CN101298541A - 芳纶帘线端头封口胶条的配方 - Google Patents

芳纶帘线端头封口胶条的配方 Download PDF

Info

Publication number
CN101298541A
CN101298541A CNA2008100736236A CN200810073623A CN101298541A CN 101298541 A CN101298541 A CN 101298541A CN A2008100736236 A CNA2008100736236 A CN A2008100736236A CN 200810073623 A CN200810073623 A CN 200810073623A CN 101298541 A CN101298541 A CN 101298541A
Authority
CN
China
Prior art keywords
carbon black
adhesive
aromatic polyamide
tire
aramid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100736236A
Other languages
English (en)
Inventor
俞华英
刘蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chemchina Shuguang Rubber Industry Research and Design Institute Co Ltd
Original Assignee
Shuguang Rubber Industry Research and Design Institute of China Rubber Group
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shuguang Rubber Industry Research and Design Institute of China Rubber Group filed Critical Shuguang Rubber Industry Research and Design Institute of China Rubber Group
Priority to CNA2008100736236A priority Critical patent/CN101298541A/zh
Publication of CN101298541A publication Critical patent/CN101298541A/zh
Pending legal-status Critical Current

Abstract

本发明是一种用作封住轮胎中芳纶带束层的芳纶帘线端头封口胶条的配方。该胶料配方以优质的天然橡胶为主材料，还有丁苯橡胶、粘合剂RS、粘合剂CRA－100、粘合增进剂AIR－201、粘合增进剂AIR－1、高耐磨炭黑、高分散性白炭黑、硅烷偶联剂、不溶性硫磺、次磺酰胺类促进剂为主要辅助材料，按一定配比而制成。本发明的优点在于该胶料具有与芳纶带束层帘线及未浸胶的芳纶帘线裁断端头高的粘合强度和动态疲劳、热老化后高的粘合保持率，同时具有拉伸强度高、撕裂强度高、定伸应力和硬度较高、与带束层挂胶性能匹配好的性能特点，可使轮胎在高速或长时间使用后，带束层端头部位不会出现脱空等质量问题，使轮胎使用安全、寿命长。

