CN101117776A - Chemical fiber tricolor developing production technique

Info

Publication number: CN101117776A
Application number: CNA2006100485012A
Authority: CN
Inventors: 郑有全
Original assignee: HENAN REBECCA HAIR PRODUCTS Inc
Current assignee: HENAN REBECCA HAIR PRODUCTS Inc
Priority date: 2006-08-01
Filing date: 2006-08-01
Publication date: 2008-02-06

Abstract

The present invention provides a tri-color production technology of chemical fiber hair for periwig, and the technology includes bundling, dyeing (discoloring), finishing, drying and etc. of chemical fiber hair. The bundling means that bundling the middle or one end of the chemical fiber hair with a plastic film and retaining a length to be colored; the dyeing means that the required dyeing materials are added into a dying channel after being weighted and combined, acetic acid, carrier and salt are added, after the water temperature reaches 60-90DEG C, the bundled chemical fiber hair is put in the dyeing channel for thermal insulation for 15-30 minutes; the discoloring means that hydrogen peroxide, ammonia water and whitening power of different concentrations are put in to the dyeing channel, with temperature rising to 85-100 DEG C, and the bundled chemical fiber hair is put into the channel for 15-20 minutes; the finishing is to put the cleaned chemical fiber hair into water added with soft oil and immerse for 10-15 minutes under the temperature of 20-30DEG C. Upon different tri-color demands, dyeing (discoloring) realizes one dyeing and one discoloring, double dyeing or double discoloring for two ends or one end for respective dyeing or discoloring, and the chemical fiber hair with the original color expresses a tri-color effect and makes the chemical fiber hair more vivid.

Description

Chemical fiber tricolor developing production technique

Technical field:

The present invention relates to a kind of multicolor dyeing and finishing method of chemical fibre, special relevant with the distinctive chemical fiber tricolor developing production technology of wig industry.

Background technology:

Chemical fibres such as terylene, modified dacron, acrylic fibers are used in the wig industry, are known as chemical fiber hairs.Because chemical fiber hairs is that the look mother is painted, i.e. production of chemical fibre comes out specific solid color is just arranged, and the single-unit chemical fiber hairs is dyed double-colored at present, but do not dye three looks, and can only dye than true qualities dark color, can not dye, can't produce the chemical fiber hairs of three looks or polychrome like this than true qualities light color.Along with the continuous enhancing of people's seeking new thoughts idea, the demand of three looks or polychrome chemical fiber hairs is with increasing.

Summary of the invention:

The present invention be directed to chemical fibre when being used to make wig the single-unit chemical fiber hairs only dye double-colored, do not dye three looks, can only dye than true qualities dark color, can not dye problem than true qualities light color, a kind of chemical fiber tricolor developing production technique is provided, particularly solve chemical fiber hairs and can only dye, can not dye a difficult problem more shallow than true qualities than this color depth.

Chemical fiber tricolor developing production technique of the present invention comprises pricks handle, dyeing (fading), post processing and dewatered drying several steps.Prick and chemical fiber hairs is cut into the length that needs, tie middle or one, stay the length that will dye or fade on request with plastic film being; Dyeing is the difference according to the chemical fiber hairs raw material, adopt DISPERSE DYES or cation dyes, required dyestuff weighing, the good back of change are added in the staining bath; bath raio 1: 40, adding 0.3-0.8 grams per liter concentration again is the glacial acetic acid of 85%-98%, and the carrier of 2-9 gram and the salt of 40-90 grams per liter; stirring is warmed up to 70-90 ℃; put into the chemical fiber hairs that ties handle then, be incubated 30-60 minute propose consistent with the sample mark; Fading is according to the look depth of fading chemical fiber hairs and the kind difference of raw material, and adding hydrogen peroxide 100-600%, ammoniacal liquor 10-60%, bleaching powder 0.4-2.5%, bath raio 1: 15, intensification 80-100 ℃ input tie the chemical fiber hairs of handle, act on 10-20 minute; Post processing is two kinds of consistent lubricants that add 2%-5% and 5%-10% respectively, and bath raio 1: 20, water temperature 20-30 ℃ are put into the chemical fiber hairs of cleaning and soaked 10-15 minute, take out dehydration, oven dry then.

Above-mentioned technology dyeing (fading) step is according to the needs of different three looks, can choose one and dye one and take off or two dye or two taking off dyeed respectively or faded chemical fiber hairs two or one, adds the chemical fiber hairs primary colors, and whole chemical fiber hairs presents three chromatic effects.

