CN101358017B - 一种以高分子脂肪酸金属盐与烃类树脂混合制成优均素的制备方法 - Google Patents
一种以高分子脂肪酸金属盐与烃类树脂混合制成优均素的制备方法 Download PDFInfo
- Publication number
- CN101358017B CN101358017B CN200810139218XA CN200810139218A CN101358017B CN 101358017 B CN101358017 B CN 101358017B CN 200810139218X A CN200810139218X A CN 200810139218XA CN 200810139218 A CN200810139218 A CN 200810139218A CN 101358017 B CN101358017 B CN 101358017B
- Authority
- CN
- China
- Prior art keywords
- resin
- carbon
- fatty acid
- hydrocarbon resin
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种以高分子脂肪酸金属盐与烃类树脂混合制成优均素的制备方法，属于有机合成技术领域。以硬脂酸锌、碳五树脂和碳九树脂为主要原料，其特征在于制备方法按如下步骤依次进行：(1)以硬脂酸锌和碳五树脂、碳九树脂为原料，在常压反应器中，控制反应温度170℃—190℃，时间≥2小时，生成高分子脂肪酸盐-烃类树脂组成的混合物。(2)在上述体系中加入橡胶沥青，控制温度170℃—190℃，时间≥2小时，生成成品优均素。本发明制备出的优均素广泛用于天然橡胶、合成橡胶及塑料，能改善不同极性、不同粘度胶料在混炼时的均相性和稳定性。显著提高胶料的定伸强度以及物理机械性能，从根本上克服了国内各类加工助剂对定伸强度降低的影响。
Description
技术领域
本发明属于有机合成技术领域，具体涉及一种优均素制备优均素的工艺技术。
背景技术
在轮胎工业中，对不同极性及粘度橡胶的混和普遍采用均匀剂。均匀剂能改善不同极性、不同粘度胶料在混炼时的均相性和稳定性，使各种助剂与填料更加迅速、均匀的分散在橡胶中。目前国内使用的均匀剂有优胶素H、均匀剂A等。对降低橡胶料的门尼粘度，提高胶料的分散性效果明显，但普遍存在对定伸强度降低的影响。
发明内容
为克服现有技术不足，本发明提供一种以高分子脂肪酸金属盐与烃类树脂混合制成优均素的制备方法，能改善不同极性、不同粘度胶料在混炼时的均相性和稳定性。
本发明解决其技术问题所采用的技术方案是：发明一种以高分子脂肪酸金属盐与烃类树脂混合制成优均素的制备方法，以硬脂酸锌、碳五树脂和碳九树脂为主要原料，其特征在于制备方法按如下步骤依次进行：
(1)复合配制：以硬脂酸锌和碳五树脂、碳九树脂为原料，在常压反应器中，控制反应温度170℃——190℃，时间≥2小时，生成高分子脂肪酸盐-烃类树脂组成的混合物。
(2)制成成品：在上述体系中加入橡胶沥青，控制温度170℃——190℃，时间≥2小时，生成成品优均素。
本发明中各种原料消耗量为：硬脂酸锌10-12份，碳五树脂18-20份，碳九树脂50-52份，橡胶沥青20-22份。
制备本发明的消耗原料的性能及要求：
硬脂酸锌：分子式[CH3(CH2)16COO]2Zn，分子量631。
性状：硬脂酸锌为白色轻质粉状，比重1.095，熔点约120℃。不溶于水，溶于热的乙醇、苯和松节油等有机溶剂，遇强酸则分解为硬脂酸和相应的锌盐。
橡胶沥青：以原油蒸馏所得的减压渣油经适当条件下的氧化而制的。
性状：黑色固体，软化点125-135℃，针入度15-25，苯溶解度≥99.5％，闪点≥230℃，不溶于低沸点烷烃和丙酮、乙醚、稀乙醇，溶于二硫化碳、四氯化碳、吡啶等。
碳五树脂：
相对分子质量500—2000
性状：碳五树脂为浅黄色固体，相对密度为0.71—1.07，软化点70—110℃，不溶于水、甲醇、乙醇，溶于丙酮、甲乙酮、醋酸乙酯、二氯乙烷、环已烷、苯、甲苯、溶剂汽油等。
碳九树脂：
结构式
相对分子质量600—3000。
性状：碳九树脂为浅黄色至深琥珀色固体，相对密度0.970—0.975，软化点80—140℃，闪点260℃，不溶于水、甲醇、乙醇，溶于芳香烃和矿物油。
本发明制备出的优均素为热塑性树脂，为褐色或深褐色固体，可替代进口均匀剂40MSF，优于国内优胶素A、H2000、均匀剂A78等产品，广泛用于天然橡胶、合成橡胶及塑料，能改善不同极性、不同粘度胶料在混炼时的均相性和稳定性。使各种助剂与填料更加迅速、均匀的分散在橡胶中，对橡胶有润滑作用，并改善胶料的热流动性，使填充更大，有利于减少外观缺陷。能显著提高胶料的定伸强度以及物理机械性能，有效的降低胶料温升，从根本上克服了国内各类加工助剂对定伸强度降低的影响，撕裂强度上升，磨耗量下降。能提高胶料压运速度，延长硫化平坦时间，提高设备利用率，也提高了产品质量，减低生产成本。可以提高炭黑的分散性，缩短混炼时间，减少混炼能量，降低能耗，提高半成品的粘性，使各批胶料质量稳定、均匀，改善了胶料平滑性、流动性、平整性。
具体实施方式：
实施例一
将硬脂酸锌10g、碳五树脂209、碳九树脂50g依次加入500ml烧瓶中，控制反应温度为170℃，时间2小时。在170℃的温度中加入229橡胶沥青，均匀搅拌时间2小时后放料，得优均素YJ800产品，熔点85℃，灰分1.4％，外观呈深褐色固体。
实施例二
将硬脂酸锌129、碳五树脂19g、碳九树脂51g依次加入500ml烧瓶中，控制反应温度为175℃，时间3小时。在175℃的温度中加入219橡胶沥青，均匀搅拌时间3小时后放料，得优均素YJ800产品，熔点89℃，灰分1.6％，外观呈深褐色固体。
实施例三
将硬脂酸锌119、碳五树脂18g、碳九树脂529依次加入500ml烧瓶中，控制反应温度190℃，时间2小时。在190℃的温度中加入20g橡胶沥青，均匀搅拌时间2小时后放料，得优均素YJ800产品，熔点87℃，灰分1.3％，外观呈深褐色固体。
Claims (1)
1.一种以高分子脂肪酸金属盐与烃类树脂混合制成优均素的制备方法，以硬脂酸锌、碳五树脂和碳九树脂为主要原料，其特征在于制备方法按如下步骤依次进行：
(1)复合配制：以硬脂酸锌和碳五树脂、碳九树脂为原料，在常压反应器中，控制反应温度170℃——190℃，时间≥2小时，生成高分子脂肪酸盐-烃类树脂组成的混合物；
(2)制成成品：在上述体系中加入橡胶沥青，控制温度170℃——190℃，时间≥2小时，生成成品优均素；
上述各种原料消耗量为：硬脂酸锌10-12份，碳五树脂18-20份，碳九树脂50-52份，橡胶沥青20-22份。