CN101407149A - Method for embedding plants on surface of pottery - Google Patents
Method for embedding plants on surface of pottery Download PDFInfo
- Publication number
- CN101407149A CN101407149A CNA2008101410328A CN200810141032A CN101407149A CN 101407149 A CN101407149 A CN 101407149A CN A2008101410328 A CNA2008101410328 A CN A2008101410328A CN 200810141032 A CN200810141032 A CN 200810141032A CN 101407149 A CN101407149 A CN 101407149A
- Authority
- CN
- China
- Prior art keywords
- production method
- plants
- ware
- gel coating
- coating resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a ceramic surface decoration method, in particular to a production method for embedding plants on the surface of chinaware. The production method for embedding the plants on the surface of the chinaware comprises the following steps: firstly, chinaware of which the inner surface and the bottom outer surface are glazed is baked; secondly, a layer of gel coat resin containing base colors is uniformly coated on the outer surface of chinaware which is not glazed, and the outer surface is grinded; thirdly, leaves or stems or flowers or roots of the plants are adhered to the surface of the gel coat resin containing the base colors; fourthly, transparent resin is uniformly coated for 8 to 10 times on the surface of the gel coat resin on which the plant materials are adhered, and the outer surface is polished; and fifthly, a layer of UV transparent clear lacquer is uniformly coated on the polished outer surface and solidified by utilization of ultraviolet rays for irradiation for 15 to 30 minutes. The invention provides the production method for embedding the plants on the surface of the chinaware, and has the advantages of simple manufacturing technique, low product cost and rich artistic expression form.
Description
(1), technical field:
The present invention relates to a kind of ceramic surface trailing, particularly a kind of production method of ware embedding plants on surface.
(2), background technology:
Pottery is a time-honored traditional handicraft of China, surface treatment in the past such as is confined to fire behind underglaze colour, overglaze color, the engraving at technology, there is one deck enamel on the traditional lacquer surface, this enamel porcelain has its special role as commodity, irreplaceability is arranged, but show monotonicity as handicraft, the form of expression is modern inadequately, fashion and abundant, and the cost of manufacture height of ceramics, cost an arm and a leg, be unfavorable for large-scale production and selling.
(3), summary of the invention:
The technical problem to be solved in the present invention is: overcome the defective of prior art, the production method of the ware embedding plants on surface that a kind of production technology is simple, product cost is low, artistic expression is abundant is provided.
Technical scheme of the present invention:
A kind of production method of ware embedding plants on surface, step is as follows:
A. fire inner surface and bottom surface outer surface rest, all the other outer surfaces are the ware of rest not;
B. evenly be coated with the gel coating resin that last layer contains background color at the ware outer surface that does not have rest,, polish then to obtain required background color effect;
C. paste the leaf of plant on the gel coating resin surface of containing background color, or the bar stem, or flowers, or coring;
D. evenly be coated with the transparent resin of 8～10 times superior in qualities on the gel coating resin surface that pastes vegetable material; to protect the formed design of natural plants; transparent resin and firm the combining of background color gel coat; the artistic effect of being like nature itself as the formation high-quality amber is polished the transparent resin surface then.
E. evenly spray the thin UV clear varnish of one deck at polished outer surface at last, 15～30 seconds the UV clear varnish was solidified with the ultraviolet ray irradiation then, with the full similar effect of outward appearance of refractory ceramics muffle painting light, like this, the surface is inlayed the ware handicraft of plant and has just been finished with acquisition.
The concrete production detail section of above production method is as follows:
The thickness that contains the gel coating resin of background color is 0.8 millimeter～1.5 millimeters, when being coated with gel coating resin, approaching and execute, too thick words can cause background color that crackle is arranged, gel coating resin contains a kind of background color of color, perhaps contains the background color of two or more color according to the design needs.
The process of polishing is: earlier described gel coating resin is roughly ground, more described gel coating resin is carried out fine grinding, corase grind adopts the paper sand of No. 240 and No. 400, the water mill sand of No. 1500, fine grinding employing and No. 2000.
