CN101062830A - Stone-pseudo glass mosaic and preparation method thereof - Google Patents
Stone-pseudo glass mosaic and preparation method thereof Download PDFInfo
- Publication number
- CN101062830A CN101062830A CN 200610079000 CN200610079000A CN101062830A CN 101062830 A CN101062830 A CN 101062830A CN 200610079000 CN200610079000 CN 200610079000 CN 200610079000 A CN200610079000 A CN 200610079000A CN 101062830 A CN101062830 A CN 101062830A
- Authority
- CN
- China
- Prior art keywords
- glass
- seals
- stone
- paste used
- red ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparing method of imitated stone glass mosaic, which comprises the following steps: allocating 20-100 wt coloring material, 20-80 wt white material, 20-80 wt water-based stamp-pad ink, 100wt glass special-purpose bottom white and 60 wt water-based stamp-pad ink; designing pattern slice; drying net; proceeding large size glass cut; coloring on the small size glass; printing bottom white, color frit and bottom closing glue consecutively; cutting; bedding board; burning; edging; sorting; packing; getting the product. This invention adopts multiplex printing craft, which possesses special granolithic effect.
Description
Technical field
The present invention relates to the inorganic silicate technical field, specifically, is a kind of stone-pseudo glass mosaic and preparation method thereof.
Background technology
Usually, mosaic is formed a relative syphon by the brick of tens of fritters.It is small and exquisite, bright-colored indoor small area ground, metope and outdoor big slightly metope and the ground of being widely used in of color.According to the surface treatment difference, can be divided into two kinds of no glaze and glazings.No glaze mosaic is the entire body mosaic again, and is wear-resisting, unfortunately surface irregularity, unglazed, water-intake rate is bigger.The glaze of glazing ceramic mosaic is thick, brightness is high, the gap is even, is present main flow ceramic mosaic.But also do not see the mosaic product of imitative stone effect in the market.
Summary of the invention
The objective of the invention is to, a kind of stone-pseudo glass mosaic and preparation method thereof is provided.
In order to realize above-mentioned goal of the invention, technical scheme of the present invention is:
A kind of stone-pseudo glass mosaic is printed on glass making by the raw material of following weight part: colorant 20-100 part, expect 20-80 part, water-based stamp-pad ink 20-80 part, white 100 parts of the special-purpose end of glass, 60 parts of water-based stamp-pad ink in vain.
Described colorant 20-100 part, expect 20-80 part, water-based stamp-pad ink 20-80 part in vain, formed colour glaze jointly; White 100 parts of the special-purpose end of described glass, water-based stamp-pad ink have been formed the end for 60 parts and have been expected in vain.
Preferably, colorant is that 80 weight parts, white material are 20 weight parts, water-based stamp-pad ink 50 weight parts.
The preparation method of this stone-pseudo glass mosaic is the pattern slice according to design, carries out large stretch of glass cutting after shining net, then at small pieces red ink paste used for seals on glass, prints the end material, colour glaze and back cover glue in vain successively; Burn till behind cutting, the bed board, packing promptly after last edging, the sorting.
810 ± 5 ℃ of described temperature of burning till, the time is 50 minutes.
Described red ink paste used for seals is 3-8 time.Red ink paste used for seals is that web plate is placed Hua Jishang, treats to carry out red ink paste used for seals next time again after the last red ink paste used for seals drying.
The invention has the advantages that:
Stone-pseudo glass mosaic of the present invention, owing to adopt multiple tracks red ink paste used for seals technology, thereby have special imitative stone effect.
Embodiment
Below providing specific embodiment further specifies.The purpose of these embodiment is illustrative, and should not be construed as limitation of the present invention.
Embodiment 1
Get the deep blue colorant 80kg of the raw material of following weight: G221, the Y203 ceramic printing is expected 20kg, Y305 water-based stamp-pad ink 50kg in vain, the three has formed colour glaze; The special-purpose white 100kg in the end of glass, Y305 water-based stamp-pad ink 60kg, the two has been formed the end and has expected in vain.
According to the pattern slice of design, carry out large stretch of glass cutting after shining net, then at small pieces red ink paste used for seals on glass, print successively the end expect in vain, red ink paste used for seals glaze 5 times and seal back cover glue; Burnt till 50 minutes at 810 ℃ behind cutting, the bed board, packing promptly gets the glass Mosaic finished product with imitative stone effect after last edging, the sorting.
