CN101279456B - 改良铜氨(胺)季铵盐木材防腐剂 - Google Patents
改良铜氨(胺)季铵盐木材防腐剂 Download PDFInfo
- Publication number
- CN101279456B CN101279456B CN2008100378039A CN200810037803A CN101279456B CN 101279456 B CN101279456 B CN 101279456B CN 2008100378039 A CN2008100378039 A CN 2008100378039A CN 200810037803 A CN200810037803 A CN 200810037803A CN 101279456 B CN101279456 B CN 101279456B
- Authority
- CN
- China
- Prior art keywords
- quaternary ammonium
- ammonium salt
- wood
- amine
- cuprammonium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种改良铜氨(胺)季铵盐木材防腐剂，其特征在于，在铜氨(胺)季铵盐木材防腐剂中，含有1、3、5-三羟乙基均三嗪。本发明中的改良铜氨(胺)季铵盐木材防腐剂，防霉效果优于未改良的ACQ木材防腐剂，而且对金属的腐蚀性小于未改良的ACQ木材防腐剂。拓宽了ACQ木材防腐剂的使用范围。
Description
技术领域
本发明涉及一种改良铜氨(胺)季铵盐木材防腐剂。
背景技术
铜氨(胺)季铵盐(ACQ)木材防腐剂是由带二价正电荷的铜和烷基铵化合物与水按一定的比例混合而成的一种水载复合防腐剂，它是由美国化学专业公司(CSI)研制开发的。1992年收入美国AWPA标准，在抗生物危害的性能方面能与CCA木材防腐剂相媲美，而在对环境和安全性方面方面大大优于CCA的新一代环保木材防腐剂，是当今世界通用的替代CCA的一种性能最佳的环保木材防腐剂。
我国是从2002年开始研制2003年起投放市场的，国外也有进口到我国的ACQ木材防腐剂，均在我国防腐木材生产单位使用。但在使用过程中用户普遍反映存在两大突出的问题：
1、防霉效果不好：经防腐处理后的ACQ防腐木，在没有出厂以前，贮存过程中就发生霉变现象。
2、在使用过程中对金属有比较严重的腐蚀作用，这不仅对防腐处理设备带来蚀影响，而且对ACQ防腐木出厂使用过程中的木结构和木构件金属紧固件造成腐蚀危害。
发明内容
本发明的目的是根据现有技术中的不足，提供一种防霉效果更好的改良铜氨(胺)季铵盐木材防腐剂。
为实现以上目的，本发明通过以下技术方案实现：
一种改良铜氨(胺)季铵盐木材防腐剂，其特征在于，在铜氨(胺)季铵盐木材防腐剂中，含有1、3、5-三羟乙基均三嗪。
其中，所述的铜氨(胺)季铵盐木材防腐剂含有铜化合物和季铵盐。
其中，以1、3、5-三羟乙基均三嗪、铜化合物和季铵盐总重量为基准，1、3、5-三羟乙基均三嗪的重量百分含量为2～8％。
其中，铜化合物与季铵盐的重量比为1.5～3∶1。
其中，1、3、5-三羟乙基均三嗪、铜化合物和季铵盐溶于溶剂中，所述的溶剂包括水、氨水和有机胺。
其中，1、3、5-三羟乙基均三嗪、铜化合物和季铵盐在防腐剂中的重量比为1％～20％。
其中，所述的铜化物选自碱式碳酸铜、氢氧化铜。
其中，所述的季铵盐选自双癸基二甲基碳酸铵。
本发明中，经过大量筛选试验在ACQ防腐剂内加入一种专用防霉剂1、3、5-三羟乙基均三嗪，此防霉剂不仅要有很好的防治木材霉菌的效果而且要能够加入到ACQ的木材防腐剂中去，需要有较好的混溶性和稳定性。
本发明中的改良铜氨(胺)季铵盐木材防腐剂，是有效组分与一定量溶剂混合，搅拌均匀即可用于对木材进行防腐处理。
本发明中的改良铜氨(胺)季铵盐木材防腐剂，防霉效果优于未改良的ACQ木材防腐剂，而且对金属的腐蚀性小于未改良的ACQ木材防腐剂。拓宽了ACQ木材防腐剂的使用范围。提高了ACQ木材防腐剂的技术含量。
具体实施方式
下面结合具体实施例对本发明的做进一步说明：
实施例1各组分重量百分比为：
碱式碳酸铜(含量以CuO计) 58.8％
双葵基二甲基碳酸铵 39.2％
1、3、5-三羟乙基均三嗪 2％
将上述三种物质混合均匀，按照每重量份加入到9重量份溶剂中，溶剂为按重量份由10％氨水、23％有机胺和47％水组成，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例2各组分重量百分比为
碱式碳酸铜(含量以CuO计) 73.5％
双葵基二甲基碳酸铵 24.5％
1、3、5-三羟乙基均三嗪 2％
