CN101318806A - 一种透光瓷的制备方法及其用途 - Google Patents
一种透光瓷的制备方法及其用途 Download PDFInfo
- Publication number
- CN101318806A CN101318806A CNA2008100283908A CN200810028390A CN101318806A CN 101318806 A CN101318806 A CN 101318806A CN A2008100283908 A CNA2008100283908 A CN A2008100283908A CN 200810028390 A CN200810028390 A CN 200810028390A CN 101318806 A CN101318806 A CN 101318806A
- Authority
- CN
- China
- Prior art keywords
- percent
- ceramic
- photopermeable
- hours
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种透光瓷的制备方法，其工艺步骤包括：制作瓷泥，按以下配比配料，SiO2 65～75％，Al2O3 20～28％，Fe2O3 0.1～0.3％，CaO 0.1～0.5％，MgO 0.3～0.8％，K2O 1～4％，NaO 0.5～1.5％；按常规与水、硅酸纳、腐植酸钠进行混合搅拌成浆；将泥浆浇注在产品造型模具上；干躁、脱模得坯体；修整、晒干或烘干；上水打磨，上奶白油；烧成，温度为1250～1300℃，时间为8～10小时；贴花纸，经720～770℃第二次烧成，时间为4～6小时。应用本发明，制备工艺简单，成本较低，用途广泛；透光效果好，既可以用作家居中如灯具的灯座及灯罩、蜡烛罩、蜡烛杯、香精炉等耐热器具，又可以作为工艺陈设品，是集照明与工艺为一体的现代用品。
Description
技术领域
本发明涉及工艺品或家居中的用品，尤其涉及一种透光瓷的制备方法及其用途。
背景技术
传统的陶瓷被普遍用作日用餐具、灯具座、工艺陈设品等，但由于其普通陶瓷透光性能较差，使陶瓷的应用受到一定的限制，如用作灯具只能作灯座，其灯罩还需用布料或玻璃来制成，布料属易燃材料，存在安全隐患，玻璃易碎，影响使用寿命；也有人试图把普通陶瓷胚体制作成薄胚来提高透光度，但效果不理想且不耐热、易碎。近来也有些企业在研究新型透光瓷，如中国专利申请号200510066031.8(公开号为CN1676346A)公开了一种新型透光瓷的制备方法及其用途，它是在普通强化瓷上通过雕通胚体使之能透光，虽然有一定的装饰效果，但雕通工艺工作量大，成本高，且不能挡风，应用领域也受到限制。
发明内容
为克服上述不足，本发明的目的在于提供一种制备简单，成本较低，不用通过雕通或做薄胚体就能达到透光效果的透光瓷的制备方法及其用途。
本发明解决其技术问题所采用的技术方案是：一种透光瓷的制备方法，其工艺步骤包括：
(1)制作瓷泥，按以下组分和重量百分比配料，制作成瓷泥：SiO2 65～75％，Al2O3 20～28％，Fe2O3 0.1～0.3％，CaO 0.1～0.5％，MgO 0.3～0.8％，K2O 1～4％，NaO 0.5～1.5％；
(2)将上述瓷泥按常规与水、硅酸纳、腐植酸钠重量进行混合，搅拌成浆；
(3)将泥浆浇注在设计好的产品造型模具上；
(4)干澡30～60分钟，脱模得陶瓷胚体；
(5)去土渣、晒干或烘干，修去模具线；
(6)上水打磨，上奶白油；
(7)烧成，制品的烧成温度为1250～1300℃，烧成时间为8～10小时，即得白色透光瓷。
它还可以包括如下步骤：
(8)贴花纸，刮干、晒干，经720～770℃第二次烧成，烧成时间为4～6小时。
上述透光瓷的用途，既可以用作家居中如灯具的灯座及灯罩、蜡烛罩等耐热器具，又可以作为工艺陈设品。
应用本发明所述透光瓷，制备工艺简单，生产成本较低，用途广泛；不用通过雕通或做薄胚体就能达到透光效果，既可以用作家居中如灯具的灯座及灯罩、蜡烛罩、蜡烛杯、香精炉等耐热器具，又可以作为工艺陈设品；如在其上面增加浮雕、阴雕或雕通花纹或图案，更能增加美术效果，是一种集照明与工艺为一体的现代用品。
具体实施方式
下面列举二个实施例，对本发明加以进一步说明，但本发明不只限于这二个实施例。
实施例1：一种圆筒形台灯具的制备方法，其工艺步骤包括：
(1)制作瓷泥，按以下组分和重量百分比配料，制作成瓷泥：SiO2 72.23％，Al2O3 23.41％，Fe2O3 0.15％，CaO 0.29％，MgO 0.62％，K2O 2.4％，NaO 0.9％；
(2)将上述瓷泥按常规与水、硅酸纳、腐植酸钠重量进行混合，搅拌成浆；
(3)将泥浆浇注在设计好的圆筒形灯具模具上；
(4)干澡45分钟，脱模得圆筒形灯具胚体；
(5)去土渣、晒干或烘干，修去模具线；
(6)上水打磨，上奶白油；
(7)烧成，制品的烧成温度为1280℃，烧成时间为9小时，即得白色透光的圆筒形灯具。
(8)贴花纸，刮干、晒干，经745℃第二次烧成，烧成时间为5小时。即得白色底并有花纹图案并透光的圆筒形灯具。
其余按常规工艺流程操作。
实施例2：一种半圆球形蜡烛罩的制备方法，其工艺步骤包括：(3)将泥浆浇注在设计好的半圆球形蜡烛罩模具上；
(7)烧成，制品的烧成温度为1250℃，烧成时间为9小时；步骤(1)(2)(4)(5)(6)与实施例1相同。即得白色透光的半圆球形蜡烛罩。
Claims (3)
1、一种透光瓷的制备方法，其特征在于：其工艺步骤包括：
(1)制作瓷泥，按以下组分和重量百分比配料，制作成瓷泥：SiO2 65～75％，Al2O3 20～28％，Fe2O3 0.1～0.3％，CaO 0.1～0.5％，MgO 0.3～0.8％，K2O 1～4％，NaO 0.5～1.5％；
(2)将上述瓷泥按常规与水、硅酸纳、腐植酸钠重量进行混合，搅拌成浆；
(3)将泥浆浇注在设计好的产品造型模具上；
(4)干澡30～60分钟，脱模得陶瓷胚体；
(5)去土渣、晒干或烘干，修去模具线；
(6)上水打磨，上奶白油；
(7)烧成，制品的烧成温度为1250～1300℃，烧成时间为8～10小时，即得白色透光瓷。
2、根据权利要求1所述透光瓷的制备方法，其特征在于：它还包括如下步骤：
(8)贴花纸，刮干、晒干，经720～770℃第二次烧成，烧成时间为4～6小时。
3、根据权利要求1或2所述透光瓷的用途，既可以用作家居中灯具、烛罩等耐热器具，又可以作为工艺陈设品。