CN109401383A - A kind of environment protection type corrosion resistant coating - Google Patents
A kind of environment protection type corrosion resistant coating Download PDFInfo
- Publication number
- CN109401383A CN109401383A CN201811362679.3A CN201811362679A CN109401383A CN 109401383 A CN109401383 A CN 109401383A CN 201811362679 A CN201811362679 A CN 201811362679A CN 109401383 A CN109401383 A CN 109401383A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- corrosion resistant
- environment protection
- protection type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment protection type corrosion resistant coatings, are made of following raw material according to parts by weight: schmigel 10-50 parts by weight, pearl powder 6-28 parts by weight, silica flour 10-50 parts by weight, bentonite 7-21 parts by weight, polyacrylamide 8-32 parts by weight, ethyl alcohol 6-36 parts by weight, rosin 8-26 parts by weight, phenolic resin 8-24 parts by weight, glycerol 6-26 parts by weight, iron oxide red 5-25 parts by weight, methyl methacrylate 5-25 parts by weight, sodium carboxymethylcellulose 4-16 parts by weight, nanometer calcium carbonate 6-24 parts by weight.The present invention has many advantages, such as that good environmental protection, corrosion-resistant intensity are high and wearability is good.
Description
Technical field
The present invention relates to coating manufacture field more particularly to a kind of environment protection type corrosion resistant coatings.
Background technique
Coating, in the entitled paint of Chinese tradition, so-called coating be coated in the body surface being protected or decorated, and
The continuous film of firm attachment can be formed with coated article, usually based on resin or oil or lotion, add or do not add face
Material, filler, add corresponding additive, the thick liquid being formulated with organic solvent or water, and coating belongs to organic chemical industry's macromolecule
Material is formed by film and belongs to high-molecular compound type.According to the classification for the chemical products that the modern times pass through, coating belongs to essence
Refine chemical product.Modern coating gradually becomes a kind of multi-functional engineering material, is a weight in chemical industry
Want industry.
But existing coating it is unreasonable because of its formulation selection the problems such as, can not have corrosion resistant effect in use process
Fruit, and part coatings do not have preferable environmental-protecting performance, not only to environment nocuousness, more having can even be caused harm to the human body, no
Conducive to the use of people.
Summary of the invention
In order to overcome the defects of the prior art described above, the object of the present invention is to provide a kind of environment protection type corrosion resistant coatings.
The present invention takes following technical scheme to realize: a kind of environment protection type corrosion resistant coating, by below according to weight
The raw material of number forms: schmigel 10-50 parts by weight, pearl powder 6-28 parts by weight, silica flour 10-50 parts by weight, bentonite 7-
21 parts by weight, polyacrylamide 8-32 parts by weight, ethyl alcohol 6-36 parts by weight, rosin 8-26 parts by weight, phenolic resin 8-24 weight
Part, glycerol 6-26 parts by weight, iron oxide red 5-25 parts by weight, methyl methacrylate 5-25 parts by weight, sodium carboxymethylcellulose
4-16 parts by weight, nanometer calcium carbonate 6-24 parts by weight.
A kind of above-mentioned environment protection type corrosion resistant coating is made of following raw material according to parts by weight: schmigel 10-45 weight
Measure part, pearl powder 6-26 parts by weight, silica flour 10-45 parts by weight, bentonite 7-18 parts by weight, polyacrylamide 8-30 weight
Part, ethyl alcohol 6-34 parts by weight, rosin 8-24 parts by weight, phenolic resin 8-22 parts by weight, glycerol 6-24 parts by weight, iron oxide red 5-
23 parts by weight, methyl methacrylate 5-23 parts by weight, sodium carboxymethylcellulose 4-12 parts by weight, nanometer calcium carbonate 6-22 weight
Part.
A kind of above-mentioned environment protection type corrosion resistant coating is made of following raw material according to parts by weight: 30 weight of schmigel
Part, 17 parts by weight of pearl powder, 30 parts by weight of silica flour, 14 parts by weight of bentonite, 20 parts by weight of polyacrylamide, 21 weight of ethyl alcohol
Part, 17 parts by weight of rosin, 16 parts by weight of phenolic resin, 16 parts by weight of glycerol, 15 parts by weight of iron oxide red, methyl methacrylate
15 parts by weight, 10 parts by weight of sodium carboxymethylcellulose, 15 parts by weight of nanometer calcium carbonate.
In summary the invention has the following advantages: the present invention have good environmental protection, corrosion-resistant intensity high and
The case where metal casting is oxidized can be effectively protected in the advantages that wearability is good in use, effective to completely cut off
Oxygen, and the heat absorption capacity of material can be effectively reduced, will not to generate coated in metal surface have environment and human body
Harmful substance has preferable environmental-protecting performance.
