CN101177468B - Water-soluble crylic acid resin and preparation method thereof - Google Patents
Water-soluble crylic acid resin and preparation method thereof Download PDFInfo
- Publication number
- CN101177468B CN101177468B CN2007100321248A CN200710032124A CN101177468B CN 101177468 B CN101177468 B CN 101177468B CN 2007100321248 A CN2007100321248 A CN 2007100321248A CN 200710032124 A CN200710032124 A CN 200710032124A CN 101177468 B CN101177468 B CN 101177468B
- Authority
- CN
- China
- Prior art keywords
- water
- acrylic resin
- mercaptoethanol
- water soluble
- soluble acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a waterborne acrylic resin and the preparation method, which aims to provide a waterborne acrylic resin and the preparation method which can not only keep the performance of organic solvent type acrylic resins, but also have friendly environmental protection property. The invention comprises the following matters of mass portion: 1 to 2 of acrylic, 15 to 29 of methyl methacrylate, 18 to 22 of butyl acrylate, 3 to 7 of styrene, 3 to 7 of 2-hydroxyethyl methacrylate, 0.25 to 0.65 of mercaptoethanol, 0.3 to 0.7 of azobisisobutyronitrile, 3 to 5 of isopropanol, 15 to 20 of ethanol, 2.5 to 8.75 of monoethanolamine and 25 to 31.5 of water.
Description
Technical field
The present invention relates to printing ink with vinyl resin and preparation method thereof, be specifically related to a kind of water soluble acrylic resin and preparation method thereof.
Background technology
In the prior art; The resin that is used for the pearly-lustre low-melting ink vehicle is the butyrous nitro-resin; But it contains a large amount of organic solvents, can pollute environment, and is also very big to the injury of human body; And dangerous, so the friendly water soluble acrylic resin of development environment is the task of top priority that addresses the above problem.
Chinese patent CN20051022901 discloses the good coating of a kind of feature of environmental protection with vinyl resin and preparation method; It is characterized in that 40-80%wt Acrylic Acid Monomer and 20-60%wt organic solvent; 0.1-10%wt initiator free radical solution polymerization; Through removing organic solvent, obtain the water-soluble vinyl resin of solid content 20-60%wt, be dissolved in the single-phase homogeneous aqueous solution in the 40-80%wt water.The use properties that has kept solvent type resin; And than the environmental protection of solvent resin; But because it contains more a large amount of strongly hydrophilic carboxyls; Coating hardness is low after causing disposing the coating drying and forming-film, and smooth property, wear resistance and resistance to bond are poor, are difficult to satisfy the requirement of paper printing ink, oil polish and water-borne wood coating.
Summary of the invention
The objective of the invention is to overcome above-mentioned defective of the prior art, a kind of performance that can keep organic solvent-type acrylic resin is provided, the water soluble acrylic resin who has the environmental friendliness characteristic again.
Another object of the present invention is to provide a kind of water soluble acrylic resin's of preparation method.
Technical scheme of the present invention is following: a kind of water soluble acrylic resin is provided, comprises following material:
Vinylformic acid: 1-2 part
TEB 3K: 15-29 part
Bing Xisuandingzhi: 18-22 part
Vinylbenzene: 3-7 part
Rocryl 400: 3-7 part
Mercaptoethanol: 0.25-0.65 part
Diisopropyl azodicarboxylate: 0.3-0.7 part
Virahol: 3-5 part
Ethanol: 15-20 part
Monoethanolamine MEA BASF: 2.5-8.75 part
Water: 25-31.5 part
It more than is mass fraction.
A kind of water soluble acrylic resin's preparation method is provided, may further comprise the steps:
A, in header tank with vinylformic acid, TEB 3K, Bing Xisuandingzhi, vinylbenzene, Rocryl 400, mercaptoethanol, Diisopropyl azodicarboxylate mix, and stir;
B, in having the reaction kettle of reflux exchanger, drop into Virahol and ethanol, be warmed up to 80 ℃, splash into the mix monomer of step a gained; Drip off the back and held temperature 10 hours at 75～80 ℃; Cool to 50 ℃ then, add Monoethanolamine MEA BASF, be neutralized to PH=7.5～8.0 back thin ups; Be cooled to room temperature, filter and package at last.
Water soluble acrylic resin provided by the invention makees solvent with water and eco-friendly etoh solvent, and performance can reach the effect of oiliness pearly-lustre low-melting ink vehicle fully.Water soluble acrylic resin's coating replaces water with most of organic volatile solvent, thereby reaches the purpose that alleviates significantly topsoil under the prerequisite that guarantees the acrylic resin paint various characteristics.To people and not injury of environment.
