CN101177354A - Water-tight fused block and method for manufacturing same - Google Patents
Water-tight fused block and method for manufacturing same Download PDFInfo
- Publication number
- CN101177354A CN101177354A CNA2006101387055A CN200610138705A CN101177354A CN 101177354 A CN101177354 A CN 101177354A CN A2006101387055 A CNA2006101387055 A CN A2006101387055A CN 200610138705 A CN200610138705 A CN 200610138705A CN 101177354 A CN101177354 A CN 101177354A
- Authority
- CN
- China
- Prior art keywords
- water
- fused block
- ball milling
- tight fused
- tight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof frit, the weight percents of the chemical compositions are 50 to 60% of SiO2, 4 to 6% of Al2O3, 5 to 10% of CaO, 1 to 3% of MgO, 3 to 6% of K2O, 1 to 2% of Na2O, 15 to 20% of TiO2 and 1 to 3% of B2O3. The producing process flow is as follows: the entry of raw material-> checking -> mixture making according to the weight proportioning of the compositions of the raw material -> adding the polymeric waterproof layer -> burning -> checking -> packaging. The founding temperature is between 1500 to 1600 DEG C; the weight percent of the ball milling glaze slurry fitness is 325 meshes: 0.15 to 0.55%; the specific gravity of the ball milling glaze slurry is 1.8 to 1.9 g/cm<3>; and the velocity of the ball milling glaze slurry flow is below 60S. The invention has the advantages of resistance of water dissolution, less liability to dirt absorption, avoidance of space discolorment due to the water infiltration of the ceramic product and applicability to production of ceramic product.
Description
Technical field
The present invention relates to a kind of pottery fritted glaze and manufacture method thereof, particularly a kind of water-tight fused block and manufacture method thereof.
Background technology
In the prior art, do the frit agent with common frit and make the glazed interior tile that ground-coat enamel (annotating: at base substrate and the middle added one deck cosmetic soil of glaze layer) is produced, because of the type ground-coat enamel, density is low, covering power is not enough, and firing range is narrow, and firing temperature is strict, cause the product poor heat stability, be easy to generate aberration, ground-coat enamel is coarse, and water-repellancy is poor, because " permeable " can make ceramic tile produce the space variable color, produces problems such as watermark; Can make ceramic tile produce be full of cracks simultaneously, thus exist quality undesirable, the defective that cost is higher.Because the defective of prior art when ceramic tile where applicable in moist or filthy environment, because its water resistance is undesirable, can produce ceramic tile variable color obfuscation in use for some time, the aged phenomenon takes place, and can not adapt to the clean demand of current society; In addition,, also can grow some mosquitoes, be unfavorable for people's health owing to humid environment, filth.
Frit is the core technology of ceramic tile manufacturer, " waterproof fully " ceramic tile of a lot of manufacturer production on the existing market, its real core technology " water-tight fused block " all is to buy from external glaze company, cost is higher, it is lower that the client is badly in need of cost, and the quality water-tight fused block identical with imported product is as the substitute of imported product.
Summary of the invention
The objective of the invention is to overcome the defective of prior art, a kind of whiteness is good, covering power is strong water-tight fused block and manufacture method thereof are provided, this frit has complete watertightness to water and aqueous fusion thing, can waterproof, dirt such as grease proofing, anti-mud, thereby erect in the middle of at the bottom of ceramic brick surface is with base " water [proof ", make the water resistance of ceramic tile better, adapt to the needs of current social enviroment protection.
The objective of the invention is to be achieved through the following technical solutions:
A kind of water-tight fused block, the weight percent of the chemical constitution of described each component of water-tight fused block is: SiO
250～60%, Al
2O
34～6%, CaO 5～10%, and MgO 1～3%, K
2O3～6%, Na
2O 1～2%, TiO
215～20%, B
2O
31～3%.
Described ball milling glaze slip fineness weight percent is 325 orders: 0.15～0.55%.
A kind of manufacture method of water-tight fused block, described manufacturing approach craft flow process is as follows: raw material advances factory → check → prepare burden → found → shrend → check → packing by the feed composition weight proportion.
Described glass melting temperature is: 1500～1600 ℃.
Described ball milling glaze slip proportion is: 1.8～1.9g/cm
3
Described ball milling glaze slip flow velocity is: below the 60S.
The present invention can reach following beneficial effect after adopting technique scheme:
1, applied widely.The manufacturing of exterior wall and ground decoration tile and any environment that needs are arranged in the present invention can be applicable to simultaneously.
2, waterproof ability height.The anti-aqueous fusion material of the present invention is difficult for soil pick-up.
3, firing temperature is wide.Firing temperature of the present invention is wide, and the frit firing temperature is 1500～1600 ℃, so be difficult for producing aberration, yield rate height.
4, technical process is reasonable.Manufacturing approach craft flow process among the present invention rationally, simply.
5, reduced cost.The external imported product of the present invention, performance perameter is identical, but its cost can reduce about 50%, and the big spoke degree of cost is reduced, and strengthened the competitiveness of product in market.
6, do not produce watermark.The invention solves the space discoloration problem that ceramic products " permeable " produces, construction process is simple, does not produce watermark, does not have watermark not do and problems such as concrete grey sees through for a long time.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further detail (each component unit of frit is weight percentage):
Continuous table
| Glass melting temperature (℃) | 1500～ 1600 | 1500 | 1550 | 1530 | 1560 | 1580 | 1590 | 1600 | 1510 |
| Ball milling slurry proportion (g/cm 3) | 1.8～1.9 | 1.85 | 1.83 | 1.86 | 1.90 | 1.88 | 1.82 | 1.84 | 1.89 |
| Flow velocity (s) | ∠60 | 59 | 58 | 48 | 39 | 28 | 19 | 6 | 26 |
| Glaze slip fineness (%) | 0.2～0.5 (325 order) | 0.2 | 0.23 | 0.25 | 0.33 | 0.35 | 0.46 | 0.5 | 0.4 |
Described water-tight fused block manufacturing approach craft flow process is as follows: raw material advances factory → check → by previous embodiment proportion ingredient → found (pressing the embodiment temperature) → shrend → check → packing.
This frit has complete watertightness to water and aqueous fusion thing, and the glaze made from this frit can form one deck waterproof layer on the ceramic surface when being used for ceramic.
Other technical process of making ceramic among the present invention can be adopted prior art.
Claims (6)
1. water-tight fused block, it is characterized in that: the weight percent of the chemical constitution of described each component of water-tight fused block is: ALO
350～60%, SiO
24～6%, CaO 5～10%, MgO1～3%, K
2O 3～6%, Na
2O 1～2%, TiO
215～20%, B
2O
31～3%.
2. a kind of water-tight fused block according to claim 1 is characterized in that: described ball milling glaze slip fineness weight percent is 325 orders: 0.15～0.55%.
3. the manufacture method of a kind of water-tight fused block according to claim 1, it is characterized in that: described manufacturing approach craft flow process is as follows: raw material advances factory → check → prepare burden → found → shrend → check → packing by the feed composition weight proportion.
4. a kind of water-tight fused block according to claim 3 is characterized in that: described firing temperature is 1500～1600 ℃.
5. a kind of water-tight fused block according to claim 3 is characterized in that: described ball milling glaze slip proportion is 1.8～1.9g/cm
3
6. a kind of water-tight fused block according to claim 3 is characterized in that: described ball milling glaze slip flow velocity is below the 60S.