CN101016209B - Low-temperature reinforcement ceramic - Google Patents
Low-temperature reinforcement ceramic Download PDFInfo
- Publication number
- CN101016209B CN101016209B CN200610054626.6A CN200610054626A CN101016209B CN 101016209 B CN101016209 B CN 101016209B CN 200610054626 A CN200610054626 A CN 200610054626A CN 101016209 B CN101016209 B CN 101016209B
- Authority
- CN
- China
- Prior art keywords
- porcelain
- firing
- temperature
- strengthening
- low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention is a kind of novel energy-saving ceramic low temperature fast firing strengthening porcelain.Using composite catalyst, facilitate crystal in 30 minutes to 45 minutes, temperature is between 1,000 1030 DEG C, and Fast Growth becomes porcelain.At present, the firing temperature of the most full porcelain is at 1,150 1360 DEG C, and the fastest firing time is 1 hour 4 hours.By comparison, low temperature fast firing strengthening porcelain reduces firing temperature, shortens firing time.Meanwhile, improve product quality, the whiteness of existing china and transparency, have again strengthening porcelain, the intensity of magnesia porcelain, also there is good heat stability.
Description
Technical field
The present invention relates to a kind of formula, change the process for calcining of traditional medium and high temperature, define a kind of new low temperature and burn
One-tenth method.
Background technology
At present, the flame that burns till both domestic and external is divided into oxidizing flame, reducing flame two kinds, and oxidizing flame firing temperature is 1,150 1360
Between DEG C, firing with reductive flame temperature is between 1,250 1400 DEG C.After using new formula, the low-temperature reinforcement ceramic burnt till with oxidizing flame
Firing temperature be only 1,000 1030 DEG C, and the porcelain color after burning till, neither the Bluish white of firing with reductive flame, is not oxygen
The yellow-white that change flame burns till, but milky therebetween, transparency is high, has a kind of naturally graceful quality.Meanwhile,
The product mechanical strength that this method is fired is between 180 220Mpa.
Summary of the invention
The invention mainly includes and have found a kind of new formula, solve the quick-fried base in the quick sintering procedure of low temperature and
Softening transform problem during porcelain, and make the product mechanical strength burnt till be not less than High-Temperature Strengthening porcelain.
Detailed description of the invention
1. formula
Serpentine 70 80%
Catalyst 20 30%
2. firing temperature 1,000 1030 DEG C
3. firing time 30 45min
4. technical target of the product
Transmittance 65 78%
Glossiness 55 65%
Hardness of glaze surface 6,500 7000
Machinery rupture strength 180 220Mpa
Water absorption rate 2 ‰
Heat stability 250 DEG C is put into 20 DEG C of water and does not splits for twice.
Beneficial effect
The invention has the beneficial effects as follows the saving energy, shorten firing time, improve kiln utilization rate 35 times, improve simultaneously
Product specification.
Claims (1)
1. a low temperature fast firing strengthening porcelain, its principal character is made up of serpentine and catalyst, and its percentage by weight is serpentine
70-80%；Its chemical composition of catalyst 20-30% see table:
Oxidation is burnt till: temperature 1000-1030 DEG C time: 30-45min.