Red ink paste used for seals is that web plate is placed Hua Jishang, treats to carry out red ink paste used for seals next time again after the last red ink paste used for seals drying.
The main component of the deep blue colorant of G221 has: cobalt oxide, cupric oxide, silicon-dioxide and potassium oxide; The main component of the white material of Y203 ceramic printing has: zirconium silicate, silicon-dioxide, fusing assistant; The main component of Y305 water-based stamp-pad ink has: polyacrylic resin, emulsifying agent, film coalescence aid, subtract the swelling thickening material; White main component has at the glass special-purpose end: stannic oxide, zirconium silicate, potassium oxide, silicon-dioxide.
Embodiment 2
Get the deep blue colorant 20kg of the raw material of following weight: G221, the Y203 ceramic printing is expected 50kg, Y305 water-based stamp-pad ink 80kg in vain, the three has formed colour glaze; The special-purpose white 100kg in the end of glass, Y305 water-based stamp-pad ink 60kg, the two has been formed the end and has expected in vain.
According to the pattern slice of design, carry out large stretch of glass cutting after shining net, then at small pieces red ink paste used for seals on glass, print successively the end expect in vain, red ink paste used for seals glaze 3 times and seal back cover glue; Burnt till 50 minutes at 805 ℃ behind cutting, the bed board, packing promptly gets the glass Mosaic finished product with imitative stone effect after last edging, the sorting.
Red ink paste used for seals is that web plate is placed Hua Jishang, treats to carry out red ink paste used for seals next time again after the last red ink paste used for seals drying.
Embodiment 3
Get the deep blue colorant 100kg of the raw material of following weight: G221, the Y203 ceramic printing is expected 80kg, Y305 water-based stamp-pad ink 20kg in vain, the three has formed colour glaze; The special-purpose white 100kg in the end of glass, Y305 water-based stamp-pad ink 60kg, the two has been formed the end and has expected in vain.
According to the pattern slice of design, carry out large stretch of glass cutting after shining net, then at small pieces red ink paste used for seals on glass, print successively the end expect in vain, red ink paste used for seals glaze 8 times and seal back cover glue; Burnt till 50 minutes at 815 ℃ behind cutting, the bed board, packing promptly gets the glass Mosaic finished product with imitative stone effect after last edging, the sorting.
Red ink paste used for seals is that web plate is placed Hua Jishang, treats to carry out red ink paste used for seals next time again after the last red ink paste used for seals drying.
More than stone-pseudo glass mosaic provided by the present invention and preparation method thereof is described in detail, used specific case herein principle of the present invention and embodiment are set forth, the explanation of above embodiment just is used for helping to understand method of the present invention and core concept thereof; Simultaneously, for one of ordinary skill in the art, according to thought of the present invention, the part that all can change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (6)
1. a stone-pseudo glass mosaic is characterized in that, is printed on glass making by the raw material of following weight part: colorant 20-100 part, expect 20-80 part, water-based stamp-pad ink 20-80 part, white 100 parts of the special-purpose end of glass, 60 parts of water-based stamp-pad ink in vain.
2. glass band course according to claim 1 is characterized in that: colorant is that 80 weight parts, white material are 20 weight parts, water-based stamp-pad ink 50 weight parts.
3. the preparation method of the described stone-pseudo glass mosaic of claim 1 is characterized in that, according to the pattern slice of design, carries out large stretch of glass cutting after shining net, then at small pieces red ink paste used for seals on glass, prints the end material, colour glaze and back cover glue in vain successively; Burn till behind cutting, the bed board, packing promptly after last edging, the sorting.
4. the preparation method of stone-pseudo glass mosaic according to claim 3, it is characterized in that: described temperature of burning till is 810 ± 5 ℃, the time is 50 minutes.
5. the preparation method of stone-pseudo glass mosaic according to claim 3, it is characterized in that: described red ink paste used for seals is 3-8 time.
6. the preparation method of stone-pseudo glass mosaic according to claim 3, it is characterized in that: described red ink paste used for seals is that web plate is placed Hua Jishang, treats to carry out red ink paste used for seals next time again after the last red ink paste used for seals drying.