CN101307163A - 硅烷交联聚乙烯绝缘电缆料及其制造方法 - Google Patents
硅烷交联聚乙烯绝缘电缆料及其制造方法 Download PDFInfo
- Publication number
- CN101307163A CN101307163A CNA2007100224943A CN200710022494A CN101307163A CN 101307163 A CN101307163 A CN 101307163A CN A2007100224943 A CNA2007100224943 A CN A2007100224943A CN 200710022494 A CN200710022494 A CN 200710022494A CN 101307163 A CN101307163 A CN 101307163A
- Authority
- CN
- China
- Prior art keywords
- crosslinked
- insulated cable
- linked polyethylene
- polyethylene insulated
- cable material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
序号 | 材料牌号或名称 | 作用 | 配比范围 |
1 | 100BW(低密度聚乙烯) | 主料,起媒体作用 | 96.5-97.5 |
2 | 有机锡 氧化二丁基锡(二丁基氧化锡) | 分散助剂 | 0.8-1.2 |
3 | 抗铜剂(N-水杨酰氨基邻苯二酰亚胺) | 在交联时氧化导体铜的保护 | 0.3-0.7 |
4 | 1010抗氧剂 四[β-(3,5-二叔丁基4-羟基苯基)丙酸]季戊四醇酯 | 对产品起抗氧作用 | 1.3-1.8 |
序号 | 名称 | 作用 |
1 | 硅烷油(乙烯基三甲氧基硅烷) | 交联桥架进行交联 |
2 | 四[β-(3,5-二叔丁基4-羟基苯基)丙酸]季戊四醇酯 | 抗氧剂,对产品协调抗氧化 |
3 | 过氧化二异丙苯 | 交联催化 |
4 | 低密度聚乙烯 | 主料平衡交联 |
5 | 聚乙烯 | 主料加速交联度 |
序号 | 名称 | 作用 |
1 | 低密度聚乙烯 | 主料,起媒体作用 |
2 | 二月桂酸二丁基锌 | 催化剂,确保在自然条件下交联 |
3 | 四[β-(3,5-二叔丁基4-羟基苯基)丙酸]季戊四醇酯 | 抗氧剂,对产品起抗氧作用 |
序号 | 项目 | 单位 | 性能要求 |
11.11.21.323 | 抗张强度和断裂伸长率原始性能抗张强度 最小断裂伸长率 最小空气烘箱老化试验老化条件:温度时间试验结果:抗张强度 最小变化率 最大断裂伸长率 最小变化率 最大人工气候老化试验老化时间试验结果a)0~1008小时抗张强度变化率 最大断裂伸长率变化率 最大b)504~1008小时抗张强度变化率 最大断裂伸长率变化率 最大重量法温度时间吸水量 最大收缩试验温度时间允许收缩率 最大热延伸试验温度载荷时间机械应力载荷下伸长率 最大冷却后永久伸长率 最大 | MPa%℃hMPa%%%h%%%%℃hmg/cm2℃h%℃minN/cm2%% | 12.5200135±3168--±25--±251008±30±30±15±1585±23361130±314200±3152017515 |
Claims (2)