CN100591820C - Flax blended spinning preparation process - Google Patents
Flax blended spinning preparation process Download PDFInfo
- Publication number
- CN100591820C CN100591820C CN200710066826A CN200710066826A CN100591820C CN 100591820 C CN100591820 C CN 100591820C CN 200710066826 A CN200710066826 A CN 200710066826A CN 200710066826 A CN200710066826 A CN 200710066826A CN 100591820 C CN100591820 C CN 100591820C
- Authority
- CN
- China
- Prior art keywords
- flax
- rove
- float
- minutes
- asia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for producing flax blended yarn used in clothes and face fabric, comprising that: preparing flax long fiber into flax bars; combing bars via at least five processes; adding bamboo fibers into combining process, while the bamboo fibers are 8-75mass% of total blended yarn mass; combing them and drawing to prepare rove; boiling and bleaching the rove; spinning into spun yarn; drying, coiling and shaping. The invention has simple process, while the product has uniform bars, beautiful appearance and smooth surface.
Description
Technical field
The present invention relates to a kind of weaving techniques, especially a kind of manufacture craft that is used for the flax blended spinning of clothes and tame textile fabric.
Background technology
Flax is a kind of rare natural species, and it is strong that natural flax fiber has hygroscopicity, and radiate heat and ventilate is good, anti-mildew is mothproof, no static, no chemical composition, and unique bacteria growing inhibiting and the ultraviolet characteristic that penetrates of efficient obstruct, be " fiber queen " by common people's good reputation.But its outward appearance of the pure spinning of flax is comparatively coarse, and bar is done uneven, and spinnability is relatively poor, and color is relatively more dull, lackluster, Boardy Feeling and do not have smooth feeling.Simultaneously, there is certain technical difficulty in pure flax yarn of spinning high-count.
Summary of the invention
Technical problem to be solved by this invention be overcome deficiency of the prior art and provide a kind of do evenly, the manufacture craft of the flax blended spinning of good spinnability, feel smoother.
The present invention solves the problems of the technologies described above used technical scheme: the manufacture craft of this flax blended spinning is made ramie stripes with flax long fiber, through the above mixing in doubling step in five roads, in the 5th road drafting process, sneak into bamboo fibre, it is 8%, 40% or 75% that described bamboo fibre accounts for the blended yarn mass percent, both and close drawing-off after make rove, rove boiled floats, described boil to float comprise that the Asia is floated with oxygen and float two processes that process is floated for add the NaCLO of 1.5g/L earlier in water in the Asia
2, pH value 2.5-3.5, initial temperature is 30 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 25-40 minute after washing, finishes the Asia and floats; Carry out oxygen then and float, add the H of 3.5g/L
2O
2, pH value 10-10.5, initial temperature is 50 ℃, is warming up to 95 ℃ with 30 minutes, is incubated 30-40 minute after washing, finishes oxygen and floats, and makes spun yarn through spinning, then oven dry, winder moulding.
The present invention compared with prior art has following beneficial effect: manufacture craft is simple, can spin very thin high-count yarn, the flax blended spinning of gained has not only that advantage but also the bar that linen fibre itself had done evenly, good spinnability, gloss appearance degree are good, the feel smoother.
Description of drawings
Fig. 1 is a process chart of the present invention.
The specific embodiment
Embodiment 1
Referring to Fig. 1, ramie stripes about 18cm is made in the combing of flax long fiber, make described ramie stripes through the multiple tracks mixing in doubling step: in the first road drafting, the second road drafting, the 3rd road drafting, the 4th road drafting, constantly linen fibre to be carried out drawing-off and close, in the 5th road drafting process, sneak into bamboo fibre, described bamboo fibre length is even, accounting for the blended yarn mass percent is 8%, and bamboo fibre and ramie stripes drawing-off are also closed and made rove.Described rove boiled float, the described process of floating of boiling comprises that the Asia is floated with oxygen and floats two processes, adds the sodium chlorite NaCLO of 1.5g/L earlier in water
2, pH value 2.5, initial temperature are 30 ℃, are warming up to 50 ℃ with 30 minutes, are incubated 30 minutes after washings, carry out oxygen then and float, and add the oxydol H of 3.5g/L
2O
2, pH value 10, initial temperature is: 50 ℃, be warming up to 95 ℃ with 30 minutes, be incubated 35 minutes after washings.Boil the rove process spinning again after floating, constantly it is carried out drawing-off, make spun yarn, after the oven dry, the winder moulding.
