CN101205435A - 太阳热反射隔热涂料及其制备方法 - Google Patents

太阳热反射隔热涂料及其制备方法 Download PDF

Info

Publication number
CN101205435A
CN101205435A CNA2006101553036A CN200610155303A CN101205435A CN 101205435 A CN101205435 A CN 101205435A CN A2006101553036 A CNA2006101553036 A CN A2006101553036A CN 200610155303 A CN200610155303 A CN 200610155303A CN 101205435 A CN101205435 A CN 101205435A
Authority
CN
China
Prior art keywords
preparation
priming paint
solvent
investment precoat
solar heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006101553036A
Other languages
English (en)
Inventor
唐小菊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2006101553036A priority Critical patent/CN101205435A/zh
Publication of CN101205435A publication Critical patent/CN101205435A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种太阳热反射隔热涂料及其制备方法，以通过辐射的形式，把建筑物吸收的日照光线和热量以一定的波长反射到空气中，从而达到良好隔热降温效果的涂料。其由面层涂料和底层涂料按1∶1.5比例混合而成。本发明对太阳的热辐射有高反射率，导热系数低，保温良好，耐候性好，不易变色、不龟裂，且应用范围广。

Description

太阳热反射隔热涂料及其制备方法
技术领域
本发明涉及一种涂料及其制备方法，更具体地说，涉及一种太阳热反射隔热涂料及其制备方法。
背景技术
热传递是通过对流、辐射及分子振动热传导三种途径来实现的。对于涂料而言，热传导主要由涂料中的固体部分来完成，热对流则主要由涂料中的空气来完成，热辐射的传递不需要任何介质。因此，要获得良好的隔热保温效果，一是要在保持足够机械强度的同时，材料的体积密度要极端的小；二是要将空气的对流减弱到极限；三是要通过近于无穷多的界面和通过材料的改性使热辐射经反射、散射和吸收而降到最低。
发明内容
本发明的目的是提供一种太阳热反射隔热涂料，以通过辐射的形式，把建筑物吸收的日照光线和热量以一定的波长反射到空气中，从而达到良好隔热降温效果的涂料。
本发明的另一目的是提供这种涂料的制备方法，以有效地提高本涂料的高热发射率。
本发明的这种太阳热反射隔热涂料，由面层涂料和底层涂料按1∶1.5比例混合而成，其各组分百分比构成如下：
面层涂料：
热塑性丙烯酸树脂  20％～30％
金红石型钛白粉    15％～20％
醋酸丁酯          25％～35％
200号溶剂油       25％～35％
白炭黑            2％～3％
邻苯二甲酸二辛酯  2％～5％
底层涂料：
高氯化聚乙烯      15％～25％
硅酸铝短纤维      20％～35％
钛白粉            3％～5％
醋酸丁酯          25％～35％
200号溶剂油         25％～35％
邻苯二甲酸二辛酯    2％～5％
本发明的制备方法包括由以下步骤组成：
1、面层涂料制备：按配方比例称取各配料配用，用溶剂将热塑性丙烯酸树脂溶解，然后加入其他配料，用球磨机球磨6h～7h，以刮板细度计检验浆体细度(以小于100um为合格)后，配色，包装；
2、底层涂料制备：按配方比例称取各配料配用，用溶剂将高氯化聚乙烯溶解，然后加入其他配料，用球磨机球磨6h～7h，配色，包装。
3、将面层涂料和底层涂料按1∶1.5比例使用即成。
本发明对太阳的热辐射有高反射率，导热系数低，保温良好，耐候性好，不易变色、不龟裂，且应用范围广。
具体实施方式
下面通过实施例进一步说明本发明。
实施例1，
本发明太阳热反射隔热涂料，由面层涂料和底层涂料按1∶1.5比例混合而成，面层涂料各成分质量份配比为：面层涂料，热塑性丙烯酸树脂20kg，金红石型钛白粉15kg，醋酸丁酯30kg，200号溶剂油30kg，白炭黑3kg，邻苯二甲酸二辛酯2kg；底层涂料，高氯化聚乙烯18kg，硅酸铝短纤维20kg，钛白粉5kg，醋酸丁酯30kg，200号溶剂油30kg，邻苯二甲酸二辛酯2kg。
面层涂料中热塑性丙烯酸树脂为成膜树脂，金红石型钛白粉为颜料，醋酸丁酯和200号溶剂油为溶剂，白炭黑为增稠剂，邻苯二甲酸二辛酯为增塑剂。
底层涂料中高氯化聚乙烯为成膜树脂，小于75um的硅酸盐纤维为填料，钛白粉为颜料，邻苯二甲酸二辛酯为增塑剂，醋酸丁酯和200号溶剂油为溶剂。
本发明除了用于建筑物外墙，还可用于汽车内表面空调器表面、金属储罐外表面、彩钢瓦等。
实施例2，
本发明太阳热反射隔热涂料，由面层涂料和底层涂料按1∶1.5比例混合而成，面层涂料各成分质量份配比为：面层涂料，热塑性丙烯酸树脂35kg，金红石型钛白粉5kg，醋酸丁酯28kg，200号溶剂油30kg，白炭黑1kg，邻苯二甲酸二辛酯2kg；底层涂料，高氯化聚乙烯20kg，硅酸铝短纤维20kg，钛白粉4kg，醋酸丁酯29kg，200号溶剂油30kg，邻苯二甲酸二辛酯2kg。
面层涂料中热塑性丙烯酸树脂为成膜树脂，金红石型钛白粉为颜料，醋酸丁酯和200号溶剂油为溶剂，白炭黑为增稠剂，邻苯二甲酸二辛酯为增塑剂。
底层涂料中高氯化聚乙烯为成膜树脂，小于75um的硅酸盐纤维为填料，钛白粉为颜料，邻苯二甲酸二辛酯为增塑剂，醋酸丁酯和200号溶剂油为溶剂。
本发明除了用于建筑物外墙，还可用于汽车内表面空调器表面、金属储罐外表面、彩钢瓦等。
实施例3，
本发明太阳热反射隔热涂料的制备方法包括由以下步骤组成：
1、面层涂料制备：按配方比例称取各配料配用，用溶剂将热塑性丙烯酸树脂溶解，然后加入其他配料，用球磨机球磨6h～7h，以刮板细度计检验浆体细度(以小于100um为合格)后，配色，包装；
2、底层涂料制备：按配方比例称取各配料配用，用溶剂将高氯化聚乙烯溶解，然后加入其他配料，用球磨机球磨6h～7h，配色，包装。
3、将面层涂料和底层涂料按1∶1.5比例使用即成。
本发明对太阳的热辐射有高反射率，导热系数低，保温良好，耐候性好，不易变色、不龟裂，且应用范围广。

