected structure. When weaving by adopting the shuttleless loom, the preparation procedures of the warp comprise the steps of twist setting, winding, warping, warp sizing and warp gaiting, and the preparation procedures of the weft comprise the steps of twist setting and winding; and when weaving by adopting the loom with shuttles, the preparation procedures of the warp comprise the steps of twist setting, winding, warping, warp sizing and warp gaiting, and the preparation procedures of the weft comprise the steps of twist setting, winding and weft winding.
Description
Technical field
The invention belongs to wall paper and Curtains Fabrics field, relate in particular to a kind of ramie/terylene two-layer fabric and manufacture method thereof that is used for wall paper and Curtains Fabrics.
Background technology
Wall paper and Curtains Fabrics are generally science fabric, though science fabric intensity is good, sun-resistant, are difficult for fold, and sucting wet air permeability is poor, and be poor with people's compatibility, and be difficult for degraded.Ramie claims " China's grass " again, it is one of Chinese distinctive plant, mainly be grown in areas such as Sichuan, Hunan, Hubei, Jiangxi, Anhui, Guizhou, Guangxi, Guangdong, Fujian, Taiwan, output accounts for more than 98% of Gross World Product, and its bast fiber is good textile raw material.As the history in existing several thousand of textile raw material, but traditional ramie textile product mostly are the plain cloth class, tiltedly block class and tribute silk class ramee in China, and its scope of application mostly is clothing fabric and bedding.Though ramie fabric has advantages such as brute force is high, sucting wet air permeability is good, well-pressed, relatively poor, the easy fold of its elastic elongation, especially machine spinning ramie fabric have prodding and itching feeling when wearing, thereby make it in the atrophy day by day of the market of clothing fabric.
Along with growth in the living standard, increasing with the market demand of wall paper and Curtains Fabrics as family expenses and hotel, therefore, the wall paper of development of new, Curtains Fabrics fabric have been subjected to people's attention.
Summary of the invention
The purpose of this invention is to provide a kind of ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics, this kind two-layer fabric has the advantage of ramie and terylene concurrently, belongs to high-grade wall paper, Curtains Fabrics.A further object of the present invention provides a kind of manufacture method of described ramie/terylene two-layer fabric.
The ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics of the present invention comprises top layer and nexine, described top layer with ramie yarn and thread be made into, nexine is made into spun polyester thread, or described top layer with spun polyester thread be made into, nexine is made into ramie yarn and thread, top layer and nexine are integral by the binding place access node.
Binding place does not all manifest at the obverse and reverse of fabric, does not promptly have spun polyester thread to manifest on the fabric side that ramie yarn and thread constitutes, and does not have ramie yarn and thread to manifest on the fabric side that spun polyester thread constitutes.
Preferred 13～60 spies of spun polyester thread, preferred 27～60 spies of ramie yarn and thread.The table organization of two-layer fabric adopts basic stitch or alternative construction or united organization or big figured texture weave, and the lining tissue adopts basic stitch or alternative construction or big figured texture weave.
According to the performance requirement of wall paper and Curtains Fabrics, the preferred 360～600g/m of the grammes per square metre of two-layer fabric
2
The manufacture method that is used for the ramie/terylene two-layer fabric of wall paper and Curtains Fabrics of the present invention is a raw material with ramie yarn and thread and spun polyester thread, comprises preparatory process and weaving process, adopts shuttleless loom or Shuttle Loom for Weaving.
(1) preparatory process
When adopting shuttleless loom to weave, the preparatory process of warp thread is dead twist, winder, warping, sizing and passes that the preparatory process of weft yarn is dead twist and winder;
When adopting Shuttle Loom for Weaving, the preparatory process of warp thread is dead twist, winder, warping, sizing and passes that the preparatory process of weft yarn is dead twist, winder and quilling.
(2) weave
Weave according to selected tissue, when shuttleless loom is weaved, select the latitude order to get in touch weft-selecting mechanism and be one with the opening card; During Shuttle Loom for Weaving, adopt the multi-shuttle box device manually shed open to be selected latitude.Can guarantee when the ramie warp thread is mentioned, to drop into the ramie weft yarn like this, drop into the terylene weft yarn when terylene warp thread is mentioned.
For binding place is not all manifested at the obverse and reverse of described ramie/terylene two-layer fabric, to weave under the employing and connect access node, binding place is arranged between the long flotation line of top layer warp thread.
