CN101347811A - 石油钻杆接头热加工冲头穿孔润滑方法 - Google Patents
石油钻杆接头热加工冲头穿孔润滑方法 Download PDFInfo
- Publication number
- CN101347811A CN101347811A CNA2007100241347A CN200710024134A CN101347811A CN 101347811 A CN101347811 A CN 101347811A CN A2007100241347 A CNA2007100241347 A CN A2007100241347A CN 200710024134 A CN200710024134 A CN 200710024134A CN 101347811 A CN101347811 A CN 101347811A
- Authority
- CN
- China
- Prior art keywords
- cup
- plunger tip
- pipe joint
- drill pipe
- during heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种石油钻杆接头热加工冲头穿孔润滑方法,其特征在于,在热加工冲头穿孔前,将装有碎屑状或粉状高温润滑材料的杯形套件套在冲头(1)上,然后进行穿孔,杯形套件随冲头(1)被压入工件(3)。高温润滑材料优选木屑,杯形套件可选用纸杯套(2)。本发明的方法简单有效、成本低;能有效保护冲头表面,方便脱模;同时也使毛坯内孔粗糙度很低,工件加工质量大大提高。
Description
技术领域
本发明涉及一种热加工冲头穿孔润滑方法,尤其是一种石油钻杆接头热加工冲头穿孔润滑方法。
背景技术
目前,石油机械配件中,在冲钻杆接头中间孔时,中间孔的润滑采用的木块燃烧形式来润滑冲头。即向中间孔中投入木块片,以供在冲孔时润滑冲头。但是这种方法缺乏均匀的涂布性,润滑不充分,加工出的工件偏心大、加工余量大;给后续工序加工带来很大的困难。
发明内容
本发明的目的是:提供一种石油钻杆接头热加工冲头穿孔润滑方法,该方法简单有效、成本低;能有效保护冲头表面,方便脱模;同时也使毛坯内孔粗糙度很低,工件加工质量大大提高。
本发明的技术方案是:一种石油钻杆接头热加工冲头穿孔润滑方法,在热加工冲头穿孔前,将装有碎屑状或粉状高温润滑材料的杯形套件置于冲头与待穿孔工件之间,然后进行穿孔,杯形套件随冲头被压入工件。
下面对上述技术方案进行进一步解释:
1.所述装有碎屑状或粉状高温润滑材料的杯形套件被套在冲头上,然后进行穿孔,杯形套件随冲头被压入工件。
2.所述高温润滑材料为可以是木屑、石墨碎屑或石墨粉、玻璃粉末等能起到高温润滑作用的原材料,优选木屑。
3.所述杯形套件为高温下易燃烧成碳的材料制成。
4.所述杯形套件为纸杯套。
本发明专利针对现有工艺方法的缺点提供了一套专用的润滑方法。下面以木屑为例,说明本发明的工作原理。在热锻压过程中,将装有少量木屑的杯形套件套在冲头上,(如附图1所示)在杯形套件被压入工件毛坯的同时,杯中的木屑开始燃烧,由于木屑的不完全燃烧,杯中的木屑形成碳粉,并布满定位冲头的表面起到润滑作用。当穿深孔时,木屑杯在压入工件过程不完全燃烧一部分碳粉在冲头前进的过程中包覆在冲头表面,另一部分在封闭的空间碳化。(如附图2所示)由于木屑迅速燃烧,所以在密闭空间会形成一个小爆炸,爆炸的气流沿着冲头的外表面排到空气中,这样在冲压过程中冲头与工件内孔就会存在很小的间隙,使冲头达到脱模容易的目的。
本发明的优点是:简单有效、成本低;能有效保护冲头表面,方便脱模;同时也使毛坯内孔粗糙度很低,工件加工质量大大提高。
附图说明
下面结合附图和实施例对本发明作进一步的描述:
图1为本发明的加工示意图(冲孔前);
图2为本发明的加工示意图(冲孔后)。
其中:1冲头;2纸杯套;3工件;4木屑。
具体实施方式
实施例一:
如图1、图2所示,一种石油钻杆接头热加工冲头穿孔润滑方法,其特征在于,在热加工冲头穿孔前,将装有木屑4的纸杯套2被套在冲头1上,然后进行穿孔,纸杯套2随冲头1被压入工件3。
具体过程如下描述:在热加工冲头穿孔前,如图1所示,将装有少量木屑4的纸杯套2套在冲头1上,在纸杯套2被压入工件3的同时,纸杯套2中的木屑4开始燃烧,由于木屑4的不完全燃烧,纸杯套2中的木屑4形成碳粉,并布满定位冲头1的表面起到润滑作用。当穿深孔时,木屑杯在压入工件3过程不完全燃烧一部分碳粉在冲头1前进的过程中包覆在冲头1表面,另一部分在封闭的空间碳化。(如图2所示)由于木屑4迅速燃烧,所以在密闭空间会形成一个小爆炸,爆炸的气流沿着冲头1的外表面排到空气中,这样在冲压过程中冲头1与工件3内孔就会存在很小的间隙,使冲头1达到脱模容易的目的。
实施例二:
本实施例与实施例一的区别在于:采用玻璃粉末作为高温润滑材料装在纸杯套2内。
实施例三:
本实施例与实施例一的区别在于:采用石墨粉作为高温润滑材料装在纸杯套2内。
应当指出,对于经充分说明的本发明来说,还可具有多种变换及改型的实施方案,并不局限于上述实施方式的具体实施例。上述实施例仅仅作为本发明的说明,而不是对本发明的限制。总之,本发明的保护范围应包括那些对于本领域普通技术人员来说显而易见的变换或替代以及改型。
Claims (7)
1.一种石油钻杆接头热加工冲头穿孔润滑方法,其特征在于:在热加工冲头穿孔前,将装有碎屑状或粉状高温润滑材料的杯形套件置于冲头(1)与待穿孔工件(3)之间,然后进行穿孔,杯形套件随冲头(1)被压入工件(3)。
2.根据权利要求1所述的石油钻杆接头热加工冲头穿孔润滑方法,其特征在于:所述装有碎屑状或粉状高温润滑材料的杯形套件被套在冲头(1)上,然后进行穿孔,杯形套件随冲头(1)被压入工件(3)。
3.根据权利要求1或2所述的石油钻杆接头热加工冲头穿孔润滑方法,其特征在于:所述高温润滑材料为木屑(4)。
4.根据权利要求1或2所述的石油钻杆接头热加工冲头穿孔润滑方法,其特征在于:所述高温润滑材料为石墨碎屑或石墨粉。
5.根据权利要求1或2所述的石油钻杆接头热加工冲头穿孔润滑方法,其特征在于:所述高温润滑材料为玻璃粉末。
6.根据权利要求1或2所述的石油钻杆接头热加工冲头穿孔润滑方法,其特征在于:所述杯形套件为高温下易燃烧成碳的材料制成。
7.根据权利要求1或2所述的石油钻杆接头热加工冲头穿孔润滑方法,其特征在于:所述杯形套件为纸杯套(2)。