Embodiment
Embodiment 1:
A kind of water soluble acrylic resin is provided, comprises following material:
Vinylformic acid: 1-2 part
TEB 3K: 15-29 part
Bing Xisuandingzhi: 18-22 part
Vinylbenzene: 3-7 part
Rocryl 400: 3-7 part
Mercaptoethanol: 0.25-0.65 part
Diisopropyl azodicarboxylate: 0.3-0.7 part
Virahol: 3-5 part
Ethanol: 15-20 part
Monoethanolamine MEA BASF: 2.5-8.75 part
Water: 25-31.5 part
It more than is mass fraction.
Embodiment 2:
A kind of water soluble acrylic resin is provided, comprises following material:
Vinylformic acid: 1-2 part
TEB 3K: 25-29 part
Bing Xisuandingzhi: 19-21 part
Vinylbenzene: 5-6 part
Rocryl 400: 4-6 part
Mercaptoethanol: 0.25-0.65 part
Diisopropyl azodicarboxylate: 0.3-0.7 part
Virahol: 3-5 part
Ethanol: 18-20 part
Monoethanolamine MEA BASF: 2.5-8.75 part
Water: 25-31.5 part
It more than is mass fraction.
Embodiment 3:
Vinylformic acid: 1-2 part
TEB 3K: 26-28 part
Bing Xisuandingzhi: 21 parts
Vinylbenzene: 7 parts
Rocryl 400: 7 parts
Mercaptoethanol: 0.25-0.65 part
Diisopropyl azodicarboxylate: 0.3-0.7 part
Virahol: 3-5 part
Ethanol: 20 parts
Monoethanolamine MEA BASF: 2.5-8.75 part
Water: 25-31.5 part
It more than is mass fraction.
A kind of preparation method who prepares above-mentioned water soluble acrylic resin is provided, may further comprise the steps:
A, in header tank with vinylformic acid, TEB 3K, Bing Xisuandingzhi, vinylbenzene, Rocryl 400, mercaptoethanol, Diisopropyl azodicarboxylate mix, and stir;
B, in having the reaction kettle of reflux exchanger, drop into Virahol and ethanol, be warmed up to 80 ℃, splash into the mix monomer of step a gained; Drip off the back and held temperature 10 hours at 75～80 ℃; Cool to 50 ℃ then, add Monoethanolamine MEA BASF, be neutralized to PH=7.5～8.0 back thin ups; Be cooled to room temperature, filter and package at last.
The present invention adopts the water soluble acrylic resin to make solvent with water and eco-friendly etoh solvent, and to people and not injury of environment, and performance can reach the effect of oiliness pearly-lustre low-melting ink vehicle fully.
Below for each item technical indicator of water soluble acrylic resin of the present invention:
Claims (4)
1. a water soluble acrylic resin is characterized in that, comprises following material:
Vinylformic acid: 1-2 part
TEB 3K: 15-29 part
Bing Xisuandingzhi: 18-22 part
Vinylbenzene: 3-7 part
Rocryl 400: 3-7 part
Mercaptoethanol: 0.25-0.65 part
Diisopropyl azodicarboxylate: 0.3-0.7 part
Virahol: 3-5 part
Ethanol: 15-20 part
Monoethanolamine MEA BASF: 2.5-8.75 part
Water: 25-31.5 part
It more than is mass fraction.
2. a kind of water soluble acrylic resin according to claim 1 is characterized in that, wherein:
Vinylformic acid 1-2 part
TEB 3K: 25-29 part
Bing Xisuandingzhi: 19-21 part
Vinylbenzene: 5-6 part
Rocryl 400: 4-6 part
Mercaptoethanol: 0.25-0.65 part
Diisopropyl azodicarboxylate: 0.3-0.7 part
Virahol: 3-5 part
Ethanol: 18-20 part
Monoethanolamine MEA BASF: 2.5-8.75 part
Water: 25-31.5 part
It more than is mass fraction.
3. water soluble acrylic resin according to claim 1 is characterized in that, wherein:
Vinylformic acid: 1-2 part
TEB 3K: 26-28 part
Bing Xisuandingzhi: 21 parts
Vinylbenzene: 7 parts
Rocryl 400: 7 parts
Mercaptoethanol: 0.25-0.65 part
Diisopropyl azodicarboxylate: 0.3-0.7 part
Virahol: 3-5 part
Ethanol: 20 parts
Monoethanolamine MEA BASF: 2.5-8.75 part
Water: 25-31.5 part
It more than is mass fraction.
4. method for preparing like claim 1 or 2 or 3 described water soluble acrylic resins may further comprise the steps:
A, in header tank with vinylformic acid, TEB 3K, Bing Xisuandingzhi, vinylbenzene, Rocryl 400, mercaptoethanol, Diisopropyl azodicarboxylate mix, and stir;
B, in having the reaction kettle of reflux exchanger, drop into Virahol and ethanol, be warmed up to 80 ℃, splash into the mix monomer of step a gained; Drip off the back and held temperature 10 hours at 75～80 ℃; Cool to 50 ℃ then, add Monoethanolamine MEA BASF, be neutralized to pH=7.5～8.0 back thin ups; Be cooled to room temperature, filter and package at last.