CN101033431A - Fast firing fuel and producing method thereof - Google Patents
Fast firing fuel and producing method thereof Download PDFInfo
- Publication number
- CN101033431A CN101033431A CN 200710077722 CN200710077722A CN101033431A CN 101033431 A CN101033431 A CN 101033431A CN 200710077722 CN200710077722 CN 200710077722 CN 200710077722 A CN200710077722 A CN 200710077722A CN 101033431 A CN101033431 A CN 101033431A
- Authority
- CN
- China
- Prior art keywords
- water
- cement
- clay
- wood chip
- fast firing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention discloses a quick ignition fuel and its production method, in which, the fuel is composed of the mateials in the following weight percentages: nitrate 4-6%, wood bits 10-25%, cement 5-7%, clay 8-15%, coal powder 20-30% and water, the nitrate is dissolved in water 1/3-1/2 to the gross water then wood bits, cement, clay and coal powder in the above mentioned ratio are added to be mixed fully then the rest water is added to adjust it to conglobation in hand to be molded by pressing and dried.
Description
Technical field
The present invention relates to the fuel field, relate in particular to a kind of pyrophoric fuel, also relate to the production method of this pyrophoric fuel simultaneously.
Background technology
Nonflammable during fuel ignition such as coal, coke, so often need to ignite with other material, pyrophoric fuel commonly used is oil, firewood etc.Oil is wayward, has potential safety hazard.And firewood is difficult for obtaining owing to the protection to ecotope.Above-mentioned two kinds of materials of igniting all are subjected to the influence of time, cause the failure of igniting if the time is controlled bad meeting.
Summary of the invention
The objective of the invention is to overcome above-mentioned shortcoming and a kind ofly lighting fast of providing, fast firing fuel that combustion time is long.
Another object of the present invention also is to provide the production method of this pyrophoric fuel.
A kind of fast firing fuel of the present invention is made by following weight percentages:.
Nitrate 4-6% wood chip (hay powder) 10-25% cement 5-7%
Clay 8-15% coal dust 20-30% surplus is a water.
Above-mentioned fast firing fuel, wherein: nitrate is saltpetre or SODIUMNITRATE.
Above-mentioned fast firing fuel, wherein:
Saltpetre 5.5% wood chip (hay powder) 15% cement 7%
Clay 12% coal dust 20% surplus is a water.
Above-mentioned fast firing fuel, wherein:
SODIUMNITRATE 5% wood chip (hay powder) 15% cement 7%
Clay 12% coal dust 20% surplus is a water.
The production method of fast firing fuel of the present invention comprises:
Nitrate is water-soluble, and the water yield is the 1/3-1/2 of Total Water, then the wood chip (hay powder) of said ratio, cement, clay and coal dust is added, and stirs and makes its thorough mixing, adds remaining water then and is adjusted to and holds agglomerating, promptly loosing of touching; Compression moulding, be drying to obtain.
The present invention compared with prior art, make setting agent with cement as can be known by such scheme, make in the drying process of pyrophoric fuel after moulding indeformable, to guarantee the intravital micropore of moulding, the carrying out that helps oozing chromatography is because nitrate mainly is distributed in the surface, make its initial stage of igniting than easy firing, burn from outside to inside, combustionvelocity is slack-off gradually, thereby prolongs the combustion time of pyrophoric fuel.But both family expenses also can be in industrial use, or is used for outdoor barbecue, heating.Thereby it is applied widely.
Embodiment
Embodiment 1: the production of cellular fast firing fuel
Take by weighing the raw material of following weight:
Saltpetre 5.5kg wood chip (hay powder) 15kg cement 7kg
Clay 12kg coal dust 20kg water 40.5kg
Saltpetre is dissolved in 13.5kg water, then above-mentioned wood chip (hay powder), cement, clay and coal dust is added, stir and make its thorough mixing, add remaining water then and be adjusted to and hold agglomerating, promptly loosing of touching; Be pressed into honeycomb type, be drying to obtain.
Embodiment 2: the production of sheet fast firing fuel
Take by weighing the raw material of following weight:
SODIUMNITRATE 5kg wood chip (hay powder) 15kg cement 7kg
Clay 12kg coal dust 20kg water 41kg
SODIUMNITRATE is dissolved in 20.5kg water, then above-mentioned wood chip (hay powder), cement, clay and coal dust is added, stir and make its thorough mixing, add remaining water then and be adjusted to and hold agglomerating, promptly loosing of touching; Be pressed into sheet type, be drying to obtain.
Embodiment 3: the production of column fast firing fuel
Take by weighing the raw material of following weight:
Saltpetre 6kg wood chip (hay powder) 25kg cement 6kg
Clay 8kg coal dust 20kg water 35kg
Saltpetre is dissolved in 17.5kg water, then above-mentioned wood chip (hay powder), cement, clay and coal dust is added, stir and make its thorough mixing, add remaining water then and be adjusted to and hold agglomerating, promptly loosing of touching; Be pressed into column type, be drying to obtain.
Embodiment 4: the production of spherical fast firing fuel
Take by weighing the raw material of following weight:
SODIUMNITRATE 4kg wood chip (hay powder) 10kg cement 5kg
Clay 15kg coal dust 30kg water 36kg
SODIUMNITRATE is dissolved in 14.5kg water, then above-mentioned wood chip (hay powder), cement, clay and coal dust is added, stir and make its thorough mixing, add remaining water then and be adjusted to and hold agglomerating, promptly loosing of touching; Be pressed into ball-type, be drying to obtain.
Claims (6)
1, a kind of fast firing fuel is made by following weight percentages:.
Nitrate 4-6% wood chip 10-25% cement 5-7%
Clay 8-15% coal dust 20-30% surplus is a water.
2, fast firing fuel as claimed in claim 1 is characterized in that:
Saltpetre 5.5% wood chip 15% cement 7%
Clay 12% coal dust 20% surplus is a water.
3, fast firing fuel as claimed in claim 1 is characterized in that:
SODIUMNITRATE 5% wood chip 15% cement 7%
Clay 12% coal dust 20% surplus is a water.
4, as the described fast firing fuel of one of claim 1-3, it is characterized in that: wood chip can substitute with hay powder.
5, as the production method of one of claim 1-3 described fast firing fuel, comprising:
Nitrate is water-soluble, and the water yield is the 1/3-1/2 of Total Water, then the wood chip of said ratio, cement, clay and coal dust is added, and stirs and makes its thorough mixing, adds remaining water then and is adjusted to and holds agglomerating, promptly loosing of touching; Compression moulding, be drying to obtain.
6, as the production method of one of claim 1-3 described fast firing fuel, wherein: wood chip can substitute with hay powder.