CN101220443B - 舰用不锈钢无缝钢管及其生产工艺 - Google Patents

舰用不锈钢无缝钢管及其生产工艺 Download PDF

Info

Publication number
CN101220443B
CN101220443B CN2008100187347A CN200810018734A CN101220443B CN 101220443 B CN101220443 B CN 101220443B CN 2008100187347 A CN2008100187347 A CN 2008100187347A CN 200810018734 A CN200810018734 A CN 200810018734A CN 101220443 B CN101220443 B CN 101220443B
Authority
CN
China
Prior art keywords
stainless steel
steel
pickling
pipe
ship
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008100187347A
Other languages
English (en)
Other versions
CN101220443A (zh
Inventor
黄志斌
俞晓东
陆翠玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU CHANGYING STAINLESS STEEL CO Ltd
Original Assignee
JIANGSU CHANGYING STAINLESS STEEL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU CHANGYING STAINLESS STEEL CO Ltd filed Critical JIANGSU CHANGYING STAINLESS STEEL CO Ltd
Priority to CN2008100187347A priority Critical patent/CN101220443B/zh
Publication of CN101220443A publication Critical patent/CN101220443A/zh
Application granted granted Critical
Publication of CN101220443B publication Critical patent/CN101220443B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及冶金行业中的不锈钢无缝钢管及其生产工艺，钢管采用00Cr24Ni6Mo2N双相不锈钢制成，制备以上所述的舰用不锈钢无缝钢管的生产工艺，具有如下生产步骤：a、圆钢准备；b、加热；c、热轧穿孔；d、切头；e、酸洗；f、修磨；g、润滑；h、冷轧加工；i、脱脂；j、固溶热处理；k、矫直；l、切管；m、酸洗；n、成品检验。本发明解决了舰船海水管道中现使用的316L不锈钢钢管存在的钢管机械强度和延伸性能较低，使用寿命较短，价格昂贵等问题，提供一种新的舰用双相不锈钢无缝钢管及其生产工艺，钢管不会产生点蚀和晶界腐蚀，机械强度和延伸性能较高，使得使用寿命长，同时价格低廉，降低了成本。

