CN101157318A - A manufacturing method of glass art picture - Google Patents
A manufacturing method of glass art picture Download PDFInfo
- Publication number
- CN101157318A CN101157318A CNA200710092834XA CN200710092834A CN101157318A CN 101157318 A CN101157318 A CN 101157318A CN A200710092834X A CNA200710092834X A CN A200710092834XA CN 200710092834 A CN200710092834 A CN 200710092834A CN 101157318 A CN101157318 A CN 101157318A
- Authority
- CN
- China
- Prior art keywords
- glass
- decorative pattern
- resin glue
- epoxide
- adhesive tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method of glass craft arts, and the method comprises the following steps: making glass substrate, wherein, paper tape is stuck around the glass, mixing up epoxy resin adhesive with curing agent proportion, painting the surface of glass by leveling; making mould, wherein, with engraving patterns on the glossy paper of sticker, the glossy paper of sticker is stuck to a plastic film, tearing up pattern, putting pattern mould on the double-sided adhesive to make mould; making craft arts on the glass substrate. When the curing extent of epoxy resin glue has reached 40 to 70 percent, the mould is put on the epoxy resin glue, squeezing down pattern mould to form three-dimensional pattern. After the epoxy resin glue cured, the mould and painting color are taken off, the glass craft arts is formed. The invention has the advantages of epoxy resin, such as strong bonding capacity, the color of epoxy resin cured is similar to that of glass, thereby forming three-dimensional painting that integrates with glass, so that the glass is strengthened, and the glass is not easily to be broken, production technology is simple, processing time is short, the glass craft arts has rich stereoscopic and layer effects.
Description
Technical field the present invention relates to the preparation method of handicraft picture, particularly a kind of preparation method of glass art picture.
Background technology is along with high development of social economy, and the human living standard improves constantly, and people are also increasing to the demand of handicraft, requires also more and more highlyer, and people are living and usually beautify the environment with handicraft in place such as work.Glass art picture is a kind of handicraft that people enjoy a lot, and present glass art picture major part all is hand engraving, also has mechanical artistic carving to draw, or ball blast engraving, not only take a lot of work but also require great effort, and require glass that enough thickness is arranged, could produce strong third dimension.In addition, single handicraft picture by glass-engraving is broken, promptly dangerous easily, is unfavorable for carrying again.
Summary of the invention purpose of the present invention is exactly at the deficiencies in the prior art, provide a kind of manufacture craft simply, more convenient, process time is short, the preparation method that is difficult for the glass art picture broken, that security is higher.
For achieving the above object, the present invention adopts following technical scheme:
A kind of preparation method of glass art picture is characterized in that may further comprise the steps:
A), make glass baseplate
Glass surface is cleaned up, periphery at glass sticks paper self-adhesive tape, the height of paper self-adhesive tape is 0.5～20mm, transparent epoxy resin glue and curing agent are mixed up in proportion, stir, be coated in uniformly again on the glass surface of paper self-adhesive tape encirclement, make epoxide-resin glue in paper self-adhesive tape, can not flow to the outside and the levelling of paper self-adhesive tape, stand-by;
B), make template
On the facial tissue of Sticky Note, engrave required decorative pattern with engraving machine, the facial tissue of Sticky Note is attached on the plastic sheeting, tear the decorative pattern part, earlier partly stick the double faced adhesive tape identical with floral designs at decorative pattern, and then on double faced adhesive tape, put the decorative pattern module that adapts with the decorative pattern shape by the shape of decorative pattern, the dapple one side of decorative pattern modular belt is fitted with double faced adhesive tape, make template, stand-by; The one side of described decorative pattern module has the three-dimensional pattern shape, and another side is the plane;
C), manufacture craft is drawn on glass baseplate
When the epoxide-resin glue of glass baseplate has reached the 40-70% state of cure, template is placed on above the epoxide-resin glue of glass baseplate, make above the epoxide-resin glue that plastic sheeting is positioned over, the decorative pattern module of the shape part of decorative pattern on the extruding Sticky Note makes the decorative pattern module section that is extruded to lower recess downwards, forms three-dimensional pattern, after treating that epoxide-resin glue solidifies fully, take away template, coat color, glass art picture.Downwards extruding decorative pattern module can with a massive plate be placed on all decorative pattern modules above, firmly extruding downwards also can be put weight on massive plate, exerts pressure; Certainly, also can be independent respectively exert pressure to each decorative pattern module.
