CN101385689B

CN101385689B - Attapulgite hair conditioner

Info

Publication number: CN101385689B
Application number: CN2008101555948A
Authority: CN
Inventors: 解云; 许庆华; 许盛英
Original assignee: Individual
Current assignee: Individual
Priority date: 2008-10-28
Filing date: 2008-10-28
Publication date: 2010-06-23
Anticipated expiration: 2028-10-28
Also published as: CN101385689A

Abstract

The invention discloses an attapulgite hair conditioner; the key point of the technical proposal thereof is that the attapulgite hair conditioner consists of modified pasty attapulgite clay, glycerol, hexadecanol, octadecyl trimethyl ammonium chloride, citric acid, glycerin monostearate, polyoxyethylene sorbitan monolaurate, methyl hydroxybenzoate, propylparaben and deionized water. The production method of the attapulgite hair conditioner comprises slurrying, sodium treatment, blending, beating, grinding, high-speed stirring, emulsification, vacuum degassing and canning into a finished product of the attapulgite hair conditioner. The attapulgite hair conditioner can well adhere to the surface of hair, and increase the contact area with the hair, which causes the washed hair to restore softness and luster, can improve dry combing and wet combing performance, causes the hair not to entwist, and improves the use effect of the attapulgite hair conditioner which is suitable for hair care.

Description

Concavo-convex rod hair conditioner

Technical field

The present invention relates to hair conditioner, be specifically related to a kind of concavo-convex rod hair conditioner.

Background technology

Healthy hair top layer is made of the protecting film of hair one group of complete hair scale sheet and excretory naturally oils and fats; too much wash reason, and hair-waving, exposure in sunshine all can destroy its natural protecting film, cause the cortex water loss; make hair withered, cause hair to follow the string and flexibility.

Influence along with various unfavorable factors such as environmental pollution, hair dyeing, hair-wavings makes people pay attention to more hair nursing, and the effect of cosmetic hair care is to make hair keep natural, healthy and appearance attractive in appearance, gives hair gloss, softness and angry.

Cosmetic hair care is various in style on the market, and also relatively more chaotic, the hair conditioner of supplying on the market is the synthetic product of industrial chemicals mostly now, and it is relatively poor that hair conditioner is coated with the adhesive force of touching on hair, directly has influence on result of use.

Summary of the invention

The objective of the invention is to overcome weak point in the prior art, a kind of concavo-convex rod hair conditioner is provided.

Concavo-convex rod hair conditioner is made up of modified cream attapulgite clay, glycerol, hexadecanol, octadecyl trimethyl ammonium chloride, citric acid, glyceryl monostearate, polyoxyethylene 20 sorbitan monolaurate, methyl hydroxybenzoate, propylparaben and deionized water.

The production method of concavo-convex rod hair conditioner is: pulping, sodium, batching, making beating, grinding, high-speed stirred, emulsifying, vacuum outgas, cannedly be the finished product of concavo-convex rod hair conditioner.

Attapulgite clay is a kind of nanometer porous fibrous silicate clay mineral of Shuifu County's magnesium that contains, and when attapulgite content 〉=80% in the attapulgite clay was above, its specific surface area was bigger, can reach 500m ²More than/the g.Use " wet beneficiation craft of attapulgite " and " attapulgite ore pul making production technology ", the screening of mineral such as the hydromica in the attapulgite clay, quartz, opal and carbonate is got rid of, obtain a kind of attapulgite sludge slurry.

Glycerol has stronger hygroscopicity, can allow the moisture on the skin can not distribute too soon, draws aqueous vapor simultaneously from air, can make skin and hair keep soft, high resilience.

Hexadecanol has inhibited oil soapy feeling, stablizes the effect of hair conditioner gel.

Produce a large amount of foams during the octadecyl trimethyl ammonium chloride concussion, with cation, non-ionic surface active agent or dyestuff excellent compatibility is arranged, chemical stability is good, and is heat-resisting, fast light, strong alkali-acid resistance has good infiltration, softness, emulsifying, antistatic and bactericidal property.

Citric acid has gentle frank tart flavour, can improve and adjust the pH value of hair conditioner.

Glyceryl monostearate makes the mastic exquisiteness of hair conditioner, increases its lubricating property.

Polyoxyethylene 20 sorbitan monolaurate has emulsifying, diffusion, solubilising, stable effect.

Methyl hydroxybenzoate has the broad-spectrum antibacterial effect, to Gram-positive, and negative bacteria, yeast and mycete have very strong inhibitory action, and the low and safety economy of working concentration uses effect duration long.Methyl hydroxybenzoate is compatible with various chemical substances easily, and the composite use of methyl hydroxybenzoate and propylparaben is to reach better antiseptic effect.

