CN1013206B - 双结构控温烧结方法 - Google Patents
双结构控温烧结方法Info
- Publication number
- CN1013206B CN1013206B CN 88107146 CN88107146A CN1013206B CN 1013206 B CN1013206 B CN 1013206B CN 88107146 CN88107146 CN 88107146 CN 88107146 A CN88107146 A CN 88107146A CN 1013206 B CN1013206 B CN 1013206B
- Authority
- CN
- China
- Prior art keywords
- sintering
- sinter
- present
- pellet
- sintering method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
本发明方法属于铁矿粉烧结造块领域。特别适用于采用细精矿粉,在控制一定的温度下,烧结成高碱度烧结矿粘结酸性球团的烧结方法。本发明方法是采用酸性生球与碱性烧结混合料进行混合后烧结,它不但能改善烧结料层的透气性,利于提高烧结机的产量,而且降低了烧结能耗,烧结矿质量有所提高。另外采用本发明方法还具有造球容易,烧结温度控温准确等特点。
Description
本发明属于铁矿粉烧结造块领域。适用于利用细铁精矿粉,在控制一定的温度下,烧结成高碱度烧结矿粘结酸性球团的烧结方法。
目前以细铁精矿粉为主要含铁原料的烧结生产方法,因精矿粉粒度细,成球性能差,经二次混合机造球后的混合料透气性差。烧结机产量低、能耗高、FeO含量高。为解决这一问题,有人提出了小球烧结法工艺。其特点是:将铁精矿粉与其它烧结料混合后,加水造成直径为3~8mm的小球,再与粗粒返矿及部分粗粒焦粉混合,然后按普通方法烧结。(《烧结球团》)80年第6期第39页)
小球烧结法可以改善混合料的透气性,提高烧结矿产量20~30%存在的问题是:
1.造直径3~8mm的小球很困难,设备复杂,生产率低。
2.由于小球烧结料层透气性过高,造成火焰传播速度与热波传播速度不同步,给烧结过程进行带来困难,烧结矿质量差、能耗高。
我国缺少酸性炉料,受高生产限制,我国生产的烧结矿大多数碱度R=CaO/SiO2=1.3~1.7。在这个碱度范围内,烧结矿的冷强度、还原性、还原粉化率等冶金性能指标都较差。
本发明的目的是提出一种克服普通烧结方法与小球烧结法所存在的不足,提高烧结机产量,降低烧结能耗,提高烧结矿质量的烧结方法。
本发明属于一种细精矿烧结方法。它是将50-100%细铁精矿粉与消石灰(或生石灰)白云石粉,焦粉(或煤粉)水和其它添加料,按一定比例配好料后,在混合机中混合,在造球机中造成直径≤15mm的酸性生球,然后按需要的配比,配入高碱度烧结混合料,在圆筒混合机中混合,提高料温。混合好的混合料,布到烧结台车上烧结。根据原料性质不同,将烧结温度可以选择在1200℃~1400℃之间的某一温度水平。通过控制配碳量,布料时粒度偏析和点火工艺制度,可将料层上部与下部烧结温度差控制在±25℃以内。在1200℃~1400℃温度范围内,酸性生球可以固结,高碱度烧结混合料可以完成固相、液相化学反应,达到半熔化状态,冷却后形成以铁酸钙为主要,粘结相的高碱度烧结矿。酸性球团矿的熔化温度一般高于1400℃,它在本方法烧结过程中一直保持固态。高碱度烧结矿在1200℃以上的温度,开始熔化,并与酸性球团矿粘结在一起,冷却后,得到高碱度烧结矿粘结酸性球团矿的新型烧结矿结构。
本发明与普通烧结法不同之处:
1.本发明将细精矿部分或全部预先造成直径≤15mm的酸性球团再与高碱度烧结混合料混合后,布到烧结台车上烧结。这样可以改善料层的透气性,提高烧结机的产量。
2.通过控制配碳量、布料偏析、点火工艺制度,控制烧结温度在1200℃~1400℃之间的某一温度水平,上部与下部温度差在±25℃以内,克服了普通烧结法在烧结过程中因料层自动蓄热而产生的料层上部烧结温度低,下部烧结温度高的问题。
3.按本发明生产出的烧结矿结构是高碱度烧结矿粘结酸性球团矿的理想结构,烧结矿质量好。
本发明与普通烧结方法比较,烧结机产量可提高20~30%,能耗可降低7~15%,烧结矿还原性可以提高10%左右,低温还原粉化率略有降低,软熔温度略有提高。
本发明不同于小球烧结法之处:
1.本发明要求细精矿造成的球团直径为≤15mm的生球,这样的生球在工厂中容易生产,克服了小球烧结法造小球难的问题。
2.本发明布到烧结台车上的混合料是酸性生球与普通高碱度烧结混合料的混合物。这种组成的混合料,具有较高的透气性,同时也具有较好的气固换热条件,克服了小球烧结法存在的热波传播速度与火焰传播速度不同步的问题,使烧结过程能很好地进行。
实施例1
本发明方法根据附图详细叙述如下,在附图1中,1、精矿粉、消石灰、白云石粉、焦粉及其其它的添加料料仓;2、配料皮带;3、混合机;4、
圆筒造球机;5、返矿、石灰石粉、焦粉、富矿粉及其它烧结原料料仓、6、配料皮带;7、圆筒混合机;8、布料器;9、点火器;10、烧结机。
本实施例的特点是:将细精矿粉与消石灰,白云石粉、焦粉、水和其它添加料,按要求配比配好料后,在混合机3中混合,在圆筒造球机中造成直径≤12mm的酸性生球,然后按需要的配比,配入粗粒的石灰石、富矿粉、焦粉、返矿、水、及其它烧结原料,在圆筒混合机7中混合,提高料温。混合好的混合料,通过布料器8布到烧结台车上10上,点火烧结。
实施例2
附图2、图中、1、精矿粉、消石灰、白云石粉、焦粉、其它添加料料仓;2、混合机;3、圆盘造球机(或圆筒造球机后加8mm筛子)4、精矿粉、返矿、石灰石、焦粉、富矿粉及其它烧结原料料仓;5、一次混合机;6、二次混合机;7、返矿、焦粉料仓;8、圆筒混合机;9、布料器;10、点火器;11、烧结机。
本实施例的特点是:50~80%的细精矿与白云石粉、消石灰、焦粉及其它添加料配料后在混合机2中混合,在圆盘造球机3中造成8~15mm的酸性生球。其余精矿与返矿、石灰石粉、消石灰、焦粉、富矿粉、其它烧结原料配料后,按一般烧结方法,先在一次混料机5中混合,在二次混合机6中造球,形成高碱度烧结混合料。造球盘3出来的酸性生球与混合机6出来的高碱度烧结混合料混合后,配入部分返矿和焦粉进入圆筒混合机8中进一步混合,提高料温,然后通过布料器9布到烧结机10上,点火烧结。
Claims (1)
1、一种铁精矿粉的烧结方法,其特征在于将50%~100%的铁精矿粉先造成直径为≤15mm的酸性生球,然后再与高碱度烧结混合料混合,烧结温度选择在1200℃-1400℃,料层上、下部温差控制在±25℃。