Claims (2)

1.一种太阳热反射隔热涂料，其由面层涂料和底层涂料按1∶1.5比例混合而成，各组分百分比构成如下：
面层涂料：
热塑性丙烯酸树脂    20％～30％
金红石型钛白粉      15％～20％
醋酸丁酯            25％～35％
200号溶剂油         25％～35％
白炭黑              2％～3％
邻苯二甲酸二辛酯    2％～5％
底层涂料：
高氯化聚乙烯        15％～25％
硅酸铝短纤维        20％～35％
钛白粉              3％～5％
醋酸丁酯            25％～35％
200号溶剂油         25％～35％
邻苯二甲酸二辛酯    2％～5％。
2.根据权利要求1所述的太阳热反射隔热涂料的制备方法包括由以下步骤组成：
a、面层涂料制备：按配方比例称取各配料配用，用溶剂将热塑性丙烯酸树脂溶解，然后加入其他配料，用球磨机球磨6h～7h，以刮板细度计检验浆体细度后，配色，包装；
b、底层涂料制备：按配方比例称取各配料配用，用溶剂将高氯化聚乙烯溶解，然后加入其他配料，用球磨机球磨6h～7h，配色，包装；
c、将面层涂料和底层涂料按1∶1.5比例使用即成。
CNA2006101553036A 2006-12-19 2006-12-19 太阳热反射隔热涂料及其制备方法 Pending CN101205435A (zh)