CN101362651A - 一种新的莫来石轻质隔热保温砖的配方 - Google Patents

一种新的莫来石轻质隔热保温砖的配方 Download PDF

Info

Publication number
CN101362651A
CN101362651A CNA2008100152282A CN200810015228A CN101362651A CN 101362651 A CN101362651 A CN 101362651A CN A2008100152282 A CNA2008100152282 A CN A2008100152282A CN 200810015228 A CN200810015228 A CN 200810015228A CN 101362651 A CN101362651 A CN 101362651A
Authority
CN
China
Prior art keywords
parts
percentage composition
heat insulating
insulating brick
light heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008100152282A
Other languages
English (en)
Other versions
CN101362651B (zh
Inventor
赵友谊
陈勇
纪淑芸
于冬镇
李建民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jingang New Materials Co., Ltd.
Original Assignee
ZOUPING JINGANG NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZOUPING JINGANG NEW MATERIAL CO Ltd filed Critical ZOUPING JINGANG NEW MATERIAL CO Ltd
Priority to CN2008100152282A priority Critical patent/CN101362651B/zh
Publication of CN101362651A publication Critical patent/CN101362651A/zh
Application granted granted Critical
Publication of CN101362651B publication Critical patent/CN101362651B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于耐火材料领域，尤其涉及一种新的莫来石轻质隔热保温砖的配方。提供了一种新的莫来石轻质隔热保温砖的配方。莫来石轻质隔热保温砖的组分包括湛江土，蓝晶石，硅线石，煅烧氧化铝，同型号废品回料，再加EPS聚轻球，锯末。该产品相同体积密度下耐压强度比同行高10％左右，比其他配方更有利于工艺过程控制和产品质量的稳定。

Description

一种新的莫来石轻质隔热保温砖的配方
技术领域
本发明属于耐火材料领域，尤其涉及一种新的莫来石轻质隔热保温砖的配方。
背景技术
莫来石是一种富铝红柱石，无色，晶体呈柱状或针状，熔融温度为1910℃，是陶瓷制品的主要成分。莫来石主要是铝硅酸盐矿物，其天然矿物在地壳中存在很少，因首先在苏格兰莫来岛发现，故称莫来石。但人造莫来石确是一种常见且应用广泛的矿物，莫来石的化学成分并不稳定，常见的有3Al2O3·2SiO2以及2Al2O3·SiO2两种形式。莫来石是一种优质的耐火原料，它具有膨胀均匀，热震稳定性极好，荷重软化点高，高温蠕变值小，硬度大，抗化学腐蚀性好等特点。传统的配方存在着如下缺陷：配方主要组成比较复杂，原料质量波动给生产带来困难，不利于工艺过程的控制和产品质量的稳定。
发明内容
本发明针对现有技术的不足，提供了一种新的莫来石轻质隔热保温砖的配方。莫来石轻质隔热保温砖的组分包括湛江土，蓝晶石，硅线石，煅烧氧化铝，同型号废品回料，再加EPS聚轻球，锯末。
莫来石轻质隔热保温砖包括如下组分，均以重量份计，湛江土28～32份，蓝晶石3～7份，硅线石7～12份，煅烧氧化铝27～31份，同型号废品回料23～29份，EPS聚轻球23～27份，锯末23～27份。
其中选用的湛江土的Al2O3百分含量不少于37％，蓝晶石的Al2O3百分含量不少于53％，硅线石的Al2O3百分含量不少于56％，煅烧氧化铝的Al2O3百分含量不少于99％。
莫来石轻质隔热保温砖的制备方法采用通常的工艺流程，即配料→精确称料→混合搅拌→陈腐→挤坯→干燥→高温烧成→切磨→检查测试→包装入库。
莫来石的有效成分是氧化铝和氧化硅，但是基于各种原料之中，氧化铝含量决定材料的耐火度，，因此在实际生产中，一般选择只调试氧化铝的含量来控制工艺过程，从而保证了莫来石产品的质量。
有益效果：该产品相同体积密度下耐压强度比同行高10％左右(3.2兆帕比2.8兆帕)选用比较常见的富含氧化铝和氧化硅的原料，供应充足且价格合适；配方组分比其他常规配方种类少，在工业生产中根据原料质量情况比较容易进行调节，而且选用的原料细度比较适中(≤200目的占≥95％)，比其他配方更有利于工艺过程控制和产品质量的稳定，更适合大规模批量型生产，其耐火温度为1520-1550℃。
具体实施方式
实施例1
莫来石轻质隔热保温砖包括如下组分，均以重量份计：湛江土28份，蓝晶石3份，硅线石7份，煅烧氧化铝27份，同型号废品回料23份，EPS聚轻球23份，锯末23份。
其中选用的湛江土的Al2O3百分含量37％，蓝晶石的Al2O3百分含量53％，硅线石的Al2O3百分含量56％，煅烧氧化铝的Al2O3百分含量99％。产品相同体积密度下耐压强度比同行高10％左右。
莫来石轻质隔热保温砖的制备方法同本发明说明书中所述。
实施例2
莫来石轻质隔热保温砖包括如下组分，均以重量份计：湛江土30份，蓝晶石5份，硅线石10份，煅烧氧化铝29份，同型号废品回料25份，EPS聚轻球25份，锯末25份。
其中选用的湛江土的Al2O3百分含量39％，蓝晶石的Al2O3百分含量55％，硅线石的Al2O3百分含量58％，煅烧氧化铝的Al2O3百分含量为99％。产品相同体积密度下耐压强度比同行高10％左右。
莫来石轻质隔热保温砖的制备方法同本发明说明书中所述。
实施例3
莫来石轻质隔热保温砖包括如下组分，均以重量份计：湛江土32份，蓝晶石7份，硅线石11份，煅烧氧化铝31份，同型号废品回料28份，EPS聚轻球26份，锯末27份。
其中选用的湛江土的Al2O3百分含量41％，蓝晶石的Al2O3百分含量56％，硅线石的Al2O3百分含量57％，煅烧氧化铝的Al2O3百分含量99％。产品相同体积密度下耐压强度比同行高10％左右。
莫来石轻质隔热保温砖的制备方法同本发明说明书中所述。

