CN102775129A - 一种莫来石轻质微孔隔热保温砖 - Google Patents

一种莫来石轻质微孔隔热保温砖 Download PDF

Info

Publication number
CN102775129A
CN102775129A CN2012102509407A CN201210250940A CN102775129A CN 102775129 A CN102775129 A CN 102775129A CN 2012102509407 A CN2012102509407 A CN 2012102509407A CN 201210250940 A CN201210250940 A CN 201210250940A CN 102775129 A CN102775129 A CN 102775129A
Authority
CN
China
Prior art keywords
mullite
heat insulating
weight
thermal insulation
insulating brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102509407A
Other languages
English (en)
Inventor
山国强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012102509407A priority Critical patent/CN102775129A/zh
Publication of CN102775129A publication Critical patent/CN102775129A/zh
Pending legal-status Critical Current

Abstract

本发明属于耐火材料领域，尤其涉及一种莫来石轻质微孔隔热保温砖，提供了一种新的莫来石轻质微孔隔热保温砖的配方。莫来石轻质微孔隔热保温砖的组分包括广西泥，蓝晶石，氧化铝粉，同型号废品回料，再加炭黑，无烟煤。该产品相同体积密度下耐压强度比同行高25%左右，热导系数低50%以上，保温效果更好，有利于节能减排，同时比其他配方更有利于工艺过程和产品质量控制。

Description

一种莫来石轻质微孔隔热保温砖
技术领域
本发明属于耐火材料领域，尤其涉及一种莫来石轻质微孔隔热保温砖的配方。 
背景技术
莫来石是一种富铝红柱石，无色，晶体呈柱状或针状，熔融温度为1840℃，莫来石主要是铝硅酸盐矿物，其天然矿物在地壳中存在很少，因首先在英国苏格兰莫来岛发现，故称莫来石。但人造莫来石确是一种常见且应用广泛的矿物，莫来石的化学成分并不稳定，常见的有3Al2O3.2SiO2以及2Al2O3.SiO2两种形式。莫来石是一种优质的耐火原料，它具有膨胀均匀，热震稳定性极好，荷重软化点高，高温蠕变值小，硬度大，抗化学腐蚀性好等特点。传统的配方存在着如下缺陷：配方主要组成比较复杂，原料质量波动给生产带来困难，不利于工艺过程的控制和产品质量的稳定。 
  
发明内容
本发明针对现有技术不足，提供了一种莫来石轻质微孔隔热保温砖的配方，莫来石轻质微孔隔热保温砖的组分包括广西泥，蓝晶石，红柱石，氧化铝微粉，同型号废品回料，再加炭黑，无烟煤。 
莫来石轻质微孔隔热保温砖包括如下组分，均以重量份计，广西泥28-32份，蓝晶石3-7份，红柱石6-11份，氧化铝微粉27-31份，同型号废品回料22-30份，炭黑24-28份，无烟煤24-28份。 
其中选用的广西泥的Al2O3百分含量不少于32%,蓝晶石的Al2O3百分含量不少于53%，红柱石的Al2O3百分含量不少于55%，氧化铝微粉的Al2O3百分含量不少于99%。 
莫来石轻质微孔隔热保温砖的制备方法采用通常的工艺流程，即配料-精确称量-混合搅拌-陈腐-挤坯-干燥-高温烧成-切磨-检查测试-包装入库。 
莫来石的有效成分是氧化铝和氧化硅，但是基于各种原料之中，氧化铝含量决定材料的耐火度，因此在实际生产中，一般选择只调试氧化铝的含量来控制工艺过程，从而保证了莫来石产品的质量。 
有益效果：该产品选用炭黑、无烟煤作为烧失物，内部形成微孔结构，根据传热学原理，在同材质同样气孔率下，微孔更有利于隔热，微孔更有利于获得高强度。相同体积密度下耐压强度比同行高25%左右，热导率低50%以上，选用比较常用的富含氧化铝和氧化 硅的原料，供应充足且价格合适；配方组分比其他常规配方种类少，在工业生产中根据原料质量情况比较容易进行调节，比其它配方更有利于工艺过程控制和产品质量的稳定，更适合大规模批量型生产，其耐火温度为1550℃以上。 
具体实施方式
实施例1 
莫来石轻质微孔隔热保温砖包括如下组分，均以重量份计：广西泥28份，蓝晶石3份，红柱石7份，氧化铝微粉27份，同型号废品回料23份，炭黑23份，无烟煤23份；其中选用的广西泥的Al2O3百分含量37%，蓝晶石的Al2O3百分含量53%，红柱石的Al2O3百分含量56%，氧化铝微粉的Al2O3百分含量99%。产品相同体积密度下耐压强度比同行高25%左右，热导率低55%； 莫来石轻质微孔隔热保温砖的制备方法同本发明说明书中所述。
实施例2 
莫来石轻质微孔隔热保温砖包括如下组分，均以重量份计：广西泥30份，蓝晶石5份，红柱石10份，氧化铝微粉29份，同型号废品回料25份，炭黑25份，无烟煤25份；其中选用的广西泥的Al2O3百分含量33%，蓝晶石的Al2O3百分含量55%，红柱石的Al2O3百分含量58%，氧化铝微粉的Al2O3百分含量为99%.产品相同体积密度下耐压强度比同行高28%左右，热导率低58%，莫来石轻质微孔隔热保温砖的制备方法同本发明说明书中所述。 

Claims (7)

1.一种新的莫来石轻质微孔隔热保温砖，其特征在于：包括如下组分：广西泥，蓝晶石，红柱石，氧化铝微粉，同型号废品回料，再加炭黑，无烟煤。
2.如权利要求1所述的莫来石轻质微孔隔热保温砖，其特征在于：包括如下组分，均以重量份计：广西泥28-32份，蓝晶石3-7份，红柱石6-11份，氧化铝微粉27-31份，同型号废品回料22-30份，炭黑24-28份，无烟煤24-28份。
3.如权利要求1所述的莫来石轻质微孔隔热保温砖，其特征在于：所述的广西泥中A12O3百分含量不少于32%。
4.如权利要求1所述的莫来石轻质微孔隔热保温砖，其特征在于：所述的蓝晶石中A12O3百分含量不少于53%。
5.如权利要求1所述的莫来石轻质微孔隔热保温砖，其特征在于：所述的红柱石中A12O3百分含量不少于55%。
6.如权利要求1所述的莫来石轻质微孔隔热保温砖，其特征在于：所述的氧化铝微粉A12O3百分含量不少于99%。
7.如权利要求1所述的莫来石轻质微孔隔热保温砖，其特征在于：所述的炭黑和无烟煤的粒度为10微米以下。 
CN2012102509407A 2012-07-19 2012-07-19 一种莫来石轻质微孔隔热保温砖 Pending CN102775129A (zh)