CN101063020A - 钢化瓷釉漆 - Google Patents

钢化瓷釉漆 Download PDF

Info

Publication number
CN101063020A
CN101063020A CNA2006100437521A CN200610043752A CN101063020A CN 101063020 A CN101063020 A CN 101063020A CN A2006100437521 A CNA2006100437521 A CN A2006100437521A CN 200610043752 A CN200610043752 A CN 200610043752A CN 101063020 A CN101063020 A CN 101063020A
Authority
CN
China
Prior art keywords
glaze paint
ceramic glaze
agent
tempering
paint according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2006100437521A
Other languages
English (en)
Other versions
CN100532477C (zh
Inventor
王健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2006100437521A priority Critical patent/CN100532477C/zh
Publication of CN101063020A publication Critical patent/CN101063020A/zh
Application granted granted Critical
Publication of CN100532477C publication Critical patent/CN100532477C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

钢化瓷釉漆，其特征在于以重量百分数计，组成为：含羟基丙烯酸树脂40～45、无机陶瓷颜料10～20、流平剂2～5、消泡剂0.5～5、防沉剂0.5～5、附着力增进剂5～10、分散剂5～10、填料5～15。本发明施工简单，可以用刷子刷涂或普通喷涂设备喷涂，具有瓷釉质的圆润、光滑、坚固、耐腐蚀等性能。经多次试验，耐低温－40℃～耐高温160℃范围内无异常变化；耐水性268小时无异常；耐碱性168小时无异常；耐洗刷性≥2000次；耐人工气候老化性1000小时不起泡、不剥落、无裂纹；施工刷涂二道无障碍；涂层耐温变性5次循环无异常。本产品价格低，寿命可达10年以上。

