CN104647550A - Antique-imitating weathering effect manufacturing method for solid wood - Google Patents
Antique-imitating weathering effect manufacturing method for solid wood Download PDFInfo
- Publication number
- CN104647550A CN104647550A CN201510071985.1A CN201510071985A CN104647550A CN 104647550 A CN104647550 A CN 104647550A CN 201510071985 A CN201510071985 A CN 201510071985A CN 104647550 A CN104647550 A CN 104647550A
- Authority
- CN
- China
- Prior art keywords
- solid wood
- raw material
- shot
- antique
- wood raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an antique-imitating weathering effect manufacturing method for solid wood, which solves the problems that an existing solid wood antique-imitating weathering effect manufacturing process is time-wasting, labor-wasting and high in labor cost, and a product is not good in antique-imitating weathering effect. The antique-imitating weathering effect manufacturing method comprises the following steps: (1) selecting corresponding solid wood raw materials according to the practical needs, putting the solid wood raw materials and steel shots into a shot blasting cleaning machine, and processing the solid wood raw materials through the shot blasting cleaning machine and the steel shots; (2) roasting the processed solid wood raw materials; (3) obtaining a molded product after roasting, and performing surface protective treatment on the molded product surface to obtain a solid wood product with an antique-imitating weathering effect. According to the antique-imitating weathering effect manufacturing method for the solid wood, the solid wood can have the antique-imitating weathering effect without manual processing, so that the production efficiency is improved, the batched antique-imitating weathering manufacturing of the solid wood is realized and the labor cost is reduced. Moreover, the solid wood is good in antique-imitating weathering effect and high in aesthetic sense and artistry. The antique-imitating weathering effect manufacturing method is very suitable for being popularized and applied.
Description
Technical field
The present invention relates to the method that a kind of solid wood weathering availability modelled after an antique makes.
Background technology
Along with the continuous progress of society, and the progressively raising of quality of the life, the demand of people to the art work is also more and more higher.The kind of the art work is very various, and the handicraft obtained after carrying out weathering modelled after an antique making to solid wood products (such as solid wood furniture, wooden process product goods of furniture for display rather than for use etc.) is exactly one wherein.The weathering modelled after an antique of so-called solid wood, be exactly by certain technological means, solid wood raw material is made into the archaizeding handicraft with unearthed relics weathering availability in ancient times, the patent application that such as application number is 200610009136.4, invention and created name is " manufacture method of a kind of weathering availability solid wood furniture modelled after an antique, timber " is exactly a kind of solid wood weathering manufacturing technology modelled after an antique wherein.What this technology adopted is, and high temperature burns, rub and mode that entirety is sprayed paint processes solid wood, thus obtains the solid wood products after weathering modelled after an antique.
At present, no matter be solid wood weathering making modelled after an antique on the market, or above-mentioned patent application technology, it is all adopt manual mode to process solid wood, thus makes solid wood possess the effect of weathering modelled after an antique.But, prior art processes owing to have employed manual mode, and home built quality is subject to impact and the restriction of producer's experience, therefore, existing solid wood weathering modelled after an antique preparation method all also exists several obviously defect, that is: waste time and energy, cost of labor is high and weathering availability modelled after an antique is not good.The impact caused thus is, existing solid wood weathering manufacture craft modelled after an antique is not only difficult to meet the collection requirement of consumer to solid wood archaizeding handicraft, and is difficult to for manufacturer brings more Multi benefit.
Summary of the invention
The method that the object of the present invention is to provide a kind of solid wood weathering availability modelled after an antique to make, mainly solve existing solid wood weathering modelled after an antique manufacture craft exist waste time and energy, the high and problem that product weathering availability modelled after an antique is not good of cost of labor.
To achieve these goals, under the present invention is based on a total inventive concept, have employed two cover technical schemes, as described below respectively:
Scheme one
The method that solid wood weathering availability modelled after an antique makes, comprises the following steps:
(1) select corresponding solid wood raw material according to actual needs, and together put in shot-blast cleaning machine by the shot of itself and 1 ~ 2 ton, 0.5 ~ 1.5mm specification, utilize shot-blast cleaning machine and shot to process solid wood raw material, process time is 1 ~ 10h;
(2) the solid wood raw material after processing is toasted, to guarantee that baking temperature is 100 ~ 120 DEG C, and baking time is 3 ~ 4h not containing moisture in solid wood raw material;
(3), after baking, obtain shaped article, then surface protection process is carried out to this shaped article, namely obtain the solid wood products with weathering availability modelled after an antique.
