CN104861722A - Preparation formula and production method for peacock blue wheat straw dye - Google Patents
Preparation formula and production method for peacock blue wheat straw dye Download PDFInfo
- Publication number
- CN104861722A CN104861722A CN201410063961.7A CN201410063961A CN104861722A CN 104861722 A CN104861722 A CN 104861722A CN 201410063961 A CN201410063961 A CN 201410063961A CN 104861722 A CN104861722 A CN 104861722A
- Authority
- CN
- China
- Prior art keywords
- wheat straw
- raw material
- solution
- parts
- mineral water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A preparation formula and production method for a peacock blue wheat straw dye are provided; with polygonum tinctorium, blueberry, lavender, palaquium formosanum leaves, alumen, an iron ion compound solution and mineral water as main raw materials, the production method comprises the main technological processes of material selection, material cutting, drying, soaking, hot boiling, mixing, precipitating, dyeing and finished product obtaining. Provided are the preparation formula and the production method for the peacock blue wheat straw dye which is prepared from purely-natural plants, is purely natural, pollution-free, green and environmentally friendly and has no toxic or side effect to human bodies.
Description
technical field:
the present invention relates to a kind of vegetable dye, particularly relates to one and prepares green rust wheat straw dye and production method.
background technology:
industrial art refers to that daily living article is after art up process, makes it the product with strong aesthetic value.We are generally the industrial art that industrial art is divided into the practical art fine arts and furnishings to appreciate.The practical art fine arts are main body and the basis of whole industrial art, comprise clothing, food, change, row, arts and crafts, practical value is the chief value of this kind of artwork, and aesthetic value exists as auxiliary value.This kind of artwork comprises tea tableware, light fixture, wood furniture, embroidered article, careless plaited bamboo articles etc. through decorative processing.Furnishings are appreciated artwork and are referred to that those are based on ornaments, the artwork viewing and admiring function, and this kind of artwork is primarily worth for it with aesthetic, and manual skill is very strong, as jadeware, jewel, ivory carving, cloisonne, lacquerware, wall hanging, pottery art etc.
china's industrial art with a long history is a bright jewel in China's culture treasure-house, plain well-known in the world.Industrial art originates from the epoch that the mankind start fabrication tool.Industrial art is that working people directly creates mostly, and the material life with people is closely related with cultural life.Its generation, often because of period of history, geographical environment, economic condition, cultural state of the art, national prevailing custom is different with aesthetic standard and show different style characteristics.
in prior art, the method that the main raw material Wheat Straw making straw patchwork dyes green rust is had a variety of, but most dyestuff is chemical dye, the green rust dyed is impure, easily fade, not only not environmentally, some dyes even can produce toxic gas, the health of harmful to human in the process of dye system.
thus, make field at straw patchwork and lack a kind of vegetable dye Wheat Straw being dyed different colours, particularly Wheat Straw is dyed the natural plant dyestuff of green rust, not only color is pure for the green rust Wheat Straw that it dyes, the straw patchwork made with its material is bright and new beautiful, not easily fade, and environmental protection, works give out plant fragrance for a long time, there is the physical and mental health of easy people, harm that other poisonous and harmful chemical dye causes people's health in dye process processed that what degree was different solve.
summary of the invention:
the object of the present invention is to provide a kind of pure natural, pollution-free, environmental protection, the person is had no side effect prepare green rust wheat straw dye and production method by the one that natural plant is mixed with.
the object of the present invention is achieved like this.It is that the raw material of being joined by following weight is made, the blue 10-25 part of amaranth, blueberry 10-25 part, lavandula angustifolia 10-25 part, great Ye black apple leaf 5-15 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.
preparing green rust wheat straw dye preferred weight ratio range of the present invention is, wherein the weight proportion of various raw material is, the blue 10-20 part of amaranth, blueberry 10-20 part, lavandula angustifolia 10-20 part, great Ye black apple leaf 5-10 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.
the optimum weight ratio range preparing green rust wheat straw dye of the present invention is that wherein the weight proportion of various raw material is: blue 15 parts of amaranth, blueberry 15 parts, lavandula angustifolia 15 parts, great Ye black apple leaf 8 parts, alum 8 parts, ferric ion compounds solution 7 parts, mineral water 60 parts.
