CN100343333C - Antistatic resin anchoring agent - Google Patents
Antistatic resin anchoring agent Download PDFInfo
- Publication number
- CN100343333C CN100343333C CNB2006100881902A CN200610088190A CN100343333C CN 100343333 C CN100343333 C CN 100343333C CN B2006100881902 A CNB2006100881902 A CN B2006100881902A CN 200610088190 A CN200610088190 A CN 200610088190A CN 100343333 C CN100343333 C CN 100343333C
- Authority
- CN
- China
- Prior art keywords
- clay
- weight
- resin anchoring
- agent
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to an antistatic resin anchoring agent prepared from clay and a curing agent, wherein the clay is prepared from the unsaturated resin of polyester, dimethylaniline, white carbon black obtained by a gas-phase method, stone powder and acetylene carbon black; the curing agent is prepared from water, stone powder, benzoyl peroxide, sodium carboxymethyl cellulose and acetylene carbon black. Because the acetylene carbon black as an antistatic agent is added to the clay and the curing agent, the clay and the curing agent have favorable antistatic performance. The antistatic resin anchoring agent can satisfy various production occasions having requirements to static electricity, and simultaneously, the antistatic resin anchoring agent has the advantages of simple production process and easy use and operation.
Description
Technical field:
The present invention relates to binding agent, particularly a kind ofly be widely used in that roadway support under the coal mine, pit gear are installed, building aseismicity is reinforced, the pedestal of equipment is fixed, the resin anchoring agent of engineerings such as hydro project bank protection, underground power house supporting and tunnel support.
Background technology:
Resin anchoring agent is as a kind of anchoring product, early is to be used under the coal mine in the supporting tunnel, but because its anchor force reaches easy construction by force, so also obtained using widely and promoting in other place.And when some special occasions is used, fixing as the precision machine tool pedestal, for to requirement of safe production, just the antistatic property to resin anchoring agent has had strict requirement, requires this product in use, does not produce static sparking.
The resin anchoring agent of present domestic use is formed by clay and solidifying agent two portions, generally also is called two component glue.During use clay and solidifying agent are mixed, clay and solidifying agent blended weight ratio are 1: 0.06~0.08; It is settable cementitious after for some time.The major ingredient of clay is polyester unsaturated polyester and stone flour.The resin anchoring agent of present domestic use does not all possess antistatic property.
Summary of the invention:
The present invention is for avoiding above-mentioned existing in prior technology weak point, a kind of antistatic resin anchoring agent being provided, to satisfy the service requirements of different occasions.
The technical scheme that technical solution problem of the present invention is adopted is:
A kind of antistatic resin anchoring agent is made up of by 1: 0.06~0.08 weight ratio clay and solidifying agent, it is characterized in that:
Described clay consisting of by weight:
Polyester unsaturated polyester 1000, xylidine 5~14, thermal silica 5~10,
Stone flour 4000~4500, Shawinigan black 30~60;
Described solidifying agent consisting of by weight:
Water 1000, stone flour 1000, benzoyl peroxide 50~80, Xylo-Mucine 200~300,
Shawinigan black 30~60.
Compared with the prior art, beneficial effect of the present invention is embodied in:
The present invention has been owing to added the static inhibitor Shawinigan black in clay, thereby makes clay have good antistatic performance, and is same, suffered at solidifying agent to have added the static inhibitor Shawinigan black, makes solidifying agent also possess good antistatic performance.The present invention has good antistatic performance, can satisfy the various uses that static had the production place of requirement.Simultaneously, production technique of the present invention is simple, uses easy to operate.
Verification experimental verification, antistatic property of the present invention reaches and is not more than 3 * 10
8Ω (being as the criterion) with test gained arithmetical av.
Embodiment:
The preparation clay
1, get the raw materials ready by any prescription of following weight part:
Polyester unsaturated polyester 1000, xylidine 5~14, thermal silica 5~10, stone flour 4000~4500, Shawinigan black 30~60;
2, aqueous material is dropped in the agitator stir earlier, powder is dropped in the agitator successively stir then, stir well even finished product, can is standby.
The preparation solidifying agent
1, get the raw materials ready by any prescription of following weight part:
Water 1000, stone flour 1000, benzoyl peroxide 50~80, Xylo-Mucine 200~300, Shawinigan black 30~60.
