CN101380870B - Production method of artificial rockery - Google Patents
Production method of artificial rockery Download PDFInfo
- Publication number
- CN101380870B CN101380870B CN2008101431894A CN200810143189A CN101380870B CN 101380870 B CN101380870 B CN 101380870B CN 2008101431894 A CN2008101431894 A CN 2008101431894A CN 200810143189 A CN200810143189 A CN 200810143189A CN 101380870 B CN101380870 B CN 101380870B
- Authority
- CN
- China
- Prior art keywords
- artificial
- lime stone
- artificial hillock
- clay powder
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a method for making an artificial rockwork which is manufactured by the procedures of welding by using framework of steel reinforcement, filling stuffing, wet masonry, superficial treatment, maintaining rockwork body, etc. The artificial rockwork made by the method has the advantages of high intensity, strong toughness, multiple shapes, excellent verisimilitude, convenient production, easy transportation, etc.
Description
Technical field
The present invention relates to a kind of preparation method of artificial rockery.
Background technology
What busy work allowed people pursue the nature a home from home requires growingly, and the hope that the restriction of city condition makes people get close to the Nature is difficult to realize.So artificial hillock in different poses and with different expressions has occurred, brought beautiful enjoyment for people's work and living environment.But natural artificial hillock quantity is few, and type is more fixing, and moulding also is difficult to change, and does not catch up with the changeable demand of people gradually.The appearance of artificial rockery has remedied the weak point of natural artificial hillock again.It can simulate stalactitic form, allows collection lime stone water quality elite in 1,100 among the Shen Zang cave and the stalactite that forms is come into everybody visual field on ordinary days.Satisfied the artistic connotation that has also enriched artificial hillock when numerous fans and audience require.
Summary of the invention
The present invention aims to provide a kind of preparation method of artificial rockery.
The preparation method of artificial rockery of the present invention is earlier according to the designing requirement weldering system framework of steel reinforcement identical with the artificial hillock shape, adopt different size, different size and difform lime stone plates as filler again, grout out the artificial hillock body with the cement of certain proportion allotment and the mortar of lime stone fine sand, with mortar the reinforcing bar that exposes outside the artificial hillock body surface is whitewashed again, and then artificial hillock body body surface is done painted processing with the thin pulp that yellow clay powder, lime stone fine sand and water are deployed into, carry out maintenance with clear water at last.
The concrete preparation method of artificial rockery of the present invention is, the framework of steel reinforcement of the artificial hillock homomorphosis at first being welded into and designing by reinforcing bar, again with different size, different sizes and difform lime stone plates are as filler, fine sand after pulverizing with 800 label cement and lime stone is made into mortar in cement than 1: 1 ratio of fine sand and grouts into the artificial hillock body, with mortar the reinforcing bar that exposes outside the artificial hillock body surface is whitewashed once again, it whitewashes thickness is the 2-5 millimeter, adopt siliceous again, the more rich diameter of calcium is that the natural yellow clay powder of 0.02-0.2 millimeter and lime stone fine sand and water that diameter is the 0.02-0.2 millimeter are made into thin pulp, thin pulp through three titration on the artificial hillock surface, its thickness is the 3-5 millimeter, after treating the slurry surface dewatering, used the clear water maintenance again 10-15 days.
The inventive method is made artificial rockery, has following advantage: 1, artificial rockery can design and produce the position of various green plantss of cultivation and flowers, and the whole layout of artificial hillock is beautified more.2, the intensity of artificial rockery, hardness are all greater than natural stalactite.Particularly impact flexibility be the nature artificial hillock 3-5 doubly.3, all identical with the natural artificial hillock rate of artificial rockery color and form reaches more than 90%.Color has particularly adopted occurring in nature is siliceous, calcium is heavier yellow or red clay to do the pigment preparation, through experiment repeatedly, no matter the sun is exposed to the sun, exposes to wind and rain, and does not fade, and is basic identical with the stalactite in the karst cave.4, artificial rockery can design and make differing heights, and different sizes, and different shape in different poses and with different expressions are to satisfy all kinds of personages' esthetic requirement.No matter 5, artificial rockery is how high much, all is an integral body, need not bonding for the second time or make up overlapping.Can in factory building, make, also can make at the scene.
Claims (1)
1. the preparation method of an artificial rockery, it is characterized in that earlier according to the designing requirement weldering system framework of steel reinforcement identical with the artificial hillock shape, adopt different size again, big or small and difform lime stone plates are as the skeleton filler, grout out the artificial hillock body with 800 label cement and lime stone fine sand with the mortar of ratio allotment in 1: 1, mortar with the 2-5 millimeters thick covers the body surface reinforcing bar again, again with siliceous, the more rich natural yellow clay of calcium is ground into the clay powder that diameter is about the 0.02-0.2 millimeter, be made into thin pulp with described clay powder with lime stone fine sand and the water identical with described clay powder degree, on the artificial hillock surface, its thickness is the 3-5 millimeter to thin pulp through three titration; After treating the slurry surface dewatering, used the clear water maintenance again 10-15 days.