According to the performance of ramie, terylene, in manufacture method, also taked following technical measures:
1, in the preparatory process, the spun polyester thread dead twist is carried out in the yarn steaming pot, and temperature is 65～110 ℃, and the time is 50～90 minutes; The ramie yarn and thread dead twist is carried out in the yarn steaming pot, and temperature is 65～110 ℃, and the time is 50～90 minutes, and the ramie yarn and thread dead twist also can be deposited under the workshop moisture temperature condition 24～48 hours through humidification at least.The arrangement ratio that disposes ramie yarn and spun polyester thread according to the density requirements and the tissue requirement of fabric levels during warping, if also having dyed yarn to dispose, each layer also need to require to determine the arrangement of look preface the yarn arrays of on Sectional warping machines, determining order warping by technology according to the flower type.
2, in the weaving process, with the lower floor of spun polyester thread as fabric, ramie yarn and thread is combined before ramie yarn and thread is worn as the upper strata of fabric, and spun polyester thread is worn the back and combined.Can alleviate like this and weave opening, reduce the broken end of ramie yarn and thread the damage that ramie yarn and thread stretches and flexing is caused.
The present invention has following beneficial effect:
1, ramie/terylene two-layer fabric of the present invention is a kind of wall paper and Curtains Fabrics grade textiles that can make ramee and polyster fibre bring into play and embody good separately physicochemical characteristics respectively; During as curtain, in the one side faced chamber that ramie constitutes, make ramee hygroscopicity, gas permeability, thermal diffusivity and outstanding with the good advantage of people's compatibility, embody natural remie fiber and be difficult for dirt, natural stype that gloss is soft, and the one side that is made of terylene is towards outdoor, can show fully that the terylene chemical stability is good, long service life, sun-resistant characteristics; During as wall paper, in the one side faced chamber that ramie constitutes, the one side that terylene constitutes is pasted mutually with wall, the weavy grain of color and luster that ramie fabric is natural and woven fabric uniqueness forms the excellent decoration effect, the good hygroscopicity of ramee can be improved interior climate simultaneously, terylene is equipped with when the less institutional framework of more smooth plain weave or its hetero-organization circulation that interweaves makes construction and is easy to paste, terylene makes the stickup fastness good well with the compatibility of pasting adhesive in addition, though it is good to have overcome natural fabric wall paper serviceability, the not enough and difficult weakness of pasting of fastness.
2, the two-layer of ramie/terylene two-layer fabric of the present invention unites two into one, and whole thick and hard, feel high resilience, body are well-pressed, brute force and fastness all are better than pure ramie and pure fabrics of polyester.
3, employing terylene and ramie formation two-layer fabric has solved pure ramie fabric elasticity, elongation is poor, the shortcoming that feel is really up to the mark, and the gloss that has yet overcome common pure dacron simultaneously is not soft, the shortcoming that hygroscopicity difference and elasticity are little.
4, ramie/terylene two-layer fabric of the present invention has vast market as wall paper, Curtains Fabrics; thereby opened up a new road for the utilization of ramie; help the utilization of Natural Resources in China; simultaneously the use of chemical fibre on wall paper, Curtains Fabrics be can reduce again, energy savings and environmental protection helped.
5, the method for the invention has guaranteed that not only the success of ramie/terylene two-layer fabric weaves, and employed equipment is conventional equipment, is convenient to promote, and helps suitability for industrialized production.
Description of drawings
Fig. 1 is the warp-wise generalized section that is used for the ramie/terylene two-layer fabric of wall paper and Curtains Fabrics of the present invention, among the figure, and 1-top layer ramie warp yarns, 2-nexine terylene warp yarns, 3-top layer ramie weft yarn, 4-nexine terylene weft yarn;
Fig. 2 is a kind of organization chart and the looming draft (comprising drafting plan and line domain) of ramie/terylene two-layer fabric Curtains Fabrics of the present invention, among the figure,
Textura epidermoidea's riser;
Nexine is organized riser;
The symbol of table through mentioning when dropping into back weft;
Back warp represents to gait symbol and peg symbol again respectively with table latitude binding place, in drafting plan and line domain;
Fig. 3 is another organization chart and the looming draft (comprising drafting plan and line domain) of ramie/terylene two-layer fabric Curtains Fabrics of the present invention, among the figure,
Textura epidermoidea's riser;
Nexine is organized riser;
The symbol of table through mentioning when dropping into back weft;
Back warp represents to gait symbol and peg symbol again respectively with table latitude binding place, in drafting plan and line domain;
Fig. 4 is a kind of organization chart and the looming draft (comprising drafting plan and line domain) of ramie/terylene two-layer fabric wall paper of the present invention.
