CN101225600A - 一种防紫外、抗静电、防花粉、防水织物整理方法 - Google Patents
一种防紫外、抗静电、防花粉、防水织物整理方法 Download PDFInfo
- Publication number
- CN101225600A CN101225600A CNA2008100195127A CN200810019512A CN101225600A CN 101225600 A CN101225600 A CN 101225600A CN A2008100195127 A CNA2008100195127 A CN A2008100195127A CN 200810019512 A CN200810019512 A CN 200810019512A CN 101225600 A CN101225600 A CN 101225600A
- Authority
- CN
- China
- Prior art keywords
- fabric
- ultraviolet
- proof
- pollen
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种防紫外、抗静电、防花粉、防水织物整理方法，按组分为防紫外剂10～60g/L、抗静电剂10～40g/L，调节整理的pH为5～6；将织物在上述整理液中进行一浸一轧，轧液率为30～80％；在160～195℃条件下焙烘30～90s；按组分为防水剂10～60g/L、防花粉60～80g/L，调节整理的pH为5～6；将织物在上述整理液中进行一浸一轧，轧液率为30～80％；在160～195℃条件下焙烘30～90s。防紫外、抗静电一浴、防花粉、防水一浴，一定程度降低了能源损耗、简化了工艺；另外采用先抗静电后防水的整理顺序，可以达到抗静电、防水效果同时达到，2道工艺流程赋予织物4种功能，且使各种功能互不影响。
Description
技术领域
本发明属于纺织品的整理方法领域，具体的是一种防紫外、抗静电、防花粉、防水织物整理方法。
背景技术
随着人们生活水平的提高，大家对纺织品的要求也越来越高，希望纺织品功能多样化，可以满足人们在不同环境中的不同需求，所以多功能整理成了当今纺织品的一个趋势。在多功能处理过程中，我们希望尽可能工艺简化，这样既可以降低能耗节约成本，又可以减少污水排放。
过度的紫外线辐射对人体有害已众所周知，人们大力研究紫外线辐射防护问题，各种防紫外线化妆品营运而生，但它的使用面积和防护能力有限，因此有必要利用合适的纺织品来有效地遮断队人体有害的过度紫外线，而防紫外后整理也就成为防护纺织品的一个趋势。
纺织品要达到防紫外线的目的，可采用TiO2粉、陶瓷粉等反光性强的物质对织物进行后整理加工，提高织物对紫外线的反射和散射的能力；或采用紫外线吸收剂对织物进行后整理加工.提高织物对紫外线的吸收能力：也可以将这两类物质混合后处理织物.使它们对紫外线既有反射和散射作用又具有吸收作用。
由于无机紫外线屏蔽剂严重影响织物的透气性和手感.目前市场上大量使用的防紫外线剂是紫外线吸收剂。适宜于纺织品应用的紫外线吸收剂应具有的条件：①吸收紫外线的波长范围要宽，吸收系数要大，尽可能吸收280～400nm，并且吸收稳定；②对纺织品无光催化现象，不影响织物的色泽、白度和色牢度；③产品安全无毒，无刺激性等有害气味，对人体皮肤无过敏反应；④与其它化学品兼容性好，具有一定的耐洗涤性能。
合成纤维纺织品虽然具有坚牢、耐用、美观大方，快干免烫等特点，但大多数合成纤维由于它们晶体结构，表面特性等赋予它们固有的疏水性，以及与此直接有关的绝缘性，使其在纺织加工生产和服装穿用过程中，出现了一系列的静电现象，给生活和生产造成了一些麻烦，尤其是在石油部门和煤矿部门，静电现象可以引起火灾，给国家财产和人民生命带来不应有的损失，因此，防静电整理是纺织品整理的一大方向。抗静电纺织品常采用抗静电剂来对纺织品进行整理。抗静电剂的主要作用是改变纤维的下列性能：1.提高纤维表面的电导率；2.在纤维和摩擦表面之间产生具有高介电常数的中间层；3.降低接触电势，提高纤维光滑性。
抗静电的最有效方法是提高纤维表面的电导率，绝大部分实际应用的抗静电剂是基于这一原理。纺丝油剂、络丝油剂等加入抗静电剂形成复配油剂也是上述作用的综合。不要把这几种作用孤立地分割开来，通过涂复亲水剂来提高电导率，同时也提高了表层的介电常数。许多仅仅改进表面电导率的抗静电剂或者赋予纤维较大光滑性的复配油剂，也就附带降低了摩擦和静电充电的倾向。降低接触电势的作用是很小的，因为这与纤维——摩擦物体的结合情况有关。
提高纤维的电导率对抗静电剂提出两种要求，一是要具有吸水性，一是具有可移动的离子化基团。只要具备其中一条，就有抗静电性能，如果二者均有，则效果更佳具有吸水性的包括各种表面活性剂，含羟基、羧基、环氧基等的化台物。季铵盐中含有可移动的卤原子，进一步强化了改善电导率的作用。
易于积聚电荷的织物也具有易玷污性，如果静电被消除，沾污自然会降低。当然，开发和利用抗静电剂主要是为了消除静电，提高织物的抗沾污性是跗带的结果。
防水透湿织物的开发、使用在欧美和日本等先进国家已有二十多年历史。随着人们对织物功能的要求越来越高，同时也因为人类生存环境的不断变化，使得这一类织物更具有远大的开发潜力。本发明采用含氟防水剂在其纤维表面形成分子屏障，由于分子屏障的低表面能，可以阻止水以及各种油污、污物的沾附和渗透，即使有水或油污在织物表面停留也是呈现液珠状，很容易去除。
