CN101191005A - 一种阻燃抗紫外型abs组合物 - Google Patents
一种阻燃抗紫外型abs组合物 Download PDFInfo
- Publication number
- CN101191005A CN101191005A CNA2006101185636A CN200610118563A CN101191005A CN 101191005 A CN101191005 A CN 101191005A CN A2006101185636 A CNA2006101185636 A CN A2006101185636A CN 200610118563 A CN200610118563 A CN 200610118563A CN 101191005 A CN101191005 A CN 101191005A
- Authority
- CN
- China
- Prior art keywords
- abs
- weight parts
- retardant
- flame retardant
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种阻燃抗紫外型ABS组合物，其组成及成分为：ABS树脂700～740重量份、主阻燃剂170重量份、辅助阻燃剂30～40重量份、增韧剂30～40重量份、光吸收剂3～5重量份、受阻胺类光稳定剂3～5重量份、光屏蔽剂10～20重量份、抗氧剂4～6重量份；其中，所述的光稳定剂为分子量大于2000的受阻胺类光稳定剂；这种阻燃抗紫外ABS组合物，由于不仅具有良好的抗紫外性、并且具备良好的加工性以及阻燃性，所以可作为各种电器的外壳和汽车的外饰件。
Description
技术领域
本发明属于阻燃产品的技术领域，具体的说，本发明涉及一种阻燃抗紫外ABS工程塑料。
背景技术
ABS塑料具有良好的耐热性，高抗冲性和优良的加工性，广泛用于汽车零部件、家用电器和电子元器件。用于家用电器和办公自动化设备外壳的材料有阻燃的要求，通常添加卤素化合物以提供阻燃性。卤系阻燃剂的成本性能平衡好，适应面广，但卤系阻燃剂本身不耐光，它的加入大大恶化了材料的抗紫外性能；ABS本身由于有双键存在，抗紫外性能也不太好；而阻燃ABS大量作为外饰件使用必须抗紫外。
溴化环氧树脂是一种优良的含溴阻燃剂，阻燃效率高，与材料的相容性好，阻燃材料的抗紫外性好。高分子量的溴化环氧树脂具有很高的耐热性，可用于阻燃各种工程塑料。
含卤阻燃的ABS塑料的抗紫外是世界性的难题，过去主要是添加钛白粉和苯并三唑类光吸收剂来提高材料的抗紫外性，这时材料的抗紫外不能达到很高的级别；受阻胺类光稳定剂由于自身的碱性会与含卤阻燃剂发生反应导致色变和材料降解因而很少在ABS中使用。
金红石型钛白粉可以作为光屏蔽剂起到抗紫外作用，但一般的金红石型钛白粉抗紫外效果不太好，经过特殊处理可以大大提高钛白粉的耐光性。
发明内容
本发明的目的旨在提供一种具有优异抗紫外性的含卤阻燃ABS组合物。
本发明的发明目的可以通过以下技术方案实现：
这种阻燃抗紫外型ABS组合物，包括：ABS树脂700～740重量份、主阻燃剂170重量份、辅助阻燃剂30～40重量份、增韧剂30～40重量份、光吸收剂3～5重量份、光稳定剂3～5重量份、光屏蔽剂10～20重量份、抗氧剂4～6重量份；其中，所述的光稳定剂为分子量大于2000的的受阻胺类光稳定剂。
所用的ABS树脂为胶含量12-16％的高抗冲ABS
所用的主阻燃剂为分子量1000～10000的羟基封端和三溴苯酚封端的溴化环氧树脂。
所用的光吸收剂为苯并三唑类光吸收剂。
所用的光屏蔽剂为处理的金红石型钛白粉。
所述的抗氧剂为受阻酚类主抗氧剂和亚磷酸酯类辅助抗氧剂。
根据以上技术方案提出的阻燃抗紫外ABS组合物，由于不仅具有良好的抗紫外性、并且具备良好的加工性以及阻燃性，所以可作为各种电器的外壳和汽车的外饰件。
具体实施方式
下面实施例进一步描述本发明，但所述实施例仅用于说明本发明而不是限制本发明。
ABS树脂和各种添加剂经高混机高速混匀后，经双螺杆挤出机进行熔融挤出，再经过冷却造粒就可得该组合物，工艺温度为200-210℃。
采用下列物料：
ABS 台湾其美公司生产，牌号747
溴化环氧树脂 环氧封端 以色列死海溴 牌号2016
溴化环氧树脂 三溴苯酚封端 以色列死海溴 牌号3516
超细三氧化二锑 上海涵丰化工
丙烯酸酯橡胶 美国Dupont HP4051
金红石型钛白粉 美国KMG公司生产 牌号CR-834
苯并三唑类光稳定剂 Ciba生产 牌号328
苯并三唑类光稳定剂 Ciba生产 牌号327
受阻胺类光稳定剂 Ciba生产 牌号119
受阻胺类光稳定剂 Basf生产 牌号5050H
抗氧剂245 瑞士Ciba生产的Irganox 245