Further, in described step (1), while shot-blast cleaning machine is processed solid wood raw material, also open the deduster be connected with shot-blast cleaning machine, the dust produced when utilizing deduster to eliminate shot-blast cleaning machine process solid wood raw material.
Again further, in described step (1), if selected solid wood raw material wood is hard, then the shot of 2 tons of 0.5mm specifications is selected to put in shot-blast cleaning machine; If selected solid wood raw material wood is soft, then the shot of 1 ton of 1.5mm specification is selected to put in shot-blast cleaning machine; If selected solid wood raw material wood is neither too hard, nor too soft, then selects 40%, specification is 0.5mm and 60%, specification is 1.5mm and the shot that gross weight is 2 tons is put in shot-blast cleaning machine.
Specifically, in described step (3), process of spraying paint and paint is comprised to the surface protection process of shaped article.
Scheme two
The method that solid wood weathering availability modelled after an antique makes, comprises the following steps:
(1) select corresponding solid wood raw material according to actual needs, and together put in shot-blast cleaning machine by the shot of itself and 1 ~ 2 ton, 0.5 ~ 1.5mm specification, utilize ball blast processing machine and shot to process solid wood raw material, process time is 1 ~ 10h;
(2) the solid wood raw material after processing is toasted, to guarantee that baking temperature is 100 ~ 120 DEG C, and baking time is 3 ~ 4h not containing moisture in solid wood raw material;
(3) pattern drawn as required, allocates the texture of pattern and raw material;
(4) according to the pattern drawn, corresponding particular manufacturing craft is made;
(5) utilize particular manufacturing craft, according to deployed texture, roughing is carried out to solid wood raw material;
(6) according to the rough machined result of particular manufacturing craft, inside and outside repairing is carried out to solid wood raw material and casts processing, make corresponding position on solid wood raw material form the preliminary profile of pattern;
(7) fine design is carried out, the modular in design of finishing patterns to the pattern of the solid wood raw material after step (6) processing;
(8) inside and outside manual modification is carried out to the pattern of solid wood raw material, obtain shaped article;
(9) surface protection process is carried out to shaped article, namely obtain the solid wood products with weathering availability modelled after an antique.
Further, in described step (1), while shot-blast cleaning machine is processed solid wood raw material, also open the deduster be connected with shot-blast cleaning machine, the dust produced when utilizing deduster to eliminate shot-blast cleaning machine process solid wood raw material.
Again further, in described step (1), if selected solid wood raw material wood is hard, then the shot of 2 tons of 0.5mm specifications is selected to put in shot-blast cleaning machine; If selected solid wood raw material wood is soft, then the shot of 1 ton of 1.5mm specification is selected to put in shot-blast cleaning machine; If selected solid wood raw material wood is neither too hard, nor too soft, then selects 40%, specification is 0.5mm and 60%, specification is 1.5mm and the shot that gross weight is 2 tons is put in shot-blast cleaning machine.
Specifically, in described step (7), polishing comprised to the fine design of solid wood raw material, lines are modified, polish and repairing treatment.
Specifically, in described step (9), process of spraying paint and paint is comprised to the surface protection process of shaped article.
Compared with prior art, the present invention has following beneficial effect:
(1) the present invention adopts shot-blast cleaning machine and shot to process solid wood raw material, directly solid wood raw material surface can be processed the effect after weathering modelled after an antique, this has benefited from once chancing on of applicant, after finding that shot-blast cleaning machine may be used for realizing the purposes of solid wood raw material weathering modelled after an antique, applicant carried out deep research and test, define the machined parameters (shot specification is chosen, weight and process time) of various solid wood raw material, make various solid wood raw material all can produce the effect of weathering modelled after an antique.Thus, the new process equipment of Design and manufacture is carried out without the need to input cost, as long as determine kind and the quality of solid wood raw material, then ready-made shot-blast cleaning machine and shot is utilized can to produce solid wood weathering product modelled after an antique fast and automatically, so not only significantly shorten the home built time, save human cost, and completely not by the impact of producer's experience, its product processed is while the depth texture maintaining protolignin and weathering primary colors, the degree of depth of solid wood can also be processed arbitrarily, not by any restriction.Therefore, the present invention breaches the constraint of traditional solid sawn weathering manufacture craft modelled after an antique, for the high-quality of solid wood archaizeding handicraft, low cost and mass production provide very favorable opportunity, is that enterprise produces and creates more benefit to the full extent.