由于人们生活水平的提高，在饮食中摄入了大量的鸡蛋、肉制品等高蛋白、高热量饮食，结果导致体内产生抗体的能力亢进，因而遇到花粉等抗原时，就更容易发生变态反应。另由于大气污染、水质污染及食品添加剂的大量应用，导致人体接触更多的抗原物质，促使人类发生变态反应性疾病，所以春暖花开时节花粉过敏者越来越多。纺织品整理过程中加入一些花粉吸附剂，吸附身体周围的花粉，使其不与人体接触或不被吸入呼吸道，从而达到防花粉过敏的功效。
发明内容
本发明的目的在于提供一种防紫外、抗静电、防花粉、防水织物整理方法，使织物具有多种功能性作用，满足人们多种需求。
本发明所述的技术方案是：将需要整理的织物进行如下步骤的整理加工：
①按组分为防紫外剂10～60g/L、抗静电剂10～40g/L，调节整理的pH为5～6；
②将织物在上述整理液中进行一浸一轧，轧液率为30～80％；
③在160～195℃条件下焙烘30～90s。
④按组分为防水剂10～60g/L、防花粉60～80g/L，调节整理的pH为5～6；
⑤将织物在上述整理液中进行一浸一轧，轧液率为30～80％；
⑥在160～195℃条件下焙烘30～90s。
所述的织物为纯涤纶、纯锦纶、涤锦织物。
与现有技术相比，本发明的优点是：防紫外、抗静电一浴、防花粉、防水一浴，一定程度降低了能源损耗、简化了工艺；另外采用先抗静电后防水的整理顺序，可以达到抗静电、防水效果同时达到，2道工艺流程赋予织物4种功能，且使各种功能互不影响。
具体实施方式
下面结合具体实例说明：
实施例1
本实施例所采用的加工方法适用于纯涤纶织物。
190T春亚纺织物采用如下方法进行整理：含防紫外剂cibafast 4566(p)40g/L、HS-2032非离子抗静电剂20g/L的整理剂，用醋酸调节pH＝6，采用一浸一轧工艺处理后，于175℃烘干定型40s。再经含防花粉剂附着剂Queenseter POL80g/L、防水剂TG-410C 20g/L的整理液一浸一轧处理，于175烘干定型40s。
未整理织物(整理前)和经本实例加工整理织物按标准做防紫外、抗静电、防水性能，其对比结果参见表1。
实施例2
本实施例所采用的加工方法适用于纯锦纶织物。
228T塔丝隆织物采用如下方法进行整理：含防紫外剂亨斯曼CEL 50g/L、HS-2032非离子抗静电剂30g/L的整理剂，用醋酸调节pH＝6，采用一浸一轧工艺处理后，于170℃烘干定型40s。再经含防花粉剂附着剂Queenseter POL80g/L、防水剂TG-410C 30g/L的整理液一浸一轧处理，于170烘干定型40s。
未整理织物(整理前)和经本实例加工整理织物按标准做防紫外、抗静电、防水性能，其对比结果参见表1。
实施例3
本实施例所采用的加工方法适用于锦涤织物。
斜纹锦涤桃皮绒织物采用如下方法进行整理：含防紫外剂cibafast 4566(p)30g/L、HS-2032非离子抗静电剂20g/L的整理剂，用HAc调节pH＝6，采用一浸一轧工艺处理后，于170℃烘干定型40s。再经含防花粉剂附着剂Queenseter POL80g/L、防水剂TG-410C 20g/L的整理液一浸一轧处理，于170℃烘干定型40s。
未整理织物(整理前)和经本实例加工整理织物分别按标准GB/T18830-2002、FZ/T 01042-1996、AATCC35-2006做防紫外、抗静电、防水性能，其对比结果参见表1。
表1
| 样品 | 实施例1 | 实施例2 | 实施例3 | ||
| 防紫外(UPF) | 整理前 | 8 | 18 | 22 | |
| 整理后 | 40 | 50 | 50+ | ||
| 抗静电 | 整理前 | 静电压(v) | 1023 | 1368 | 1707 |
| 半衰期(s) | ＞99.9 | ＞99.9 | ＞99.9 | ||
| 整理后 | 静电压(v) | 259 | 652 | 57 | |
| 半衰期(s) | 0.6 | 1.1 | 0.3 | ||
| 防水(分) | 整理前 | 0 | 0 | 0 | |
| 整理后 | 100 | 100 | 100 | ||
表1是上述实施例样品整理前后防紫外、抗静电、防水性能测试结果对照，测试方法按。由表1可以看出，按本发明技术方案经整理加工的织物具有优良的防紫外、抗静电、防水性能。
Claims (6)
1.一种防紫外、抗静电、防花粉、防水织物整理方法，其特征是先对织物进行防紫外、抗静电整理，后防水、防花粉整理。
2.如权利要求1所述的防紫外、抗静电整理方法，其特征是用防紫外剂和抗静电剂的混合溶液对织物一浸一轧整理后烘干处理，使织物具有防紫外和抗静电功能。
3.如权利要求1所述的防水、防花粉整理方法，其特征是以防水剂和防花粉剂的混合溶液对织物进行一浸一轧整理后烘干处理，使织物具有防水、防花粉功能。
4.如权利要求1所述防紫外、抗静电功能织物整理方法，其特征是防紫外剂用量是10～60g/L，抗静电剂用量是10～40g/L。
5.如权利要求1所述防水、防花粉功能织物整理方法，其特征是防水剂用量是10～40g/L，防花粉剂用量是40～80g/L。
6.如权利要求1所述防紫外、抗静电、防花粉、防水整理方法用于涤纶、锦纶、涤锦的用途。