Description

钢化瓷釉漆
技术领域
本发明属于涂料领域，特别涉及一种钢化瓷釉漆。
背景技术
瓷砖主要用于建筑物内外墙壁的装饰和防护，瓷砖釉表面光滑，色泽艳丽，耐腐蚀能力强。但随着时间的推移，太阳的暴晒及大气环境的污染，瓷砖变旧龟裂失去原有的色彩和光泽，特别是受酸雨及海风浸蚀的外墙更是斑痕累累，严重影响美观和市容市貌。但是瓷砖和建筑物已结合为一体，已无法重新烧制。由于瓷砖外表十分光滑，一般涂料和油漆等很难长期附着在其表面，所以采用刷涂料的方式并不能解决问题。如果把旧瓷砖砸掉再重新装贴，既需要很多的人力和物力，又浪费时间和金钱，并且给周边的环境和交通造成很大的不便。
发明内容
本发明所要解决的技术问题是提供一种钢化瓷釉漆，可以直接喷涂在瓷砖表面，达到瓷砖釉的效果。
本发明钢化瓷釉漆，其特征在于以重量百分数计，组成为：含羟基丙烯酸树脂40～45、无机陶瓷颜料10～20、流平剂2～5、消泡剂0.5～5、防沉剂0.5～5、附着力增进剂5～10、分散剂5～10和填料5～15。
所述流平剂可以选择丙烯酸酯型流平剂(如牌号为MFAOH、MFPX50的产品)、蜡粉或特殊改性反应型聚硅氧烷(如牌号为DE2890、DE8380的产品)。
所述消泡剂可以选择破泡聚硅氧烷溶液如牌号861、891、非硅脱气消泡剂(组成为高分子量乙烯醚/酯共聚物)CFC-2000或硬脂酸钙。
所述防沉剂可以选择HFGEL系列有机膨润土变助剂140型或160型、聚酰胺防流挂(如牌号为CIMA240-20或290-20的产品)。
所述附着力增进剂可以选用硅烷(如牌号为KEPER 993)。
所述分散剂可以选择硬脂酸锌、硬脂酸铝或硬脂酸钡。
所述填料可以选择钛白粉、碳酸钙、氧化铝粉或天那水。
无机陶瓷颜料可以是市售的公知的各种陶瓷颜料产品，根据要求的颜色不同，选择适合的颜料，如金棕、铬绿等。
本发明在制作时，固体组分应在800目以上，陶瓷颜料在600目以上，具体的制作方法为：按照各原料配比，在不锈钢或搪瓷搅拌机内先放入含羟基丙烯酸树脂、无机陶瓷颜料，混合均匀，然后加入其它组分，慢速搅拌6～8小时，再装入不锈钢或搪瓷反应罐进行沉浮互渗4～6小时，最后加入到不锈钢研磨机内研磨4～6小时，放料，装入包装桶。
本发明产品的施工方法象通常的涂料一样只需常温刷涂或喷涂固化，即可达到瓷釉质的圆润、光滑、坚固、耐腐蚀等性能。
本发明的优点：
施工简单，可以用刷子刷涂或普通喷涂设备喷涂，具有瓷釉质圆润、光滑、坚固、耐腐蚀等性能。耐污性强，易清洗，解决了传统乳胶漆耐污差，不易清洗的弊病。经多次试验，耐低温-40℃～耐高温160℃范围内无异常变化；耐水性268小时无异常；耐碱性168小时无异常；耐洗刷性≥2000次；耐人工气候老化性1000小时不起泡、不剥落、无裂纹；施工刷涂二道无障碍；涂层耐温变性5次循环无异常。本产品价格低，寿命可达10年以上。
本发明产品还具有很强的防腐、防水能力，可广泛用于立交桥、钢结构、石化、电力等行业的罐装设备及管道，用于新楼房的装饰和防护。
以下为山东省涂料颜料产品质量检验中心对该产品样品的检验报告：
  序号   检验项目   单位   技术要求   检验结果   单项判定
  1   容器中状态   无硬块，搅拌后呈均匀状态   符合要求   合格
  2   施工性   刷涂二道无障碍   符合要求   合格
  3   干燥时间(表干)   ＜＜2   1   合格
  4   涂膜外观   正常   符合要求   合格
  5   对比率(白色和浅色)   ＞＞0.87   0.90   合格
  6   耐水性   168h无异常   符合要求   合格
  7   耐碱性   48h无异常   符合要求   合格
  8   耐洗刷性   次   ＞＞2000   ＞2000   合格
9   耐人工气候老化性   300h不起泡、不剥落、无裂纹   符合要求   合格
  粉化   级   ＜＜1   1   合格
  变色   级   ＜＜2   1   合格
  10   耐沾污性   ％   ＜＜15   13   合格
  11   涂层耐温变性(5次循环)   无异常   符合要求   合格
具体实施方式
以下实施例以重量份数计，本发明并不限于以下实施例。
实施例1：
含羟基丙烯酸树脂(牌号AH2870)    43
无机陶瓷颜料    15
丙烯酸酯型流平剂(MFAOH)    4
消泡剂：破泡聚硅氧烷溶液861    2
防沉剂：HFGEL系列有机膨润土变助剂140型    3
附着力增进剂：硅烷(KEPER993)    7
分散剂：硬脂酸锌    8
填料：钛白粉    10
实施例2：
含羟基丙烯酸树脂(牌号AH2870)    40
无机陶瓷颜料    10
流平剂：蜡粉(DE8418)    3
消泡剂：CFC-2000    0.5
防沉剂：HFGEL系列有机膨润土变助剂160型    1
附着力增进剂：硅烷(KEPER993)    5
分散剂：硬脂酸铝    5
填料：碳酸钙    5
实施例3：
含羟基丙烯酸树脂(牌号AH2870)    45
无机陶瓷颜料    20
流平剂：特殊改性反应型聚硅氧烷(DE2890)    5
消泡剂：硬脂酸钙    5
防沉剂：聚酰胺防流挂(CIMA240-20)    5
附着力增进剂：硅烷(KEPER993)    10
分散剂：硬脂酸钡    9
填料：氧化铝粉    12
实施例4：
含羟基丙烯酸树脂(牌号AH2870)    42
无机陶瓷颜料    16
流平剂：特殊改性反应型聚硅氧烷(DE8380)    2
消泡剂：硬脂酸钙    3
防沉剂：聚酰胺防流挂(CIMA290-20)    0.5
附着力增进剂：硅烷(KEPER993)    5
分散剂：硬脂酸锌    7
填料：天那水    8

Claims (7)

1、一种钢化瓷釉漆，其特征在于以重量百分数计，组成为：含羟基丙烯酸树脂40～45、无机陶瓷颜料10～20、流平剂2～5、消泡剂0.5～5、防沉剂0.5～5、附着力增进剂5～10、分散剂5～10和填料5～15。
2、根据权利要求1所述的钢化瓷釉漆，其特征在于所述流平剂为丙烯酸酯型流平剂、蜡粉或特殊改性反应型聚硅氧烷。
3、根据权利要求1所述的钢化瓷釉漆，其特征在于所述消泡剂为破泡聚硅氧烷溶液861、破泡聚硅氧烷溶液891、非硅脱气消泡剂CFC-2000或硬脂酸钙。
4、根据权利要求1所述的钢化瓷釉漆，其特征在于所述防沉剂为HFGEL系列有机膨润土变助剂140型或160型、聚酰胺防流挂CIMA240-20或290-20。
5、根据权利要求1所述的钢化瓷釉漆，其特征在于所述附着力增进剂为KEPER 993硅烷。
6、根据权利要求1所述的钢化瓷釉漆，其特征在于所述分散剂为硬脂酸锌、硬脂酸铝或硬脂酸钡。
7、根据权利要求1所述的钢化瓷釉漆，其特征在于所述填料为钛白粉、碳酸钙、氧化铝粉或天那水。
CNB2006100437521A 2006-04-28 2006-04-28 钢化瓷釉漆 Expired - Fee Related CN100532477C (zh)