CN101338252A - Automobile coating cleaning and repairing agent and method for preparing same - Google Patents
Automobile coating cleaning and repairing agent and method for preparing same Download PDFInfo
- Publication number
- CN101338252A CN101338252A CNA2008100701078A CN200810070107A CN101338252A CN 101338252 A CN101338252 A CN 101338252A CN A2008100701078 A CNA2008100701078 A CN A2008100701078A CN 200810070107 A CN200810070107 A CN 200810070107A CN 101338252 A CN101338252 A CN 101338252A
- Authority
- CN
- China
- Prior art keywords
- portions
- cleaning
- diatomite
- repairing agent
- automobile coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an automobile paint cleaning and repairing additive and the preparation method. The cleaning and repairing additive can remove the besmirch, rust and asphalt stain from the automobile surface paint, treat the yellowing and color changing of the paint surface, repair the scratch on the paint surface. The luster of the paint surface can be increased after being cleaned and repaired. The automobile paint cleaning and repairing additive mainly comprises the components with the following weight portions of 30-38 portions of diatomite, 6-8 portions of mineral oil, 15-20 portions of sulfonation succinic acid sodium caprylate, 6-10 portions of tween 80, 30-387 portions of water and the total portion is 100. The preparation method is that the diatomite is crushed to 300-400 meshes, and then the powder diatomite, water, mineral oil, sulfonation succinic acid sodium caprylate and tween 80 are in turn put into a stirring disperser. The mixture is heated to 70-80 DEG C. The materials are added while stirring. After stirring for 1-1.5 hours, the mixture should be kept in still. The next day, the mixture should be stirred again for 15-20 minutes and then the products can be filled to the bottle and packaged.
Description
Technical field
The present invention relates to the Motor Maintenance technical field, particularly a kind of automobile coating cleaning and repairing agent.
Background technology
The scuffing trace of variable color jaundice or black splotch or rusty stain even shallow table may appear in automobile on the automobile case lacquer painting in the use of varying environment, when this kind situation occurring, adopt simoniz to nurse usually.Simoniz mainly is made up of paraffin, ceresine, liquid wax, and its function is that car surface lacquer is removed dust and dirt, increases gloss, for stupid dirty spot, as pitch stain, rusty stain, lacquer painting variable color jaundice, that shallow table scratches trace is powerless.Pitch stain for automobile finish can adopt " removing pitch water " to remove.But " remove pitch water " is the solvent-borne type product, and it is to be main raw by methylene dichloride, and methylene dichloride is poisonous.During with the pitch stain on its removing automobile finish, easily injure automobile finish, and operator's health is brought very big injury.
Summary of the invention
The object of the present invention is to provide a kind of automobile coating cleaning and repairing agent, this cleaning and repairing agent can be removed spot, rusty stain, pitch stain to the car surface lacquer, handle lacquer painting jaundice variable color, repair the shallow table of lacquer painting and scratch trace, the lacquer painting after repairing through cleaning can increase gloss.
Technical solution proposed by the invention is such: a kind of automobile coating cleaning and repairing agent, and described automobile coating cleaning and repairing agent mainly is made up of following component, by weight percentage:
Diatomite 30-38;
Mineral oil 6-8;
Sulfonation Succinic Acid Sodium octoate 15-20;
Tween 80 6-10;
Water 30-38;
Add up to 100.
Diatomite in the described automobile coating cleaning and repairing agent component is pulverized the 300-400 order that sieves, successively konilite, water, mineral oil, sulfonation Succinic Acid Sodium octoate and tween 80 are put into the dispersed with stirring device then, be heated to 70-80 ℃, stir while feeding in raw material, churning time is static parking after 1-1.5 hour, the second day restir 15-20 minute packing of can bottling.Have decolouring, pure white effect as the diatomite of abrasive material, can remove stupid dirt, spot fast.As the sulfonation Succinic Acid Sodium octoate of water-soluble permeate agent spot, rust spot, pitch point there are rapid osmotic, moistening effect.Tween 80 as tween can strengthen water, oily emulsification degree of mixing, reduces water, oil content layer phenomenon, and self-cleaning effect is also arranged simultaneously.Mineral oil has and adds lustre to and auxiliary scrubbing effect.This preparation is a kind of water-soluble products of environmental protection, pH value 7, and potential of hydrogen belongs to neutral, does not hinder hand, and outward appearance is light beige, and is liquid, if need other colors, can add corresponding colorant.
