CN101053965A - Archaizing processing technology for environment protection type wooden furniture decorative board - Google Patents
Archaizing processing technology for environment protection type wooden furniture decorative board Download PDFInfo
- Publication number
- CN101053965A CN101053965A CN 200710107243 CN200710107243A CN101053965A CN 101053965 A CN101053965 A CN 101053965A CN 200710107243 CN200710107243 CN 200710107243 CN 200710107243 A CN200710107243 A CN 200710107243A CN 101053965 A CN101053965 A CN 101053965A
- Authority
- CN
- China
- Prior art keywords
- sheet material
- lime
- processing technology
- dalle
- colouring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to an archaistic processing technology for environmental protection wooden furniture dalle. The dalle is processed by sintering using quicklime, and then the tintage, disinsection and sterilization process are finished. More specifically, the dalle is immersed into a heating pool of quicklime added with water to be sintered. The dalle after sintering using quicklime can be used for manufacturing top grade furniture, decorating material, indoor wood door and musical instrument. The present invention is environmental friendly, the indoor furniture and decorating material will not release harmful gas and off odour, which is favor for the health of human body. In the present invention, the course of processing will not pollute environment, the dalle will not deform or crack with a high density. The environmental protection dalle mainly has three colors that is red, yellow and black, and has a lines feature of more wiping brighter.
Description
Technical field
The present invention relates to the surface treatment method of wood-based planet, be specifically related to a kind of treatment process method that makes wood furniture decoration board have antique effect.Belong to International Classification of Patents B27M " timber processing " and " manufacturing of extraordinary woodwork " technical field.
Background technology
At the fifties, occurred exceeding a century and the solid wood furniture of not painting, but this so far thenceforth furniture just made no public appearances, lost because of this technology, people have no way of seeing, buy, enjoying the furniture of this ancient system on market.Furniture in the market mostly is composite plate series in the ornament materials, the chemical gas that discharges is harmful to health.Entered since 21 century, country vigorously advocates environmental consciousness, and all are from the angle of environmental protection and consider.In period in ancient times, people adopted lime, salt, food alkali, the bittern of making bean product and dyestuff to handle sheet material, and this former at first simple and unsophisticated processing method provides research thinking that forget for a long time, uncared-for for the people of current era.
Summary of the invention
Purpose of the present invention is to remedy the shortage of prior art, provides a kind of deep processing by secondary to handle, and makes sheet material have the archaizing processing technology of the environment protection type wooden furniture decorative board of color and luster modelled after an antique and breath.
The objective of the invention is to be achieved through the following technical solutions.
A kind of archaizing processing technology of environment protection type wooden furniture decorative board is to utilize to give birth to the whitewash burning bubble machining sheet that lime is made, and carries out the colouring and the Pesticidal and sterilizing of sheet material.Detailed process is: 300 kilogram of raw limes are joined in 1 ton the clear water, in tank with heating apparatus or pond, carry out efflorescence, chemical reaction takes place, be the gruel shape, put into sheet material and burn bubble, and the temperature in control tank or the pond is at 90 ℃-95 ℃, reach 0.6mm-1.0mm until the last color depth of sheet material, take out sheet material, finish colouring for the first time.
In 50 ℃-60 ℃ whitewash, the above-mentioned sheet material of having finished the burning bubble first time is put into the pond heat; In addition the living lime piece of about 500 grams of weight is put into heating cabinet and heat, to 50 ℃-60 ℃; Sheet material is picked up, select wood grain one to face up and be placed on the workbench preferably, the living lime piece that heat is got wet, place dry combustion method on the described plate surface equably, make the shank that burns out multiple pattern on the plate surface colored; Then sheet material is moved in the moist closet of stuffy, no sunlight, dehydration is 5 naturally, dries after the dehydration again, makes sheet material reach the use standard.
Described living lime is meant the piece lime, and lime is fired in kiln by lime stone and formed, in kiln burned after, the proterties of lime stone does not have big change, but after adding water for the piece lime, it i.e. efflorescence apace, becomes the lime face; In Hebei province and offshore Qinhuangdao inside the province, the Funing County utilizes lime kiln to produce lime in a large number, can become the source place of raw material.
Described sheet material is from multiple fruit tree, as mahogany, apricot wood, chestnut; After the colouring first time of sheet material, former mahogany sheet material becomes redness, and the apricot wood plank becomes golden yellow, and chestnut sheet material becomes black, and the last color depth of sheet material was 0.6mm-1.0mm after colouring was finished for the first time; After utilizing living lime piece sheet material to be advanced secondary colouring and dry combustion method, can make plate surface the shank flower of multiple pattern occur.