Description

舰用不锈钢无缝钢管及其生产工艺
技术领域
本发明涉及冶金行业中的不锈钢无缝钢管及其生产工艺，主要应用于舰船海水管道。
背景技术
不锈钢无缝钢管是常见的冶金金属制品，目前市场上应用于舰船海水管道主要采用双相不锈钢无缝钢管，因其特殊的环境要求，现使用的双相不锈钢无缝钢管具有较好的耐腐蚀性、耐点蚀性和抗应力性能，最常用的材质为316L，也就是00Cr17Ni14Mo2，这种材质的钢管虽能基本符合舰船海水管道的基本要求，但是总的来说各方面性能并不是很理想，特别是容易产生点蚀和晶界腐蚀，直接导致钢管机械强度和延伸性能的降低，使得钢管使用寿命比较短，而且其价格昂贵，并不是理想的材质。
发明内容
本发明要解决的技术问题是：解决舰船海水管道中现使用的316L不锈钢钢管存在的一系列问题，包括容易产生点蚀和晶界腐蚀，钢管机械强度和延伸性能较低，使用寿命较短，价格昂贵等问题，提供一种新的舰用双相不锈钢无缝钢管及其生产工艺，使得钢管不会产生点蚀和晶界腐蚀，机械强度和延伸性能较高，使得使用寿命长，同时价格低廉，降低了成本。
本发明解决其技术问题所采用的技术方案是：一种舰用不锈钢无缝钢管，钢管采用00Cr24Ni6Mo2N双相不锈钢制成。
制备以上所述的舰用不锈钢无缝钢管的生产工艺，具有如下生产步骤：a、圆钢准备；b、加热；c、热轧穿孔；d、切头；e、酸洗；f、修磨；g、润滑；h、冷轧加工；i、脱脂；j、固溶热处理；k、矫直；l、切管；m、酸洗；n、成品检验。
采用00Cr24Ni6Mo2N双相不锈钢为材料制备钢管，在所述步骤a中，圆钢中各组分质量比为：C≤0.03％、Mn≤2.0％、S≤0.03％、P≤0.035％、Si≤1.0％、Ni：4.5％～7.5％、Cr：23％～26％、Mo：2.0％～3.0％、N≤0.2％、Fe：60.205％～70.5％。
为了给不锈钢钢管加热到所需要的温度，以利于后续的加工，所述的步骤b中，把圆钢放入电弧炉里进行加热。
为了在酸洗过程中能有效的缩短生产周期和生产成本，采用配比浓度为HF∶HNO3∶H2O＝1∶1∶10的酸液在温度为60℃～80℃时进行酸洗5～6小时，不但保证了不锈钢管坯的洁净度，同时对砷、锡、铅、锑等微量有害元素也做了很好的处理。
为了使得所述的步骤j中固溶热处理能充分、有效的改善钢管的塑性，采用煤气发生炉对钢管进行固溶热处理，温度为1130℃～1180℃，使得酸洗时间只需6小时，有效的节省了时间，降低了成本。同时对于成品钢管来说，此最后一道工序应保证钢管的硬度、工艺性能、机械性能在顾客及标准所规定的范围内，在热处理时须根据管壁的大小调试加热温度及保温时间，一般温度宜控制在1050℃～1090℃，采用冷水急速冷却的热处理方式，保证了成品的质量。
以下是00Cr24Ni6Mo2N双相不锈钢与现在使用的316L不锈钢各方面性能的对比：
1、化学成分
Figure 2008100187347A00800031
2、机械性能
Figure 2008100187347A00800032
3、耐点蚀性能
Figure 2008100187347A00800033
由以上各性能对比可以看出，00Cr24Ni6Mo2N不锈钢材料与316L不锈钢材料因含P、Ni、Cr和Fe含量不同而性能不同，00Cr24Ni6Mo2N不锈钢的机械性能明显高于316L不锈钢，抗应力腐蚀性能强，耐磨、耐压性好，可以承受海水在7m/s以上的流速，还能很好的抵抗强烈的砂体侵蚀，管壁表面会形成稳定的钝化膜，即使遭到破坏，也会自行修复；对于耐点蚀性能，由表3可知，00Cr24Ni6Mo2N具有很好的耐氯离子腐蚀性能，试验阶段未出现点蚀状，可见比316L不锈钢耐腐蚀性能好很多。另外，对两种不锈钢材料同时做试验表明，00Cr24Ni6Mo2N不锈钢不会产生晶界腐蚀，也避免了因晶界腐蚀导致的钢管机械性能的降低，延长了钢管的使用寿命，具有良好的综合加工能力。
本发明的有益效果是：以上可知，由00Cr24Ni6Mo2N不锈钢材料制成的无缝钢管具有耐应力腐蚀和耐氯离子腐蚀的性能，有较高的机械强度和延伸性能，也不会产生点蚀和晶界腐蚀，使得钢管使用寿命延长，同时价格低廉，降低了成本，具有很好的市场前景。
具体实施方式
以下以具体实施方式为例做进一步说明：
一种舰用不锈钢无缝钢管采用00Cr24Ni6Mo2N双相不锈钢制成，具体生产步骤如下：a、圆钢准备，圆钢中各组分质量比为：C≤0.03、Mn≤2.0、S≤0.03、  P≤0.035、Si≤1.0、Ni：4.5～7.5、Cr：23～26、Mo：2.0～3.0、N≤0.2、Fe：60.205～70.5；b、把圆钢放入电弧炉里进行加热；c、热轧穿孔；d、切头；e、采用配比浓度为HF∶HNO3∶H2O＝1∶1∶10的酸液在温度为60℃～80℃时对钢管进行酸洗5～6小时；f、修磨；g、润滑；h、冷轧加工；i、脱脂；j、采用煤气发生炉对钢管进行固溶热处理，温度为1130℃～1180℃；k、矫直；l、切管；m、采用配比浓度为HF∶HNO3∶H2O＝1∶1∶10的酸液在温度为60℃～80℃时对钢管进行酸洗5～6小时；n、成品检验。

Claims (1)

1.一种舰用不锈钢无缝钢管的生产工艺，所述的钢管采用O0Cr24Ni6Mo2N双相不锈钢制成，其特征是具有如下生产步骤：
a、圆钢准备：圆钢中各组分质量比为：C≤0.03％、Mn≤2.0％、S≤0.03％、P≤0.035％、Si≤1.0％、Ni：4.5％～7.5％、Cr：23％～26％、Mo：2.0％～3.0％、N≤0.2％、Fe：60.205％～70.5％；
b、加热：把圆钢放入电弧炉里进行加热；
c、热轧穿孔；
d、切头；
e、酸洗：采用配比浓度为HF∶HNO3∶H2O＝1∶1∶10的酸液在温度为60℃～80℃时进行酸洗5～6小时；
f、修磨；
g、润滑；
h、冷轧加工；
i、脱脂；
j、固溶热处理：采用煤气发生炉对钢管进行固溶热处理，温度为1130℃～1180℃；
k、矫直；
l、切管；
m、酸洗：采用配比浓度为HF∶HNO3∶H2O＝1∶1∶10的酸液在温度为60℃～80℃时进行酸洗5～6小时；
n、成品检验。
CN2008100187347A 2008-01-22 2008-01-22 舰用不锈钢无缝钢管及其生产工艺 Expired - Fee Related CN101220443B (zh)