CN101376577A - Plastic and solid waste combined building material and production method thereof - Google Patents
Plastic and solid waste combined building material and production method thereof Download PDFInfo
- Publication number
- CN101376577A CN101376577A CNA2007101211298A CN200710121129A CN101376577A CN 101376577 A CN101376577 A CN 101376577A CN A2007101211298 A CNA2007101211298 A CN A2007101211298A CN 200710121129 A CN200710121129 A CN 200710121129A CN 101376577 A CN101376577 A CN 101376577A
- Authority
- CN
- China
- Prior art keywords
- plastics
- mixing
- solid waste
- manufacture method
- weight parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a plastic and solid waste composite building material which comprises the following raw materials: 30-60 weight parts of plastic and 40-70 weight parts of solid waste, wherein, the plastic is one or more mixture from polyethylene, polyvinyl chloride, polypropylene, polystyrene and polyethylene terephthalate; the solid waste is one or more mixture from of furnace slag, fly ash, building material industry dust and dewatered sludge; and the building material is obtained by uniformly mixing the raw materials in proportion and delivering the raw materials to a pressing machine for press forming after the temperature is raised to 120-180 DEG C. The invention has the advantages that the sources of the raw materials are wider, washing is not required in processing, no adhesive is adopted, and the plastic raw material cannot decompose, thereby having no environmental pollution during the production process; and the product is nontoxic and odorless, and can be recycled for reuse after abrasion, no secondary pollution is caused, scraps and scrap products are all recycled and reutilized in time, and the requirements and the predominant ideas of clean production are satisfied.
Description
Technical field
The present invention relates to a kind of material of construction and manufacture method thereof, particularly a kind of plastics and solid waste combined material of construction and manufacture method thereof.
Background technology
Along with the raising of people's living standard, the waste that produces in the daily life is also said benefit and is increased, and causes the environmental pollution and the wasting of resources.For this reason, the multiple building material product that utilizes waste to make appears in the prior art, CN1109451 discloses a kind of foaming plastic ceramic coals ash cement light wall material, by 1.0-2.5 weight part particle diameters be not more than expanded plastic (polystyrene) waste of 10mm, ceramics powder, 20-40 weight part flyash and 100 parts by weight of cement that 5-15 weight part particle diameters are not more than 1mm mix, add an amount of water furnishing pasty state, the mould that injects required specification solidifies and gets, this materials for wall need use a large amount of cement, and cost is higher.
CN1386797 discloses a kind of material of construction and manufacture method thereof, it is characterized in that making by flyash, waste and old or new plastic, the weight percentage of each composition is: coal dust ash 40-75%, waste and old or new plastic 60-25%, the method for making this product are to finish through batching, heating, extrusion molding operation.But this method adopts 250-290 ℃ of high temperature to make plastic melt, and extrusion molding because the pyrolysated effect can generate poisonous and irritating smog, causes environmental pollution, does not meet the requirement of cleaner production.
CN1405226 discloses a kind of waste-plastic-ceramic powder light pseudo-white-marble building decorative material and manufacture method thereof, the raw material that adopts is the waste polyethylene particle 21%～60% of 2～3 millimeters of particle diameters, waste and old polystyrol particle 0～18%, fineness is the ripe ceramics powders 35%～65% of 1000～1500 purposes, pigment 0～5%, manufacture method is for to be ground into 2～3 millimeters fritter with waste polyethylene and/or polystyrene, waste old ceramics is ground into 1000～1500 purpose particles, again the two and pigment are mixed, and be heated to 90～95 degrees centigrade, drop into mould, with 200～315 tons of pressing machine compactings 5～10 minutes.This method only can be applicable to and adopt ripe ceramics powder to make pseudo-white-marble building decorative material, and its Heating temperature is 90～95 degrees centigrade, and plastics have just begun to soften under this temperature, as yet with the unclassified stores fusion, therefore the material of construction performance that obtains is general.
Summary of the invention
Therefore, the object of the present invention is to provide a kind of plastics and solid waste combined material of construction, this material of construction main raw material is plastics and solid waste, and its excellent property.