Embodiment 2
Referring to Fig. 1, ramie stripes about 18cm is made in the combing of flax long fiber, make described ramie stripes through the multiple tracks mixing in doubling step: in the first road drafting, the second road drafting, the 3rd road drafting, the 4th road drafting, constantly linen fibre to be carried out drawing-off and close, in the 5th road drafting process, sneak into bamboo fibre, described bamboo fibre length is even, accounting for the blended yarn mass percent is 40%, and bamboo fibre and ramie stripes drawing-off are also closed and made rove.Described rove boiled float, the described process of floating of boiling comprises that the Asia is floated with oxygen and floats two processes, adds the sodium chlorite NaCLO of 1.5g/L earlier in water
2, pH value 3, initial temperature are 30 ℃, are warming up to 50 ℃ with 30 minutes, are incubated 40 minutes after washings, carry out oxygen then and float, and add the oxydol H of 3.5g/L
2O
2, pH value 10, initial temperature is: 50 ℃, be warming up to 95 ℃ with 30 minutes, be incubated 40 minutes after washings.Boil the rove process spinning again after floating, constantly it is carried out drawing-off, make spun yarn, after the oven dry, the winder moulding.
Embodiment 3
Referring to Fig. 1, ramie stripes about 18cm is made in the combing of flax long fiber, make described ramie stripes through the multiple tracks mixing in doubling step: in the first road drafting, the second road drafting, the 3rd road drafting, the 4th road drafting, constantly linen fibre to be carried out drawing-off and close, in the 5th road drafting process, sneak into bamboo fibre, described bamboo fibre length is even, accounting for the blended yarn mass percent is 75%, and bamboo fibre and ramie stripes drawing-off are also closed and made rove.Described rove boiled float, the described process of floating of boiling comprises that the Asia is floated with oxygen and floats two processes, adds the sodium chlorite NaCLO of 1.5g/L earlier in water
2, pH value 3.5, initial temperature are 30 ℃, are warming up to 50 ℃ with 30 minutes, are incubated 25 minutes after washings, carry out oxygen then and float, and add the oxydol H of 3.5g/L
2O
2, pH value 10.5, initial temperature is: 50 ℃, be warming up to 95 ℃ with 30 minutes, be incubated 30 minutes after washings.Boil the rove process spinning again after floating, constantly it is carried out drawing-off, make spun yarn, after the oven dry, the winder moulding.
Claims (1)
1, a kind of manufacture craft of flax blended spinning, it is characterized in that: flax long fiber is made ramie stripes, through the above mixing in doubling step in five roads, in the 5th road drafting process, sneak into bamboo fibre, it is 8%, 40% or 75% that described bamboo fibre accounts for the blended yarn mass percent, both and close drawing-off after make rove, rove is boiled floats, described boil to float comprise that the Asia is floated with oxygen and float two processes that process is floated for add the NaCLO of 1.5g/L earlier in water in the Asia
2, pH value 2.5-3.5, initial temperature is 30 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 25-40 minute after washing, finishes the Asia and floats; Carry out oxygen then and float, add the H of 3.5g/L
2O
2, pH value 10-10.5, initial temperature is 50 ℃, is warming up to 95 ℃ with 30 minutes, is incubated 30-40 minute after washing, finishes oxygen and floats, and makes spun yarn through spinning, then oven dry, winder moulding.