The specific embodiment
Below in conjunction with accompanying drawing ramie/terylene two-layer fabric and the manufacture method thereof that is used for wall paper and Curtains Fabrics of the present invention is described further.
Embodiment 1: ramie/terylene two-layer fabric Curtains Fabrics I and manufacture method thereof
In the present embodiment, be used for Curtains Fabrics the ramie/terylene two-layer fabric structure as shown in Figure 1, comprise top layer and nexine, described top layer constitutes with spun polyester thread with ramie yarn and thread formation, nexine, top layer and nexine are integral by the binding place access node, binding place does not all manifest at the obverse and reverse of fabric, and its technical specification sees Table 1.
Table 1 ramie/terylene two-layer fabric Curtains Fabrics I technical specification
Present embodiment is weaved on HZF758 type Rapier looms, and technological process is as follows:
(1) preparatory process
The preparatory process of warp thread is dead twist, winder, warping, sizing and passes that the preparatory process of weft yarn is dead twist and winder.
Dead twist: the dead twist of terylene warp thread, weft yarn and ramie warp thread, weft yarn is carried out in ZDKX vacuum HEAT SETTING yarn steaming pot, and temperature is about 90 ℃, and the time is about 80 minutes.
Warping: earlier ramie yarn and Polyester Yarns are carried out pre-warping by design-calculated head part respectively.Again with ramie yarn starching on Sizing machines, and then on Sectional warping machines, ramie yarn and Polyester Yarns are compared warping by 1: 1 arrangement.
Sizing: on the Sizing machines with ramie yarn on 2% starch slurry so that plume of ramie yarn pastes clothes.
Warp thread can pass standbyly behind the section warping beaming, and terylene weft yarn, ramie weft yarn are standby behind winder.
(2) weave
Organization chart and looming draft are weaved according to Fig. 2 as shown in Figure 2, select latitude order to get in touch with the opening card weft-selecting mechanism with dobby device and are one, drop into the ramie weft yarn at table when mentioning, drop into the terylene weft yarn when back warp is mentioned guaranteeing.With the lower floor of spun polyester thread as fabric, ramie yarn and thread is combined before ramie yarn and thread is worn as the upper strata of fabric, and spun polyester thread is worn the back and combined; Connect access node under adopting, binding place is arranged between the long flotation line of top layer warp thread.Its knitting technology parameter sees Table 2.
Table 2 ramie/terylene two-layer fabric Curtains Fabrics is weaved knitting technology
Embodiment 2: ramie/terylene two-layer fabric Curtains Fabrics II and manufacture method thereof
In the present embodiment, the ramie/terylene two-layer fabric that is used for Curtains Fabrics comprises top layer and nexine, described top layer constitutes with spun polyester thread with ramie yarn and thread formation, nexine, top layer and nexine are integral by the binding place access node, binding place does not all manifest at the obverse and reverse of fabric, its organization chart and looming draft are seen Fig. 3, and technical specification sees Table 3.
Present embodiment is weaved on HZF758 type Rapier looms, and technological process is as follows:
(1) preparatory process
Dead twist: the dead twist of terylene warp thread, weft yarn and ramie warp thread, weft yarn is carried out in ZDKX vacuum HEAT SETTING yarn steaming pot, and temperature is about 100 ℃, and the time is about 70 minutes.
Warping: earlier ramie yarn and Polyester Yarns are carried out pre-warping by design-calculated head part respectively.Again with ramie yarn starching on Sizing machines, and then on Sectional warping machines, ramie yarn and Polyester Yarns are compared warping by 1: 1 arrangement.
Sizing: ramie yarn carries out sizing on Sizing machines, and last 2% starch slurry is so that plume of ramie yarn pastes clothes.
Warp thread can pass standbyly behind the section warping beaming, and terylene weft yarn, ramie weft yarn are standby behind winder.
(2) weave
Organization chart and looming draft are weaved according to Fig. 3 as shown in Figure 3, select latitude order to get in touch with the opening card weft-selecting mechanism with dobby device and are one, drop into the ramie weft yarn at table when mentioning, drop into the terylene weft yarn when back warp is mentioned guaranteeing.With the lower floor of spun polyester thread as fabric, ramie yarn and thread is combined before ramie yarn and thread is worn as the upper strata of fabric, and spun polyester thread is worn the back and combined; Connect access node under adopting, binding place is arranged between the long flotation line of top layer warp thread.Its knitting technology parameter sees Table 4.
