CN101190971B - 片状模塑料及其应用 - Google Patents
片状模塑料及其应用 Download PDFInfo
- Publication number
- CN101190971B CN101190971B CN2007101906028A CN200710190602A CN101190971B CN 101190971 B CN101190971 B CN 101190971B CN 2007101906028 A CN2007101906028 A CN 2007101906028A CN 200710190602 A CN200710190602 A CN 200710190602A CN 101190971 B CN101190971 B CN 101190971B
- Authority
- CN
- China
- Prior art keywords
- portions
- parts
- sheet molding
- molding compound
- environmental protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种片状模塑料，其组份按质量份数，不饱和聚酯树脂20～60份，低收缩添加剂6份～15份，5mm～12mm的长玻璃纤维8～20份，直径为2μm～20μm且长度为3mm～10mm的不锈钢纤维6～20份，石墨粉10～40份，有机硅0～3份，2∶1混合的1250目和500目的碳酸钙20～60份，氢氧化铝20～45份，有机过氧化物0.2～1份，增稠剂0.3～1.2份以及脱模剂1～4份。本发明具有机械强度高，尺寸精度好，环保阻燃并具有导电性能，可应用于电磁屏蔽的电子电器设备部件或环保阻燃、且有抗静电的煤矿用设备部件。
Description
技术领域
本发明涉及一种片状模塑料及其应用，属于纤维增强模塑料技术领域。
技术背景
片状模塑料(SMC)是以不饱和聚酯树脂、增稠剂、引发剂、交联剂、低收缩添加剂、填料、内脱模剂和着色剂等原料混合成树脂糊，浸渍短切纤维粗纱或玻璃纤维毡，并在两面用聚乙烯或聚丙烯薄膜包覆起来制成的片状模压材料。片状模塑料作为一种发展迅速的新型模压料，具有许多特点：①、流动性好可成型各种复杂制件；②、模压工艺对温度和压力要求不高，适用范围广，生产效率高，能大幅度降低生产成本；③、具有优越的耐腐蚀性能；④、机械性能可以与部分金属材料相媲美；⑤、能具备绝缘性能及阻燃性能；⑥、质轻、工程设计容易等。由于这些特点使片状模塑料广泛应用于运输车辆、建筑、电子电气行业中。随着片状模塑料应用范围的不断扩大，对其应用范围的探索也就越来越多。由于它只具有阻燃和绝缘的作用，而没有导电及抗静电的作用，导致其不能用于需要具备电磁屏蔽的电子电器设备部件和具备环保阻燃要求且有抗静电要求的煤矿用设备部件。
发明内容
本发明的目的是提供一种具有机械强度高，尺寸精度好，环保阻燃并具有导电性能的片状模塑料及用途。
本发明为达到上述目的的技术方案是：一种片状模塑料，其组份按质量份数：不饱和聚酯树脂20～60份，低收缩添加剂6～15份，5mm～12mm的长玻璃纤维8～20份，直径为2μm～20μm长度为3mm～10mm的不锈钢纤维6～20份，石墨粉10～40份，有机硅0～3份，2∶1混合的1250目和500目的碳酸钙20～60份，氢氧化铝20～45份，有机过氧化物0.2～1份，增稠剂0.3～1.2份以及脱膜剂1～4份。
本发明的片状模塑料应用于需要具备电磁屏蔽的电子电气设备部件或具有环保阻燃抗静电要求的煤矿用设备部件。
本发明在片状模塑料的配方体系中，采用了不饱和聚酯树脂、低收缩添加剂、玻璃纤维及有机过氧化物、增稠剂、脱膜剂等，不仅保持原片状模塑料所具有的耐高温、耐老化、耐腐蚀、机械强度高、尺寸精度好等优点。且在配方体系中加入了不锈钢纤维和石墨粉，不锈钢纤维定向分布在片状材料中，具有极好的流动性和成型表面，不仅能进一步提高片状模塑料制品的机械强度和耐高温性能，而且在不锈钢和石墨粉的作用下，具有导电性能。本发明采用2∶1混合的1250目和500目的碳酸钙，通过不同粒径大小碳酸钙的混合来提高片状模塑料制品的填充性能，从而提高制品的密实度和表面质量。本发明采用氢氧化铝，着火时通过结晶水被炽热而释放出水蒸汽，来阻隔火焰而起到环保阻燃作用，再增加有机硅使材料具有较好的阻燃性能，因此可用于制作具备电磁屏蔽的电子电器设备部件，或既需阻燃又需导电或抗静电的电子电器设备部件。