2, Xylo-Mucine is put into water by prescription requirements, soaks after 48 hours other material of input and stir jointly, put into colloidal mill after stirring and grind, be finished product until the one-tenth toothpaste-like, can is standby.
Embodiment 1:
Clay consisting of by weight: polyester unsaturated polyester 1000, xylidine 14, thermal silica 10, stone flour 4500, Shawinigan black 60;
Solidifying agent consisting of by weight: water 1000, stone flour 1000, benzoyl peroxide 80, Xylo-Mucine 300, Shawinigan black 60.
During use, clay: solidifying agent mixed by weight 1: 0.08 and fully stirs evenly.
Present embodiment ultimate compression strength is 60MPa, and the presetting period is 8~41 seconds, and its antistatic property can satisfy under the coal mine and to antistatic has the occasion of particular requirement to use, and cost is lower simultaneously.
Embodiment 2:
Clay consists of by weight: polyester unsaturated polyester 1000, xylidine 5, thermal silica 5, stone flour 4000, Shawinigan black 30;
Solidifying agent consists of by weight: water 1000, stone flour 1000, benzoyl peroxide 50, Xylo-Mucine 200, Shawinigan black 30.
During use, clay: solidifying agent mixed by weight 1: 0.07 and fully stirs evenly.
Present embodiment ultimate compression strength is 65MPa, and the presetting period is 41~90 seconds, and its antistatic property can satisfy under the coal mine and to antistatic has the occasion of particular requirement to use.
Embodiment 3:
Clay consisting of by weight: polyester unsaturated polyester 1000, xylidine 12, thermal silica 8, stone flour 4200, Shawinigan black 50;
Solidifying agent consisting of by weight: water 1000, stone flour 1000, benzoyl peroxide 70, Xylo-Mucine 250, Shawinigan black 50.
During use, clay: solidifying agent mixed by weight 1: 0.06 and fully stirs evenly.
Present embodiment anchoring agent intensity is 75MPa, and the presetting period is 91~180 seconds, and its antistatic property can satisfy under the coal mine and to antistatic has the occasion of particular requirement to use, and cost is lower simultaneously.
Solidifying agent mainly influences set time of the present invention to what of clay add-on, and when the solidifying agent add-on was big, shortened set time, and intensity slightly descends, otherwise prolongs set time, and intensity slightly raises; The add-on of stone flour is also slightly influential to intensity of the present invention in the clay, and when the stone flour add-on was big, intensity slightly descended, otherwise intensity slightly rises.In actual the use,, take the circumstances into consideration to change the blending ratio of prescription and clay and solidifying agent, satisfy the requirement of various production scenes according to processing requirement and envrionment temperature.
Claims (4)
1, a kind of antistatic resin anchoring agent is made up of by 1: 0.06~0.08 weight ratio clay and solidifying agent, it is characterized in that: described clay consisting of by weight:
Polyester unsaturated polyester 1000, xylidine 5~14, thermal silica 5~10,
Stone flour 4000~4500, Shawinigan black 30~60;
Described solidifying agent consisting of by weight:
Water 1000, stone flour 1000, benzoyl peroxide 50~80, Xylo-Mucine 200~300,
Shawinigan black 30~60.
2, antistatic resin anchoring agent according to claim 1 is characterized in that,
Described clay consisting of by weight:
Polyester unsaturated polyester 1000, xylidine 14, thermal silica 10,
Stone flour 4500, Shawinigan black 60;
Described solidifying agent consisting of by weight:
Water 1000, stone flour 1000, benzoyl peroxide 80, Xylo-Mucine 300, Shawinigan black 60.
3, antistatic resin anchoring agent according to claim 1 is characterized in that,
Described clay consisting of by weight:
Polyester unsaturated polyester 1000, xylidine 5, thermal silica 5,
Stone flour 4000, Shawinigan black 30;
Described solidifying agent consisting of by weight:
Water 1000, stone flour 1000, benzoyl peroxide 50, Xylo-Mucine 200, Shawinigan black 30.
4, antistatic resin anchoring agent according to claim 1 is characterized in that,
Described clay consisting of by weight:
Polyester unsaturated polyester 1000, xylidine 12, thermal silica 8,
Stone flour 4200, Shawinigan black 50;
Described solidifying agent consisting of by weight:
Water 1000, stone flour 1000, benzoyl peroxide 70, Xylo-Mucine 250, Shawinigan black 50.