Another object of the present invention is to provide the manufacture method of a kind of plastics and solid waste combined material of construction, and this method environmental pollution is little, and its manufacturing processed meets the requirement of cleaner production.
In order to realize purpose of the present invention, a kind of plastics and solid waste combined material of construction are provided, the raw material of described material of construction is the plastics of 30-60 weight parts and the solid waste of 40-70 weight parts; Described plastics are one or more the mixing in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate; Described solid waste is one or more the mixing in boiler ash sediment, flyash, building material industry dust and the dewatered sludge; Described material of construction is by with described raw material uniform mixing and be warming up to 120-180 ℃ and send into that compression moulding makes in the pressing machine again in proportion.Among the present invention, boiler ash sediment, flyash mainly are the coal slags after the burning, the industrial dust that building material industry dust mainly produces in process of production from building material industry departments such as cement mill, Bricks and Tiles Plant, asbestos factory, ore powder factories, dewatered sludge are mainly from sewage being handled the mud that the back produces.Material of construction of the present invention can utilize multiple plastics and solid waste, and raw material sources are extensive.And, during intensification temperature is controlled at 120-180 ℃ and can guarantees plastics fully fusing in this process, but do not begin to decompose, simultaneously the mixture of raw material begins fluffy softening, outward appearance and is loose cotton-shaped, suppress under such situation, both make plastics and other compositions combine closely, do not produced the gas that environment is polluted again.
Plastics of the present invention are preferably the mixing of waste plastic bag or multiple waste plastic bag; The major ingredient of this waste plastic bag is a kind of in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate, in addition also may contain a small amount of conventional auxiliary material.It is that the multiple waste plastic bag of major ingredient mixes and is used as one of raw material of material of construction of the present invention that the present invention can adopt with the different material.Adopting the waste plastic bag is the handling problem that raw material can solve the waste plastic bag, reduces the environmental pollution that produces because of landfill or burning " white garbage ".Simultaneously, the waste plastic bag is because itself is more frivolous than plastic grain, in technological process of the present invention with other compositions to combine effect better, the quality product that obtains under same intensification temperature is better.Adopting the waste plastic bag is under the situation of raw material, and the used starting material of the present invention are all taken from waste, and product processing does not produce pollution, finished product base material reusable edible.
In order to realize another object of the present invention, the manufacture method of a kind of plastics and solid waste combined material of construction is provided, this method may further comprise the steps successively:
A. prepare the plastics of 30-60 weight parts and the solid waste of 40-70 weight parts, and solid waste is processed into meal;
B. with the above-mentioned raw materials uniform mixing, be warming up to 120-180 ℃; And
C. raw material is sent into compression moulding in the pressing machine.
Wherein, described plastics are one or more the mixing in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate; Described solid waste is one or more the mixing in boiler ash sediment, flyash, building material industry dust and the dewatered sludge.Described plastics are the mixing of waste plastic bag or multiple waste plastic bag; The major ingredient of described waste plastic bag is a kind of in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate.
100-1000 purpose meals preferably are processed into solid waste in the present invention.Meal in this scope is easier to combine with plastics, and forms fluffy floss in the time of 120-180 ℃.
The pressure of preferred pressure machine of the present invention is 200-315 tons.The time of preferred compression moulding is 5-10 minutes, and the product that obtains in such short period can reach requirement, has improved production efficiency, has reduced cost.Pressing machine of the present invention is a 200-315 ton four-column hydraulic press.
Intensification of the present invention is evenly to heat up, and the heating-up time is 30-60 minutes.Even intensification like this can guarantee further that plastics change molten state gradually into, decomposing phenomenon can not take place, and also helps the formation of fluffy floss.
Intensification of the present invention with mix and can carry out simultaneously, further shorten the process time, raise the efficiency, save cost.
The outlet temperature that the present invention heats up can be more preferably 140-160 ℃.
The preferred described mixing of the present invention is carried out the mixing machine in the promptly mechanical industry standard among the JB/T7669-2004 with intensification in plastics mixer.Can adopt vertical or horizontal cold mixing machine that raw material is mixed the back with extra heating unit heating raw, the preferred Hot mixer that adopts is finished mixing and heating simultaneously, process time can be shortened, raise the efficiency, save cost, fluffy softening, the outward appearance that can also increase the raw material when mixing are loose cotton-shaped effect, more help the raising of final product quality.