Claims (9)

1.一种新的莫来石轻质隔热保温砖，其特征在于：包括如下组分：湛江土，蓝晶石，硅线石，煅烧氧化铝，同型号废品回料，再加EPS聚轻球，锯末。
2.如权利要求1所述的莫来石轻质隔热保温砖，其特征在于：包括如下组分，均以重量份计：湛江土28～32份，蓝晶石3～7份，硅线石7～12份，煅烧氧化铝27～31份，同型号废品回料23～29份，EPS聚轻球23～27份，锯末23～27份。
3.如权利要求1所述的莫来石轻质隔热保温砖，其特征在于：所述的湛江土中Al2O3百分含量不少于36％。
4.如权利要求1所述的莫来石轻质隔热保温砖，其特征在于：所述的蓝晶石中Al2O3百分含量不少于53％。
5.如权利要求1所述的莫来石轻质隔热保温砖，其特征在于：所述的硅线石中Al2O3百分含量不少于56％。
6.如权利要求1所述的莫来石轻质隔热保温砖，其特征在于：所述的煅烧氧化铝Al2O3百分含量不少于99％。
7.如权利要求1所述的莫来石轻质隔热保温砖包括如下组分，均以重量份计：湛江土28份，蓝晶石3份，硅线石7份，煅烧氧化铝27份，同型号废品回料23份，EPS聚轻球23份，锯末23份；其中选用的湛江土的Al2O3百分含量37％，蓝晶石的Al2O3百分含量53％，硅线石的Al2O3百分含量56％，煅烧氧化铝的Al2O3百分含量99％。
8.如权利要求1所述的莫来石轻质隔热保温砖包括如下组分，均以重量份计：湛江土30份，蓝晶石5份，硅线石10份，煅烧氧化铝29份，同型号废品回料25份，EPS聚轻球25份，锯末25份；其中选用的湛江土的Al2O3百分含量39％，蓝晶石的Al2O3百分含量55％，硅线石的Al2O3百分含量58％，煅烧氧化铝的Al2O3百分含量为99％。
9.如权利要求1所述的莫来石轻质隔热保温砖包括如下组分，均以重量份计：湛江土32份，蓝晶石7份，硅线石11份，煅烧氧化铝31份，同型号废品回料28份，EPS聚轻球26份，锯末27份；其中选用的湛江土的Al2O3百分含量41％，蓝晶石的Al2O3百分含量56％，硅线石的Al2O3百分含量57％，煅烧氧化铝的Al2O3百分含量99％。
CN2008100152282A 2008-04-11 2008-04-11 一种新的莫来石轻质隔热保温砖的配方 Expired - Fee Related CN101362651B (zh)