(2) the present invention is after utilizing shot-blast cleaning machine and shot to carry out weathering processing modelled after an antique to solid wood raw material, also solid wood is toasted, guarantee solid wood not containing any moisture, so can make solid wood raw material after making weathering handicraft modelled after an antique, possess the condition of persistence.
(3) the present invention has also carried out surface treatment to solid wood, and in guarantee, it while persistence, can improve one-tenth colourity and the quality of product, and then improve the reserve value of solid wood archaizeding handicraft effectively.
(4) the present invention is on the basis in conjunction with solid wood weathering modelled after an antique, have devised the technological process of Mold Making and hand engraving modification, any shape-designing of solid wood pattern and any combination collocation of more than one piece solid wood archaizeding handicraft can be realized, and the present invention also allocates on the texture of solid wood according to pattern, thus after in conjunction with kinds of processes mode, product expression not only can have been made to go out weathering availability modelled after an antique more true to nature, but also enhance aesthetic property and the artistry of product; Simultaneously, the present invention can also carry out personal customization according to consumer to the requirement of artistry flexibly, and therefore, it meets the various demands of archaizeding handicraft fan completely, really complied with the trend of development in science and technology, the present invention has very high practical value and promotional value.
Accompanying drawing explanation
Fig. 1 is the process chart of the present invention-embodiment 1.
Fig. 2 is the process chart of the present invention-embodiment 2.
Detailed description of the invention
Below in conjunction with drawings and Examples, the invention will be further described, and embodiments of the present invention include but not limited to the following example.
Embodiment 1
As shown in Figure 1, the invention provides a kind of method that the objects such as solid wood furniture, wooden process product goods of furniture for display rather than for use, solid wood carving root and solid wood potted landscape can be produced weathering availability modelled after an antique, its realization flow mainly comprises the selection of solid wood raw material, Raw material processing, the large step of product surface process three, as described below respectively.
One, the selection of solid wood raw material
Be one of topmost link to the selection of solid wood raw material, the quality of raw material is the basis of the shaping rear artistry of Product processing and sight.As a rule, solid wood raw material can be selected according to conditions such as the place of production of solid wood raw material, growth year, raw material varieties.
Two, Raw material processing
After having chosen solid wood raw material, the shot of itself and 1 ~ 2 ton, 0.5 ~ 1.5mm specification is together put in shot-blast cleaning machine, utilizes shot-blast cleaning machine and shot to process solid wood raw material.The step adopting shot-blast cleaning machine and shot to process solid wood raw material is extremely important, and it can directly make solid wood Raw material processing go out the effect of weathering modelled after an antique.What deserves to be explained is, this step finds after the once accidental operation error of applicant, because shot-blast cleaning machine is not that its existing purposes carries out sand removal, rust cleaning and descale to forge piece for processing solid wood raw material.And applicant has found the novelty teabag of shot-blast cleaning machine, so on this basis, applicant is after testing, and for multiple different solid wood raw material, the process time determining shot-blast cleaning machine is 1 ~ 10h.Meanwhile, applicant is also further it is well established that in the step of impeller blasting machined solid wood raw material, if selected solid wood raw material wood is hard, then preferably the shot of 2 tons of 0.5mm specifications is put in shot-blast cleaning machine; If selected solid wood raw material wood is soft, then preferably the shot of 1 ton of 1.5mm specification is put in shot-blast cleaning machine; If selected solid wood raw material wood is neither too hard, nor too soft, then preferably 40%, specification is 0.5mm and 60%, specification is 1.5mm and the shot that gross weight is 2 tons is put in shot-blast cleaning machine.
