CN101058695A - 用于金属的涂料 - Google Patents
用于金属的涂料 Download PDFInfo
- Publication number
- CN101058695A CN101058695A CN 200710057555 CN200710057555A CN101058695A CN 101058695 A CN101058695 A CN 101058695A CN 200710057555 CN200710057555 CN 200710057555 CN 200710057555 A CN200710057555 A CN 200710057555A CN 101058695 A CN101058695 A CN 101058695A
- Authority
- CN
- China
- Prior art keywords
- polyamide
- main body
- cresol
- coupling agent
- main
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种成本低、强度高的用于金属的涂料。本发明用于金属的涂料,包括以下组分按下述重量百分比组成:主体料85-90%、偶联剂7-10%、颜料3-8%;所述主体料由15%-23%的主体固化物、40-50%的主溶剂和35-40%的助溶剂组成;所述主体固化物为聚酰胺(PA)、聚酰胺(PA6)、聚酰胺(PA66)、聚酰胺(PA610)、聚酰胺(PA1010、聚酰胺(PA12)中的任意一种;所述主溶剂为间甲酚、间对甲酚、三混甲酚、苯酚中的一种或几种;所述助溶剂为二甲苯、甲苯、二甲基甲酰胺、丁醇、乙二醇乙醚、乙二醇丁醚中的一种或几种;所述偶联剂为环氧聚硅烷(THO-501、THO-502)。本发明用于金属丝上更能突出其优异的物理及化学性能。
Description
技术领域
本发明涉及化学涂料领域,更具体地说,是涉及一种用于金属表面的涂料。
背景技术
随着金属制品的不断增多,以及金属材料广泛用于各行业,随之用于对金属材料表面进行加工处理的涂料材料需求也在增加,但目前的金属涂料普遍存在制造成本高、附着力差的缺陷,不能满足现有市场对金属涂料的需求。对于金属丝外表的防腐、装饰、耐久及易于使用等方面更需要一种特殊性能的外表涂层。
发明内容
本发明所要解决的技术问题是,克服现有技术中存在的不足,提供一种成本低、强度高的用于金属的涂料。
本发明用于金属的涂料,通过下述技术方案予以实现,所述涂料包括以下组分按下述重量百分比组成:主体料85-90%、偶联剂7-10%、颜料3-8%;
所述主体料由15%-23%的主体固化物、40-50%的主溶剂和35-40%的助溶剂组成;
所述主体固化物为聚酰胺(PA)、聚酰胺(PA6)、聚酰胺(PA66)、聚酰胺(PA610)、聚酰胺(PA1010、聚酰胺(PA12)中的任意一种;
所述主溶剂为间甲酚、间对甲酚、三混甲酚、苯酚中的一种或几种;
所述助溶剂为二甲苯、甲苯、二甲基甲酰胺、丁醇、乙二醇乙醚、乙二醇丁醚中的一种或几种;
所述偶联剂为环氧聚硅烷(THO-501、THO-502)。
本发明根据不同需要可调制不同颜色,根据用户要求,从色板上选取色号,可进行调制,一般有白、黑、红、兰、黄、绿、紫等以及它们的合成色,另外可制成金、银、铜、珠光、荧光等特殊色。采用颜料在有机、无机中选择,当然选择相溶性越高者品质越好,色泽越鲜艳。
本发明是一种特用涂料,它可以涂附在钢、铁、铁镀锌、铁镀镍、铁镀铬等丝网上,可以附在铜、银、金等金属丝、箔上。本发明形成的涂层坚韧并且强度高,耐磨性优良,绕曲性优良突出,在金属上附着力强,表面光滑,光亮度很好,并兼有优良的耐酸、碱性,在日光下耐紫外线很好。本发明用于金属丝上更能突出其优异的物理及化学性能。
本发明中除主体料外,具有关键作用的偶联剂所带有的化学官能团与主体固化物中聚酰胺基在适宜的加工条件下发生反应,偶联成网状结构而形成坚硬的漆膜。
具体实施方式
下面结合实施例对本发明做进一步描述。
实施例1:
主体固化物为聚酰胺(PA):18kg
主溶剂:苯酚39kg
助溶剂:二甲苯36kg
偶联剂:7kg
将上述组分混匀即可,然后使用浸涂法,用自流或磨具更好,干燥用烘烤热干法,经过固定的烘炉或通道,除掉溶剂,使之经过化学交联固化形成坚韧的膜层而成型。
实施例2:
主体固化物为PA6:20kg
主溶剂:三混甲酚40kg
助溶剂:二甲基甲酰氨20kg、丁醇12kg
偶联剂:8kg
实施例3:
主体固化物为PA66:16kg
主溶剂:苯酚20kg、间对甲酚19kg
助溶剂:二甲苯18kg、乙二醇乙醚15kg
偶联剂:9kg
白色颜料:3kg
实施例4:
主体固化物为PA610:12kg
主溶剂:苯酚36kg
助溶剂:二甲苯16kg、乙二醇丁醚17kg
偶联剂:8kg
红色颜料:5kg
实施例5:
主体固化物为PA1010:15kg
主溶剂:苯酚20kg、三混甲酚20kg
助溶剂:二甲苯15kg、丁醇14kg
偶联剂:10kg
黄色颜料:8kg
上面所述的实施例仅仅是对本发明优选实施方式进行描述,并非对本发明的构思和范围进行限定,在不脱离本发明设计思想的前提下,本领域中普通工程技术人员对本发明的技术方案作出的各种变形和改进,均应属于本发明的保护范围。
Claims (1)
1.一种用于金属的涂料,其特征是,所述涂料包括以下组分按下述重量百分比组成:主体料85-90%、偶联剂7-10%、颜料3-8%;
所述主体料由15%-23%的主体固化物、40-50%的主溶剂和35-40%的助溶剂组成;
所述主体固化物为聚酰胺、聚酰胺6、聚酰胺66、聚酰胺610、聚酰胺1010、聚酰胺12中的任意一种;
所述主溶剂为间甲酚、间对甲酚、三混甲酚、苯酚中的一种或几种;
所述助溶剂为二甲苯、甲苯、二甲基甲酰胺、丁醇、乙二醇乙醚、乙二醇丁醚中的一种或几种;
所述偶联剂为环氧聚硅烷。