The present invention is achieved by following technical proposals:

1, the batching of concavo-convex rod hair conditioner is made up of following component by weight percentage: modified cream attapulgite clay 20～50%, glycerol 2～10%, hexadecanol 0.1～5%, octadecyl trimethyl ammonium chloride 0.1～5%, citric acid 0.01～5%, glyceryl monostearate 0.1～5%, polyoxyethylene 20 sorbitan monolaurate 0.1～5%, methyl hydroxybenzoate 0.05～0.5%, propylparaben 0.05～0.5% and deionized water 30～60%.

Described modified cream attapulgite clay is on attapulgite ore pul making production technology basis, attapulgite sludge slurry is carried out sodium handle, and the mud of process post precipitation is modified cream attapulgite clay.Lip lipstick attapulgite clay becomes the special good natural gelinite of a kind of thixotropy and gumminess through powerful stirring at a high speed, and viscosity is up to more than the 10000mPas, and absorption property and performance of keeping humidity have all obtained further raising.

Attapulgite ore pul making production technology is: will stir in the attapulgite ore deposit input blender, after extruder is squeezed into lamellar, import once more in the blender and stir, natural drying after extruder is squeezed into lamellar, air dried attapulgite ore deposit is transported in the feed reservoir soaks, dash with air pump and to turn over, post precipitation is emitted immersion water, the sieve decontamination in the input semi-finished product pond, is soaked again, dash with air pump and to turn over, post precipitation is emitted immersion water, and the slurry transportation of post precipitation is arrived in the finished product pond, is attapulgite sludge slurry finished product.

Above-mentioned production technology is to adopt " the attapulgite ore pul making production technology " in application on January 6th, 2004 by the inventor, and the Chinese patent Granted publication number is: CN1287965C, Granted publication day: on December 6th, 2006.

The production technology of described modified cream attapulgite clay is: (1) selects for use attapulgite sludge slurry to be body material, and attapulgite sludge slurry is made up of following component by weight percentage: attapulgite clay 15～35% and water 65～85%; (2) sodium is handled: attapulgite sludge slurry is transported in the blender, stirs after adding sodium hydroxide, through the attapulgite sludge slurry that stirs, be transported in the sodium pond sodium and handle and be modified cream attapulgite clay in 1～7 day; The sodium batching is made up of following component by weight percentage: attapulgite sludge slurry 85～99% and sodium hydroxide 1～15%.

2, the production method of concavo-convex rod hair conditioner: 1. pulling an oar in the batching adding beater with concavo-convex rod hair conditioner, is the mixture of concavo-convex rod hair conditioner behind the making beating mix homogeneously; 2. the mixture that 1. step is obtained is imported to grind in the multi-functional colloid mill and is pasty mixture, and fineness of the particles is less than 0.015 millimeter; 3. the pasty mixture after the grinding that 2. step is obtained carries out powerful stirring of high speed and is the paste semi-finished product in the input ultrahigh speed blender; 4. the paste semi-finished product that 3. step obtained carry out vacuum degassing process to be handled, and canned is the finished product of concavo-convex rod hair conditioner.

After attapulgite sludge slurry was handled through sodium, lip lipstick attapulgite clay became a kind of thixotropy and the special good natural magnesium aluminium silicate gel of gumminess.Concavo-convex rod hair conditioner can be well attached to the surface of hair, increases the contact area with hair, makes the hair after the hair washing recover flexibility and gloss, can improve to do comb and wet and comb performance, and hair can not tangled, and has improved the result of use of concavo-convex rod hair conditioner.

Concavo-convex rod hair conditioner is applicable to hair nursing.

The specific embodiment

The invention will be further described below in conjunction with embodiment:

1, the batching of concavo-convex rod hair conditioner is made up of following component by weight percentage: modified cream attapulgite clay 32%, glycerol 8%, hexadecanol 4%, octadecyl trimethyl ammonium chloride 3%, citric acid 2%, glyceryl monostearate 1.5%, polyoxyethylene 20 sorbitan monolaurate 1.3%, methyl hydroxybenzoate 0.15%, propylparaben 0.05% and deionized water 48%.

The production technology of described modified cream attapulgite clay is: (1) selects for use attapulgite sludge slurry to be body material, and attapulgite sludge slurry is made up of following component by weight percentage: attapulgite clay 30% and water 70%; (2) sodium is handled: attapulgite sludge slurry is transported in the blender, stirs after adding sodium hydroxide, through the attapulgite sludge slurry that stirs, be transported in the sodium pond sodium and handle and be modified cream attapulgite clay in 5 days; The sodium batching is made up of following component by weight percentage: attapulgite sludge slurry 97% and sodium hydroxide 3%.

Claims

1. concavo-convex rod hair conditioner, it is characterized in that the batching of concavo-convex rod hair conditioner is made up of following component by weight percentage: modified cream attapulgite clay 20～50%, glycerol 2～10%, hexadecanol 0.1～5%, octadecyl trimethyl ammonium chloride 0.1～5%, citric acid 0.01～5%, glyceryl monostearate 0.1～5%, polyoxyethylene 20 sorbitan monolaurate 0.1～5%, methyl hydroxybenzoate 0.05～0.5%, propylparaben 0.05～0.5% and deionized water 30～60%;