The invention has the beneficial effects as follows: the present invention can utilize multiple plastics and multiple solid waste to obtain material of construction, and the source of raw material is wider; When the present invention heats up temperature is controlled at 120-180 ℃ and can guarantees plastics fully fusing in this process, but do not begin to decompose, the mixture of raw material began fluffy softening, outward appearance and was loose cotton-shaped this moment, drop into mould through the pressing machine compacting, make closely knit, the curing molding at normal temperatures of mixture, can be made into brick, watt and section bar, simultaneously can also be to the raw material sterilization that carries out disinfection in this temperature; Therefore the present invention does not need washing man-hour adding, and does not adopt any tackiness agent yet, and plastic raw materials can not decompose yet, and can not produce environmental pollution in process of production; Product is nonpoisonous and tasteless, can also recycle and reuse after the breakage, does not produce secondary pollution, and all scrap stock and scrap products are all recycled immediately, meets the requirement and the dominant ideas of cleaner production.
Product of the present invention detects according to the building material industry standard JC/T446-2000 of the People's Republic of China (PRC), and its result is:
A) ultimate compression strength mean value 〉=35.0
B) folding strength mean value 〉=5.00
C) fastness to rubbing 〉=1.9
D) water-intake rate (%)≤8.0
E) frost resistance≤20%
Therefore, product of the present invention meets building materials environmental-protecting performance, technical feature, quality life-span performance etc. fully and characterizes performance index of product technologies requirement, mainly can be used as the special-purpose pavior brick of ancient building, city brick, watt, city sidewalk floor tile, paving tile, lawn brick, " city furniture " (as road side seat chair, greenery patches guardrail, Hua Chi, litterbin), and light body sound absorption and insulation plate and artwork etc.
Embodiment
Embodiment 1
With 100 purpose flyash uniform mixing of the polyvinyl chloride particles of 30 weight parts and 70 weight parts and be warming up to 140 ℃, adopt vertical cold mixing machine to mix, heating up is even intensification, adopts the container of strap clamp cover, and logical steam heats up in the chuck, and the heating-up time is 60 minutes.At last fluffy softening, outward appearance is loose cotton-shaped raw material and sends into compression moulding in the pressing machine, pressure is 200 tons, and the time of compression moulding is 10 minutes, can obtain product.
Embodiment 2
With 500 purpose boiler ash sediment uniform mixing of the waste and old polypropylene particle of 40 weight parts and 60 weight parts and be warming up to 150 ℃, adopt horizontal cold mixing machine to mix, heating up is even intensification, adopts the container of strap clamp cover, logical steam heats up in the chuck, and the heating-up time is 50 minutes.At last fluffy softening, outward appearance is loose cotton-shaped raw material and sends into compression moulding in the pressing machine, pressure is 240 tons, and the time of compression moulding is 9 minutes, can obtain product.
Embodiment 3
The major ingredient of 50 weight parts is 1000 purpose building material industry dust uniform mixing of poly waste plastic bag and 50 weight parts and is warming up to 120 ℃ heating up is even intensification, adopt Hot mixer, mix with intensification and carry out simultaneously, the heating-up time is 30 minutes.At last fluffy softening, outward appearance is loose cotton-shaped raw material and sends into compression moulding in the pressing machine, pressure is 315 tons, and the time of compression moulding is 5 minutes, can obtain product.
Embodiment 4
The major ingredient of 60 weight parts is 800 purpose dewatered sludge uniform mixing of waste polyethylene terephthalate plastics bag and 40 weight parts and is warming up to 180 ℃, heat up to evenly heating up, adopt Hot mixer, mix with intensification and carry out simultaneously, the heating-up time is 20 minutes.At last fluffy softening, outward appearance is loose cotton-shaped raw material and sends into compression moulding in the pressing machine, pressure is 350 tons, and the time of compression moulding is 4 minutes, can obtain product.