抗氧剂168 瑞士Ciba生产的Irganox 168
冲击强度和缺口冲击强度按ASTM D256测试。
色差按ASTM D4459测试，条件如下
| 光照强度 | 0.3W/m2 |
| 光源 | Xenon arc |
| 温度 | 55±2℃. |
| 相对湿度 | 55±5％ |
| 光照时间 | 300hours |
根据美国UL94标准测试垂直燃烧性能。
以下给出本发明的实施例，并进一步阐述本发明。
实施例1～3的配方
| 对照例 | 实施例1 | 实施例2 | 实施例3 | ||
| 基础树脂 | ABS747 | 710 | 710 | 700 | 740 |
| 主阻燃剂 | 溴化环氧2016 | 170 | 170 | 170 | 170 |
| 辅助阻燃剂 | 三氧化二锑 | 60 | 60 | 60 | 40 |
| 增韧剂 | HP4051 | 40 | 40 | 40 | 30 |
| 光屏蔽剂 | CR826 | 10 | 20 | 10 | |
| CR834 | 10 | ||||
| 光吸收剂 | 327 | 3 | 3 | ||
| 328 | 3 | 5 | |||
| 光稳定剂 | 119 | 3 | |||
| 5050H | 3 | 5 | |||
| 770 | 3 | ||||
| 抗氧剂 | 168 | 3 | 2 | 3 | 3 |
| 抗氧剂 | 245 | 3 | 2 | 3 | 3 |
所得材料的测试结果如下：
| 性能 | 对比例 | 实施例1 | 实施例2 | 实施例3 |
| IZOD冲击 | NB | NB | NB | NB |
| 缺口冲击 | 12 | 10 | 10 | 10 |
| 阻燃1.6mm | V-0 | V-0 | V-0 | V-0 |
| 色差200h | 4.51 | 0.68 | 0.85 | 0.75 |
| 色差300h | 6.82 | 0.72 | 1.02 | 0.85 |
实施例4～6的配方
| 对照例 | 实施例1 | 实施例2 | 实施例3 | ||
| 基础树脂 | ABS747 | 710 | 710 | 700 | 740 |
| 主阻燃剂 | 溴化环氧3516 | 170 | 170 | 170 | 170 |
| 辅助阻燃剂 | 三氧化二锑 | 60 | 60 | 60 | 40 |
| 增韧剂 | HP4051 | 40 | 40 | 40 | 30 |
| 光屏蔽剂 | CR826 | 10 | 20 | 10 | |
| CR834 | 10 | ||||
| 光吸收剂 | 327 | 3 | 3 | ||
| 328 | 3 | 5 | |||
| 光稳定剂 | 119 | 3 | |||
| 5050H | 3 | 5 | |||
| 770 | 3 | ||||
| 抗氧剂 | 168 | 3 | 2 | 3 | 3 |
| 抗氧剂 | 245 | 3 | 2 | 3 | 3 |
材料的测试结果如下：
| 性能 | 对比例 | 实施例1 | 实施例2 | 实施例3 |
| IZOD冲击 | NB | NB | NB | NB |
| 缺口冲击 | 16 | 15 | 16 | 16 |
| 阻燃1.6mm | V-0 | V-0 | V-0 | V-0 |
| 色差200h | 5.53 | 1.62 | 1.15 | 1.04 |
| 色差300h | 8.87 | 2.02 | 1.50 | 1.24 |
由上面的结果可知两种不同的阻燃体系都有良好的抗紫外性，2016的耐光性更好，但冲击差一些；3516冲击好些，性能比较均衡，说明特殊的低碱性的高分子受阻胺类与抗氧剂配合可以加入含卤阻燃的ABS合金中，能起到很好的抗紫外作用。
Claims (6)
1.这种阻燃抗紫外型ABS组合物，包括：ABS树脂700～740重量份、主阻燃剂170重量份、辅助阻燃剂30～40重量份、增韧剂30～40重量份、光吸收剂3～5重量份、光稳定剂3～5重量份、光屏蔽剂10～20重量份、抗氧剂4～6重量份；其中，所述的光稳定剂为分子量大于2000的的受阻胺类光稳定剂。
2.如权利要求1所述的一种阻燃抗紫外ABS组合物，其特征在于：所述的ABS树脂为胶含量12～16％的高抗冲ABS。
3.如权利要求1所述的一种阻燃抗紫外ABS组合物，其特征在于：所述的主阻燃剂为分子量1000～10000的羟基封端和三溴苯酚封端的溴化环氧树脂。
4.如权利要求1所述的一种阻燃抗紫外ABS组合物，其特征在于：所述的光吸收剂为苯并三唑类。
5.如权利要求1所述的一种阻燃抗紫外ABS组合物，其特征在于：所述的光屏蔽剂为经过处理的金红石型钛白粉。
6.如权利要求1所述的一种阻燃抗紫外ABS组合物，其特征在于：所述的抗氧剂为受阻酚类主抗氧剂和亚磷酸酯类辅助抗氧剂。