The sheet material that utilizes the inventive method to make can be produced top-grade furniture, ornament materials, indoor timber, musical instrument.The environmental consciousness that the present invention advocates based on country, the protection people health is without prejudice, make indoor furniture and ornament materials not discharge pernicious gas and peculiar smell, technology combines at all times, process can not cause environmental pollution, sheet material after the processing is modification, crack not, has increased material density; And Pesticidal and sterilizing.That color mostly is is red, yellow, black three looks, has the environment-friendly type new material of the bright more former patterned feature of wiping more.The present invention is the sheet material treatment technology of a kind of not painting and direct colouring.
The specific embodiment
At first, will give birth to lime and put into burning bubble pond, add clear water, promptly present the gruel shape after the lime efflorescence.With the sheet material that same wood is planted, it is identical to get thickness, through polishing and grinded sheet material, put into the pond and burn bubble, the temperature in the burning bubble pond is given time enough at 90 ℃-95 ℃, last color depth until sheet material reaches 0.6mm-1.0mm, takes out sheet material, finishes colouring for the first time.Sheet material is tripped out, stand-by.The ratio of lime and clear water of giving birth to is joined 1 ton of clear water about the living lime of 300KG.
Preparation is similar to above-mentioned whitewash in tank in addition, and the ratio of giving birth to lime reduces, and concentration is rarer.Water temperature is at 50 ℃-60 ℃ in the groove, and sheet material is immersed, be warming up to tank in consistent water temperature, promptly 50 ℃-60 ℃.
Trip out sheet material, select attractive in appearance one the facing up and be placed on the workbench of wood grain, the living lime piece that heat is got wet, place dry combustion method on the described plate surface equably, make the shank that burns out multiple pattern on the plate surface colored, last color depth does not become.Wash the lime of plate surface off, then sheet material is moved in the moist closet of stuffy, no sunlight, dehydration is 5 naturally, dries after the dehydration again; When temperature reaches 35 ℃, ventilate once, make sheet material reach the use standard.
Can carry out the processing of plate surface subsequently---polishing, grinded sheet material can be made product, and is anti-dried, damp proof for preventing the aging of sheet material color, can bake wax to sheet material and handle.Density, hardness and the color of reply sheet material are carried out reasonably combined when needing.
The sheet material of above-mentioned processing has at first solved colouring, cracking, the problem on deformation of sheet material, Pesticidal and sterilizing, and strengthened the density and the hardness of sheet material.By the secondary deep processing, changed the color of plate face, it is very fine and smooth that the plate face seems.Can make high-grade solid wood furniture, ornament materials and musical instrument.
About the burning bubble time of sheet material, the sheet material of different-thickness needs the different colouring time, and once Shang Se time is as follows:
Sheet metal thickness 50-100mm, no matter the length of sheet material and width, burning the bubble time is 48 hours, and temperature is 90-95 ℃ in the pond, and the last color depth of sheet material is 0.6-1.0mm.
Sheet metal thickness 150-200mm, burning the bubble time is 72 hours, and temperature is 90-95 ℃ in the pond, and the last color depth of sheet material is 0.6-1.0mm.
Sheet metal thickness 250-300mm, burning the bubble time is 96 hours, and temperature is 90-95 ℃ in the pond, and the last color depth of sheet material is 0.6-1.0mm.
Sheet metal thickness 350-400mm, burning the bubble time is 120 hours, and temperature is 90-95 ℃ in the pond, and the last color depth of sheet material is 0.6-1.0mm.
Sheet material is gone into the warm-up time in pond for the second time:
Sheet metal thickness 50-100mm, no matter the length of sheet material and width, temperature is 50-60 ℃ in the tank, the warm-up time that sheet material is gone into the pond is half an hour.Quick lime is heated to 50-60 ℃ in heating cabinet, trips out sheet material, select the good one side of wood grain upwards to be placed on the workbench.To give birth to dry combustion method on the surface that places sheet material after the lime piece gets wet equably, finish after the thorough efflorescence of living lime.The efflorescence time is about 30 minutes.Then sheet material is moved on to the indoor dehydration 5 days of stuffy, no sunlight, dry again; When temperature reaches 35 ℃, ventilate once, make sheet material reach the use standard.