The effect of plastic sheeting is to make resin and mould separately, and resin does not melt mutually with film, so mould is to reuse.
Characteristics such as epoxyn is the very excellent adhesive kind of performance, and particularly its environmental suitability is strong, adhesion strength is strong, the feature of environmental protection is good make its extensive attention that is subjected to people, range of application and wide.
The advantage of epoxyn: compare with the adhesive of other types, epoxyn has the following advantages:
1, epoxy resin contains various polarity group and active very big epoxy radicals, thereby with various polarity materials such as metal, glass, cement, timber, plastics, especially the material that surface-active is high has very strong bonding force, the cohesive strength of curable epoxide thing is also very big simultaneously, so its glue-joint strength is very high.
2, essentially no low molecular weight volatile deposits yields during resin solidification.The cubical contraction of glue-line is little, and is about 1% one 2%, is one of kind of cure shrinkage minimum in the thermosetting resin.The linear expansion coefficient of curable epoxide thing is also very little.Therefore internal stress is little, and is little to the glue-joint strength influence.The creep of curable epoxide thing is little in addition, so the dimensional stability of glue-line is good.
3, the kind of epoxy resin, curing agent and modifier is a lot, can be by prescription design rationally and cleverly, make adhesive have needed manufacturability (as curing in quick curing, cold curing, low-temperature setting, the water, low viscosity, high viscosity etc.), and have desired serviceability (as high temperature resistant, low temperature resistant, high strength, high flexibility, ageing-resistant, conduction, magnetic conduction, heat conduction etc.).
The present invention selects water white in the epoxy resin for use, the two canned epoxide-resin glue of high rigidity, in proportion epoxy resin and curing agent are mixed up in proportion, stir, be poured on the glass surface of paper self-adhesive tape encirclement, form the approximate resin bed of epoxy resin and glass baseplate color, when utilizing epoxide-resin glue to be cured to a certain degree, during as 40～70% states of cure, though the surface is Guization substantially, do not have viscosity, and its subsurface resin bed hardness does not also reach maximum, have plastic characteristic, form uneven by downward extrusion die, three-dimensional pattern reaches the purpose of making glass art picture, it is strong to make full use of the adhering with epoxy resin ability, has plasticity, the characteristics that color after the curing and glass are approximate can form the stereo art painting with the glass one, and glass is enhanced, it is broken that glass is difficult for, even so broken because the safe effect that has resin glue can not hurt sb.'s feelings.
The crystal that Dongguan spademan Chemical Industry Science Co., Ltd produces drips the ZY-806 in the glue (plane ebonite series), and characteristics: the plane is rigid, high gloss, and water white transparency, self-defoaming is good, good fluidity.Ratio: A: B=3: 1; Condition of cure: 60 ℃ * 1.2H, normal temperature: 25 ℃ * 12H.
ZY-602, characteristics: the plane is rigid, high gloss, water white transparency, self-defoaming is good, good fluidity.Ratio: A: B=2: 1 solidifies: 60 ℃ * 1.5H, and normal temperature: 25 ℃ * 12H five metals jewellery.
ZY-820, characteristics: the plane is rigid, high gloss, water white transparency, self-defoaming is good, good fluidity, piece is done.Ratio: A: B=3: 1; Condition of cure: 60 ℃ * 1H, normal temperature: 25 ℃ * 8H.
ZY-243, characteristics: the plane is rigid. and the high gloss transparency is good. and self-defoaming is good. ultrahard. will never change colour. winter protection. especially adhesive force is good.Ratio: A: B=3: 1, A: B=2: 1; Condition of cure: 60 ℃ * 2.5H100 ° ~ 120 ℃ * 2H (polishing).
A in the above-mentioned epoxide-resin glue is an epoxy resin, and B is a curing agent, can be as the material of glass art picture making.