Process provided by the invention has enlarged the range of application of chemical fiber hairs, makes the chemical fiber hairs color more bright and colourful, and the effect that the section of presenting is dyed and excessive section is dyed, and makes wig fashion more.

The specific embodiment:

Below two embodiment can describe chemical fiber tricolor developing production technique of the present invention in detail.

Example 1,1B/30#/27# three look production technologies.Step is as follows:

1, prick handle: selecting color for use is the chemical fiber hairs of 30#, and intercepted length is that every section 20CM amounts to 10kg, ties one with plastic film, reserves 6CM.

2, dyeing: the cation dyes weighing is accurate, change good back and add in the staining bath, bath raio 1: 40 adds 0.5 grams per liter concentration and is 98% glacial acetic acid again, the salt of the carrier of 3 grams per liters and 55 grams per liters, stir, be warmed up to 85 ℃, put into the chemical fiber hairs that ties handle then, be incubated 30 minutes, the range estimation that gets sample is dyed the 1B look and number can be gone out machine, rinses well.

3, fade: untie plastic film, tie the other end with plastic film again, reserve 6CM, add 350% hydrogen peroxide, 30% ammoniacal liquor and 1.2% bleaching powder, bath raio 1: 15 is warmed up to 85 ℃, input ties the chemical fiber hairs of handle, acts on 10 minutes, and it is clean to take off 27# tinctorial pattern afterflush.

4, post processing: untie plastic film, adding 3% and 5% two kind of consistent lubricant, bath raio 1: 20 at room temperature, is put into treatment fluid to chemical fiber hairs and was soaked 15 minutes.

5, dehydration, oven dry.

Top is 1B look (length 6CM) like this, and the centre is that 30# look (length is 8CM) bottom is three looks of 27# look (length 6CM).

Example 2,2#/27#/2# three look production technologies.Step is as follows:

1, prick handle: selecting color for use is the chemical fiber hairs of 27#, and intercepted length is 30CM, amounts to 10kg, and in the middle of tying with plastic film, 10CM is flowed out at two respectively,

2, dyeing: the dispersion fuel weighing is accurate, change good back and add in the staining bath bath raio 1: 40, adding 0.5 grams per liter concentration is 98% glacial acetic acid, 2.5 the salt of the carrier of grams per liter and 40 grams per liters stirs, and is warmed up to 75 ℃, put into the chemical fiber hairs that ties handle then, be incubated 25 minutes, the 2# look is dyed in the range estimation that gets sample, can go out machine, rinse well.

3, post processing: untie plastic film, adding 3% and 5% two kind of consistent lubricant, bath raio 1: 20 at room temperature, is put into treatment fluid to chemical fibre and was soaked 15 minutes.

4, dehydration, oven dry.

Two is 2# look (length all is 10CM) like this, and the centre is three looks of 27# look (length 10CM).

Claims

1. chemical fiber tricolor developing production technique, comprise chemical fiber hairs is pricked handle, dyeing (fading), post processing and dewatered drying several steps, it is characterized in that: prick being the length that chemical fiber hairs is cut into needs, tie middle or one, stay the length that will dye or be faded on request with plastic film; Dyeing is that required dyestuff weighing, the good back of change are added in the staining bath; bath raio 1: 40; adding 0.3-0.8 grams per liter concentration again is the glacial acetic acid of 85%-98%; the carrier of 2-9 gram and the salt of 40-90 grams per liter; stirring is warmed up to 70-90 ℃; put into the chemical fiber hairs that ties handle then, be incubated 30-60 minute proposes consistent with the sample mark; Fading is according to the look depth of fading chemical fiber hairs and the kind difference of raw material, and adding hydrogen peroxide 100-600%, ammoniacal liquor 10-60%, bleaching powder 0.4-2.5%, bath raio 1: 15, intensification 80-100 ℃ input tie the chemical fiber hairs of handle, act on 10-20 minute; Post processing is two kinds of consistent lubricants that add 2%-5% and 5%-10% respectively, and bath raio 1: 20, water temperature 20-30 ℃ are put into the chemical fiber hairs of cleaning and soaked 10-15 minute;

2. above-mentioned technology dyeing (fading) step is according to the needs of different three looks, can choose one and dye one and take off or two dye or two taking off dyeed respectively or faded two or one.