Temperature is 50-60 ℃ in the sheet metal thickness 150-200mm, tank, and it is 40 minutes that sheet material is gone into the pond warm-up time.Quick lime is heated to 50-60 ℃ in heating cabinet, trips out sheet material, select the good one side of wood grain upwards to be placed on the workbench.To give birth to dry combustion method on the surface that places sheet material after the lime piece gets wet equably, finish after the thorough efflorescence of living lime.The efflorescence time is about 30 minutes.Then sheet material is moved on to the indoor dehydration 5 days of stuffy, no sunlight, dry again; When temperature reaches 35 ℃, ventilate once, make sheet material reach the use standard.
Temperature is 50-60 ℃ in the sheet metal thickness 250-300mm, tank, and it is 50 minutes that sheet material is gone into the pond warm-up time.Quick lime is heated to 50-60 ℃ in heating cabinet, trips out sheet material, select the good one side of wood grain upwards to be placed on the workbench.To give birth to dry combustion method on the surface that places sheet material after the lime piece gets wet equably, finish after the thorough efflorescence of living lime.The efflorescence time is about 30 minutes.Then sheet material is moved on to the indoor dehydration 5 days of stuffy, no sunlight, dry again; When temperature reaches 35 ℃, ventilate once, make sheet material reach the use standard.
Temperature is 50-60 ℃ in the sheet metal thickness 350-400mm, tank, and it is 1 hour that sheet material is gone into the pond warm-up time.Quick lime is heated to 50-60 ℃ in heating cabinet, trips out sheet material, select the good one side of wood grain upwards to be placed on the workbench.To give birth to dry combustion method on the surface that places sheet material after the lime piece gets wet equably, finish after the thorough efflorescence of living lime.The efflorescence time is about 30 minutes.Then sheet material is moved on to the indoor dehydration 5 days of stuffy, no sunlight, dry again; When temperature reaches 35 ℃, ventilate once, make sheet material reach the use standard.
Claims (4)
1. the archaizing processing technology of an environment protection type wooden furniture decorative board is characterized in that: be to utilize to give birth to the whitewash burning bubble machining sheet that lime is made, carry out the colouring and the Pesticidal and sterilizing of sheet material; Detailed process is: 300 kilogram of raw limes are joined in 1 ton the clear water, in tank with heating apparatus or pond, carry out efflorescence, chemical reaction takes place, be the gruel shape, puts into sheet material and burn bubble, and the temperature in control tank or the pond is at 90 ℃-95 ℃, reach 0.6mm until the last color depth of sheet material---1.0mm, take out sheet material, finish colouring for the first time.
2. the archaizing processing technology of environment protection type wooden furniture decorative board according to claim 1 is characterized in that: in 50 ℃-60 ℃ whitewash, the above-mentioned sheet material of having finished the burning bubble first time is put into the pond heat; In addition the living lime piece of about 500 grams of weight is put into heating cabinet and heat, to 50 ℃-60 ℃; Sheet material is picked up, select wood grain one to face up and be placed on the workbench preferably, the living lime piece that heat is got wet, place dry combustion method on the described plate surface equably, make the shank that burns out multiple pattern on the plate surface colored; Then sheet material is moved in the moist closet of stuffy, no sunlight, dehydration is 5 naturally, dries after the dehydration again, makes sheet material reach the use standard.
3. the archaizing processing technology of environment protection type wooden furniture decorative board according to claim 1, it is characterized in that: described living lime, be meant the piece lime, lime is fired in kiln by lime stone and is formed, in kiln burned after, the proterties of lime stone does not have big change, but after adding water for the piece lime, it i.e. efflorescence apace, becomes the lime face; In Hebei province and offshore Qinhuangdao inside the province, the Funing County utilizes lime kiln to produce lime in a large number, can become the source place of raw material.
4. the archaizing processing technology of environment protection type wooden furniture decorative board according to claim 1, it is characterized in that: described sheet material is from multiple fruit tree, as mahogany, apricot wood, chestnut; After the colouring first time of sheet material, former mahogany sheet material becomes redness, and the apricot wood plank becomes golden yellow, and chestnut sheet material becomes black, and the last color depth of sheet material was 0.6mm-1.0mm after colouring was finished for the first time; After utilizing living lime piece sheet material to be advanced secondary colouring and dry combustion method, can make plate surface the shank flower of multiple pattern occur.