Preferably, described decorative pattern module has multiple shape, as flower, petal, blade, birds, fish, animal, trees, mountain, grass, pole etc.; And each decorative pattern module all is ascending many groups.So long as the pattern element that has in drawing can be made into the decorative pattern module, the decorative pattern module of accumulating over a long period is just very abundant, and the decorative pattern module is by packet numbering, as long as the pattern and the decorative pattern module of logging template correspondence, trying to locate by following up a clue when producing this glass art picture again gets final product.The decorative pattern module can adopt methods such as engraving, casting to make.
Preferably, described decorative pattern module, be according to the concavo-convex degree of depth requirement of the decorative pattern of needed performance on the decorative pattern facial tissue, be stained with the above thickness of 2mm, with decorative pattern or the identical double faced adhesive tape of non-floral designs, and then adhere on the hard plate that adapts with the floral designs size, form as plank or glass etc.This decorative pattern module is applicable to that production lot is smaller, and the decorative pattern module is inadequate, the glass art picture production that time requirement is tight.
Preferably, in step c, be earlier when the epoxide-resin glue of glass baseplate has reached 20～30% states of cure, do bubble earlier, with the syringe suction air that has syringe needle, inject epoxy glue layer, form the effect of bubble; Bubble completes, and after epoxy glue layer was solidified fully, a, b, c made glass art picture set by step on the epoxy glue layer of bubble making again.Drawing with glass machinery artistic carving, or in the ball blast artistic carving picture, be difficult to produce bubble, and can arbitraryly produce bubble in the present invention, increasing the artistic effect of glass art picture.
Preferably, in step a, when epoxide-resin glue has reached 20～30% states of cure, blow the epoxide-resin glue surface with high wind and make epoxide-resin glue surface waviness shape.The picture of glass art picture is more lively.
Preferably, in step a, when epoxide-resin glue has reached 20～30% states of cure, insert in the resin, take down after the curing, form three-dimensional cylinder with erectting as the pole instrument.
Preferably, in step c, form three-dimensional pattern, take away plastic sheeting, Sticky Note after, paint brush and be stained with the transparent epoxy resin glue of converting, brush forms the skin texture of textured on epoxy glue layer.Skin texture mainly is third dimension and the stereovision that increases glass art picture.
Preferably, described step a, b, c can repeat repeatedly.Repeat repeatedly can produce multi-level glass art picture relief painting, this point is that direct engraving on glass institute is inaccessiable, and engraving on glass can not be carved after once once more.
The beneficial effect of a kind of glass technology method for making picture of the present invention is, the characteristics that make full use of that the adhering with epoxy resin ability is strong, the color after solidifying and glass are similar to, can form relief painting with the glass one, glass is enhanced, it is broken that glass is difficult for, manufacture craft of the present invention is simple, process time short, and the third dimension of glass art picture and stereovision are abundant.
Appended drawings is a schematic diagram of the present invention
The present invention is further illustrated below in conjunction with the specific embodiment for the specific embodiment, but therefore do not limit the present invention among the described scope of embodiments.
Embodiment 1:
A kind of preparation method of glass art picture is characterized in that may further comprise the steps:
A), make glass baseplate
Glass surface is cleaned up, periphery at glass sticks paper self-adhesive tape, the height of paper self-adhesive tape is 1mm, and the crystal that spademan Chemical Industry Science Co., Ltd in Dongguan is produced drips glue ZY-602, and in A epoxy resin: the ratio of B curing agent=2: 1 mixes up, stir, be poured on uniformly again on the glass surface of paper self-adhesive tape encirclement, make epoxide-resin glue in paper self-adhesive tape, can not flow to the outside of paper self-adhesive tape, and levelling, stand-by;
B), make template
On the facial tissue of Sticky Note, engrave required decorative pattern with engraving machine, the facial tissue of Sticky Note is attached on the plastic sheeting, tear the decorative pattern part, earlier partly stick the double faced adhesive tape identical with floral designs at decorative pattern, and then on double faced adhesive tape, put the decorative pattern module that adapts with the decorative pattern shape by the shape of decorative pattern, the dapple one side of decorative pattern modular belt is fitted with double faced adhesive tape, make template, stand-by;
C), manufacture craft is drawn on glass baseplate
When the epoxide-resin glue of glass baseplate has reached the 40-70% state of cure, template is placed on above the epoxide-resin glue of glass baseplate, make above the epoxide-resin glue that plastic sheeting is positioned over, with a massive plate be placed on all decorative pattern modules above, on massive plate, put weight, the shape decorative pattern module partly of exerting pressure and pushing decorative pattern on the Sticky Note downwards, make the decorative pattern module section that is extruded to lower recess, form three-dimensional pattern, after treating that epoxide-resin glue solidifies fully, take away template, coat color, glass art picture.