The detailed process of step c is: screen pasting vegetable material earlier, unnecessary part is weeded out, only stay the part that needs, utilize a heatable brick bed room that the moisture content of vegetable material is removed then, utilize pressing machine that material is pressed into plane lamina or curved surface thin slice again, be beneficial to paste operation, with seccotine the material of different shaping sticked on ceramic surface at last, to the processing of can dyeing of the vegetable material of removing moisture content and suppressed at the ceramic surface of Different Plane or curved surface.
The detailed method that is coated with transparent resin in the steps d is: dip in a little transparent resin with brush earlier, be coated with equably and invest described gel coating resin surface, wait for 8～15 minutes so that transparent resin solidifies fully, and then carry out the coated of next time, can cover stick-on vegetable material up to transparent resin.
The process of polishing is: slightly throw earlier, carry out essence again and throw, the thick throwing uses stationary cloth buff polishing machine to polish, and dips in a little buffing wax on the transparent resin surface earlier during smart the throwing, polishes with hand-held wool polishing machine then.
When using the ultraviolet ray irradiation among the step e, because will use the very strong ultraviolet radiator of light, so will note operating personnel's protection, both hands will be worn protective gloves, and head will be worn safety goggles.
Beneficial effect of the present invention:
1, the present invention is directed to the raising of the aesthetic level of people and the demand of market diversification, further investigation ceramic surface treatment technology, invent out ceramic surface embedding plants technology, it has broken through the limitation of former traditional technique of expression, the ceramic surface treatment technology is broken through to combination ceramic and resin, natural plants from single firing, enriched the technique of expression of this artistic carrier of pottery.
2, the present invention completely is integral natural plants material representative element and pottery, form a kind of minute surface and inlay the artistic effect of plant, modern more, the fashion of this traditional artistic carrier performance of pottery, be a breakthrough of ceramic surface treatment technology for thousands of years.
3, the present invention adopts ultraviolet ray irradiation heating, homogeneous heating, and solidification effect is good.In addition, transparent resin adopts the layering brushing both to increase cohesion, prevents from once to brush blocked up embrittlement that causes and wrinkle again.
4, the present invention has adopted cheap natural plants material as raw material, with resin ceramic blank is brushed again, adopts clear varnish to be heating and curing then, does not need to fire once more, and its production technology is simple, product cost is low.
(4), description of drawings:
Fig. 1 inlays one of the sample drawing of the ware of wheat stalk picture for the surface that makes according to method of the present invention;
Fig. 2 inlay for the surface that makes according to method of the present invention wheat stalk picture ware sample drawing two;
(5), the specific embodiment:
The production method that ware surface wheat stalk picture is inlayed, step is as follows:
A. fire inner surface and bottom surface outer surface rest, all the other outer surfaces are the ware of rest not;
B. evenly be coated with the gel coating resin that last layer contains background color at the ware outer surface that does not have rest,, polish then to obtain required background color effect;
C. paste wheat stalk picture on the gel coating resin surface of containing background color, more attractive in appearance in order to make ware, also can utilize traditional transfer technique with gold or/and the pattern of silver color or/and the writing brush word transfer printing on described gel coating resin background color surface;
D. evenly be coated with the transparent resin of 9 times superior in qualities on the gel coating resin surface that pastes wheat stalk picture; to protect the formed design of natural plants; transparent resin and firm the combining of background color gel coat; the artistic effect of being like nature itself as the formation high-quality amber is polished the transparent resin surface then.
E. evenly spray the thin UV clear varnish of one deck at polished outer surface at last, 20 seconds the UV clear varnish was solidified with the ultraviolet ray irradiation then, to obtain with the full similar effect of outward appearance of refractory ceramics muffle painting light, like this, the surface is inlayed the ware handicraft of wheat stalk picture and has just been finished, referring to Fig. 1 and Fig. 2.
The concrete production detail section of above production method is as follows:
The thickness that contains the gel coating resin of background color is 1 millimeter, when being coated with gel coating resin, approaching and execute, and too thick words can cause background color that crackle is arranged, and the background color of gel coating resin is red, and gel coating resin is a phenolic resins, and its model is 141.