Description

芳纶帘线端头封口胶条的配方
技术领域：
本发明涉及帘线封口胶的配方，具体是芳纶帘线端头封口胶条的配方。
背景技术：
芳纶帘线是一种新型的轮胎用骨架材料。芳纶帘线作为轮胎带束层的骨架材料，具有高强度、高模量、热稳定性好等诸多优点，但芳纶帘线存在着与橡胶胶料粘合不好的技术问题，尤其是裁断后露出的没有浸胶层的芳纶帘线端头部份与橡胶胶料粘合困难。现有的芳纶帘线裁断端头封口胶条与芳纶帘线端头部位粘合强度低、动态使用后粘合保持率低。
发明内容：
本发明的目的是要提供一种芳纶帘线端头封口胶条的配方，用这种配方制成的封口胶，其与芳纶帘线裁断端头部位粘合强度高、动态疲劳和热老化后粘合保持率高，解决了芳纶帘线裁断端头与橡胶胶料粘合不好的问题，使使用芳纶帘线作带束层的轮胎在高速或长时间行驶时带束层端头部位不会出现脱空问题，轮胎使用安全、寿命长。
本配方以优质的天然橡胶为主原料，以丁苯橡胶、粘合剂RS、粘合剂CRA-100、粘合增进剂AIR-201、粘合增进剂AIR-1、高耐磨炭黑、高分散性白炭黑、硅烷偶联剂、不溶性硫磺、次磺酰胺类促进剂为主要辅料，再配以氧化锌、硬脂酸、对苯二胺类防老剂和酮胺类防老剂辅料组成，各组份原料用量重量百分比为：
1#烟片胶                          80～95
丁苯橡胶                          5～20
高耐磨炭黑                        20～40
高分散性白炭黑                    5～20
硅烷偶联剂                        0.5～5
氧化锌                            2～10
硬脂酸                            0.5～2
对苯二胺类防老剂                  0.5～4
酮胺类防老剂                      0.5～4
不溶性硫磺                        1～3
次磺酰胺类促进剂                  1～3
粘合增进剂AIR-201                 1～4
粘合增进剂AIR-1                   3～10
粘合剂RS                          2～4
粘合剂CRA-100                     2～6。
所述的辅料中丁苯橡胶为SBR1500，高耐磨炭黑为N330，高分散性白炭黑为Jc sil 150或Ultra sil 7000GR，硅烷偶联剂为KH-845-4，不溶性硫磺为IS-60或IS-90，次磺酰胺类促进剂为NS或NOBS。
配方中的粘合增进剂AIR-201可明显提高橡胶胶料与芳纶帘线的粘合强度；粘合剂RS、粘合剂CRA-100和高分散性白炭黑加入胶料中可提高橡胶胶料与未浸胶的芳纶帘线端头部份的粘合强度；加入粘合增进剂AIR-1可帮助胶料渗入芳纶帘线缝隙，提高胶料与帘线的接触面积，使粘合强度提高；使用不溶性硫磺可避免因硫磺喷出而造成半成品表面不粘的问题；
使用次磺酰胺类促进剂可使胶料具有较长的焦烧时间和较快的硫化速度，同样有利于胶料与芳纶帘线的粘合。
经测试，本发明封口胶条的性能如下表：
  项目   单位   性能范围
  初始粘合强度(H抽出值)   N/10mm   180～250
  100℃×24h热老化后粘合强度(H抽出值)   N/10mm   180～250
  300％定伸应力   MPa   10.0～20.0
  硬度(邵尔A)   度   65～85
  撕裂强度   kN/m   110～180
  拉伸强度   MPa   20～30
  扯断伸长率   ％   400～500。
本发明的优点是：该胶料具有与芳纶带束层帘线及未浸胶的芳纶帘线裁断端头高的粘合强度和动态疲劳、热老化后高的粘合保持率，同时具有拉伸强度高、撕裂强度高、定伸应力和硬度较高、与带束层挂胶性能匹配好的性能特点。该胶料用作芳纶帘线带束层裁断端头的封口胶条，可使轮胎在高速或长时间使用后，带束层端头部位不会出现脱空等质量问题，轮胎使用安全、寿命长。
具体实施方式：
下面将描述本发明的几个实施例，但本发明的内容完全不局限于此。
下表实施例中各组份原料用量为重量份：
  原材料名称   实施例1   实施例2   实施例3
  1#烟片胶   80   90   95
  丁苯橡胶(SBR1500)   20   10   5
  高耐磨N330炭黑   25   30   35
  高分散性白炭黑Jc sil 150或Ultra sil 7000GR   15   10   5
  硅烷偶联剂KH-845-4   2   1   0.5
  氧化锌   5   5   5
  硬脂酸   1   0.5   0.5
  对苯二胺类防老剂4020或4010NA   1.5   1.5   1.5
  酮胺类防老剂BLE或RD   2.5   2.5   2.5
  不溶性硫磺IS-60或IS-90   2.3   2.1   1.8
  次磺酰胺类促进剂NS或NOBS   1.8   2   2.2
  粘合增进剂AIR-201   1   2   3
  粘合增进剂AIR-1   5   5   5
  粘合剂RS   1.5   2   3
  粘合剂CRA-100   2.5   3   4。
上述各实施例制备工艺相同，按原料配比通过密炼机混炼，制造出混炼胶，用挤出机挤出的方式将混炼胶制成封口胶条半成品，在成型机上将封口胶条半成品贴于带束层端头部位，制成轮胎胎坯，并通过硫化机将胎坯硫化而成为轮胎成品。

Claims (3)

1、芳纶帘线端头封口胶条的配方，其特征是：以天然橡胶为主原料，以丁苯橡胶、粘合剂RS、粘合剂CRA-100、粘合增进剂AIR-201、粘合增进剂AIR-1、高耐磨炭黑、高分散性白炭黑、硅烷偶联剂、不溶性硫磺、次磺酰胺类促进剂为主要辅料配置而成，各组份用量重量份比为：
1#烟片胶                     80～95
丁苯橡胶                     5～20
高耐磨炭黑                   20～40
高分散性白炭黑               5～20
硅烷偶联剂                   0.5～5
不溶性硫磺                   1～3
次磺酰胺类促进剂             1～3
粘合增进剂AIR-201            1～4
粘合增进剂AIR-1              3～10
粘合剂RS                     2～4
粘合剂CRA-100                2～6。
2、根据权利要求1所述的配方，其特征是：还含有下述重量份的辅料：
氧化锌                       2～10
硬脂酸                       0.5～2
对苯二胺类防老剂4020或4010NA 0.5～4
酮胺类防老剂BLE或RD          0.5～4。
3、根据权利要求1所述的配方，其特征是：所述的辅料中丁苯橡胶为SBR1500，高耐磨炭黑为N330，高分散性白炭黑为Jc sil 150或Ultra sil 7000GR，硅烷偶联剂为KH-845-4，不溶性硫磺为IS-60或IS-90，次磺酰胺类促进剂为NS或NOBS。
CNA2008100736236A 2008-06-16 2008-06-16 芳纶帘线端头封口胶条的配方 Pending CN101298541A (zh)