CN101012362A - 汽车密封条用聚氨酯植绒胶的制备方法 - Google Patents
汽车密封条用聚氨酯植绒胶的制备方法 Download PDFInfo
- Publication number
- CN101012362A CN101012362A CN 200710036922 CN200710036922A CN101012362A CN 101012362 A CN101012362 A CN 101012362A CN 200710036922 CN200710036922 CN 200710036922 CN 200710036922 A CN200710036922 A CN 200710036922A CN 101012362 A CN101012362 A CN 101012362A
- Authority
- CN
- China
- Prior art keywords
- sealing strip
- preparation
- automobile sealing
- organic solvent
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及聚氨酯植绒胶技术领域,具体的说是一种汽车密封条用聚氨酯植绒胶的制备方法,将异氰酸酯或异氰酸酯混合物(A)、含两个或两个以上羟基的聚酯多元醇和含两个或两个以上羟基的聚醚多元醇混合物(B)、具有氨基或羟基的低分子化合物(C)、有机锡类催化剂(D)、高沸点有机溶剂(E)在50-100℃进行反应1~6小时,然后降温至20-35℃,加入有机溶剂(F)稀释至40-60%的固含量,过滤包装即得成品。与现有技术相比,本发明产品干燥速度适中、粘结牢度高等优点,适合不同工艺条件,降低了技术难度,原料环保,保证了汽车配件生产过程和成品的环保,保证了胶水本身生产过程无害。
Description
[技术领域]
本发明涉及聚氨酯植绒胶技术领域,具体的说是一种汽车密封条用聚氨酯植绒胶的制备方法。
[技术背景]
汽车密封条目前大多用橡胶、聚氯乙稀等制成,耐侯性能、密封性能和耐磨性能较差,用静电植绒技术和聚氨酯植绒胶喷涂技术可以解决这一问题,其中用了静电植绒技术以后,密封条的密封新能和耐磨性能大大提高,但是怎样将绒毛均匀植于密封条上,其中的胶水选择是个复杂的问题。
[发明内容]
本发明的目的是为了克服现有技术的不足,选用环保原料,降低技术难度,而设计的一种汽车密封条用聚氨酯植绒胶的制备方法。
为实现上述目的,提供一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:将异氰酸酯或异氰酸酯混合物(A)、含两个或两个以上羟基的聚酯多元醇和含两个或两个以上羟基的聚醚多元醇混合物(B)、具有氨基或羟基的低分子化合物(C)、有机锡类催化剂(D)、高沸点有机溶剂(E)在50-100℃进行反应1~6小时,然后降温至20-35℃,加入有机溶剂(F)稀释至40-60%的固含量,过滤包装即得成品。所述的异氰酸酯或异氰酸酯混合物(A)是以碳化二亚胺改性的二苯基甲烷二异氰酸酯或其和1,6-二次甲基二异氰酸酯的混合物。所述的含有两个或两个以上羟基的聚酯多元醇为经过100-130℃真空脱水后的聚己二酸乙二醇酯或聚己二酸丁二醇酯或聚己二酸乙二醇丁二醇酯中的一种或两种以上的混合物。所述的含有两个或两个以上羟基的聚醚多元醇为经过100-130℃真空脱水后的聚氧化丙稀二醇或聚醚三醇或聚四氢呋喃多元醇中的一种或两种以上的混合物。所述的具有氨基或羟基的低分子化合物(C)为1,4-丁二醇或1,6--己二醇或甲基丙二醇或乙二胺或三乙烯二胺或三羟甲基丙烷。所述的有机锡类催化剂(D)为二月硅酸二丁基锡或辛酸亚锡或二醋酸二丁基锡。所述的高沸点有机溶剂(E)是沸点在90℃以上的非芳烃类有机溶剂。所述的有机溶剂(F)为酮类和酯类的混合有机溶剂。
与现有技术相比,本发明产品具有干燥速度适中、粘结牢度高等优点,可以适合不同汽车配件厂的不同工艺条件,降低了技术难度,同时在原料选择上遵循环保要求,保证了汽车配件生产过程和成品的环保,还保证了胶水本身生产过程无害。
[具体实施方式]
下面对本发明作进一步说明,本发明对于本专业技术领域的人来说还是比较清楚地。
以碳化二亚胺改性的二苯基甲烷二异氰酸酯或其和1,6-二次甲基二异氰酸酯的混合物A,含两个或两个以上羟基的聚酯多元醇和聚醚多元醇混合物B、具有氨基或羟基的低分子化合物C、有机锡类催化剂D、高沸点有机溶剂E在50-100℃进行反应1~6小时,然后降温至20-35℃,再根据现场工艺的不同要求,加入相应的有机溶剂F稀释至40-60%的所需固含量,过滤包装即得成品。
按上述制备方法,用以下原料配比进行聚氨酯植绒胶的制备:
实施例1.