将上述三种物质混合均匀，按照每重量份改良铜氨(胺)季铵盐木材防腐剂加入到99重量份溶剂中，溶剂为按重量份由10％氨水、30％乙醇胺和60％水组成，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例3各组分重量百分比为
纳米碱式碳酸铜(含量以CuO计) 57％
双葵基二甲基碳酸铵 38％
1、3、5-三羟乙基均三嗪 5％
将上述三种物质混合均匀，按照每重量份加入到5重量份溶剂中，溶剂为按重量份由10％氨水、30％有机胺和60％水组成，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例4各组分重量百分比为
纳米碱式碳酸铜(含量以CuO计) 63％
双葵基二甲基碳酸铵 32％
1、3、5-三羟乙基均三嗪 5％
将上述三种物质混合均匀，按照每重量份加入到5重量份溶剂中，溶剂为按重量份由12％氨水、33％有机胺和55％水组成，，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例5各组分重量百分比为
纳米碱式碳酸铜(含量以CuO计) 67.15％
双葵基二甲基碳酸铵 26.85％
1、3、5-三羟乙基均三嗪 6％
将上述三种物质混合均匀，按照每重量份加入到7重量份溶剂中，溶剂为按重量份由8％氨水、40％有机胺和52％水组成，，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例6各组分重量百分比为
纳米氢氧化铜(含量以CuO计) 62％
双葵基二甲基碳酸铵 31％
1、3、5-三羟乙基均三嗪 7％
将上述三种物质混合均匀，按照每重量份加入到15重量份溶剂中，溶剂为按重量份由12％氨水、33％有机胺和55％水组成，，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例7各组分重量百分比为
纳米氢氧化铜(含量以CuO计) 65.72％
双葵基二甲基碳酸铵 26.28％
1、3、5-三羟乙基均三嗪 8％
将上述三种物质混合均匀，按照每重量份加入到30重量份溶剂中，溶剂为按重量份由12％氨水、33％有机胺和55％水组成，，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例8各组分重量百分比为
纳米氢氧化铜(含量以CuO计) 54.83％
双葵基二甲基碳酸铵 42.17％
1、3、5-三羟乙基均三嗪 3％
将上述三种物质混合均匀，按照每重量份加入到溶剂中，溶剂为按重量份由15％氨水、35％乙醇胺和50％水组成，搅拌混合均匀，即可用于对木材进行防腐处理。
实施例9各组分重量百分比为
纳米氢氧化铜(含量以CuO计) 63.4％
双葵基二甲基碳酸铵 31.6％
1、3、5-三羟乙基均三嗪 5％
将上述三种物质混合均匀，按照每重量份加入到8重量份溶剂中，溶剂为按重量份由10％氨水、25％乙醇胺和65％水组成，，搅拌混合均匀，即可用于对木材进行防腐处理。
将实施例9所制备的防腐剂与其它未改良的ACQ防腐剂，分别对木材按照常规防腐处理工艺处理木材，防霉效果如表1所示：
防霉试验结果表1
| 防腐剂名称 | 平均彼害值(D) | 防治效力(E)％ |
| 改良ACQ | 0.42 | 89.5 |
| 国产ACQ | 1.50 | 62.5 |
| 进口ACQ(一) | 1.33 | 66.7 |
| 防腐剂名称 | 平均彼害值(D) | 防治效力(E)％ |
| 进口ACQ(二) | 0.89 | 77.8 |
将实施例9所制备的防腐剂与其它未改良的ACQ防腐剂，在相同条件下分别测试对常用金属的腐蚀性，结果如图2所示：
金属腐蚀试验结果 表2
从上表可以看出，本发明中的改良防腐剂防霉效果比未经改良的防腐剂更好，而且，对各种常用金属的腐蚀性更低。
Claims (3)
1.一种改良铜氨(胺)季铵盐木材防腐剂，其特征在于，在铜氨(胺)季铵盐木材防腐剂中，含有1、3、5-三羟乙基均三嗪，所述铜氨(胺)季铵盐木材防腐剂中还含有铜化合物和季铵盐，且以1、3、5-三羟乙基均三嗪、铜化合物和季铵盐总重量为基准，1、3、5-三羟乙基均三嗪的重量百分含量为2～8％；其中，所述的铜化合物为纳米氢氧化铜，所述的季铵盐为双癸基二甲基碳酸铵，且所述1、3、5-三羟乙基均三嗪、铜化合物和季铵盐在防腐剂中的重量比为1％～20％。
2.根据权利要求1所述的改良铜氨(胺)季铵盐木材防腐剂，其特征在于，铜化合物与季铵盐的重量比为1.5～3∶1。
3.根据权利要求1-2任一权利要求所述的改良铜氨(胺)季铵盐木材防腐剂，其特征在于，1、3、5-三羟乙基均三嗪、铜化合物和季铵盐溶于溶剂中，所述的溶剂包括水、氨水和有机胺。