Further, for meeting the requirement of environmental protection, in the process of impeller blasting machined solid wood raw material, additionally using deduster and carrying out dedusting, to prevent contamination by dust surrounding environment.
After utilizing impeller blasting machined solid wood raw material, take out solid wood raw material, and it is toasted, to remove moisture wherein, enable product while having weathering availability modelled after an antique, possess the condition of persistence.In this baking procedure, baking temperature is 100 ~ 120 DEG C, and baking time is 3 ~ 4h.
Three, product surface process
After baking, need to carry out surface treatment to product, be specially spraying paint and painting of product surface, and be the processing requirements of satisfied different solid wood products, spray paint can adopt wax oil, japanning, varnish mode process.
After above-mentioned steps process, can obtain there is weathering availability modelled after an antique and quality and the high solid wood weathering product modelled after an antique of quality.
Embodiment 2
As shown in Figure 2, be only with the difference of embodiment 1, the solid wood products that the present embodiment processes, it be designed with pattern, and the design of product pattern and process as follows:
(1), after toasting solid wood, the pattern drawn as required, allocates the texture of pattern and solid wood raw material, and produces corresponding particular manufacturing craft (can adopt numerical control device processing and fabricating);
(2) after making particular manufacturing craft, according to deployed texture, utilize mould to carry out roughing to solid wood raw material, and coordinate the inside and outside modification processing of solid wood raw material, make the corresponding texture bits of solid wood raw material be set up the preliminary profile processing pattern;
(3) carry out fine design to the pattern of solid wood raw material, the modular in design of finishing patterns, the fine design in this step comprises the processing modes such as polishing, lines modification, polishing and repairing;
(4) again inside and outside manual modification is carried out to the pattern of solid wood raw material, shaping product can be obtained.
After obtaining shaped article, just in the same manner as in Example 1, surface treatment is carried out to product, obtain the figuratum solid wood of tool weathering handicraft modelled after an antique, finally handicraft is packed.The product that the present invention obtains can be independent artistic product, and also can be any combination collocation of the more than one piece art work, mainly different according to people requirements makes.
In addition, also it should be noted that, for the raw material of rotten wood shape, through of the present invention beautify processing after, it can become a goods of furniture for display rather than for use art work, so, just effectively improves the value of rotten wood, really achieves the effect of " change rotten wood be mystery ".And the present invention can also carry out large-area concavo-convex " negative and positive " engraving to the surface of carving root, goods of furniture for display rather than for use, furniture, makes it have extraordinary sight and artistry, all can display in any place such as household, exhibition room.
In addition, the goods of furniture for display rather than for use that the present invention processes as the base of various unearthed relics in ancient times (object such as such as bronze ware), thus can also show the characteristic of the simple and unsophisticated elegance of traditional Chinese culture and the long property of history more.
Through overtesting, the weathering modelled after an antique that the present invention also can be used for other wood furnitures, wood artwork and weathering wood raw material makes.
The present invention can carry out characteristic customization according to people to the requirement of artistry flexibly, its product made weathering availability modelled after an antique is very true to nature, not only significantly meet the collection demand of archaizeding handicraft fan, and preparation method is taken the course of its own, the production of mass can be realized, highly shortened the time of making, decrease the expenditure of cost of labor, and machining accuracy is very high, not by impact and the restriction of producer's experience, pattern forming effect is all good.Therefore, the present invention is compared with prior art, progressive fairly obvious, and it has outstanding substantive distinguishing features and significant progress.
Above-described embodiment is only the preferred two kinds of embodiments of the present invention; be not construed as limiting the scope of the present invention; in every case design principle of the present invention being adopted, and the change carried out non-creativeness work on this basis and make, all should belong within protection scope of the present invention.
Claims (9)
1. a method for solid wood weathering availability making modelled after an antique, is characterized in that, comprise the following steps:
(1) select corresponding solid wood raw material according to actual needs, and together put in shot-blast cleaning machine by the shot of itself and 1 ~ 2 ton, 0.5 ~ 1.5mm specification, utilize shot-blast cleaning machine and shot to process solid wood raw material, process time is 1 ~ 10h;
(2) the solid wood raw material after processing is toasted, to guarantee that baking temperature is 100 ~ 120 DEG C, and baking time is 3 ~ 4h not containing moisture in solid wood raw material;
(3), after baking, obtain shaped article, then surface protection process is carried out to this shaped article, namely obtain the solid wood products with weathering availability modelled after an antique.
