CN101302397A - Lignose raw lacquer composite coating - Google Patents
Lignose raw lacquer composite coating Download PDFInfo
- Publication number
- CN101302397A CN101302397A CNA2008101500860A CN200810150086A CN101302397A CN 101302397 A CN101302397 A CN 101302397A CN A2008101500860 A CNA2008101500860 A CN A2008101500860A CN 200810150086 A CN200810150086 A CN 200810150086A CN 101302397 A CN101302397 A CN 101302397A
- Authority
- CN
- China
- Prior art keywords
- raw lacquer
- composite coating
- lignose
- xylogen
- lignin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses lignin raw lacquer composite coating. The lignin raw lacquer composite coating prepared mainly comprises raw lacquer, lignin, functional auxiliary agent and diluting agent. The lignin raw lacquer composite coating introduces the lignin extracted from sulphite liquor into the raw lacquer, and effectively utilizes the lignin in the sulphite liquor and reduces the cost when the performance of the raw lacquer is maintained simultaneously. The product is acid resistant, alkali resistant, water resistant, oil resistant and abrasion resistant, has high glossiness and strong adhesion, and is suitable for anti-corrosive application in deep color hardwood furniture and the industry.
Description
Technical field
The present invention relates to a kind of coating, particularly a kind of lignose raw lacquer composite coating, this lignose raw lacquer composite coating are that a kind of dark hardwood furniture is covered with paint, lacquer, colour wash, etc., industrial antisepsis coating.Be mainly used in dark hardwood furniture, industrial antisepsis application.Product performance are stable, and are wear-resisting, anticorrosion, strong adhesion, glossiness height.
Background technology
Xylogen is one of plant structure composition, also is the spent pulping liquor extract in the paper industry, and development product is many at present, as emulsifying agent, synthetic paint etc.Raw lacquer is special product of China, and laccol in the raw lacquer and xylogen belong to Polyphenols bio-based product, can use by compatibility, can obtain satisfied effect.
Raw lacquer is mainly used in the heavy anti-corrosion paint of household objects and metallic substance; have excellent film performance, splendid decorate properties, corrosionproof protection performance and optical property, xylogen is the constituent of plant matrix; its turnout accounts for the 20-30% of plant materials, but real practical technology seldom.
Summary of the invention
In order to break through the limitation that xylogen uses, characteristic in conjunction with xylogen and raw lacquer, the objective of the invention is to, a kind of lignose raw lacquer composite coating is provided, this lignose raw lacquer composite coating has been broken through the limitation of xylogen use properties, raw lacquer and xylogen are made with extra care processing in enzyme reactor, be equipped with film coalescence aid modulation again, at last through smart filter lignose raw lacquer composite coating.For the development and use of xylogen provide a new approach.
In order to realize above-mentioned task, the technical solution used in the present invention is:
A kind of lignose raw lacquer composite coating, it is characterized in that, this lignose raw lacquer composite coating that makes is made up of following raw materials according and mass percent thereof: raw lacquer: 40%～60%, xylogen: 15%～35%, functional aid: 0.1%～25%, thinner: 15%～25%, the per-cent sum of above-mentioned raw materials is 100%.
The preparation of above-mentioned lignose raw lacquer composite coating is to mix according to prescription to get final product.
Described raw lacquer is produced one or more of Qi by Qi, city mouth Qi from peace health Qi, the Chinese, hair dam Qi, Qin Ling Qi and other areas, and it is fried in shallow oil and coils mark more than 65%, and laccol content is more than 50%.
Described xylogen is one of alkali wood xylogen or pure molten xylogen or more than one.
Described functional aid is KD550, wilkinite one of them or more than one.
Described thinner is No. 200 solvent oils, turps, white oil of camphor one of them or more than one.
