CN101245142B - 一种双马树脂改性氰酸酯预浸料的制备方法 - Google Patents

一种双马树脂改性氰酸酯预浸料的制备方法 Download PDF

Info

Publication number
CN101245142B
CN101245142B CN2007103003406A CN200710300340A CN101245142B CN 101245142 B CN101245142 B CN 101245142B CN 2007103003406 A CN2007103003406 A CN 2007103003406A CN 200710300340 A CN200710300340 A CN 200710300340A CN 101245142 B CN101245142 B CN 101245142B
Authority
CN
China
Prior art keywords
cyanate
resin
modified cyanate
resin modified
bismaleimide resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2007103003406A
Other languages
English (en)
Other versions
CN101245142A (zh
Inventor
王震
刘敬峰
杨慧丽
孟祥胜
范卫锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou Institute Of Energy Storage Materials & Devices
Original Assignee
Changchun Institute of Applied Chemistry of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changchun Institute of Applied Chemistry of CAS filed Critical Changchun Institute of Applied Chemistry of CAS
Priority to CN2007103003406A priority Critical patent/CN101245142B/zh
Publication of CN101245142A publication Critical patent/CN101245142A/zh
Application granted granted Critical
Publication of CN101245142B publication Critical patent/CN101245142B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种双马来酰亚胺树脂改性氰酸酯预浸料的制备方法。该方法将马来酐封端的氧醚酰亚胺与氰酸酯溶于二氧六环、乙二醇单甲醚、乙二醇二甲醚三者之一或三者混合物中加热搅拌就得到可以用来浸渍纤维的树脂溶液。其优点在于采用了成型工艺较好的双马树脂和氰酸酯共聚物，并且采用低沸点溶剂，有利于高性能复合材料的制备，其玻璃纤维增强的复合材料拉伸强度大于300MPa，断裂伸长率大于10％，和普通双马改性氰酸酯相比，本发明的双马树脂改性氰酸酯制备的复合材料具有较高的韧性。

Description

一种双马树脂改性氰酸酯预浸料的制备方法
技术领域
本发明属于一种双马树脂改性氰酸酯预浸料的制备方法。
背景技术
氰酸酯(CE)树脂由于其具有优良的综合性能而成为极具吸引力的高性能聚合物，广泛应用于多层印刷线路版、光电装置的高速基材、雷达天线罩、高增益天线、隐形航空器及结构复合材料等高科技领域。CE适用于模压，传递模塑，热压、缠绕和挤拉等各种成型工艺。但CE的缺点主要是固化树脂的脆性较大，使用温度偏低。日本和中国台湾分别在二十世纪七十年代和九十年代制备了一系列改性的氰酸酯树脂(美国专利4110364；5886134)，它是采用双马来酰亚胺树脂与氰酸酯共聚改性得到的树脂，也叫做BT树脂(bismaleimide triazine)，该共聚物具有良好的耐热性、耐湿热性、低介电性能等。但是用普通双马树脂即4，4′-双马来酰亚胺基二苯甲烷(BMI)改性氰酸酯得到的BT树脂，其结构如下：
Figure G200710300340601D00011
由于BMI的分子量低，BT树脂的交联密度比较大，断裂伸长率一般小于5％，还存在树脂韧性差的问题。
发明内容
本发明提供了一种双马树脂改性氰酸酯预浸料的制备方法，步骤和条件法如下：
将双马树脂加入氰酸酯中，氰酸酯：双马树脂的重量比为30∶(3.33～70)，再加入混合溶剂，氰酸酯的重量(g)∶混合溶剂的体积(ml)为30∶(78～234)；加热回流5～60分钟，制得一种双马树脂改性氰酸酯预浸料。
所述的混合溶剂由二氧六环、乙二醇单甲醚、乙二醇二甲醚三者之一或者三者任意体积比组成的；
所述的氰酸酯为双酚A型氰酸酯(BCE)，其结构如下：
Figure G200710300340601D00021
所述的双马树脂为马来酐封端的氧醚酰亚胺，其具有下面的结构式：
式中，聚合度n为1，2，3，4，5。
以下，把聚合度n为1，2，3，4，5的马来酐封端的氧醚酰亚胺分别标记为M1，M2，M3，M4，M5；
有益效果：
本发明的一种双马树脂改性氰酸酯预浸料的制备方法，其优点在于采用了成型工艺较好的双马树脂和氰酸酯共聚物，并且采用低沸点溶剂，有利于高性能复合材料的制备，其玻璃纤维增强的复合材料拉伸强度大于300MPa，断裂伸长率大于10％，和普通双马改性氰酸酯相比，新型双马树脂改性氰酸酯制备的复合材料具有较高的韧性。
具体实施方式
实施例1：室温下称取BCE树脂30g，M1树脂70g于反应瓶中，加入二氧六环、乙二醇单甲醚、乙二醇二甲醚混合(体积比为3/4/4)溶剂234ml，回流5分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例2：室温下称取BCE树脂30g，M1树脂30g于反应瓶中，加入二氧六环、乙二醇单甲醚混合溶剂(体积比为6/4)140ml，回流30分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例3：室温下称取BCE树脂30g，M1树脂3.33g于反应瓶中，加入二氧六环、乙二醇二甲醚混合溶剂(体积比为5/5)78ml，回流60分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例4：室温下称取BCE树脂30g，M3树脂70g于反应瓶中，再加入乙二醇单甲醚、乙二醇二甲醚混合溶剂(体积比为4/6)234ml，回流5分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例5：室温下称取BCE树脂30g，M3树脂30g于反应瓶中，加入乙二醇单甲醚溶剂140ml，回流30分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例6：室温下称取BCE树脂30g，M3树脂3.33g于反应瓶中，加入乙二醇二甲醚溶剂78ml，回流60分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例7：室温下称取BCE树脂30g，M5树脂70g于反应瓶中，加入二氧六环溶剂234ml，然后升温至100℃并同时搅拌，回流5分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例8：室温下称取BCE树脂30g，M5树脂30g于反应瓶中，加入二氧六环溶剂140ml，回流15分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例9：室温下称取BCE树脂30g，M5树脂3.33g于反应瓶中，加入二氧六环、乙二醇单甲醚、乙二醇二甲醚混合(体积比为4/3/3)溶剂78ml，回流30分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。
实施例10：室温下称取BCE树脂30g，M5树脂3.33g于反应瓶中，加入二氧六环溶剂78ml，回流60分钟后，于室温条件下静置得一种双马树脂改性氰酸酯预浸料。

Claims (1)

1.一种双马树脂改性氰酸酯预浸料的制备方法，步骤和条件如下：将双马树脂加入氰酸酯中，氰酸酯∶双马树脂的重量比为30∶(3.33～70)，再加入混合溶剂，氰酸酯的重量g∶混合溶剂的体积ml为30∶(78～234)；加热回流5～60分钟，制得一种双马树脂改性氰酸酯预浸料，所述的混合溶剂由二氧六环、乙二醇单甲醚、乙二醇二甲醚三者之一或者三者任意体积比组成的；
所述的氰酸酯为双酚A型氰酸酯BCE，其结构如下：
Figure FA20192211200710300340601C00011
所述的双马树脂为马来酐封端的氧醚酰亚胺，其具有下面的结构式：
Figure FA20192211200710300340601C00012
式中，聚合度n为1，2，3，4，5。
CN2007103003406A 2007-12-27 2007-12-27 一种双马树脂改性氰酸酯预浸料的制备方法 Expired - Fee Related CN101245142B (zh)