聚己二酸乙二醇丁二
液化MDI A 20-50g B 200-600g
醇酯
三羟甲基丙烷 C 5-35g T-12 D 0.1-0.5g
50-
醋酸丁酯 E 丁酮 F 30-500g
650g
30-
环己酮 F 醋酸乙酯 F 30-200g
200g
实施例2.
聚己二酸乙二醇酯和聚
液化MDI+HDI A 10-60g B 200-600g
氧化丙稀二醇混合物
1,4-丁二醇 C 10-50g T-12 D 0.1-0.5g
NN-二甲基甲酰胺 E 50-650g 丁酮 F 30-500g
环己酮 F 30-200g 醋酸乙酯 F 30-200g
实施例3.
聚己二酸丁二醇酯和聚液化MDI+HDI A 15-55g B 200-600g
氧化丙稀三醇混合物
二乙醇胺 C 5-30g T-12 D 0.1-0.5g
NN-二甲基甲酰胺 E 50-650g 丁酮 F 30-500g
环己酮 F 30-200g
由上述配方制得的聚氨酯植绒胶用于汽车密封条植绒后具有良好的耐水解性——植绒后室温下水浸泡7天无变化;还具有较高的粘结强度、良好的耐热性——80-100℃存放120h涂层无变化;耐磨性——绒毛耐磨仪,350g加重,耐磨次数>15000次;同时该植绒胶具有合适的干燥速度,胶体流平性佳,可同时满足机器和手工作业。
Claims (8)
1、一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:将异氰酸酯或异氰酸酯混合物(A)、含两个或两个以上羟基的聚酯多元醇和含两个或两个以上羟基的聚醚多元醇混合物(B)、具有氨基或羟基的低分子化合物(C)、有机锡类催化剂(D)、高沸点有机溶剂(E)在50-100℃进行反应1~6小时,然后降温至20-35℃,加入有机溶剂(F)稀释至40-60%的固含量,过滤包装即得成品。
2、如权利要求1所述的一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:所述的异氰酸酯或异氰酸酯混合物(A)是以碳化二亚胺改性的二苯基甲烷二异氰酸酯或其和1,6-二次甲基二异氰酸酯的混合物。
3、如权利要求1所述的一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:所述的含有两个或两个以上羟基的聚酯多元醇为经过100-130℃真空脱水后的聚己二酸乙二醇酯或聚己二酸丁二醇酯或聚己二酸乙二醇丁二醇酯中的一种或两种以上的混合物。
4、如权利要求1所述的一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:所述的含有两个或两个以上羟基的聚醚多元醇为经过100-130℃真空脱水后的聚氧化丙稀二醇或聚醚三醇或聚四氢呋喃多元醇中的一种或两种以上的混合物。
5、如权利要求1所述的一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:所述的具有氨基或羟基的低分子化合物(C)为1,4-丁二醇或1,6-己二醇或甲基丙二醇或乙二胺或三乙烯二胺或三羟甲基丙烷。
6、如权利要求1所述的一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:所述的有机锡类催化剂(D)为二月硅酸二丁基锡或辛酸亚锡或二醋酸二丁基锡。
7、如权利要求1所述的一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:所述的高沸点有机溶剂(E)是沸点在90℃以上的非芳烃类有机溶剂。
8、如权利要求1所述的一种汽车密封条用聚氨酯植绒胶的制备方法,其特征在于:所述的有机溶剂(F)为酮类和酯类的混合有机溶剂。