Embodiment 2:
A kind of preparation method of glass art picture is characterized in that may further comprise the steps:
A), make glass baseplate
Glass surface is cleaned up, periphery at glass sticks paper self-adhesive tape, the height of paper self-adhesive tape is 10mm, and the crystal that spademan Chemical Industry Science Co., Ltd in Dongguan is produced drips glue ZY-820, and in A epoxy resin: the ratio of B curing agent=3: 1 mixes up, stir, be poured on uniformly again on the glass surface that paper self-adhesive tape surrounds, make epoxide-resin glue can not flow to the outside of paper self-adhesive tape, and concordant with the upper edge of paper self-adhesive tape, and levelling, stand-by;
B), make template
On the facial tissue of Sticky Note, engrave required decorative pattern with engraving machine, the facial tissue of Sticky Note is attached on the plastic sheeting, tear decorative pattern or non-decorative pattern part, on the decorative pattern facial tissue according to the concavo-convex degree of depth requirement of the decorative pattern of needed performance, be stained with the above thickness of 2mm, with decorative pattern or the identical double faced adhesive tape of non-floral designs, and then adhere on the hard plate that adapts with the floral designs size, make template;
C), on glass baseplate, make the handicraft picture that has bubble
When the epoxide-resin glue of glass baseplate has reached 20～30% states of cure, in the time of promptly 2 hours, do bubble earlier, with the syringe suction air that has syringe needle, inject epoxy glue layer, form the effect of bubble; Bubble completes, after epoxy glue layer is solidified fully, repeating step a, when the epoxide-resin glue of glass baseplate has reached 60～70% states of cure, in the time of promptly 12 hours, template is placed on above the epoxide-resin glue of glass baseplate, make above the epoxide-resin glue that plastic sheeting is positioned over, with a massive plate be placed on all decorative pattern modules above, firmly push the decorative pattern module of the shape part of decorative pattern on the Sticky Note downwards, make the decorative pattern module section that is extruded to lower recess, form three-dimensional pattern, treat that epoxide-resin glue solidifies fully after, take away template, paint brush and be stained with the transparent epoxy resin glue of converting, brush forms the skin texture of textured on epoxy glue layer; Coat color, glass art picture;
Embodiment 3:
A kind of preparation method of glass art picture is characterized in that may further comprise the steps:
A), make glass baseplate
Glass surface is cleaned up, periphery at glass sticks paper self-adhesive tape, the height of paper self-adhesive tape is 10mm, transparent epoxy resin glue and curing agent are mixed up in proportion, stir, be poured on uniformly again on the glass surface of paper self-adhesive tape encirclement, make epoxide-resin glue can not flow to the outside of paper self-adhesive tape, and, and levelling concordant with the upper edge of paper self-adhesive tape; When epoxide-resin glue has reached 20～30% states of cure, blow the epoxide-resin glue surface with high wind and make epoxide-resin glue surface waviness shape, stand-by;
B), make template
On the facial tissue of Sticky Note, engrave required decorative pattern with engraving machine, the facial tissue of Sticky Note is attached on the plastic sheeting, tear the decorative pattern part, earlier partly stick the double faced adhesive tape identical with floral designs at decorative pattern, and then on double faced adhesive tape, put the decorative pattern module that adapts with the decorative pattern shape by the shape of decorative pattern, the dapple one side of decorative pattern modular belt is fitted with double faced adhesive tape, make template, stand-by;
C), manufacture craft is drawn on glass baseplate
When the epoxide-resin glue of glass baseplate has reached the 60-70% state of cure, template is placed on above the epoxide-resin glue of glass baseplate, make above the epoxide-resin glue that plastic sheeting is positioned over, the decorative pattern module of the shape part of decorative pattern on the extruding Sticky Note makes the decorative pattern module section that is extruded to lower recess downwards, forms three-dimensional pattern, after treating that epoxide-resin glue solidifies fully, take away template, coat color, glass art picture.
