CN101407956A - Corn viscose blended yarn and preparing method thereof - Google Patents
Corn viscose blended yarn and preparing method thereof Download PDFInfo
- Publication number
- CN101407956A CN101407956A CNA2008102344338A CN200810234433A CN101407956A CN 101407956 A CN101407956 A CN 101407956A CN A2008102344338 A CNA2008102344338 A CN A2008102344338A CN 200810234433 A CN200810234433 A CN 200810234433A CN 101407956 A CN101407956 A CN 101407956A
- Authority
- CN
- China
- Prior art keywords
- corn
- blended yarn
- viscose
- viscose blended
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a zein viscose blended yarn and a preparation method thereof, comprising the following steps: main materials, namely, zein fibers and viscose fibers, are mixed according to a certain proportion, and a finished product is prepared by the steps of cotton cleaning, cotton carding, drawing, roving, spinning, winding, twisting and reeling. The invention adopts zein and viscose to be blended into yarn, and prepares an environment-friendly and degradable zein viscose blended yarn with the advantages of clear yarn evenness, soft texture, fullness, air permeability in dressing and sweat absorption, thus being suitable to be prepared into fabrics which can be closely worn by people of different ages all around the year.
Description
Technical field
The present invention relates to a kind of yarn and manufacture method thereof, be specifically related to a kind of do clear, quality is soft, plentiful, dress is ventilative, the corn viscose blended yarn and the manufacture method thereof of absorbing sweat and degradable environmental protection.
Background technology
Blended yarn on the market is a lot of now, has bar to do linen blended yarn clearly, the Modal yarn of better softness is arranged, but be exactly not have degradable environmental protection yarn.And above-mentioned linen blended yarn has possessed clear dried characteristics but can not have characteristics such as flexibility, absorption of perspiration; Though it is dried clear that Modal yarn softness does not but possess bar, the most important thing is that the Modal yarn easily hardens at low temperatures, cools off.That is to say does not have also in the market that function is complete, quality is fit to the degraded yarn of wearing next to the shin and makes underwear.
Summary of the invention
Task of the present invention is to provide a kind of corn viscose blended yarn and manufacture method thereof, specifically be a kind of do clear, quality is soft, plentiful, dress is ventilative, the corn viscose blended yarn and the manufacture method thereof of absorbing sweat and degradable environmental protection.
In order to solve above technical problem, a kind of corn viscose blended yarn of the present invention, it is characterized in that: the composition of described corn viscose blended yarn is: zein fiber 50%-70%; Viscose 30%-50%.
A kind of method of making the corn viscose blended yarn by blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn, winder, twist thread, shake into step and constitute, is characterized in that: adopt in the described blowing step that many pines fewly beat, light comb lacks the mode that falls and carries out blowing; Adopt chemical fibre to leak the end in the described comb and parallel cotton fibers prior to spinning step, reduce noil, slow down, tightly space; Head in the described drafting step also strengthens first break draft, and two and reduce first break draft; In the described rove step yarn is reduced first break draft; Described spun yarn step medium velocity improves, twisting count reduces.
Described scutcher hired roughneck rotating speed 480rpm, hired roughneck's form changes card wire into by blade.
Breast swift rotating speed 300rpm in the described comb and parallel cotton fibers prior to spinning step, licker-in rotating speed 900rpm uses chemical fibre instead and leaks the end at the bottom of the little leakage, the import 10mm that spaces.
1.63 times of the head of the drawing frame in the described drafting step and first break draft, two and 1.55 times.
Speed frames first break draft multiple in the described rove step is 1.3 times.
Fine spining machine front roller rotating speed 200rpm in the described spun yarn step, the coefficient of twisting thread is 300.
The advantage of the yarn that above-mentioned technology produces is: the present invention adopts corn to become yarn with viscose blended, produce a kind of do clear, quality is soft, plentiful, dress is ventilative, the corn viscose blended yarn of absorbing sweat and degradable environmental protection, be fit to manufacture lining, for next to the shin throughout the year the wearing of people of all ages and classes.