2. the method for a kind of solid wood according to claim 1 weathering availability making modelled after an antique, it is characterized in that, in described step (1), while shot-blast cleaning machine is processed solid wood raw material, also open the deduster be connected with shot-blast cleaning machine, the dust produced when utilizing deduster to eliminate shot-blast cleaning machine process solid wood raw material.
3. the method for a kind of solid wood according to claim 1 and 2 weathering availability making modelled after an antique, is characterized in that, in described step (1), if selected solid wood raw material wood is hard, then selects the shot of 2 tons of 0.5mm specifications to put in shot-blast cleaning machine; If selected solid wood raw material wood is soft, then the shot of 1 ton of 1.5mm specification is selected to put in shot-blast cleaning machine; If selected solid wood raw material wood is neither too hard, nor too soft, then selects 40%, specification is 0.5mm and 60%, specification is 1.5mm and the shot that gross weight is 2 tons is put in shot-blast cleaning machine.
4. the method for a kind of solid wood according to claim 3 weathering availability making modelled after an antique, is characterized in that, in described step (3), comprise to the surface protection process of shaped article process of spraying paint and paint.
5. a method for solid wood weathering availability making modelled after an antique, is characterized in that, comprise the following steps:
(1) select corresponding solid wood raw material according to actual needs, and together put in shot-blast cleaning machine by the shot of itself and 1 ~ 2 ton, 0.5 ~ 1.5mm specification, utilize ball blast processing machine and shot to process solid wood raw material, process time is 1 ~ 10h;
(2) the solid wood raw material after processing is toasted, to guarantee that baking temperature is 100 ~ 120 DEG C, and baking time is 3 ~ 4h not containing moisture in solid wood raw material;
(3) pattern drawn as required, allocates the texture of pattern and raw material;
(4) according to the pattern drawn, corresponding particular manufacturing craft is made;
(5) utilize particular manufacturing craft, according to deployed texture, roughing is carried out to solid wood raw material;
(6) according to the rough machined result of particular manufacturing craft, inside and outside repairing is carried out to solid wood raw material and casts processing, make corresponding position on solid wood raw material form the preliminary profile of pattern;
(7) fine design is carried out, the modular in design of finishing patterns to the pattern of the solid wood raw material after step (6) processing;
(8) inside and outside manual modification is carried out to the pattern of solid wood raw material, obtain shaped article;
(9) surface protection process is carried out to shaped article, namely obtain the solid wood products with weathering availability modelled after an antique.
6. the method for a kind of solid wood according to claim 5 weathering availability making modelled after an antique, it is characterized in that, in described step (1), while shot-blast cleaning machine is processed solid wood raw material, also open the deduster be connected with shot-blast cleaning machine, the dust produced when utilizing deduster to eliminate shot-blast cleaning machine process solid wood raw material.
7. the method that the weathering availability modelled after an antique of a kind of solid wood according to claim 5 or 6 makes, is characterized in that, in described step (1), if selected solid wood raw material wood is hard, then selects the shot of 2 tons of 0.5mm specifications to put in shot-blast cleaning machine; If selected solid wood raw material wood is soft, then the shot of 1 ton of 1.5mm specification is selected to put in shot-blast cleaning machine; If selected solid wood raw material wood is neither too hard, nor too soft, then selects 40%, specification is 0.5mm and 60%, specification is 1.5mm and the shot that gross weight is 2 tons is put in shot-blast cleaning machine.
8. the method for a kind of solid wood according to claim 7 weathering availability making modelled after an antique, is characterized in that, in described step (7), comprises polishing, lines are modified, polishes and repairing treatment to the fine design of solid wood raw material.
9. the method for a kind of solid wood according to claim 8 weathering availability making modelled after an antique, is characterized in that, in described step (9), comprise to the surface protection process of shaped article process of spraying paint and paint.