CN1603375A - 一种聚氨酯仿幕墙涂料 - Google Patents

一种聚氨酯仿幕墙涂料 Download PDF

Info

Publication number
CN1603375A
CN1603375A CN 03151449 CN03151449A CN1603375A CN 1603375 A CN1603375 A CN 1603375A CN 03151449 CN03151449 CN 03151449 CN 03151449 A CN03151449 A CN 03151449A CN 1603375 A CN1603375 A CN 1603375A
Authority
CN
China
Prior art keywords
component
imitates
curtain wall
wall coating
following constituent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 03151449
Other languages
English (en)
Inventor
陈寿生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Chenchen Chemical Industry Co Ltd
SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd
Shanghai Fuchen Chemical Co Ltd
Original Assignee
Beijing Chenchen Chemical Industry Co Ltd
SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd
Shanghai Fuchen Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Chenchen Chemical Industry Co Ltd, SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd, Shanghai Fuchen Chemical Co Ltd filed Critical Beijing Chenchen Chemical Industry Co Ltd
Priority to CN 03151449 priority Critical patent/CN1603375A/zh
Publication of CN1603375A publication Critical patent/CN1603375A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种聚氨酯仿幕墙涂料，其特征在于：由A、B两组份构成，A组份有下列组成物及重量百分比组成：羟基丙烯酸树脂40.0％～73.0％，防沉剂0.1％～0.6％，有机溶剂5.2％～7.2％，助剂1.8％～3.8％，颜料15.0％～35.0％，B组份有下列组成物及重量百分比组成：六亚甲基二异氰酸酯55.0％～85.0％，醋酸丁酯15.0％～45.0％，甲组份与乙组份按6～8∶1比例混和配比。本发明的优点是其具有乳胶漆难以达到仿石材、仿镜面、仿铝板和仿木纹效果。

Description

一种聚氨酯仿幕墙涂料
技术领域
本发明涉及一种建筑涂料，特别是一种聚氨酯仿幕墙涂料。
背景技术
目前建筑物表面的装饰，通常采用石材、板材、瓷砖、马赛克和乳胶漆等建筑材料。石材、铝板成本高，施工难，色泽简单，大量浪费能源，不环保；瓷砖和马赛克的缺陷是防水效果差、不易清洗、易脱落；乳胶漆难以达到近似石材、镜面、铝板和木纹效果。
发明内容
本发明的目的是解决现有技术中乳胶漆所存在的问题，提供一种可用于建筑物表面装饰的涂料，其具有乳胶漆难以达到仿石材、仿镜面、仿铝板和仿木纹效果。本发明设计一种聚氨酯仿幕墙涂料，其特征在于：由A、B两组份构成，
A组份有下列组成物及重量百分比组成：
羟基丙烯酸树脂                  40.0％～73.0％，
防沉剂                          0.1％～0.6％，
有机溶剂                        5.2％～7.2％，
助剂                            1.8％～3.8％，
颜料                            15.0％～35.0％，
B组份有下列组成物及重量百分比组成：
六亚甲基二异氰酸酯              55.0％～85.0％，
醋酸丁酯                        15.0％～45.0％，
甲组份与乙组份按6～8∶1比例混和配比。羟基丙烯酸树脂也可以是聚醚多元醇、改性醇酸树脂或羟基丙烯酸树脂、聚醚多元醇、改性醇酸树脂的混合物。有机溶剂为醋酸乙酯、甲基异丁基酮等或它们的混合物。助剂为分散剂efka-4050、消泡剂BYK141或它们的混合物。本发明的优点是其具有乳胶漆难以达到仿石材、仿镜面、仿铝板和仿木纹效果。
下面结合实施例对本发明作详细说明，
具体实施方式
本发明主要利用配方中的羟基丙烯酸树脂(或聚醚多元醇、改性醇酸树脂)、有机溶剂、涂料助剂、钛白粉(或其它颜料、染料)、消光剂、固化剂等，对经建筑专用腻子处理后的建筑物表面进行涂装，使建筑物表面达到类似的幕墙装饰效果。
经检测，主要质量技术指标如下：
    序号 检验项目 技术指标 检验结果
    1     干燥时间，h     ≤2   1
    2     对比率(白色及浅色)     ≥0.93   0.96
    3     耐水性(168h)     无异常   无异常
    4     耐碱性(48h)     无异常   无异常
    5     耐洗刷性，次     ≥5000   超5000
6     耐人工老化性粉化，≤1级变色，≤2级     1000h不起泡、不剥落、无裂纹 1000h1级变色，无粉化
    7     耐沾污性(白色和浅色)，％     ≤10   2
    8     涂层耐温变性(5次循环)     无异常   无异常
9 粘结强度，MPa   标准     ＞0.5   0.54
  浸水后     ＞0.3   1.0
取羟基丙烯酸树脂60千克，防沉剂(6901-20X)0.6千克，有机溶剂(醋酸乙酯)6千克，助剂(分散剂efka-4050、消泡剂BYK141或它们的混合物)2.4千克，颜料(钛白粉)31千克，再取六亚甲基二异氰酸酯10千克，醋酸丁酯2.5千克，在高速分散机中混合均匀。施工时可根据具体情况加入适量的溶剂调节粘度。本发明的涂装工艺要求为，调好聚氨酯仿幕墙涂料，用喷涂或刷涂的方法施工。

Claims (4)

1、一种聚氨酯仿幕墙涂料，其特征在于：由A、B两组份构成，
A组份有下列组成物及重量百分比组成：
羟基丙烯酸树脂                    40.0％～73.0％，
防沉剂                            0.1％～0.6％，
有机溶剂                          5.2％～7.2％，
助剂                              1.8％～3.8％，
颜料                              15.0％～35.0％，
B组份有下列组成物及重量百分比组成：
六亚甲基二异氰酸酯                55.0％～85.0％，
醋酸丁酯                          15.0％～45.0％，
甲组份与乙组份按6～8∶1比例混和配比。
2、权利要求1所述的一种聚氨酯仿幕墙涂料，其特征在于：羟基丙烯酸树脂也可以是聚醚多元醇、改性醇酸树脂或羟基丙烯酸树脂、聚醚多元醇、改性醇酸树脂的混合物。
3、权利要求1所述的一种聚氨酯仿幕墙涂料，其特征在于：有机溶剂为醋酸乙酯、甲基异丁基酮等或它们的混合物。
4、权利要求1所述的一种聚氨酯仿幕墙涂料，其特征在于：助剂为分散剂efka-4050、消泡剂BYK141或它们的混合物。
CN 03151449 2003-09-29 2003-09-29 一种聚氨酯仿幕墙涂料 Pending CN1603375A (zh)