CN101117511A - 导静电耐蚀涂料生产方法 - Google Patents

导静电耐蚀涂料生产方法 Download PDF

Info

Publication number
CN101117511A
CN101117511A CNA2006100150517A CN200610015051A CN101117511A CN 101117511 A CN101117511 A CN 101117511A CN A2006100150517 A CNA2006100150517 A CN A2006100150517A CN 200610015051 A CN200610015051 A CN 200610015051A CN 101117511 A CN101117511 A CN 101117511A
Authority
CN
China
Prior art keywords
xylene
formaldehyde
stirring
hours
methanol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CNA2006100150517A
Other languages
English (en)
Inventor
张云波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Zhendong Paints Co Ltd
Original Assignee
Tianjin Zhendong Paints Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Zhendong Paints Co Ltd filed Critical Tianjin Zhendong Paints Co Ltd
Priority to CNA2006100150517A priority Critical patent/CN101117511A/zh
Publication of CN101117511A publication Critical patent/CN101117511A/zh
Withdrawn legal-status Critical Current

Abstract

一种导静电耐蚀涂料生产方法，将间二甲苯、甲醇、三氟化硼乙醚混合搅拌均匀，在100℃反应2小时，加入甲醛，并滴加硫酸，反应3小时，停止加热，自然冷却至室温，出料后静置沉降分离，甲醇回收，然后用氢氧化钠、水的溶液中和至pH值7；将苯酚、甲醛、氢氧化钡、间二甲苯甲醛树脂、甲醇混合搅拌均匀，在100℃反应1小时，抽真空脱水；将E42环氧树脂、间二甲苯酚醛树脂、有机硅树脂、邻苯酸二丁酯、正硅酸乙酯混合搅拌均匀，加入钛粉，搅拌均匀，然后加入无水乙醇、乙二胺搅拌均匀。本发明的优点：生产成本低、导静电性能稳定、耐蚀性能稳定、干固快、涂膜坚固、施工简便。

Description

导静电耐蚀涂料生产方法
技术领域
本发明涉及一种导静电耐蚀涂料生产方法。
背景技术
目前，导静电耐蚀涂料，生产成本高，导静电性能、耐蚀性能不稳定，施工复杂。
发明内容
本发明的目的在于克服上述的缺陷，提供一种导静电耐蚀涂料生产方法。
本发明的技术方案是：一种导静电耐蚀涂料生产方法，其特征在于：将8份E42环氧树脂、2份间二甲苯酚醛树脂、0.005份有机硅树脂、1份邻苯酸二丁酯、0.0035份正硅酸乙酯混合搅拌均匀，加入12份钛粉，搅拌均匀，然后加入4份无水乙醇、0.5份乙二胺搅拌均匀；将100份间二甲苯、12份甲醇、2份三氟化硼乙醚混合搅拌均匀，在100℃反应2小时，加入200份甲醛，并滴加4份硫酸，反应3小时，停止加热，自然冷却至室温，出料后静置沉降分离，甲醇回收，然后用氢氧化钠4份和8.5份水溶液中和至pH值7；将150份苯酚、80份甲醛、2.25份氢氧化钡、150份间二甲苯甲醛树脂、10份甲醇混合搅拌均匀，在100℃反应1小时，抽真空脱水。
本发明具有以下优点：生产成本低、导静电性能稳定、耐蚀性能稳定、干固快、涂膜坚固、施工简便。
具体实施方式
实施例：一种导静电耐蚀涂料生产方法，将间二甲苯100Kg、甲醇12Kg、三氟化硼乙醚2Kg混合搅拌均匀，在100℃反应2小时，加入甲醛200Kg，并滴加硫酸4Kg，反应3小时，停止加热，自然冷却至室温，出料后静置沉降分离，甲醇回收，然后用氢氧化钠4Kg、水8.5Kg的溶液中和至PH值7；将苯酚150Kg、甲醛80Kg、氢氧化钡2.25Kg、间二甲苯甲醛树脂150Kg、甲醇10Kg混合搅拌均匀，在100℃反应1小时，抽真空脱水；将E42环氧树脂8Kg、间二甲苯酚醛树脂2Kg、有机硅树脂0.005Kg、邻苯酸二丁酯1Kg、正硅酸乙酯0.0035Kg混合搅拌均匀，加入钛粉12Kg，搅拌均匀，然后加入无水乙醇4Kg、乙二胺0.5Kg搅拌均匀。

Claims (1)

1.一种导静电耐蚀涂料生产方法，其特征在于：将间二甲苯100Kg、甲醇12Kg、三氟化硼乙醚2Kg混合搅拌均匀，在100℃反应2小时，加入甲醛200Kg，并滴加硫酸4Kg，反应3小时，停止加热，自然冷却至室温，出料后静置沉降分离，甲醇回收，然后用氢氧化钠4Kg、水8.5Kg的溶液中和至PH值7；将苯酚150Kg、甲醛80Kg、氢氧化钡2.25Kg、间二甲苯甲醛树脂150Kg、甲醇10Kg混合搅拌均匀，在100℃反应1小时，抽真空脱水；将E42环氧树脂8Kg、间二甲苯酚醛树脂2Kg、有机硅树脂0.005Kg、邻苯酸二丁酯1Kg、正硅酸乙酯0.0035Kg混合搅拌均匀，加入钛粉12Kg，搅拌均匀，然后加入无水乙醇4Kg、乙二胺0.5Kg搅拌均匀。
CNA2006100150517A 2006-08-01 2006-08-01 导静电耐蚀涂料生产方法 Withdrawn CN101117511A (zh)