Embodiment 5
Mixing together according to 1:1:1 (weight) polyethylene, polypropylene, the polyethylene terephthalate waste plastic bag of totally 40 weight parts, the ratio of mixture of 60 weight parts is 600 purpose boiler ash sediments, flyash and the dewatered sludge uniform mixing of 1:1:1 (weight) and is warming up to 160 ℃ again, heat up to evenly heating up, adopt Hot mixer, mix with intensification and carry out simultaneously, the heating-up time is 60 minutes.At last fluffy softening, outward appearance is loose cotton-shaped raw material and sends into compression moulding in the pressing machine, pressure is 280 tons, and the time of compression moulding is 7 minutes, can obtain product.
Embodiment 6
The waste and old polystyrol particle of 60 weight parts and the ratio of mixture of 40 weight parts are 1200 purpose flyash, the building material industry dust uniform mixing of 1:2 and are warming up to 170 ℃, heat up to evenly heating up, adopt Hot mixer, mix with intensification and carry out simultaneously, the heating-up time is 80 minutes.At last fluffy softening, outward appearance is loose cotton-shaped raw material and sends into compression moulding in the pressing machine, pressure is 220 tons, and the time of compression moulding is 15 minutes, can obtain product.
Above embodiment is used to explain the present invention, and unrestricted the present invention.Wherein, the plastics in the raw material can be new, old plastic grain or waste plastic bag, and composition/major ingredient is that one or more the mixing in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate all can realize the present invention; Equally, solid waste is that one or more mixing in boiler ash sediment, flyash, building material industry dust and the dewatered sludge also all can realize the present invention; In addition, mix and intensification equipment also can adopt other similar devices of the prior art, it is other pressing machinees of 200-315 tons that pressing machine also can be selected pressure for use; Press time, the simple change of the granularity of raw material etc. all should belong within protection scope of the present invention.
Claims (10)
1. plastics and solid waste combined material of construction is characterized in that, the raw material of described material of construction is the plastics of 30-60 weight parts and the solid waste of 40-70 weight parts; Described plastics are one or more the mixing in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate; Described solid waste is one or more the mixing in boiler ash sediment, flyash, building material industry dust and the dewatered sludge; Described material of construction is by with described raw material uniform mixing and be warming up to 120-180 ℃ and send into that compression moulding makes in the pressing machine again in proportion.
2. material of construction as claimed in claim 1 is characterized in that, described plastics are the mixing of waste plastic bag or multiple waste plastic bag; The major ingredient of described waste plastic bag is a kind of in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate.
3. the manufacture method of plastics and solid waste combined material of construction is characterized in that this method may further comprise the steps successively:
A. prepare the plastics of 30-60 weight parts and the solid waste of 40-70 weight parts, and solid waste is processed into meal;
B. with the above-mentioned raw materials uniform mixing and be warming up to 120-180 ℃; And
C. raw material is sent into compression moulding in the pressing machine;
Wherein, described plastics are one or more the mixing in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate; Described solid waste is one or more the mixing in boiler ash sediment, flyash, building material industry dust and the dewatered sludge.
4. manufacture method as claimed in claim 3 is characterized in that, described plastics are the mixing of waste plastic bag or multiple waste plastic bag; The major ingredient of described waste plastic bag is a kind of in polyethylene, polyvinyl chloride, polypropylene, polystyrene, the polyethylene terephthalate.
5. manufacture method as claimed in claim 3 is characterized in that, described meal is 100-1000 purpose meals.
6. manufacture method as claimed in claim 3 is characterized in that the pressure of described pressing machine is 200-315 tons.
7. as claim 3 or 6 described manufacture method, it is characterized in that the time of described compression moulding is 5-10 minutes.
8. manufacture method as claimed in claim 3 is characterized in that, described intensification is evenly to heat up, and the heating-up time is 30-60 minutes.
9. as claim 3 or 8 described manufacture method, it is characterized in that described mixing is carried out simultaneously with intensification.
10. as claim 3 or 8 or 9 described manufacture method, it is characterized in that described mixing is carried out in plastics mixer with intensification.