CN101298538A - 一种水性防锈隔热涂料 - Google Patents
一种水性防锈隔热涂料 Download PDFInfo
- Publication number
- CN101298538A CN101298538A CNA200710027813XA CN200710027813A CN101298538A CN 101298538 A CN101298538 A CN 101298538A CN A200710027813X A CNA200710027813X A CN A200710027813XA CN 200710027813 A CN200710027813 A CN 200710027813A CN 101298538 A CN101298538 A CN 101298538A
- Authority
- CN
- China
- Prior art keywords
- percent
- rust
- heat insulating
- coating
- insulating coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性防锈隔热涂料，其特征在于该涂料主要由下述重量百分含量的物料组成：软水10－30％、羟乙基纤维素0.1－0.3％、防腐剂0.1－0.2％、防霉剂0.2－0.4％、胺盐分散剂0.2－0.5％、低泡润湿剂0.02－0.1％、消泡剂0.1－0.3％、乙二醇1－4％、重钙3－13％、滑石粉3－20％、钛白粉18－25％、有机胺0.1－0.6％、煅烧高岭土3－6％、Tg35℃以上的硅丙乳液28－43％、十二醇酯1.3－2.8％、平均粒径约10－30um的空心硅酸钠颗粒3－13％、增稠剂0.1－0.6％、硅灰石粉3－12％，调pH10－pH11本发明用于铁皮屋顶，外墙等防锈隔热效果好，耐久性好，易储藏，易涂布，成本较低，水性环保。
Description
技术领域
本发明涉及一种水性涂料，特别是一种用于铁皮屋顶，外墙等防锈隔热效果好，耐久性好，易储藏，易涂布的水性防锈隔热涂料。
背景技术
目前用于铁皮屋顶，外墙等的涂料为油性涂料或普通水性建筑涂料等，油性涂料不环保，不易涂布，成本高，隔热效果不太好；而普通水性建筑涂料等防锈隔热效果不太好，耐久性也不太好。总的说来，缺乏一种用于铁皮屋顶，外墙等涂装的综合性能较好的涂料。主要原因是有机容剂含量较高；或成膜物质结构不太致密，抗老化性较差；或无机物抗光热性较差，隔热方式单一，隔热效果较差等。
发明内容
为了克服现有技术的不足，本发明提供一种用于铁皮屋顶，外墙等防锈隔热效果好，耐久性好，易储藏，易涂布，成本较低，水性环保的防锈隔热涂料。
本发明解决其技术问题所采用的技术方案是：
一种水性防锈隔热涂料，其特征在于该涂料主要由下述重量百分含量的物料组成：软水10-30％、羟乙基纤维素0.1-0.3％、防腐剂0.1-0.2％、防霉剂0.2-0.4％、胺盐分散剂0.2-0.5％、低泡润湿剂0.02-0.1％、消泡剂0.1-0.3％、乙二醇1-4％、重钙3-13％、滑石粉3-20％、钛白粉18-25％、有机胺0.1-0.6％、煅烧高岭土3-6％、Tg35℃以上的硅丙乳液28-43％、十二醇酯1.3-2.8％、平均粒径约10-30um的空心硅酸钠颗粒3-13％、增稠剂0.1-0.6％，硅灰石粉3-12％，调PH10-PH11。
本发明采用的物料均可从市场直接购到，如Tg35℃以上的硅丙乳液采用广东美侨公司生产的MQ-2001，平均粒径约10-30um的空心硅酸钠颗粒可从河北五阳防腐材料厂购，十二醇酯可从湖北新华化工公司购。
本发明除平均粒径约10-30um的空心硅酸钠颗粒最后添加，低速分散，调PH10-PH11外，其它物料均按乳胶漆常规工艺依次投入生产。
本发明有益效果是：用于铁皮屋顶，外墙等防锈隔热效果好，耐久性好，易储藏，易涂布，成本较低，水性环保等。由于本发明中加入的Tg35℃以上的硅丙乳液成膜后抗老化性好，硬度高；金红石钛白粉热反射强，耐侯性好；平均粒径约10-30um的空心硅酸钠颗粒中空阻热，与金红石钛白粉双重隔热，它还具有收缩弹性，防热涨冷缩引起的涂层破坏，增白遮蔽，防腐，防紫外线，有利涂层耐久；硅灰石粉等提供较高的PH值有利防锈。
下面结合实施例对本发明进一步说明。
具体实施方式
实施例1(单位：公斤；总量：100公斤)
软水：余量、羟乙基纤维素0.2、防腐剂0.1、防霉剂0.4、胺盐分散剂0.43、低泡润湿剂0.05、消泡剂0.26、乙二醇2、重钙5、滑石粉3、钛白粉18、有机胺：适量、煅烧高岭土4、Tg35℃以上的硅丙乳液35、十二醇酯1.8、平均粒径约10-30um的空心硅酸钠颗粒5、增稠剂：适量，硅灰石粉6，调PH10-PH11。
实施例2(单位：公斤；总量：100公斤)
软水：余量、羟乙基纤维素0.18、防腐剂0.13、防霉剂0.35、胺盐分散剂0.46、低泡润湿剂0.05、消泡剂0.28、乙二醇3、重钙6、滑石粉3、钛白粉20、有机胺：适量、煅烧高岭土3、Tg35℃以上的硅丙乳液38、十二醇酯2、平均粒径约10-30um的空心硅酸钠颗粒6、增稠剂：适量，硅灰石粉7，调PH10-PH11。
实施例3(单位：公斤；总量：100公斤)
软水：余量、羟乙基纤维素0.23、防腐剂0.13、防霉剂0.48、胺盐分散剂0.47、低泡润湿剂0.04、消泡剂0.3、乙二醇1.8、重钙3、滑石粉3、钛白粉18、有机胺：适量、煅烧高岭土3、Tg35℃以上的硅丙乳液40、十二醇酯2、平均粒径约10-30um的空心硅酸钠颗粒7、增稠剂：适量，硅灰石粉5，调PH10-PH11。
Claims (3)
1.一种水性防锈隔热涂料，其特征在于该涂料主要由下述重量百分含量的物料组成：软水10-30％、重钙3-13％、滑石粉3-20％、钛白粉18-25％、有机胺0.1-0.6％、煅烧高岭土3-6％、Tg35℃以上的硅丙乳液28-43％、十二醇酯1.3-2.8％、平均粒径约10-30um的空心硅酸钠颗粒3-13％、增稠剂0.1-0.6％、硅灰石粉3-12％，调PH10-PH11。
2.根据权利要求1所述的一种水性防锈隔热涂料，其特征在于其还包含有防霉剂0.2-0.4％、胺盐分散剂0.2-0.5％、低泡润湿剂0.02-0.1％、消泡剂0.1-0.3％、乙二醇1-4％、
3.根据权利要求2所述的一种水性防锈隔热涂料，其特征在于其还包含有羟乙基纤维素0.1-0.3％、防腐剂0.1-0.2％。