Claims (8)
1. the preparation method of a glass art picture is characterized in that may further comprise the steps:
A), make glass baseplate
Glass surface is cleaned up, periphery at glass sticks paper self-adhesive tape, the height of paper self-adhesive tape is 0.5～20mm, transparent epoxy resin glue and curing agent are mixed up in proportion, stir, be coated in uniformly again on the glass surface of paper self-adhesive tape encirclement, make epoxide-resin glue in paper self-adhesive tape, can not flow to the outside and the levelling of paper self-adhesive tape, stand-by;
B), make template
On the facial tissue of Sticky Note, engrave required decorative pattern with engraving machine, the facial tissue of Sticky Note is attached on the plastic sheeting, tear the decorative pattern part, earlier partly stick the double faced adhesive tape identical with floral designs at decorative pattern, and then on double faced adhesive tape, put the decorative pattern module that adapts with the decorative pattern shape by the shape of decorative pattern, the dapple one side of decorative pattern modular belt is fitted with double faced adhesive tape, make template, stand-by; The one side of described decorative pattern module has the three-dimensional pattern shape, and another side is the plane;
C), manufacture craft is drawn on glass baseplate
When the epoxide-resin glue of glass baseplate has reached the 40-70% state of cure, template is placed on above the epoxide-resin glue of glass baseplate, make above the epoxide-resin glue that plastic sheeting is positioned over, the decorative pattern module of the shape part of decorative pattern on the extruding Sticky Note makes the decorative pattern module section that is extruded to lower recess downwards, forms three-dimensional pattern, after treating that epoxide-resin glue solidifies fully, take away template, coat color, glass art picture.
2. the preparation method of a kind of glass art picture according to claim 1, it is characterized in that: described decorative pattern module has multiple shape, as flower, petal, blade, birds, fish, animal, trees, mountain, grass, pole etc.; And each decorative pattern module all is ascending many groups.
3. the preparation method of a kind of glass art picture according to claim 1, it is characterized in that: described decorative pattern module, be according to the concavo-convex degree of depth requirement of the decorative pattern of needed performance on the decorative pattern facial tissue, be stained with the above thickness of 2mm, with decorative pattern or the identical double faced adhesive tape of non-floral designs, and then adhere on the hard plate that adapts with the floral designs size, form as plank or glass etc.
4. the preparation method of a kind of glass art picture according to claim 1, it is characterized in that: in step c, be earlier when the epoxide-resin glue of glass baseplate has reached 20～30% states of cure, do bubble earlier, with the syringe suction air that has syringe needle, inject epoxy glue layer, form the effect of bubble; Bubble completes, and after epoxy glue layer was solidified fully, a, b, c made glass art picture set by step on the epoxy glue layer of bubble making again.
5. the preparation method of a kind of glass art picture according to claim 1 is characterized in that: in step a, when epoxide-resin glue has reached 20～30% states of cure, blow the epoxide-resin glue surface with high wind and make epoxide-resin glue surface waviness shape.
6. the preparation method of a kind of glass art picture according to claim 1 is characterized in that: when epoxide-resin glue has reached 20～30% states of cure, insert in the resin with erectting as the pole instrument in step a, take down after the curing, form three-dimensional cylinder.
7. the preparation method of a kind of glass art picture according to claim 1 is characterized in that: in step c, form three-dimensional pattern, after taking away plastic sheeting, Sticky Note, paint brush and be stained with the transparent epoxy resin glue of converting, brush forms the skin texture of textured on epoxy glue layer.
8. the preparation method of a kind of glass art picture according to claim 1, it is characterized in that: described step a, b, c can repeat repeatedly.