具体实施方式
下面结合实施例对本发明作进一步详细说明。
实施例1
本发明的片状模塑料，其组份按质量份数，不饱和聚酯树脂20～30份，低收缩添加剂6份～10份，5mm～8mm的长玻璃纤维8～15份，直径为2μm～10μm且长度为3mm～6mm的不锈钢纤维6～12份，石墨粉10～25份，2∶1混合的1250目和500目的碳酸钙40～60份，氢氧化铝35～55份，有机过氧化物0.2～0.5份，增稠剂0.3～0.6份，该增稠剂为氢氧化钙或氧化镁。以及脱模剂2～4份，脱模剂为硬脂酸钙或硬脂酸锌，经树脂糊制备、上糊操作、纤维切割沉降及浸渍、树脂稠化等工艺制成片状模塑料，用模压成型法制成不同的制品，制品可用于抗静电并需阻燃的电子电器设备部件或煤矿用设备部件，如煤矿用防护栏。
实施例2
本发明的片状模塑料，其组份按质量份数，不饱和聚酯树脂30～40份，低收缩添加剂9份～12份，6mm～10mm的长玻璃纤维10～18份，直径为5μm～10μm且长度为5mm～8mm的不锈钢纤维8～15份，石墨粉25～35份，有机硅0.5～1份，2∶1混合的1250目和500目的碳酸钙30～40份，氢氧化铝25～35份，有机过氧化物0.5～0.8份，增稠剂0.5～0.8份，该增稠剂为氢氧化钙或氧化镁，以及脱模剂2～3份，脱模剂为硬脂酸钙或硬脂酸锌，经树脂糊制备、上糊操作、纤维切割沉降及浸渍、树脂稠化等工艺制成片状模塑料，用模压成型制成不同的制品，制品可用于需防电磁渗透的电子电器设备部件，如仪表罩等。
实施例3
本发明的片状模塑料，其组份按质量份数，不饱和聚酯树脂40～60份，低收缩添加剂10～15份，8mm～12mm的长玻璃纤维12～20份，直径为10μm～20μm且长度为8mm～10mm的不锈钢纤维12～20份，石墨粉30～40份，有机硅1～3份，2∶1混合的1250目和500目的碳酸钙20～30份，氢氧化铝20～30份，有机过氧化物0.8～1份，增稠剂0.8～1.2份，该增稠剂为氢氧化钙或氧化镁，以及脱模剂1～3份，脱模剂为硬脂酸钙或硬脂酸锌，经树脂糊制备、上糊操作、纤维切割沉降及浸渍、树脂稠化等工艺制成片状模塑料，用模压成型制成不同的制品，制品可用于电磁场的屏蔽设备部件，如制备电磁屏蔽室的部件。
分别对上述各实施例的片状模塑料制品按GB标准进行检测，结果见表1
表1
| 检测项目 | 实施例1 | 实施例2 | 实施例3 |
| 冲击强度(KJ/m<sup>2</sup>) | ≥75 | ≥80 | ≥90 |
| 弯曲强度(Mpa) | ≥100 | ≥110 | ≥120 |
| 检测项目 | 实施例1 | 实施例2 | 实施例3 |
| 拉伸强度(Mpa) | ≥80 | ≥100 | ≥115 |
| 模塑收缩率(％) | ≤0.30 | ≤0.15 | ≤0.10 |
| 电阻率(Ω) | ≤450 | ≤320 | ≤200 |
| 氧指数(％) | 50 | 48 | 48 |
Claims (4)
1.一种片状模塑料，其特征在于：其组份按质量份数，不饱和聚酯树脂20～60份，低收缩添加剂6份～15份，5mm～12mm的长玻璃纤维8～20份，直径为2μm～20μm且长度为3mm～10mm的不锈钢纤维6～20份，石墨粉10～40份，有机硅0～3份，2∶1混合的1250目和500目的碳酸钙20～60份，氢氧化铝20～45份，有机过氧化物0.2～1份，增稠剂0.3～1.2份以及脱模剂1～4份。
2.根据权利要求1所述的片状模塑料，其特征在于：所述的脱模剂为硬脂酸钙或硬脂酸锌。
3.根据权利要求1所述的片状模塑料，其特征在于：所述的增稠剂为氢氧化钙或氧化镁。
4.根据权利要求1所述的片状模塑料在电磁屏蔽的电子电器设备部件或环保阻燃、且有抗静电的煤矿用设备部件的应用。