Table 3 ramie/terylene two-layer fabric Curtains Fabrics II technical specification
Table 4 ramie/terylene two-layer fabric Curtains Fabrics II weaves knitting technology
Embodiment 3: ramie/terylene two-layer fabric wall paper and manufacture method thereof
In the present embodiment, the ramie/terylene two-layer fabric that is used for wall paper comprises top layer and nexine, described surface constitutes with spun polyester thread with ramie yarn and thread formation, the inside, top layer and nexine are integral by the binding place access node, binding place does not all manifest at the obverse and reverse of fabric, its organization chart and looming draft as shown in Figure 4, technical specification sees Table 5.
Table 5 ramie/terylene two-layer fabric wall paper technical specification
The production technology of present embodiment is substantially the same manner as Example 1, and difference is: with comprehensive number is 11 pages, and wherein ground heddle is 9 pages, and the limit is combined 2 pages; Cloth machine pickwheel is 63 teeth, supports 2 teeth at every turn.
Claims (10)
1, a kind of ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics, comprise top layer and nexine, it is characterized in that described top layer with ramie yarn and thread be made into, nexine is made into spun polyester thread, or described top layer with spun polyester thread be made into, nexine is made into ramie yarn and thread, top layer and nexine are integral by the binding place access node.
2, the ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics according to claim 1 is characterized in that binding place does not all manifest at the obverse and reverse of fabric.
3, the ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics according to claim 1 and 2 is characterized in that spun polyester thread is 13～60 spies, and ramie yarn and thread is 27～60 spies.
4, the ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics according to claim 1 and 2, the table organization that it is characterized in that described two-layer fabric adopts basic stitch or alternative construction or united organization or big figured texture weave, and the lining tissue adopts basic stitch or alternative construction or big figured texture weave.
5, the ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics according to claim 3, the table organization that it is characterized in that described two-layer fabric adopts basic stitch or alternative construction or united organization or big figured texture weave, and the lining tissue adopts basic stitch or alternative construction or big figured texture weave.
6, the ramie/terylene two-layer fabric that is used for wall paper and Curtains Fabrics according to claim 5, the grammes per square metre that it is characterized in that described two-layer fabric is 360～600g/m
2
7, a kind of manufacture method that is used for the ramie/terylene two-layer fabric of wall paper and Curtains Fabrics comprises preparatory process and weaving process, adopts shuttleless loom or Shuttle Loom for Weaving, it is characterized in that:
(1) be raw material with ramie yarn and thread and spun polyester thread;
(2) preparatory process:
When adopting shuttleless loom to weave, the preparatory process of warp thread is dead twist, winder, warping, sizing and passes that the preparatory process of weft yarn is dead twist and winder;
When adopting Shuttle Loom for Weaving, the preparatory process of warp thread is dead twist, winder, warping, sizing and passes that the preparatory process of weft yarn is dead twist, winder and quilling;
(3) weave:
Weave according to selected tissue, when shuttleless loom is weaved, select the latitude order to get in touch weft-selecting mechanism and be one with the opening card; During Shuttle Loom for Weaving, adopt the multi-shuttle box device manually shed open to be selected latitude.
8, the manufacture method that is used for the ramie/terylene two-layer fabric of wall paper and Curtains Fabrics according to claim 7 is characterized in that weaving and connects access node under adopting, and binding place is arranged between the long flotation line of top layer warp thread.
9, according to claim 7 or the 8 described manufacture methods that are used for the ramie/terylene two-layer fabric of wall paper and Curtains Fabrics, it is characterized in that spun polyester thread dead twist carries out in the yarn steaming pot, temperature is 65～110 ℃, the time is 50～90 minutes; The ramie yarn and thread dead twist is carried out in the yarn steaming pot, and temperature is 65～110 ℃, and the time is 50～90 minutes, or deposits under the workshop moisture temperature condition 24～48 hours through humidification.
10, the manufacture method that is used for the ramie/terylene two-layer fabric of wall paper and Curtains Fabrics according to claim 9, when it is characterized in that weaving with the lower floor of spun polyester thread as fabric, ramie yarn and thread is combined before ramie yarn and thread is worn as the upper strata of fabric, and spun polyester thread is worn the back and combined.