The lignose raw lacquer composite coating of the present invention's preparation has been introduced the xylogen that spent pulping liquor extracts in raw lacquer, when keeping the raw lacquer performance, effectively utilized the xylogen in the spent pulping liquor, reduced cost, can directly coat with lacquer and be coated with anticorrosive coating in dark hardwood furniture and lacquerware technology product or the metal with lignose raw lacquer composite coating, have excellent corrosion resistance, acidproof, water-fast, medium-resistance is good, has good glossiness.Be applicable to the anticorrosive coating in dark hardwood furniture, the industry.
Embodiment
The specific embodiment that provides below in conjunction with the contriver is described in further detail the present invention.
Embodiment 1:
| Component | Weight (%) |
| Hanzhong raw lacquer | 55 |
| Alkali wood xylogen | 25 |
| KD550 | 0.3 |
| Wilkinite | 1 |
| Turps | 18.7 |
Its preparation method is to mix according to prescription to get final product.
Embodiment 2:
| Component | Weight (%) |
| Safe and comfortable raw lacquer | 60 |
| The molten xylogen of alcohol | 20 |
| KD550 | 0.2 |
| Wilkinite | 1 |
| White oil of camphor | 18.8 |
The preparation method is with embodiment 1.
Embodiment 3:
| Component | Weight (%) |
| Hair dam raw lacquer | 50 |
| The molten xylogen of alcohol | 15 |
| Alkali wood xylogen | 15 |
| KD550 | 0.3 |
| Wilkinite | 1.5 |
| No. 200 solvent oils | 18.2 |
The preparation method is with embodiment 1.
Embodiment 4:
| Component | Weight (%) |
| Entrance of the city raw lacquer | 55 |
| Alkali wood xylogen | 25 |
| Wilkinite | 2 |
| Turps | 18 |
The foregoing description can exclusive list, certainly, also can use the mixed Qi of closing that produce in Qi, city mouth Qi, hair dam Qi, Qin Ling Qi and other areas in peace health Qi, the Chinese, and it fries in shallow oil the dish mark more than 65%, and laccol content is all can more than 50%.
During use, lignose raw lacquer composite coating is directly brushed on coated article with brush, be placed into temperature then and be heat and moisture preserving space inner drying under 25 ℃, humidity 80% condition.
The performance index of the lignose raw lacquer composite coating of the present invention's preparation see table.
Mu Zhi Su Qi performance index:
| Project | Index | The method of inspection |
| Paint film appearance | Coffee-like | |
| Solid content, %, ≮ | 55％ | GB/T6470 |
| No impression time of drying, h, ≯ | 4 | GB/T6753.2 |
| Water tolerance, ≮ 90d | Paint film do not come off, non-foaming, do not chap | GB/T1733 |
| Anti-sulfuric acid, ≮ 90d | Paint film do not come off, non-foaming, do not chap | GB/T9274.1 |
| Resistance to salt water (sodium-chlor), ≮ 90d | Paint film do not come off, non-foaming, do not chap | GB/T10834 |
| Petrol-resistance, ≮ 90d | Paint film do not come off, non-foaming, do not chap | GB/T1734 |
Claims (5)
1. lignose raw lacquer composite coating, it is characterized in that, this lignose raw lacquer composite coating that makes is made up of following raw materials according and mass percent thereof: raw lacquer: 40%～60%, xylogen: 15%～35%, functional aid: 0.1%～25%, thinner: 15%～25%, the per-cent sum of above-mentioned raw materials is 100%.
2. the compound Tu Liao of xylogen raw lacquer as claimed in claim 1 Qi, it is characterized in that, described raw lacquer is produced one or more of Qi by Qi, city mouth Qi from peace health Qi, the Chinese, hair dam Qi, Qin Ling Qi and other areas, and it is fried in shallow oil and coils mark more than 65%, and laccol content is more than 50%.
3. lignose raw lacquer composite coating as claimed in claim 1 is characterized in that, described xylogen is alkali wood xylogen or pure molten xylogen.
4. lignose raw lacquer composite coating as claimed in claim 1 is characterized in that, described functional aid is KD550, wilkinite one of them or more than one.
5. lignose raw lacquer composite coating as claimed in claim 1 is characterized in that, described thinner be No. 200 solvent oils, turps, white oil of camphor one of them.