The process of polishing is: earlier described gel coating resin is roughly ground, more described gel coating resin is carried out fine grinding, corase grind adopts the paper sand of No. 240 and No. 400, the water mill sand of No. 1500, fine grinding employing and No. 2000.
The detailed process of step c is: screen pasting vegetable material earlier, unnecessary part is weeded out, only stay the part that needs, utilize a heatable brick bed room that the moisture content of vegetable material is removed then, utilize pressing machine that material is pressed into plane lamina or curved surface thin slice again, be beneficial to paste operation, with seccotine the material of different shaping sticked on ceramic surface at last at the ceramic surface of Different Plane or curved surface.
The detailed method that is coated with transparent resin in the steps d is: dip in a little transparent resin with brush earlier, be coated with equably and invest described gel coating resin surface, wait for 10 minutes so that transparent resin solidifies fully, and then carry out the coated of next time, can cover stick-on vegetable material up to transparent resin, transparent resin is a phenolic resins, and its model is 141.
The process of polishing is: slightly throw earlier, carry out essence again and throw, the thick throwing uses stationary cloth buff polishing machine to polish, and dips in a little buffing wax on the transparent resin surface earlier during smart the throwing, polishes with hand-held wool polishing machine then.
When using the ultraviolet ray irradiation among the step e, because will use the very strong ultraviolet radiator of light, so will note operating personnel's protection, both hands will be worn protective gloves, and head will be worn safety goggles.
Claims (9)
1, a kind of production method of ware embedding plants on surface is characterized in that:
A. fire inner surface and bottom surface outer surface rest, all the other outer surfaces are the ware of rest not;
B. evenly be coated with the gel coating resin that last layer contains background color at the ware outer surface that does not have rest, polish then;
C. paste the leaf of plant on the gel coating resin surface of containing background color, or the bar stem, or flowers, or coring;
D. evenly be coated with n on the gel coating resin surface that pastes vegetable material all over transparent resin, then polishing.
E. at last evenly spray one deck UV clear varnish, 15～30 seconds the UV clear varnish was solidified with the ultraviolet ray irradiation then at polished outer surface.
2. the production method of ware embedding plants on surface according to claim 1, it is characterized in that: the described thickness that contains the gel coating resin of background color is 0.8 millimeter～1.5 millimeters, gel coating resin contains a kind of background color of color, perhaps contains the background color of two or more color according to the design needs.
3. the production method of ware embedding plants on surface according to claim 1 is characterized in that: the process of described polishing is: earlier described gel coating resin is roughly ground, more described gel coating resin is carried out fine grinding.
4, the production method of ware embedding plants on surface according to claim 3 is characterized in that: described corase grind adopts the paper sand of No. 240 and No. 400, the water mill sand of No. 1500, described fine grinding employing and No. 2000.
5, the production method of ware embedding plants on surface according to claim 1, it is characterized in that: the process of described step c is: screen pasting vegetable material earlier, unnecessary part is weeded out, only stay the part that needs, utilize a heatable brick bed room that the moisture content of vegetable material is removed then, utilize pressing machine that material is pressed into plane lamina or curved surface thin slice again, be beneficial to paste operation, with seccotine the material of different shaping sticked on ceramic surface at last at the ceramic surface of Different Plane or curved surface.
6, the production method of ware embedding plants on surface according to claim 5 is characterized in that: to removing the processing of can dyeing of moisture content and the vegetable material suppressed.
7, the production method of ware embedding plants on surface according to claim 1, it is characterized in that: the method that is coated with transparent resin in the described steps d is: n=8～10, dip in brush earlier when being coated with transparent resin and get transparent resin, be coated with equably and invest described gel coating resin surface, wait for 8～15 minutes so that transparent resin solidifies fully, and then carry out the coated of next time, can cover stick-on vegetable material up to transparent resin.
8, the production method of ware embedding plants on surface according to claim 1 is characterized in that: the process of described polishing is: slightly throw earlier, carry out essence again and throw.
9, the production method of ware embedding plants on surface according to claim 8 is characterized in that: the thick throwing uses stationary cloth buff polishing machine to polish, and dips in buffing wax on the transparent resin surface earlier during smart the throwing, polishes with hand-held wool polishing machine then.