CN103756444A - 一种高导热散热型粉末涂料 - Google Patents

一种高导热散热型粉末涂料 Download PDF

Info

Publication number
CN103756444A
CN103756444A CN201410018131.2A CN201410018131A CN103756444A CN 103756444 A CN103756444 A CN 103756444A CN 201410018131 A CN201410018131 A CN 201410018131A CN 103756444 A CN103756444 A CN 103756444A
Authority
CN
China
Prior art keywords
parts
powder coating
raw material
powder
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410018131.2A
Other languages
English (en)
Inventor
张庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Baoyi Amusement Equipment Co Ltd
Original Assignee
Wuhu Baoyi Amusement Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Baoyi Amusement Equipment Co Ltd filed Critical Wuhu Baoyi Amusement Equipment Co Ltd
Priority to CN201410018131.2A priority Critical patent/CN103756444A/zh
Publication of CN103756444A publication Critical patent/CN103756444A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高导热散热型粉末涂料，它是由下述重量份的原料组成的：氯化聚乙烯86-90、聚乙烯蜡7-8、不锈钢粉1-2、丙二醇甲醚醋酸酯2-4、4,4’-二甲氧基二苯胺1-2、四氯间苯二甲腈0.1-0.2、铝酸钙3-5、棕油1-2、丙烯醇4-6、高岭土粉末7-10、N-乙基-邻对甲苯磺酰胺1-2、竹纤维2-4、改性填料10-13；本发明的粉末涂料可以直接涂覆或喷涂在散热器的表面，可以加速散发电子元器件产生的热量、降低电子元器件的运行温度、提高电子元器件的使用寿命。

Description

一种高导热散热型粉末涂料
技术领域
    本发明主要涉及一种粉末涂料，尤其涉及一种高导热散热型粉末涂料。
背景技术
导热散热涂料被广泛的应用于电脑、笔记本电脑、LED 照明、通信、整流器，医疗及工业设备等有散热要求的领域，主要涂覆在散热器的表面。
目前生产的散热涂料一般多应用于CPU 等电子产品的元器件的散热及LED 灯具散热，对于涂刷的介质要求较高，对于较粗糙、疏松的物体表面附着力不强，使用效果不理想，适用范围较小。
发明内容
本发明目的就是提供一种高导热散热型粉末涂料。
本发明是通过以下技术方案实现的：
一种高导热散热型粉末涂料，其特征在于它是由下述重量份的原料组成的：
氯化聚乙烯86-90、聚乙烯蜡7-8、不锈钢粉1-2、丙二醇甲醚醋酸酯2-4、4,4’-二甲氧基二苯胺1-2、四氯间苯二甲腈0.1-0.2、铝酸钙3-5、棕油1-2、丙烯醇4-6、高岭土粉末7-10、N-乙基-邻对甲苯磺酰胺1-2、竹纤维2-4、改性填料10-13；
所述的改性填料是由下述重量份的原料组成的：
黄土20-24、碱式硫酸镁晶须6-8、三水铝石5-7、甲苯二异氰酸酯交联改性聚乙烯醇胶2-4、六方氮化硼2-3、松焦油1-2；
将上述黄土在600-700℃下煅烧1-2小时，冷却至室温，与六方氮化硼混合研磨成粉；将上述碱式硫酸镁晶须与三水铝石混合，在120-160℃下加热搅拌3-4分钟，降低温度至60-70℃，加入甲苯二异氰酸酯交联改性聚乙烯醇胶，200-300转/分搅拌10-20分钟；将上述处理后的各原料与剩余各原料混合，充分球磨，即得所述改性填料。
一种高导热散热型粉末涂料的制备方法，包括以下步骤：
将上述聚乙烯蜡与高岭土粉末混合，搅拌均匀后加入铝酸钙，60-80℃下保温搅拌10-14分钟，加入剩余各原料，充分混合，送入双螺杆挤出机，进行熔融、挤出和造粒，磨成细粉并过120-160目筛，即得所述高导热散热型粉末涂料。
本发明的优点是：
    本发明的粉末涂料可以直接涂覆或喷涂在散热器的表面，可以加速散发电子元器件产生的热量、降低电子元器件的运行温度、提高电子元器件的使用寿命。
具体实施方式
实施例1
一种高导热散热型粉末涂料，其特征在于它是由下述重量份（公斤）的原料组成的：
氯化聚乙烯90、聚乙烯蜡7、不锈钢粉1-2、丙二醇甲醚醋酸酯4、4,4’-二甲氧基二苯胺2、四氯间苯二甲腈0.2、铝酸钙3、棕油1、丙烯醇6、高岭土粉末7、N-乙基-邻对甲苯磺酰胺2、竹纤维4、改性填料13；
所述的改性填料是由下述重量份的原料组成的：
黄土24、碱式硫酸镁晶须8、三水铝石7、甲苯二异氰酸酯交联改性聚乙烯醇胶2、六方氮化硼2、松焦油2；
将上述黄土在700℃下煅烧1小时，冷却至室温，与六方氮化硼混合研磨成粉；将上述碱式硫酸镁晶须与三水铝石混合，在160℃下加热搅拌4分钟，降低温度至70℃，加入甲苯二异氰酸酯交联改性聚乙烯醇胶，300转/分搅拌20分钟；将上述处理后的各原料与剩余各原料混合，充分球磨，即得所述改性填料。
一种高导热散热型粉末涂料的制备方法，包括以下步骤：
将上述聚乙烯蜡与高岭土粉末混合，搅拌均匀后加入铝酸钙，80℃下保温搅拌14分钟，加入剩余各原料，充分混合，送入双螺杆挤出机，进行熔融、挤出和造粒，磨成细粉并过160目筛，即得所述高导热散热型粉末涂料。
性能测试：
耐溶剂：240小时，无变化；
盐雾试验（1000h）：无变化。

Claims (2)

1.一种高导热散热型粉末涂料，其特征在于它是由下述重量份的原料组成的：
氯化聚乙烯86-90、聚乙烯蜡7-8、不锈钢粉1-2、丙二醇甲醚醋酸酯2-4、4,4’-二甲氧基二苯胺1-2、四氯间苯二甲腈0.1-0.2、铝酸钙3-5、棕油1-2、丙烯醇4-6、高岭土粉末7-10、N-乙基-邻对甲苯磺酰胺1-2、竹纤维2-4、改性填料10-13；
所述的改性填料是由下述重量份的原料组成的：
黄土20-24、碱式硫酸镁晶须6-8、三水铝石5-7、甲苯二异氰酸酯交联改性聚乙烯醇胶2-4、六方氮化硼2-3、松焦油1-2；
将上述黄土在600-700℃下煅烧1-2小时，冷却至室温，与六方氮化硼混合研磨成粉；将上述碱式硫酸镁晶须与三水铝石混合，在120-160℃下加热搅拌3-4分钟，降低温度至60-70℃，加入甲苯二异氰酸酯交联改性聚乙烯醇胶，200-300转/分搅拌10-20分钟；将上述处理后的各原料与剩余各原料混合，充分球磨，即得所述改性填料。
2.一种如权利要求1所述的高导热散热型粉末涂料的制备方法，其特征在于包括以下步骤：
将上述聚乙烯蜡与高岭土粉末混合，搅拌均匀后加入铝酸钙，60-80℃下保温搅拌10-14分钟，加入剩余各原料，充分混合，送入双螺杆挤出机，进行熔融、挤出和造粒，磨成细粉并过120-160目筛，即得所述高导热散热型粉末涂料。
CN201410018131.2A 2014-01-15 2014-01-15 一种高导热散热型粉末涂料 Pending CN103756444A (zh)