Compared with prior art, the present invention has following unusual effect:
(1) this preparation has the powerful stupid dirty effect of removing, the zone of oxidation, pitch stain, sewage that comprises automobile finish hang stain, rust water hang stain, the spot on motor car engine surface, the spot of automotive seat corium face etc. can both the rapid cleaning reparation after wiping is made in this cleaning reparation, and do not hinder article surface, to becoming xanchromatic white car lacquer, renovation bleaches more remarkable especially.
(2) the shallow table that occurs for automobile finish of this preparation scratches the vestige that trace and vehicle door handle place scratched by nail all perfect reparation effect.
(3) this preparation can also cleaning glass, more can show its cleaning effect to the glass that is stained with oil smoke, and the glass that was cleaned by this agent simultaneously also has anti-fog effect.
(4) object all can increase gloss after being cleaned by this agent.The object that was cleaned by this agent will increase smooth feel if desired, then can add the small amount of hydroxyl groups silicon emulsion in this preparation and get final product.
Embodiment
By following embodiment the present invention is further elaborated.
Embodiment 1
A kind of automobile coating cleaning and repairing agent mainly is made up of following component, by weight percentage:
Diatomite 30
Mineral oil 8
Sulfonation Succinic Acid Sodium octoate 20
Tween 80 6
Water 36
Add up to 100.
The step of preparation process of automobile coating cleaning and repairing agent is as follows:
Diatomite was pulverized 300 mesh sieves, put into the dispersed with stirring device, and put into water then and stir, put into mineral oil, sulfonation Succinic Acid Sodium octoate and tween 80 more successively, be heated to 70 ℃, stir while feeding in raw material, churning time is static parking after 1 hour, second day restir packing of can bottling in 15 minutes.
Using method: in article surface wiping back and forth, wipe clean with clean towel or paper handkerchief again and get final product with towel or a little this cleaning and repairing agent of the paper handkerchief libation at an ancient wedding ceremony.
Embodiment 2
A kind of automobile coating cleaning and repairing agent mainly is made up of following component, by weight percentage:
Diatomite 32
Mineral oil 6
Sulfonation Succinic Acid Sodium octoate 17
Tween 80 7
Water 38
Add up to 100.
During preparation, remove diatomite and pulverized 350 mesh sieves, heat 75 ° and stir outside 1.2 hours, all the other are identical with example 1.
Embodiment 3
A kind of automobile coating cleaning and repairing agent mainly is made up of following component, by weight percentage:
Diatomite 38
Mineral oil 7
Sulfonation Succinic Acid Sodium octoate 15
Tween 80 10
Water 30
Add up to 100.
During preparation, remove diatomite and pulverized 400 mesh sieves, heat 80 ℃ of stirrings 1.5 o'clock, outside second day restir 20 minutes, all the other are identical with example 1.
Claims (2)
1, a kind of automobile coating cleaning and repairing agent is characterized in that: described automobile coating cleaning and repairing agent mainly is made up of following component, by weight percentage:
Diatomite 30-38;
Mineral oil 6-8;
Sulfonation Succinic Acid Sodium octoate 15-20;
Tween 80 6-10;
Water 30-38;
Add up to 100.
2, the method for preparing the described automobile coating cleaning and repairing agent of claim 1, it is characterized in that: the diatomite in the described automobile coating cleaning and repairing agent component is pulverized the 300-400 order that sieves, successively konilite, water, mineral oil, sulfonation Succinic Acid Sodium octoate and tween 80 are put into the dispersed with stirring device then, be heated to 70-80 ℃, stir while feeding in raw material, churning time is static parking after 1-1.5 hour, the second day restir 15-20 minute packing of can bottling.