above-mentioned each component is made green rust wheat straw dye of the present invention and production method, technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the amaranth indigo plant, blueberry, lavandula angustifolia, great Ye black apple leaf, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, by the raw material selected except alum, ferric ion compounds solution, mineral water are cut into bulk respectively; C, oven dry, will be cut into block stock and be placed in stoving oven mummification respectively, temperature controls at 100-120 DEG C, 30 minutes time, evaporation raw material moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure green rust cellulose solution; H, dyeing, the temperature of 100 liters of pure green rust cellulose solutions is raised to more than 80 DEG C gradually, Wheat Straw after sterilization, desulfurization, boiling process is soaked wherein, constant temperature leaves standstill 12-14 hour, Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb peacock cyanine solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, at room temperature the slowly blue Wheat Straw finished product of dry pore-forming sparrow.
the invention has the advantages that: 1, select raw material, scientific formulation, color is pure; 2, do not add sanitas in product, industrial chemicals, pure natural, to human body without any injury, the straw patchwork works made with its raw material not only distribute Scent, and anticorrosive; 3 raw material sources are extensive, add process line short, the easy processing and manufacturing of product.
Embodiment
below in conjunction with specific embodiment, the present invention is further illustrated:
embodiment 1:
preparing green rust wheat straw dye weight proportion scope of the present invention is: the blue 10-25 part of amaranth, blueberry 10-25 part, lavandula angustifolia 10-25 part, great Ye black apple leaf 5-15 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.
embodiment 2:
preparing green rust wheat straw dye preferred weight ratio range of the present invention is: the blue 10-20 part of amaranth, blueberry 10-20 part, lavandula angustifolia 10-20 part, great Ye black apple leaf 5-10 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.
embodiment 3:
preparing green rust wheat straw dye optimum weight ratio range of the present invention is: blue 15 parts of amaranth, blueberry 15 parts, lavandula angustifolia 15 parts, great Ye black apple leaf 8 parts, alum 8 parts, ferric ion compounds solution 7 parts, mineral water 60 parts.
above-mentioned each component is made green rust wheat straw dye of the present invention and production method, technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the amaranth indigo plant, blueberry, lavandula angustifolia, great Ye black apple leaf, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, by the raw material selected except alum, ferric ion compounds solution, mineral water are cut into bulk respectively; C, oven dry, will be cut into block stock and be placed in stoving oven mummification respectively, temperature controls at 100-120 DEG C, 30 minutes time, evaporation raw material moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure green rust cellulose solution; H, dyeing, the temperature of 100 liters of pure green rust cellulose solutions is raised to more than 80 DEG C gradually, Wheat Straw after sterilization, desulfurization, boiling process is soaked wherein, constant temperature leaves standstill 12-14 hour, Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb peacock cyanine solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, at room temperature the slowly blue Wheat Straw finished product of dry pore-forming sparrow.
Claims (4)
1. prepare green rust wheat straw dye for one kind, it is characterized in that: it is made up of the raw material of following weight proportioning, the blue 10-25 part of amaranth, blueberry 10-25 part, lavandula angustifolia 10-25 part, great Ye black apple leaf 5-15 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.
2. prepare green rust wheat straw dye for one kind, it is characterized in that: wherein the weight proportion of various raw material is, the blue 10-20 part of amaranth, blueberry 10-20 part, lavandula angustifolia 10-20 part, great Ye black apple leaf 5-10 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.
3. prepare a green rust wheat straw dye, it is characterized in that: wherein the weight proportion of various raw material is, blue 15 parts of amaranth, blueberry 15 parts, lavandula angustifolia 15 parts, great Ye black apple leaf 8 parts, alum 8 parts, ferric ion compounds solution 7 parts, mineral water 60 parts.
4. the one according to claim 1-3 prepares green rust wheat straw dye and production method, it is characterized in that: technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the amaranth indigo plant, blueberry, lavandula angustifolia, great Ye black apple leaf, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, by the raw material selected except alum, ferric ion compounds solution, mineral water are cut into bulk respectively; C, oven dry, will be cut into block stock and be placed in stoving oven mummification respectively, temperature controls at 100-120 DEG C, 30 minutes time, evaporation raw material moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure green rust cellulose solution; H, dyeing, the temperature of 100 liters of pure green rust cellulose solutions is raised to more than 80 DEG C gradually, Wheat Straw after sterilization, desulfurization, boiling process is soaked wherein, constant temperature leaves standstill 12-14 hour, Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb peacock cyanine solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, at room temperature the slowly blue Wheat Straw finished product of dry pore-forming sparrow.