Specific embodiment
Embodiment 1
A kind of environment protection type corrosion resistant coating is made of following raw material according to parts by weight: 10 parts by weight of schmigel, pearl powder 6
Parts by weight, 10 parts by weight of silica flour, 7 parts by weight of bentonite, 8 parts by weight of polyacrylamide, 6 parts by weight of ethyl alcohol, 8 weight of rosin
Part, 8 parts by weight of phenolic resin, 6 parts by weight of glycerol, 5 parts by weight of iron oxide red, 5 parts by weight of methyl methacrylate, carboxymethyl are fine
Tie up 4 parts by weight of plain sodium, 6 parts by weight of nanometer calcium carbonate.
Embodiment 2
A kind of environment protection type corrosion resistant coating is made of following raw material according to parts by weight: 30 parts by weight of schmigel, pearl powder 17
Parts by weight, 30 parts by weight of silica flour, 14 parts by weight of bentonite, 20 parts by weight of polyacrylamide, 21 parts by weight of ethyl alcohol, 17 weight of rosin
Measure part, 16 parts by weight of phenolic resin, 16 parts by weight of glycerol, 15 parts by weight of iron oxide red, 15 parts by weight of methyl methacrylate, carboxylic
10 parts by weight of sodium carboxymethylcellulose pyce, 15 parts by weight of nanometer calcium carbonate.
Embodiment 3
A kind of environment protection type corrosion resistant coating is made of following raw material according to parts by weight: 50 parts by weight of schmigel, pearl powder 28
Parts by weight, 50 parts by weight of silica flour, 21 parts by weight of bentonite, 32 parts by weight of polyacrylamide, 36 parts by weight of ethyl alcohol, 26 weight of rosin
Measure part, 24 parts by weight of phenolic resin, 26 parts by weight of glycerol, 25 parts by weight of iron oxide red, 25 parts by weight of methyl methacrylate, carboxylic
16 parts by weight of sodium carboxymethylcellulose pyce, 24 parts by weight of nanometer calcium carbonate.
The present invention has many advantages, such as that good environmental protection, corrosion-resistant intensity are high and wearability is good, in use can be with
The case where metal casting is oxidized is effectively protected, has effectively completely cut off oxygen, and the suction of material can be effectively reduced
Hot property will not generate to environment and the harmful substance of human body coated in metal surface, have preferable environmental-protecting performance.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (3)
1. a kind of environment protection type corrosion resistant coating, which is characterized in that be made of following raw material according to parts by weight: schmigel 10-
50 parts by weight, pearl powder 6-28 parts by weight, silica flour 10-50 parts by weight, bentonite 7-21 parts by weight, polyacrylamide 8-32 weight
Measure part, ethyl alcohol 6-36 parts by weight, rosin 8-26 parts by weight, phenolic resin 8-24 parts by weight, glycerol 6-26 parts by weight, iron oxide red
5-25 parts by weight, methyl methacrylate 5-25 parts by weight, sodium carboxymethylcellulose 4-16 parts by weight, nanometer calcium carbonate 6-24 weight
Measure part.
2. a kind of environment protection type corrosion resistant coating according to claim 1, which is characterized in that by it is following according to parts by weight
Raw material composition: schmigel 10-45 parts by weight, pearl powder 6-26 parts by weight, silica flour 10-45 parts by weight, bentonite 7-18 weight
Part, polyacrylamide 8-30 parts by weight, ethyl alcohol 6-34 parts by weight, rosin 8-24 parts by weight, phenolic resin 8-22 parts by weight, glycerol
6-24 parts by weight, iron oxide red 5-23 parts by weight, methyl methacrylate 5-23 parts by weight, sodium carboxymethylcellulose 4-12 weight
Part, nanometer calcium carbonate 6-22 parts by weight.
3. a kind of environment protection type corrosion resistant coating according to claim 1, which is characterized in that by it is following according to parts by weight
Raw material composition: 30 parts by weight of schmigel, 17 parts by weight of pearl powder, 30 parts by weight of silica flour, 14 parts by weight of bentonite, polyacrylamide
20 parts by weight of amine, 21 parts by weight of ethyl alcohol, 17 parts by weight of rosin, 16 parts by weight of phenolic resin, 16 parts by weight of glycerol, iron oxide red 15
Parts by weight, 15 parts by weight of methyl methacrylate, 10 parts by weight of sodium carboxymethylcellulose, 15 parts by weight of nanometer calcium carbonate.