CN101020328A

CN101020328A - Making process of ancient wood furniture and door with weathering effect

Info

Publication number: CN101020328A
Application number: CN 200610009136
Authority: CN
Inventors: 赵文
Original assignee: ZHANJIANG XINWEI HANDICRAFT CO Ltd
Current assignee: ZHANJIANG XINWEI HANDICRAFT CO Ltd
Priority date: 2006-02-13
Filing date: 2006-02-13
Publication date: 2007-08-22

Abstract

The making process of ancient wood furniture and door with weathering effect includes the following steps: producing members of wood furniture and door, burning the surface of the members in high temperature flame of 800-1100 deg.c for 0.5-1.2 sec, brushing off the charred soft xylem with a wire brush, assembling the product, burning the surface in high temperature flame of 800-1100 deg.c for 0.5-1.2 sec, brushing off the charred soft xylem with a wire brush to expose the heat resistant grain parts, and final integrally painting. The product has excellent grains and naturally weathered color.

Description

The manufacture method of a kind of weathering availability solid wood furniture modelled after an antique, timber

Technical field

The present invention relates to solid wood furniture, full Solid Door manufacturing field, the manufacture method of particularly a kind of weathering availability solid wood furniture modelled after an antique, timber.

Background technology

In furniture, the timber industry of wood products, solid wood furniture modelled after an antique, the traditional manufacture method of timber are:

1, timber is dried processing;

2, make each member of solid wood furniture, timber by specification;

3, overall package;

4, carrying out application by required antique effect paints;

5, whole topcoating.

Its weak point is an antique effect nature inadequately, fades easily, and has the slot part contraction back trough rim of going into of solid wood pond board member to expose solid wood plate primary colors (i.e. white) easily.

Summary of the invention

The objective of the invention is to overcome the prior art shortcoming, a kind of manufacture method that antique effect and solid wood pond plate show money or valuables one carries unintentionally because of contraction of having improved is provided.Utilize this method can significantly improve the weathering availability that belongs to natural primary color modelled after an antique of solid wood furniture, timber, reduce application oiling process program, processing is simple, and having solved solid wood pond board member well goes into slot part and exposes the defective of solid wood plate primary colors because of contraction makes trough rim, greatly improve product quality and product specification, created high value.

The present invention is achieved by following technical proposals:

1, be that 6～20% timber requires to make each member according to product specification with moisture content;

2, to containing solid wood pond board member in the product with the fire combustion equably rapidly in 0.5～1.2 second of 800～1100 ℃ high temperature naked light flame contact solid wood pond plate plate face, with wire brush monoblock solid wood pond plate is carried out scouring then, that wipes surface attachment is carbonized cork matter part, makes resistant to elevated temperatures wood grain part of not burnt highlight naturally;

3, overall package;

4, to product except that the plate of solid wood pond remaining part with the fire combustion equably rapidly in 0.5～1.2 second of 800～1100 ℃ high temperature naked light flame contact plate face, with wire brush monoblock solid wood pond plate is carried out scouring then, that wipes surface attachment is carbonized cork matter part, makes resistant to elevated temperatures wood grain part of not burnt highlight naturally;

5, whole topcoating.

The present invention adopts and earlier monoblock solid wood pond plate is carried out assembling after high-temperature process reaches weathering availability modelled after an antique, and then all the other members are carried out high-temperature process, thereby has solved following two problems:

1, having solved solid wood pond board member goes into slot part and exposes the defective of solid wood plate primary colors because of contraction makes trough rim;

2, make produced product keep the depth texture and the natural weathering primary colors of protolignin, and forever can not fade, weathering availability modelled after an antique is remarkable.

Description of drawings

Fig. 1 is the accompanying drawing of the embodiment of the invention

The specific embodiment

Be that the present invention is further illustrated for example below with the Solid Door

As shown in Figure 1, Solid Door has comprised upper and lower pond plate 2,5, the horizontal a tree, used in making timber for boats 1,4,8 in upper, middle and lower, upper and lower perpendicular a tree, used in making timber for boats 3,6, limit a tree, used in making timber for boats 7 members such as grade.At first each member of Solid Door is made by specification, first with on the monoblock before assembling then, lower storage reservoir plate 2, the thermal-flame contact chamber plate plate face that 5 usefulness are 800～1100 ℃, preferably temperature is 1000 ℃, fire combustion equably rapidly in 0.5～1.2 second, be preferably 1 second, with wire brush monoblock solid wood pond plate is carried out scouring again, that wipes surface attachment is carbonized cork matter part, make resistant to elevated temperatures wood grain part of not burnt highlight naturally, carry out overall package with other members then, after being assembled into as shown in Figure 1 finished product, to not burn carbonization other members (on, in, lower cross tiebeam 1,4,8, on, following perpendicular a tree, used in making timber for boats 3,6, limit a tree, used in making timber for boats 7) with 800～1100 ℃ thermal-flame contact plate face, preferably temperature is 1000 ℃, fire combustion equably rapidly in 0.5～1.2 second, golden hour is 1 second, with wire brush product is carried out scouring again, the wood grain part of not burnt is highlighted naturally, carry out whole topcoating then.

Make the weathering availability modelled after an antique of produced Solid Door present natural primary color and wooden depth texture like this, reduced the application process of painting, and the solid wood pond board member that makes Solid Door is gone into the color that slot part reveals when shrinking consistent with overall color, thereby make the quality of product be guaranteed with weathering availability modelled after an antique remarkable.

Claims

1, the manufacture method of a kind of weathering availability solid wood furniture modelled after an antique, timber is characterized in that may further comprise the steps:

1., be that 6～20% timber requires to make each member according to product specification with moisture content;

2., to containing solid wood pond board member in the product, high temperature naked light flame contact solid wood pond plate plate face fire combustion equably rapidly in 0.5～1.2 second with 800～1100 ℃, with wire brush monoblock solid wood pond plate is carried out scouring then, that wipes surface attachment is carbonized cork matter part;

3., overall package;

4., to product remaining part except that the plate of solid wood pond, with the fire combustion equably rapidly in 0.5～1.2 second of 800～1100 ℃ high temperature naked light flame contact plate faces, with wire brush monoblock solid wood pond plate is carried out scouring then, that wipes surface attachment is carbonized cork matter part;

5., whole topcoating.

2, the manufacture method of a kind of weathering availability solid wood furniture modelled after an antique according to claim 1, timber is characterized in that: described step 2., the high temperature naked light flame temperature in 4. is 900～1000 ℃.

3, the manufacture method of a kind of weathering availability solid wood furniture modelled after an antique according to claim 1, timber is characterized in that: described step 2., 4. the time with 900～1000 ℃ high temperature naked light flame contact plate face is 0.8～1.0 second.