CN101350406A - 储能用管式固定型铅酸蓄电池正极活性物质 - Google Patents

储能用管式固定型铅酸蓄电池正极活性物质 Download PDF

Info

Publication number
CN101350406A
CN101350406A CNA2008101396640A CN200810139664A CN101350406A CN 101350406 A CN101350406 A CN 101350406A CN A2008101396640 A CNA2008101396640 A CN A2008101396640A CN 200810139664 A CN200810139664 A CN 200810139664A CN 101350406 A CN101350406 A CN 101350406A
Authority
CN
China
Prior art keywords
lead
active substance
powder
respect
weight ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008101396640A
Other languages
English (en)
Other versions
CN101350406B (zh
Inventor
孔德龙
祝夫勤
赵兴强
宋斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Sacred Sun Power Sources Co Ltd
Original Assignee
Shandong Sacred Sun Power Sources Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Sacred Sun Power Sources Co Ltd filed Critical Shandong Sacred Sun Power Sources Co Ltd
Priority to CN2008101396640A priority Critical patent/CN101350406B/zh
Publication of CN101350406A publication Critical patent/CN101350406A/zh
Application granted granted Critical
Publication of CN101350406B publication Critical patent/CN101350406B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

储能用管式固定型铅酸蓄电池正极活性物质，由铅粉、红丹、纳米石墨、硫酸镁、木炭粉、二氧化硅组成。有益效果是：红丹的添加，可以提高正极活性物质的转化效率，缩短化成时间；纳米石墨的添加，其导电性能良好，可提高活性物质的导电能力，有利于蓄电池的充放电；硫酸镁、木炭粉、二氧化硅的添加，可有效提高活性物质的孔率，构建活性物质的网络结构，使电解液能有效地进入活性物质内部，以利于提高电池的大电流放电性能及活性物质的利用率；并且节能环保。

Description

储能用管式固定型铅酸蓄电池正极活性物质
技术领域
本发明涉及铅酸蓄电池领域，更具体地为一种储能用管式固定型铅酸蓄电池正极活性物质。
背景技术
铅酸蓄电池的性能好坏主要取决于正极的性能，尤其是管式固定型铅酸蓄电池，由于极板较厚，且骨架外部安装有一层涤纶材料的排管，有一定的电阻，长期以来存在着正极化成困难、活性物质(即铅膏)利用率低等问题，这就严重影响了电池的整体性能，使得重量比能量低且循环寿命短。针对此种情况，许多厂家采用小电流长时间化成工艺，虽然在一定程度上对正极板的化成有所提升，但此方法导致化成时间太长，浪费了大量的电能，从而造成了能源的浪费，且生产周期的增长，致使生产效率低下，无经济性可言。还有部分厂家在正极活性物质中加入某种单一的添加剂，虽然对管式正极板的化成有所改善，但总体作用不大，效果不够理想。
发明内容
本发明的目的是：克服目前管式固定型铅酸蓄电池技术中存在的不足，提供一种能够提高管式固定型铅酸蓄电池正极活性物质的孔率和利用率、缩短化成时间、提高蓄电池循环寿命、节能环保的储能用管式固定型铅酸蓄电池正极活性物质。
本发明的解决问题的技术方案是：储能用管式固定型铅酸蓄电池正极活性物质，由铅粉、红丹(Pb3O4)、纳米石墨(导电剂)、硫酸镁(MgSO4)、木炭粉、二氧化硅(SiO2)组成，其各成分所占的重量百分比为：
铅粉：65％-85％
红丹：(Pb3O4)：15％-35％
纳米石墨：1％-3％(相对于铅粉和红丹质量和的重量比)
硫酸镁：0.2％-0.4％(相对于铅粉和红丹质量和的重量比)
木炭粉：1％-4％(相对于铅粉和红丹质量和的重量比)
二氧化硅：0.5％-3.5％。(相对于铅粉和红丹质量和的重量比)。
储能用管式固定型铅酸蓄电池正极活性物质，其各成分所占的重量百分比最佳配比为：
铅粉：70％-75％
红丹：25％-30％
纳米石墨：1.5％-2.5％(相对于铅粉和红丹质量和的重量比)
硫酸镁：0.2％-0.3％(相对于铅粉和红丹质量和的重量比)
木炭粉：2.5％-3.0％(相对于铅粉和红丹质量和的重量比)
二氧化硅：2％-3％(相对于铅粉和红丹质量和的重量比)。
本发明的有益效果是：
1、红丹(Pb3O4)的添加，可以提高正极活性物质的转化效率，缩短化成时间。
2、纳米石墨的添加，其导电性能良好，可提高活性物质的导电能力，有利于蓄电池的充放电。
3、硫酸镁(MgSO4)、木炭粉、二氧化硅(SiO2)的添加，可有效提高活性物质的孔率，构建活性物质的网络结构，使电解液能有效地进入活性物质内部，以利于提高电池的大电流放电性能及活性物质的利用率。
具体实施方式
储能用管式固定型铅酸蓄电池正极活性物质，其各成分所占的重量百分比最佳配比为：
铅粉：70％-75％
红丹(Pb3O4)：25％-30％
纳米石墨：1.5％-2.5％(相对于铅粉和红丹质量和的重量比)
MgSO4：0.2％-0.3％(相对于铅粉和红丹质量和的重量比)
木炭粉：2.5％-3.0％(相对于铅粉和红丹质量和的重量比)
SiO2：2％-3％(相对于铅粉和红丹质量和的重量比)。

Claims (2)

1.储能用管式固定型铅酸蓄电池正极活性物质，其特征在于它包括铅粉、红丹、纳米石墨、硫酸镁、木炭粉、二氧化硅，其各成分所占的重量百分比为：
铅粉：65％-85％
红丹：15％-35％
纳米石墨：1％-3％(相对于铅粉和红丹质量和的重量比)
硫酸镁：0.2％-0.4％(相对于铅粉和红丹质量和的重量比)
木炭粉：1％-4％(相对于铅粉和红丹质量和的重量比)
二氧化硅：0.5％-3.5％。(相对于铅粉和红丹质量和的重量比)。
2.如权利要求1所述的储能用管式固定型铅酸蓄电池正极活性物质，其特征在于其各成分所占的重量百分比最佳配比为：
铅粉：70％-75％
红丹：25％-30％
纳米石墨：1.5％-2.5％(相对于铅粉和红丹质量和的重量比)
硫酸镁：0.2％-0.3％(相对于铅粉和红丹质量和的重量比)
木炭粉：2.5％-3.0％(相对于铅粉和红丹质量和的重量比)
二氧化硅：2％-3％(相对于铅粉和红丹质量和的重量比)。
CN2008101396640A 2008-08-29 2008-08-29 储能用管式固定型铅酸蓄电池正极活性物质 Active CN101350406B (zh)