Description of drawings
Figure is a process flow diagram of the present invention.
The specific embodiment
For union twist yarn of the present invention and preparation method are had further understanding, as shown in the figure, set forth in conjunction with the embodiments.
Embodiment:
Major ingredient: zein fiber and viscose glue.Weight is respectively: zein fiber and viscose glue weight ratio are 60: 40, make the specification 18.2tex of union twist yarn.The concrete step of making is as follows: two kinds of admixed together being sent in the scutcher of major ingredient that will weigh up.
In the blowing program, hired roughneck's rotating speed of scutcher is reduced to 480rpm, hired roughneck's form changes card wire into by blade, adjust machine after, two kinds of fibers are fully mixed in scutcher after, deliver to the carding machine combing.The process of blowing focuses on controlling the parameter of above scutcher, to few the beating of the many pines of fiber, reaches the purpose that light comb falls less.
During combing, adopt the A186C type, chemical fibre leaks the end, and the major parameter of this carding machine is set to then: cylinder rotating speed 300rpm, licker-in rotating speed 900rpm uses chemical fibre instead and leaks the end at the bottom of the little leakage, the import 10mm that spaces.Use above parameter, on speed, reduce, reduce damage fiber; On spacing, tighten, reduce cotton knot.
After combing finishes, enter the drafting program.Drafting separately and and two and twice.Described head and in, 1.63 times of head and first break draft are to strengthen first break draft.Two and in, two and 1.55 times, be to reduce first break draft.Head and strengthen first break draft like this, two and the purpose that reduces first break draft with improve bar and do.
Next be rove.With the first break draft multiple is 1.3 times, and it is to reduce first break draft that this adjustment makes rove, also is to do in order to improve bar.
Rove is a spun yarn later.The front roller rotating speed of fine spining machine transfers to 200rpm, and the coefficient of twisting thread is 300.
After above step completes, just with the mode winder of routine, twist thread, shake, just finished product.
Claims (7)
1, a kind of corn viscose blended yarn, it is characterized in that: the composition of described corn viscose blended yarn is: zein fiber 50%-70%; Viscose 30%-50%.
2, a kind of method of making the described corn viscose blended yarn of claim 1, by blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn, winder, twist thread, shake into step and constitute, it is characterized in that: adopt in the described blowing step that many pines fewly beat, light comb lacks the mode that falls and carries out blowing; Adopt chemical fibre to leak the end in the described comb and parallel cotton fibers prior to spinning step, reduce noil, slow down, tightly space; Head in the described drafting step also strengthens first break draft, and two and reduce first break draft; In the described rove step yarn is reduced first break draft; Described spun yarn step medium velocity improves, twisting count reduces.
3, a kind of method of making the corn viscose blended yarn according to claim 2 is characterized in that: described scutcher hired roughneck rotating speed 480rpm, hired roughneck's form changes card wire into by blade.
4, a kind of method of making the corn viscose blended yarn according to claim 3 is characterized in that: the breast swift rotating speed 300rpm in the described comb and parallel cotton fibers prior to spinning step, licker-in rotating speed 900rpm uses chemical fibre instead and leaks the end at the bottom of the little leakage, the import 10mm that spaces.
5, a kind of method of making the corn viscose blended yarn according to claim 3 is characterized in that: 1.63 times of the head of the drawing frame in the described drafting step and first break draft, two and 1.55 times.
6, a kind of method of making the corn viscose blended yarn according to claim 3 is characterized in that: the Speed frames first break draft multiple in the described rove step is 1.3 times.
7, a kind of method of making the corn viscose blended yarn according to claim 3 is characterized in that: the fine spining machine front roller rotating speed 200rpm in the described spun yarn step, the coefficient of twisting thread is 300.